Root filling quality and bond strength of endodontic sealers to human and bovine dentin / Qualidade da obturação e resistência de união de cimentos endodônticos à dentina humana e bovina

Objetivo: Este estudo teve como objetivo comparar a qualidade da obturação e a resistência de união de dois cimentos endodônticos, AH Plus e Bio-C Sealer, em dentes humanos e bovinos. Métodos: Os canais radiculares de 60 dentes unirradiculares [30 humanos (H) e 30 bovinos (B)] foram preparados e obturados por condensação lateral da guta-percha e AH Plus (grupos AP-H e AP-B) ou Bio-C Sealer (grupos BC-H e BC-B). Seis fatias de 1,5 mm de espessura foram obtidas de cada raiz. Os espécimes foram observados em estereomicroscópio para avaliar a qualidade da obturação, considerando possíveis espaços vazios no material obturador. Posteriormente, as fatias radiculares foram avaliadas em termos de resistência de união por push-out e modo de falha. Os dados foram analisados pelos testes de Mann-Whitney e coeficientes de correlação de Spearman (α=5%). Resultados: A qualidade de obturação fornecida por AP e BC foi semelhante em ambos os substratos de dentina. No entanto, ao comparar dentes humanos e bovinos, os escores de espaços vazios foram maiores nas amostras bovinas, para ambos os cimentos. AP teve maior resistência de união à dentina humana e bovina do que BC. No entanto, não houve diferença significativa na resistência de união entre os substratos dentinários, para ambos os cimentos testados. Além disso, houve uma correlação positiva e moderada entre os valores de resistência de união de dentes humanos e bovinos. O modo de falha misto foi o mais prevalente. Conclusão: AP e BC fornecem qualidade de obturação semelhante, mas o primeiro apresenta maiores valores de resistência de união à dentina humana e bovina. A utilização de dentes bovinos como substitutos de amostras humanas parece ser adequada em estudos relacionados à resistência de união, mas não naqueles que testam a qualidade da obturação endodôntica.(AU)

Objective: This study aimed to compare the filling quality and bond strength of two endodontic sealers, AH Plus and Bio-C Sealer, in human and bovine teeth. Methods: The root canals of 60 [30 human (H) and 30 bovine (B)] single-rooted teeth were prepared and filled by lateral condensation of gutta-percha and AH Plus (groups AP-H and AP-B) or Bio-C Sealer (groups BC-H and BC-B). Six 1.5-mm-thick slices were obtained from each root. The specimens were observed under a stereomicroscope to assess filling quality, considering possible voids within the filling material. Subsequently, root slices were evaluated in terms of push-out bond strength and failure mode. Data were analyzed by Mann-Whitney tests and Spearman correlation coefficients (α=5%). Results: The filling quality provided by AP and BC was similar in both dentin substrates. However, when comparing human and bovine teeth, void scores were greater in the bovine samples, for both sealers. AP had higher bond strength to human and bovine dentin than BC. However, there was no significant difference in bond strength between dentin substrates, for both sealers tested. Also, there was a positive and moderate correlation between the bond strength values of human and bovine teeth. The mixed failure mode was the most prevalent. Conclusion: AP and BC provide similar filling quality, but the first presents higher bond strength values to human and bovine dentin. The use of bovine teeth as substitutes for human samples seems adequate in studies related to bond strength, but not in those testing root canal filling quality.(AU)

Influência da adição de partículas de vidro bioativas em adesivos resinosos, na cimentação de bráquetes ortodônticos / Influence of the addition of bioactive glass particles in resin adhesives in the cementation of orthodontic brackets

O objetivo deste estudo foi desenvolver e avaliar um adesivo resinoso modificado com a incorporação de partículas de vidro bioativas (SCHOTT Bioactive Glass) em diferentes concentrações. Foram avaliados a resistência ao cisalhamento (RU), o índice de remanescente dentário (IRA), o grau de conversão (GC) e a liberação de cálcio. Foram utilizados 50 incisivos bovinos que foram fixados, através de suas raízes, em um molde de PVC, com resina acrílica autopolimerizável. As amostras foram alocadas em 5 grupos (n=10): TXT - Adesivo Transbond XT (3M Unitek, Monrovia, CA, EUA) sem adição de partículas de vidro bioativas, TXT20, TXT30, TXT50 ­ Adesivo Transbond XT acrescido respectivamente de 20%, 30% e 50% de partículas de vidro bioativas e SH - Adesivo resinoso FL BOND ll (SHOFU Inc.) com biomaterial SPRG. As amostras receberam uma profilaxia com pedra pomes e condicionamento com ácido fosfórico à 37%. Em seguida foi aplicada uma fina camada do sistema adesivo indicado na face vestibular dos incisivos bovinos, em todos os grupos e fotopolimerizado por 20 segundos, utilizando-se um fotopolimerizador RADII-Cal (SDI, Victoria, Austrália). Depois foi aplicada uma pequena quantidade de pasta resinosa fotopolimerizável Transbond XT (3M Unitek, Monrovia, CA, EUA) sobre a superfície dos bráquetes autoligados (MORELLI, Sorocaba, São Paulo, Brasil) e estes foram devidamente colados na face vestibular, no centro da coroa clínica do incisivo bovino e fotopolimerizado por 20 segundos, em cada face. Posteriormente as amostras foram submetidas ao teste de resistência ao cisalhamento. O índice de remanescente adesivo foi avaliado em estereomicroscópio DISCOVERY V20 (ZEISS). Os adesivos resinosos foram submetidos ao teste de grau de conversão e liberação de cálcio. Os dados foram inicialmente submetidos ao teste de normalidade e depois submetidos ao teste de ANOVA um fator, seguido do teste de Tukey para análise de comparações múltiplas, com nível de significância de 0,05. De acordo com os resultados obtidos na resistência de união ao cisalhamento (MPa±Dp) a maior média foi observada no grupo TXT 19,50±1,40A, seguida do grupo TXT20 18,22±1,04AB, seguida do grupo SH 17,62±1,45B, seguida do grupo TXT30 14,48±1,46C e a menor média TXT50 14,13±1,02C. No grau de conversão a maior média foi observada no grupo TXT20 73,02±3,33A que foi estatisticamente semelhante ao grupo SH 68,50±1,09A, seguida do grupo TXT 60,28±1,06B e TXT30 58,84±4,06B e a menor média foi do grupo TXT50 40,67±1,21C.Para a liberação de cálcio a maior média foi TXT50 2,23±0,11D, seguida por TXT30 0,74±0,00C, TXT20 0,55±0,00B, SH 0,47±0,04B e TXT 0,14±0,00A. Concluiu-se que a incorporação de partículas de vidro bioativas influenciou na resistência de união ao cisalhamento, no grau de conversão e na liberação de cálcio (AU).

The objective of this study was to develop and evaluate a resin adhesive modified with the incorporation of bioactive glass particles (SCHOTT Bioactive Glass) in different concentrations. Shear bond strength (SBS), adhesive remnant index (ARI), degree of conversion (DC) and calcium release were evaluated. Fifty bovine incisors were used, which were fixed through their roots in a PVC mold with self-curing acrylic resin. The samples were allocated into 5 groups (n=10): TXT ­ Transbond XT Adhesive (3M Unitek, Monrovia, CA, USA) without addition of bioactive glass particles, TXT20, TXT30, TXT50 ­ Transbond XT Adhesive rescpectively increased by 20%, 30% and 50% bioactive glass particles and SH ­ FL BOND ll resin adhesive (SHOFU Inc.) with SPRG biomaterial. The samples received prophylaxis with pumice stoe and conditioning with 37% phosphoric acid. Then, a thin layer of the indicated adhesive system was applied to the buccal surface of the bovine incisors, in all groups, and light cured for 20 seconds, using a RADII-Call curing light (SDI, Victoria, Australia). Then, a small amount of Transbond XT light-curing resinous paste (3M Unitek, Monrovia, CA, USA) was applied on the surface of the self-ligating brackets (MORELLI, Sorocaba, São Paulo, Brazil) and these were duly bonded on the buccal surface, in the center of the clinical crown of the bovine incisor and light cured for 20 seconds, on each side. Subsequently, the samples were submitted to the shear bond test. The adhesive remnant index was evaluated using a DISCOVERY V20 stereomicroscope (ZEISS). The resin adhesives were submitted to the degree of conversion and calcium release test. The data were initially submitted to the normality test and then submitted to the one-way ANOVA test, followed by the Tukey test for analysis of multiple comparisons, with a significance level of 0.05. According to the results obtained in the shear bond strength (MPa±Dp), the highest average was observed in the TXT group 19.50±1.40A, followed by the TXT20 group 18.22±1.04AB, followed by the SH group 17.62±1.45B, followed by the TXT30 group 14.48±1.46C and the lowest mean TXT5014.13±1.02C. In the degree of conversion, the highest average was observed in the TXT20 73.02±3.33A group, wich was statiscally like the SH group 68.50±1.09A, followed by the TXT 60.28±1.06B and TXT30 group 58.84±4.06B and the lowest mean was for the TXT50 group 40.67±1.21C. For calcium release, the highest mean was TXT50 2.23±0.11D, followed by TXT30 0.74±0.00C, TXT20 0.55±0.00B, SH 0.47±0.04B and TXT 0.14±0.00A. It was concluded that the incorporation of bioactive glass particles influenced in the shear bond strength, in the degree of conversion and in the release of calcium (AU).

Effect of time and dental substrate on the bond strength of a universal adhesive system: in vitro study / Efeito do tempo e do substrato dental na resistência de união de um sistema adesivo universal: estudo in vitro

Introduction: Dentin adhesives provide union between the dental substrate and composite resin, but this union can be influenced by the cleaning agent. Objective: Evaluate the use of ozonated water as a cavity cleaning solution. Material and method: 40 bovine dental crowns were selected, divided into four groups: AD (dentin cleaning with distilled water) and AO (dentin cleaning with ozonized distilled water). Each group was divided into two storage periods (24h and 30 days) kept at 37 °C. The selected universal system adhesive was employed according to the manufacturer's instructions and light cured for 20 seconds. At that time, three cylinders were made (Tygon matrix with an internal diameter of 2 mm and a height of 2 mm) of composite resin in the crowns in the cervical, médium, and incisal regions and light cured for 30 seconds. After storage, the bonding strength was tested by micro-shear, and fracture type analysis was performed. The data were submitted to statistical analysis using the Shapiro-Wilk test with a significance level of 95%, ANOVA, and Turkey. Result: There was a statistically significant difference between the bond strength values, only in the intergroup analysis for the time of 24 hours, between the middle third of the groups (LDAO24 = 2.70 (± 2.39); LDAO30 = 3.82 (± 2.31)). The predominant fracture type for both groups was an adhesive fracture, except in the medium and incisal thirds of the AD, which was a cohesive dentin fracture. Conclusion: The utilization of ozone did not change the bond strength adhesive.

Introdução: Os adesivos dentinários proporcionam união entre o substrato dental e resina composta, porém esta união pode ser influenciada pelo agente de limpeza. Objetivo: Avaliar a influência na resistência de união (RU) de um sistema adesivo universal associado à da água ozonizada como solução de limpeza cavitária. Material e método: Foram selecionadas 40 coroas de dentes anteriores bovinos divididos em 4 grupos: AD (limpeza dentinária com água destilada) e AO (limpeza dentinária com água destilada ozonizada). Cada grupo foi subdividido em outros dois grupos de acordo com o tempo de armazenamento (24h e 30 dias) armazenados a 37ºC. A limpeza dentinária foi realizada por meio de uma seringa de 60mL de cada solução e fricção por 10 segundos. O sistema adesivo universal selecionado foi aplicado de acordo com as instruções do fabricante e fotoativado por 20 segundos. Em seguida, foram confeccionados 3 cilindros (matriz Tygon com um diâmetro interno de 2 mm e 2 mm de altura) de resina composta nas coroas nas regiões cervical, média e incisal e fotoativados por 30 segundos. Após o armazenamento foi realizado o teste de RU por microcisalhamento e análise do tipo de fratura. Os dados coletados foram submetidos a análise estatística através do teste de Shapiro Wilk com nível de significância de 95%, ANOVA e Tukey. Resultado: Houve diferença estatística significativa entre os valores de RU apenas na análise intergrupos para o tempo de 24 horas, entre o terço médio dos grupos (LDAO24 = 2,70 (± 2,39); LDAO30 = 3,82 (± 2,31)). O tipo de fratura predominante para ambos os grupos em todos os tempos foi de fratura adesiva, com exceção ao terço médio e incisal do AD, que foi fratura coesiva de dentina. Conclusão: A utilização do ozônio não alterou a resistência de união adesiva.

Antimicrobial efficacy of S-PRG containing toothpastes on S. mutans biofilm development / Eficácia antimicrobiana de dentifrícios contendo S-PRG sobre o desenvolvimento de biofilme de S. mutans

Objective: to investigate the antimicrobial effects of toothpastes containing bioactive surface pre-reacted glass particles (S-PRG) on S. mutans biofilms adherence, initial colonization and maturation. Material and Methods: a reference UA 159 and a clinical S. mutans (SM6) strain were used. Bovine enamel specimens were randomly allocated into the groups (n=5): toothpastes containing 0%; 1%; 5%; 20%; 30% S-PRG; positive control dentifrice (NaF+triclosan); and negative control (distilled water). For biofilm development, samples were placed in a 24-well plate containing artificial saliva (4h), followed by adding 1mL of artificial saliva, BHI broth and 225µL of S. mutans suspension. Treatments with toothpastes were applied previously or after 4h and 24h of biofilm formation. Samples were incubated for 48h at 37°C in 5%CO2 and biofilm was detached and seeded in Petri dishes for determining the number of viable cells. Data were analyzed by ANOVA and Tukey test (5%). Results: significantly lower microorganisms' adherence (p<0.05) was obtained for all S-PRG toothpastes, with similar results to NaF+triclosan for SM6 and 20 and 30%S-PRG groups exhibiting higher inhibition effect than the NaF+Triclosan for UA159. Antibacterial effect on the early-stage biofilm was also observed for the S-PRG groups, but was not superior to the NaF+Triclosan toothpaste. For the mature biofilm, the effective antimicrobial potential of S-PRG toothpastes was observed only for the SM6 clinical strain, but was not higher than the positive control. Conclusion: experimental S-PRG toothpastes were effective to inhibit S. mutans biofilm growth by exhibiting antimicrobial activity, being promising agents to prevent cariogenic biofilm development (AU)

Objetivo: investigar o efeito de dentifrícios contendo S-PRG sobre a colonização inicial e maturação de biofilmes de S. mutans. Material e Métodos: uma cepa de referência (UA 159) e uma cepa clínica de S. mutans (SM6) foram utilizadas. Espécimes de esmalte bovino foram alocados nos grupos (n=5): dentifrícios contendo 0%; 1%; 5%; 20% e 30%S-PRG; controle positivo (NaF+triclosan); e controle negativo (água destilada). Os espécimes foram inseridos em uma placa de 24 poços contendo saliva artificial (4h), seguido por adição de 1mL de saliva artificial, BHI, 225µL de suspensão de S. mutans e foram tratados com suspensões de dentifrícios antes ou depois de 4 e 24h da formação do biofilme. Os espécimes foram incubados por 48h e o biofilme foi removido dos espécimes e semeado em placas de Petri para contagem de UFC/mL. Os dados foram analisados por ANOVA e teste de Tukey (5%). Resultados: houve diminuição na adesão de microrganismos para os grupos tratados com S-PRG (p<0.05). Para SM6, os dentifrícios contendo S-PRG apresentaram resultados semelhantes ao NaF+triclosan e para a cepa UA159 o dentifrício com 30%S-PRG apresentou efeito superior. Efeito antimicrobiano no biofilme recém-formado (4h) foi observado para os grupos contendo S-PRG, mas não foi observado efeito superior ao NaF+Triclosan. Para o biofilme maduro, efeito antimicrobiano do S-PRG foi observado apenas para a cepa clínica, mas não superior ao efeito do NaF+Triclosan. Conclusão: dentifrícios contendo S-PRG foram eficazes na inibição do desenvolvimento de biofilmes de S. mutans, sendo promissores agentes para prevenir o desenvolvimento de biofilme cariogênico. (AU)

Análise de metodologias para avaliação da solubilidade do cimento à base de silicato de cálcio Bio-C Sealer / Analysis of methodologies for evaluating the solubility of calcium silicate-based sealer Bio-C Sealer

Introdução: Cimentos endodônticos à base de silicato de cálcio demonstram maior solubilidade em água destilada. Emprego de metodologias alternativas pode auxiliar em melhor compreensão sobre a solubilidade desses materiais. Objetivo: Avaliar o efeito da solução de imersão e do tipo de modelo experimental na solubilidade de cimento pronto para uso Bio-C Sealer. Material e método: Modelos circulares de polietileno ou dentina bovina (n = 16) foram confeccionados. Após inserção do cimento, os espécimes foram mantidos em estufa a 37 °C por 48 horas. Posteriormente, as amostras foram pesadas em balança de precisão para determinação da massa inicial. Na sequência, os espécimes foram imersos em 7,5 mL de água destilada (pH 6,5) ou PBS (pH 7,0) (n = 8) por 28 dias. Após isso, as amostras foram removidas das soluções e pesadas a cada 24 horas até a estabilização da massa final (0,001g). Corpos de prova confeccionados com Bio-C Sealer foram empregados como controle. A solubilidade foi avaliada de acordo com a diferença entre a massa inicial e final em porcentagem. Teste ANOVA Two-Way e teste post-hoc de Tukey foram realizados (α = 0,05). Resultado: Imersão em água destilada proporcionou maior solubilidade em comparação com PBS, independentemente do modelo experimental (p < 0,05). Corpos de prova apresentaram maior solubilidade, seguidos dos modelos de polietileno e dentina imersos em água destilada (p < 0,05). Não houve diferença entre os modelos experimentais imersos em PBS (p > 0,05). Conclusão: Bio-C Sealer apresenta solubilidade significativamente maior em água destilada do que em PBS em todas condições. Modelo experimental empregando dentina bovina e PBS como solução de imersão demonstra diminuir a perda de massa de Bio-C Sealer e pode ser uma alternativa valiosa para avaliar a solubilidade de cimentos biocerâmicos

Introduction: Calcium silicate-based sealers demonstrate greater solubility in distilled water. The use of alternative methodologies can help at better understanding the solubility of these materials. Objective: To evaluate the effect of the immersion solution and the type of experimental model on the solubility of readyto-use Bio-C Sealer. Material and method: Circular models of polyethylene or bovine dentin (n = 16) were made. After insertion of the sealer, the specimens were kept in an oven at 37°C and 95% humidity for 48h. Subsequently, the samples were weighed on a precision balance to determine the initial mass. Next, the specimens were immersed in 7.5 mL of distilled water (pH 6.5) or PBS (pH 7.0) (n = 8) for 28 days. After that, the samples were removed from the solutions and weighed every 24 hours until the final mass stabilized (0.001g). Test specimens made with Bio-C Sealer were used as a control. Solubility was evaluated according to the difference between the initial and final mass in percentage. Two-Way ANOVA test and Tukey post-hoc tests were performed (α=0.05). Result: Immersion in distilled water provided greater solubility compared to PBS regardless of the experimental model (p<0.05). The test specimens showed greater solubility, followed by polyethylene and dentin models immersed in distilled water (p<0.05). There was no difference between the experimental models immersed in PBS (p>0.05). Conclusion: Bio-C Sealer presents significantly greater solubility in distilled water than in PBS under all conditions. Experimental model using bovine dentin and PBS as an immersion solution demonstrates reduction in the mass loss of Bio-C Sealer and can be a valuable alternative for evaluating the solubility of bioceramic sealers

A new proposal for evaluating of the solubility of bioceramic materials in dentin tubes after immersion in PBS: a laboratory investigation / Nova proposta para avaliação da solubilidade de materiais biocerâmicos em tubos de dentina após imersão em PBS: um estudo laboratorial

Introdução: Materiais reparadores devem apresentar baixa solubilidade. Solução salina tamponada com fosfato (PBS) permite simular condição clínica e interação com dentina pode ser importante para correta avaliação da perda de massa de cimentos biocerâmicos. Objetivo: Avaliou o efeito da imersão em água destilada (AD) ou PBS na solubilidade de Bio-C Repair (BCR, Angelus) ou MTA Repair HP (MTAHP, Angelus) usando modelo de tubo de dentina. Material e método: Tubos de dentina bovina foram confeccionados com 4 mm de comprimento, 1,5 mm de diâmetro interno e 1 mm aproximadamente de espessura de parede. Os espécimes foram imersos em AD por 24h, posteriormente preenchidos com BCR ou MTAHP (n = 14) e armazenados em estufa a 37°C e umidade 95% por 24h. Após serem pesados em balança de precisão para determinação da massa inicial, os corpos de prova foram imersos em AD (pH 6,5) ou PBS (pH 7,0) (n = 7) por 28 dias. Tubos vazios também foram utilizados para o cálculo de perda de massa da dentina (n=4). Após esse período, os espécimes foram pesados até a estabilização da massa final (0,001g). A solubilidade de cada material foi avaliada. Testes estatísticos ANOVA e Tukey foram realizados (α=0,05). Resultado: BCR e MTAHP apresentaram ganho de massa em AD e perda de massa em PBS (p<0,05). Conclusão: A solução de imersão influencia a solubilidade de BCR e MTAHP usando modelo de tubo de dentina. Nova proposta metodológica poderá ser uma alternativa às normas ISO para testar a solubilidade de cimentos biocerâmicos

Introduction: Repair materials must have low solubility. Phosphate buffered saline (PBS) allows simulating clinical condition and interaction with dentin may be important for the correct evaluate of mass loss of bioceramic cements. Objective: To evaluate the effect of distilled water (DW), or PBS immersion on the solubility of Bio-C Repair (BCR, Angelus) or MTA Repair HP (MTAHP, Angelus) using a dentin tube model. Material and method: Bovine dentin tubes with a length of 4 mm, an internal diameter of 1.5 mm and walls thickness of approximately 1 mm were made. The specimens were immersed in DW for 24h, then filled with BCR or MTAHP (n = 14) and stored in an oven at 37°C and 95% humidity for 24h. After being weighed on a precision balance to determine the initial mass, the specimens were immersed in DW (pH 6.5) or PBS (pH 7.0) (n = 7) for 28 days. Empty tubes also were used for calculating the mass loss of the dentin (n=4). After this period, the specimens were weighed until stabilization of the final mass occurred (0.001g). The solubility of each material was evaluated. ANOVA and Tukey statistical tests were performed (α=0.05). Result: BCR and MTAHP showing gain of mass in DW and mass loss in PBS (p<0.05). Conclusion: The immersion solution influenced the solubility of BCR and MTAHP using dentin tube model. The new methodological proposal could be an alternative to ISO standards for testing the solubility of bioceramic cement

Efeito de dentifrícios com alta concentração de flúor na remineralização de substrato dentário com cárie artificial / Effect of toothpaste with high fluoride concentration on remineralization of dental substrate with artificial caries

Introduction: fluoride toothpaste is widely used by the population. Objective: dentifrices with a high concentration of sodium fluoride and the presence of tricalcium phosphate were developed, providing additional protection to patients vulnerable to the development of caries. This study aimed to evaluate the influence of different dentifrices on the surface and internal hardness and enamel wear after artificial caries, pH cycling, and toothbrushing. Material and method: enamel blocks (4x4 mm) were obtained from 20 bovine teeth. The specimens were submitted to artificial caries lesion and then to pH cycling and brushing according to the dentifrice: Colgate Total 12 and Clinpro + Tricalcium Phosphate. Result: after this period, they were submitted to analysis of superficial and internal hardness and profilometry. Scanning Electron Microscopy (SEM) was performed. The data obtained were evaluated by one-way Analysis of Variance (ANOVA) to evaluate the mineral recovery and profilometry, and two-way repeated measures ANOVA to evaluate the superficial and internal hardness. Conclusion: analyzing the surface hardness, after caries induction, there was a significant reduction in hardness that was partially recovered regardless of the dentifrice used. For internal hardness, Clinpro obtained lower values on the control side and up to 90 micrometers on the test side. As for profilometry, Colgate Total 12 showed greater wear when compared to Clinpro. It was concluded that Clinpro promoted lower internal hardness, however, Colgate Total 12 resulted in greater surface wear of tooth enamel.

Introdução: dentifrícios fluoretados são amplamente utilizados pela população. Foram desenvolvidos dentifrícios com alta concentração de fluoreto de sódio e presença de tricálcio fosfato, fornecendo proteção adicional a pacientes vulneráveis ao desenvolvimento da cárie. Objetivo: o objetivo deste estudo foi avaliar a influência de diferentes dentifrícios na dureza superficial, interna e desgaste do esmalte após cárie artificial, ciclagem de pH e escovação. Material e método: blocos de esmalte (4x4 mm) foram obtidos a partir de 20 dentes bovinos. Os espécimes foram submetidos à lesão de cárie artificial e, em seguida, à ciclagem de pH e escovação de acordo com o dentifrício: Colgate Total 12 e Clinpro + Tricálcio Fosfato. Após este período, foram submetidos à análise de dureza superficial e interna e perfilometria. Foi realizada microscopia eletrônica de varredura. Resultado: os dados obtidos foram avaliados por ANOVA um critério para avaliar a recuperação mineral e perfilometria, ANOVA dois critérios medidas repetidas para avaliar a dureza superficial e interna. Conclusão: analisando a dureza superficial, após a indução da cárie houve uma redução significativa na dureza que foi parcialmente recuperada independente do dentifrício utilizado. Para dureza interna, Clinpro obteve valores menores no lado controle e até 90 micrômetros no lado teste. Quanto à perfilometria, o Colgate Total 12 apresentou maior desgaste quando comparado ao Clinpro. Concluiu-se que Clinpro promoveu menor dureza interna, porém, o Colgate Total 12 resultou em maior desgaste superficial do esmalte dentário.

The effectiveness of EDTA 17% as a cleaning solution for the fiber post space after filling with cements

Aim: To evaluate the resistance of the union between a glass fiber post and radicular dentine after cleaning the root with 17% EDTA and filling with different endodontic cements. Methods: Forty uniradicular bovine incisors were removed to obtain root lengths of 18 mm. Endodontic treatment was performed on all roots using different filling cements (zinc oxide and eugenol-based, OZE; cement based on epoxy resin, AH) and cleaning solutions (saline, SA or EDTA), which made it possible to obtain four groups: OZESA, OZEEDTA, AHSA and AHEDTA. Subsequently, 12 mm of filling material was removed from the roots, and they were prepared to receive fiber posts luted with resin cement. To execute the mechanical cycles (2x106 cycles, 90 N, 4 Hz), coronal reconstruction was performed with a silicon matrix. The roots were then sliced (2-mm thick) to perform the push-out test. The results were analyzed using analysis of variance (one factor and two factors) and Tukey's test (α=0,05). Results: Bond strength (Mpa) was significantly higher for OZEEDTA (9,18) and AHEDTA (8,70) than for OZESA (6,06) AHSA (8,7). OZEEDTA also presented the highest values in the cervical region (15,18) but was significantly lower in the apical region (2,99). However, AHEDTA had a homogeneous bond strength in all thirds. Conclusion: Regardless of the endodontic cement used, EDTA was used as an irrigating solution, culminating in a higher bond strength between the glass fiber post and dentin

Avaliação da resistência adesiva de restaurações indiretas em resina composta com ou sem uso de material forrador após remoção seletiva da dentina / Evaluation of the adhesive strength of indirect composite resin restorations with or without the use of linear material after selective removal of dentin

O objetivo deste estudo foi analisar a resistência de união de restaurações indiretas cimentadas em superfícies dentinárias desmineralizadas com simulação da remoção seletiva da dentina com e sem uso de material forrador. Foram utilizados 60 dentes bovinos com a superfície vestibular desgastada até dentina sadia e divididos em quatro grupos: dentina sadia (controle), dentina desmineralizada (des), dentina desmineralizada e selada com resina flow (des-flow) e dentina desmineralizada e coberta com cimento de inonômero de vidro (des-civ). Todos os espécimes receberam condicionamento com ácido fosfórico (37% Condac, FGM) previamente a hibridização com adesivo universal (Single Bond Universal; 3M). O grupo des-civ recebeu uma cobertura de cimento de ionômero de vidro previamente ao condicionamento e hibridização e o grupo des-flow recebeu um selamento com resina flow (Resina Filtek Z350 XT Supreme Flowable, 3M) após condicionamento e hibridização. Em sequência, foram cimentadas peças simulando restaurações indiretas em resina composta (Grandioso ­ VOCO) na região condicionada de cada amostra. O conjunto recebeu fotoativação por 60 segundos em cada face da peça cimentada. Após 48 horas da cimentação, os espécimes dos três primeiros grupos foram submetidos aos testes mecânicos de tração, com velocidade de 1 mm/min. E após 29 dias, o quarto grupo foi submetido ao mesmo teste. A análise do tipo de fratura foi realizada por estereomicroscopia e os dados foram convertidos em MPa. Os resultados apresentaram diferença estatística de acordo com o teste ANOVA a 1 fator (p=0,011). Para as comparações múltiplas, o teste de Tukey apontou que o grupo des-flow apresentou valores menores do que o grupo controle. Todas as outras comparações foram similares. Concluiu-se que o grupo des-flow, quando comparado ao grupo controle, apresentou uma adesão inferior e que os materiais forradores não diferiram entre si (AU)

The aim of this study was to analyze the bond strength of cemented indirect restorations on demineralized dentin surfaces by simulating selective dentin removal with and without the use of a liner material. Sixty bovine teeth were used with the buccal surface worn down to healthy dentin and divided into four groups: healthy dentin (control), demineralized dentin (des), demineralized dentin sealed with flow resin (desflow) and demineralized dentin covered with glass ionomer cement (des-civ). All specimens were etched with phosphoric acid (37% Condac, FGM) prior to hybridization with universal adhesive (Single Bond Universal; 3M). The des-civ group received a glass ionomer cement cover prior to etching and hybridization, and the desflow group received a flowable resin seal (Filtek Z350 XT Supreme Flowable Resin, 3M) after etching and hybridization. Subsequently, specimens simulating indirect composite resin restorations (Grandioso - VOCO) were cemented in the etched region of each sample. The set was photoactivated for 60 seconds on each side. 48 hours after cementation, the specimens from the first three groups were subjected to mechanical tensile testing at a speed of 1 mm/min. After 29 days, the fourth group was subjected to the same test. The analysis of the fracture type was performed by stereomicroscopy and the data were converted into MPa. The results showed statistical difference according to the one-way ANOVA (p=0.011). For multiple comparisons, the Tukey's test showed that the des-flow group presented lower values than the control group. All other comparisons were similar. It was concluded that the des-flow group, when compared to the control group, presented lower adhesion and that the liner materials did not differ among themselves.(AU)

Avaliação da influência de diferentes configurações de bases de bráquetes na força de remoção e remanescente de resina / Evaluation of the influence of different bracket bases designs on debonding force and resin remnant

Resumo A produção contemporânea de bráquetes ortodônticos inclui tecnologia de injeção, com diferentes desenhos de base de colagem que interferem, diretamente, na força de adesão ao esmalte e na facilidade de remoção posterior. O objetivo foi avaliar a resistência ao cisalhamento de bráquetes metálicos de três diferentes bases de colagem, verificando a força necessária para descolagem e o remanescente de resina na base do bráquete. Foram utilizados 30 dentes bovinos, colados com bráquetes U-Clip (Orthometric, Marília, SP, Brasil); ID-ALL (ID-Logical, São José do Rio Preto, SP, Brasil) e Mini Twin, (3M ESPE, St Paul, Minnesota, EUA). Todos os bráquetes foram colados com a resina Transbond XT®, (3M ESPE, St Paul, Minnesota, EUA). Após a colagem, os corpos de prova foram submetidos ao teste de cisalhamento, com registro das forças de descolagem e, posteriormente, foram avaliados o adesivo remanescente e o padrão de falha em um estereomicroscópio óptico. As forças de cisalhamento foram semelhantes entre os grupos U-Clip e ID-ALL, que foram estatisticamente diferentes do grupo Mini-Twin. Os bráquetes U-Clip e Mini-Twin apresentaram todo o remanescente de resina aderido à base do bráquete, enquanto o bráquete ID-ALL apresentou mais da metade do remanescente aderido à base do bráquete, resultado estatisticamente significante. Conclui-se os bráquete nacionais apresentam menor força de cisalhamento, estatisticamente significante quando comparados ao bráquete Mini-Twin. O bráquete ID-ALL apresentou o menor remanescente de resina, denotando que a fratura ocorreu na camada de resina, enquanto que nos grupos U-Clip e Mini-Twin, a fratura ocorreu na interface resina/esmalte. (AU)

Abstract The contemporary production of orthodontic brackets includes injection technology, with different designs of bonding bases that interfere directly with the bond strength to enamel and the ease of subsequent removal. The aim was to evaluate the shear bond strength of metal brackets of three different bonding bases, checking the force required for debonding and the rates of resin remaining on the bracket base. The sample consisted of 30 bovine teeth bonded with brackets U-Clip (Orthometric, Marília, SP, Brazil), ID-ALL (ID-Logical, São José do Rio Preto, SP, Brazil), and Mini Twin (3M ESPE, St Paul, Minnesota, USA). All brackets were bonded with Transbond XT resin (3M ESPE, St Paul, Minnesota, USA). After bonding, the specimens were subjected to a shear bond test. The forces required for debonding were recorded. Posteriorly, the remaining adhesive and failure patterns were evaluated in an optical stereomicroscope. The shear forces were similar for U-Clip and ID-ALL, which were significantly different from the Mini-Twin group. The U-Clip and Mini-Twin brackets showed the resin remnant totally adhered to the bracket base, while the ID-ALL bracket had more than half of the resin remnant attached to the bracket base, a statistically significant result. It was concluded that shear forces were lower for the national brackets, statistically significant. Bracket ID-ALL had the least resin remnant in the base, denoting that the fracture occurred in the resin layer. In contrast, in the U-Clip and Mini-Twin brackets groups, the fracture occurred at the resin/enamel interface (AU)

Effects of dentinary contamination by endodontic irrigants on bonding strength of adhesive systems

This study aimed to evaluate if 2.5% sodium hypochlorite compromises the adhesion of bonding materials. The factors in the study were the irrigation solutions in two levels: 2.5% sodium hypochlorite and saline solution; and the adhesive systems used in three levels: three-step adhesive, universal adhesive, and two-step self-etch adhesive systems. The answer variable used was the microshear bond strength obtained through a universal testing machine and fracture mode. Six groups were obtained (n=10) : Etch-and-rinse/Saline (saline solution + 3-step adhesive system - Scotchbond Multipurpose, 3M ESPE); Universal/saline (saline solution + universal adhesive system ­ Prime&Bond,); Self-etch/saline (saline solution + 2-step self-etch adhesive systems - Clearfil SE Bond); Etch-and-rinse/Hypo (sodium hypochlorite 2,5% + 3-step adhesive system - Scotchbond Multiuso); Universal/Hypo (sodium hypochlorite 2,5% + universal adhesive system ­ Prime&Bond); Self-etch/Hypo (sodium hypochlorite 2,5% + 2-step self-etch adhesive system - Clearfil Se Bond). The specimens were obtained from 60 healthy bovine incisors. The crowns were separated from the roots, and the regularization of the buccal surface was performed. The groups received saline solution and 2.5% sodium hypochlorite for 30 minutes, respectively. A matrix of 1mm and 3mm oh height was stabilized by Scotch tape to obtain the resin sticks. Afterward, the bond strength test was performed in a universal testing machine at 1mm/min speed. The data were analyzed with normality Shapiro-Wilk, two-way ANOVA, and Tukey's tests (p<0.001). Etch-and-rinse and Self-etch adhesives presented the highest bond strength values after irrigation with saline solution and 2.5% sodium hypochlorite, respectively (P < 0.01). The irrigation with 2.5% sodium hypochlorite decreased the bond strength values of Etch-and-rinse and Universal (P < 0.01). On the other hand, 2.5% sodium hypochlorite improved the bond strength values of Self-etch (P < 0.01). In conclusion, 2.5% sodium hypochlorite negatively impacted the bond strength of Etch-and-rinse and Universal but improved the adhesion of Self-etch.

Effect of Xylitol Varnishes on the Inhibition of Demineralization in Vitro

Abstract Objective: To evaluate the efficacy of xylitol varnishes in the inhibition of enamel demineralization in vitro. Material and Methods: Bovine enamel blocks (n=120) were randomly allocated to four groups (n = 30), and the surface hardness (SH) was measured at baseline. The blocks were treated with the following varnishes: 20% xylitol, 20% xylitol plus F (5% NaF), Duraphat™ (5% NaF, positive control), and placebo (no-F/xylitol, negative control). The varnishes were applied and removed after 6 h of immersion in artificial saliva. The blocks were subjected to pH cycles (demineralization and remineralization for 2 and 22h/day, respectively, for 8 days). Surface and cross-sectional hardnesses were measured to calculate the percentage of SH loss (%SHL) and the integrated loss of the subsurface hardness (ΔKHN). Data were statistically analyzed using Kruskal-Wallis and Tukey's tests (p<0.05). Results: %SHL was significantly decreased by 20% xylitol plus F, Duraphat™, and 20% xylitol varnishes compared to placebo. The use of 20% xylitol plus F varnish led to a significantly lower percentage of SH loss compared to the use of 20% xylitol varnish without F. However, the experimental and commercial varnishes led to significantly lower subsurface demineralization compared to placebo and did not differ from each other. Conclusion: Xylitol varnishes, especially when combined with F, effectively prevent enamel demineralization (AU).

Influence of customization and light-curing device on the bond strength of glass fiber posts - in vitro study / Influência da reanatomização e do aparelho fotopolimerizador na resistência de união de pinos de fibra de vidro - estudo in vitro

Introduction: Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective: An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method: Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result: For the customization factor, Tukey's test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion: The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.

Introdução: Dentes com extensa perda de estrutura podem comprometer a retenção das restaurações ao remanescente dental, onde pinos intraradiculares são indicados. Objetivo: Avaliou-se in vitro a união de pinos de fibra de vidro à dentina radicular em função de diferentes modos de reanatomização, fotopolimerizadores e regionalização radicular. Material e método: Noventa (n=10) raízes bovinas uniradiculares foram usadas num estudo fatorial 3 x 3 x 3 com parcelas subdivididas: Reanatomização do pino, variando a presença e tipo de resina (Sem reanatomização, Resina Convencional e Resina Bulkfill); Fotopolimerizador (Valo, Radii-cal, Rainbow); e Terço radicular (cervical, médio e apical). Resultado: O teste de Tukey (5%) evidenciou para o Fator Reanatomização superioridade dos grupos BulkFill (8.16MPa) e Z350 (7.40MPa) ao grupo Controle (4.92MPa), sem diferirem entre si. Todos os fotopolimerizadores diferiram entre si, com superioridade de Valo (9.36MPa), Radii (6.96MPa) intermediário, e inferioridade de Raiwbow (4.17MPa). O terço radicular cervical (7.81MPa) foi superior e o apical inferior (5.80MPa), com o terço médio (6.88MPa) intermediário e sem diferir dos demais. Conclusão: Conclui-se que a reanatomização de pinos de fibra de vidro aumenta a resistência de união à dentina radicular, independentemente da resina utilizada, havendo prejuízo no terço apical e quando são empregados fotopolimerizadores com menor intensidade luminosa.

Avaliação da membrana de colágeno de peixe na regeneração óssea guiada: estudo histológico, histomorfométrico, imunoistoquímico, micro tomográfico em calotas de ratos / Evaluation of fish collagen membrane in guided bone regeneration: histological, histomorphometric, immunohistochemical, micro tomographic study on ice caps rats

O processo de regeneração óssea guiada é amplamente conhecido na literatura, e para que essa técnica possa ser realizada com sucesso a escolha da barreira biológica no tocante ao seu tempo de degradação e sua reação tecidual é de fundamental importância. Assim, o objetivo deste estudo foi avaliar o processo de reparo de defeitos ósseos críticos em calotas de ratos, utilizando o princípio de osteopromoção, comparando a membrana teste de colágeno de peixe funcionalizando com hidroxiapatita com as membrana de colágeno bovino associada à hidroxiapatita e a membrana de colágeno porcino. Para o estudo foram utilizados 96 ratos Albinus Wistar, divididos em quatro grupos, sendo 24 animais para cada grupo: Grupos BG (BioGide®); CB (ColHap®); CP (colágeno de peixe) e CG (Coágulo) analisados em quatro tempos experimentais, 7, 15, 30 e 60 dias. Os resultados mostraram um perfil inflamatório maior no grupo CP em relação aos grupos BG e CB (p< 0,05) nos primeiros 15 dias. O grupo CP, aos 60 dias apresentou um bom potencial osteopromotor ao compará-lo com o grupo BG (p = 0,199) e o grupo CB demonstrou o menor desempenho osteopromotor. Na análise tridimensional, os resultados anteriores foram confirmados com o pior desempenho em relação a menor média detecido ósseo neoformado para o grupo CP de 9,560mm3 , CB com 11,850mm3 e BG 14,247mm3 (p< 0,05). Concluí-se que as membranas aqui estudadas tiveram um bom comportamento biológico, e todas auxiliaram no processo de regeneração óssea guiada e que a membrana de colágeno de peixe teve um bom desempenho na osteopromoção óssea(AU)

Guided bone regeneration is a widely described alveolar ridge augmentation technique that has been shown to produce excellent and reproducible results with high long-term success rates in several studies. Thus, this study aimed to evaluate the bone repair of critical size defects calavaria using an osteopromotive principle the fish collagen membrane functionalized with hydroxyapatite compare to collagen membrane associated with hydroxyapatite and porcine membrane. For the study, 96 Albinus Wistar rats were used, divided into four groups, with 24 animals for each group: Groups BG (BioGide®); CB (ColHap®); CP (fish collagen) and CG (clot) analyzed in four experimental times, 7, 15, 30 and 60 days. The results showed a higher inflammatory profile in the CP group compared to the BG and CB groups (p< 0.05) in the first 15 days after the surgery. The CP group, at 60 days, showed a good osteopromotor potential when compared with the BG group (p = 0.199) and the CB group showed the smaller osteopromotor performance. In the three-dimensional analysis, the previous results were confirmed with the worst performance in relation to the lowest mean of neoformed bone tissue for the CP group of 9.56mm3 , CB with 11.85mm3 and BG 14.247mm3 (p< 0.05). In conclusion with the results obtained by this work, the membranes studied here had a good biological behavior, and all of them helped in the guided bone regeneration process and the fish collagen membrane performed well in bone osteopromotion(AU)

Bond strength of different orthodontic brackets produced with different materials and fabrication methods / Resistência de união de bráquetes ortodônticos produzidos com diferentes materiais e métodos de fabricação

Objective: The aim of this study was to evaluate the effects of material and processing methods on the bond strength of orthodontic brackets. Material and Methods: Five types of brackets were tested: Conventional metallic (CM), metallic sandblasted (SB), ceramic (C), polycarbonate (PC), and metallic fabricated by melting injection molding (MIM). Shear bond strength (SBS) was conducted to check bond strength of the brackets bonded to bovine teeth (n=10/group), and tensile bond strength (TBS) (20 brackets/group) to check bracket retention to bonding material (n=20/group). Both, SBS and TBS were conducted with 1mm/min crosshead speed in a universal testing machine. Bond strength was calculated in Megapascal (MPa) based on force (N) and bracket area (mm 2). Data normality was verified, and One-way ANOVA was the statistical test with Tukey post-hoc (α=0.05). Results: SB and MIM presented higher SBS compared to C, PC, and CM (p<0.05). SB and MIM also presented significantly higher TBS compared to CM and PC (p<0.05). However, MIM was not different of C for TBS. Conclusion: The type of material and method of fabrication are determinant factors that affect bond strength of orthodontic brackets and melting injection molding (MIM) is a remarkable technology to improve brackets retention during the orthodontic treatment. (AU)

Objetivo: O objetivo deste estudo foi avaliar os efeitos dos materiais e métodos de processamento na resistência de união de bráquetes ortodônticos. Material e Métodos: Cinco tipos de bráquetes foram testados: Convencionais metálicos (CM), metálicos jateados (SB), cerâmico (C), policarbonato (PC), e metálico fabricado por injeção de metal fundido em molde (MIM). A resistência de união ao cisalhamento (SBS) foi conduzida para verificar a resistência de união dos bráquetes aderidos a dentes bonivos (n=10/grupo) e a resistência à tração (TBS) (20 bráquetes/grupo) para verificar a retenção do bráquete ao material adesivo (n=20/grupo). SBS e TBS foram conduzidas com relação carga/velocidade de 1mm/min em uma máquina de ensaios universal. A resistência de união foi calculada em Megapascal (MPa) com base na força (N) pela área do bráquete (mm 2). A normalidade dos dados e a estatística foi realizada utilizando One-way ANOVA e Tukey post-hoc (α=0.05). SB e MIM apresentaram os maiores valores de SBS comparados com C, PC e CM (p<0.05). Resultados: SB e MIM também apresentaram valores significativamente maiores de TBS comparados com CM e PC (p<0.05). Contudo, os valores de TBS para o grupo MIM não foram significativamente diferentes de C. Conclusão: O tipo de material e o método de fabricação são fatores determinantes que afetam a resistência de união de bráquetes ortodônticos e a injeção de metal fundido em molde (MIM) é uma tecnologia relevante para melhorar a retenção dos bráquetes durante o tratamento ortodôntico. (AU)

Efficacy of 30% and 38% Silver Diamine Fluoride in Arresting Caries Lesions After Different Application Times: An in Vitro Study

Abstract Objective: To evaluate the efficacy of silver diamine fluoride (SDF) in arresting dentin caries lesions when applied under different concentrations and times. Material and Methods: Forty-two bovine blocks were selected and fixed in 24-well plates. Each well received a mixed bacterial inoculum added to the culture medium with 5% sucrose. The plates were incubated in microaerophilia (7 days) for caries formation, confirmed by micro-CT (M1). SDF was applied over the carious lesions for different times and concentrations (n=6): SDF 30% - immediate removal, 1 minute and 3 minutes; SDF 38%, - immediate removal, 1 minute and 3 minutes. The group without treatment was the control. Then, the samples were again scanned by micro-CT (M2) and submitted to a second cariogenic challenge for 21 days. Then, a final scan was performed (M3). Results: Mean pH at the culture medium and lesion depth were compared using Kruskal-Wallis and Wilcoxon tests. 38% SDF showed the lowest metabolic activity of the biofilm. All 38% groups and 30% 1 and 3 minutes did not show an increase in mean lesion depth comparing M3 with M1. However, only 30% 3 minutes and 38% 1 and 3 minutes showed a significant reduction of lesion depth. Conclusion: The minimum application time of 30% SDF to arrest dentin caries lesion was 1 minute, while 38% SDF arrested with application and immediate removal.

Effect of desensitizing dentifrices on eroded dentin wettability / Efeito de dentifrícios dessensibilizantes na molhabilidade da dentina erodida

Objective: To analyze the wettability on the surface of eroded dentin in teeth submitted to abrasive wear with desensitizing dentifrices. Material and Methods: Bovine dentin specimens were polished and immersed in 10 mL of citric acid (pH=3.2) for 2 h. The eroded specimens were submitted to mechanic brushing according to the 4 dentifrices adopted: Colgate Total (control); Colgate Sensitive Pro-Relief; Sensodyne Repair & Protect; or Sensodyne Rapid Relief. Afterwards, it was conditioned in 37% aqueous phosphoric acid solution. Wettability of 80 specimens (n=10) brushed for 7 or 21 days was evaluated by measuring the contact angle between the dentin surface and a drop of the adhesive Single Bond Universal® (3M) with a goniometer. Changes in the surface morphology of 12 specimens (n = 3) brushed for 21 days were followed by confocal laser scanning microscopy (CLSM). Data were analyzed by two-way ANOVA and Tukey test (p > 0.05). Results: Groups treated with desensitizing dentifrices did not differ significantly (p ≤ 0.05). Surface treatment and abrasive wear did not interact significantly (p ≤ 0.05). Brushing along 7 days gave the smallest contact angle value (p ≥ 0.05). CLSM images showed morphological changes for all the groups. Conclusion: The desensitizing dentifrices did not interfere in eroded dentin wettability after brushing along 7 or 21 days. Brushing with any of the dentifrices along 21 days promoted open dentinal tubules.(AU)

Objetivo: Analisar a aplicação de um adesivo na superfície de dentina erodida em dentes submetidos ao desgaste abrasivo com agentes dessensibilizantes. Material e Métodos: Espécimes de dentina bovina foram polidos e imersos em 10 mL de ácido cítrico (pH=3,2) por 2 h. Os espécimes erodidos foram submetidos à escovação mecânica de acordo com os 4 dentifrícios adotados: Colgate Total (controle); Colgate Sensitive Pro-Alívio; Sensodyne Repair & Protect; ou Sensodyne Rápido Alívio. Em seguida, foram condicionados em ácido fosfórico a 37%. A molhabilidade de 80 espécimes (n=10) escovados por 7 ou 21 dias foi avaliada medindo-se o ângulo de contato entre a superfície dentinária com uma gota do adesivo Single Bond Universal® (3M) por um goniômetro. Alterações na morfologia da superfície de 12 espécimes (n = 3) escovados por 21 dias foram seguidos por Microscopia Confocal de Varredura a Laser (MCVL). Os dados foram analisados por ANOVA dois fatores e teste de Tukey (p > 0,05). Resultados: Os grupos tratados com dentifrícios dessensibilizantes não diferiram significativamente (p ≤ 0,05). O tratamento de superfície e o desgaste abrasivo não interagiram significativamente (p ≤ 0,05). A escovação ao longo de 7 dias apresentou o menor valor de ângulo de contato (p ≥ 0,05). As imagens do MCVL mostraram alterações morfológicas para todos os grupos. Conclusão: Os dentifrícios dessensibilizantes não interferiram na molhabilidade da dentina erodida após escovação ao longo de 7 ou 21 dias. A escovação com qualquer um dos dentifrícios ao longo de 21 dias promoveu a abertura dos túbulos dentinários (AU)

Restaurações diretas com materiais bioativos: observações clínicas, in vitro e revisão sistemática / Direct restorations with bioactive materials: clinical observations, in vitro and systematic review

O objetivo do ensaio clínico foi avaliar o desempenho clínico de 2 materiais bioativos (Cention N e EQUIA Forte) em comparação a resina composta. O estudo in vitro teve como objetivo avaliar o desenvolvimento de lesões de cárie induzida por desafio cariogênico bacteriano na margem de restaurações em esmalte e dentina com Cention N com e sem adesivo, EQUIA Forte e resina composta. A revisão sistemática teve como objetivo responder a seguinte pergunta: A avaliação clínica de restaurações em dentes permanentes com materiais bioativos evidencia maior sucesso do que restaurações com materiais não bioativos? Para o estudo clínico foram selecionados 120 participantes aleatoriamente divididos em 3 grupos (n=40), TC: Tetric N-Ceram, EF: EQUIA Forte, CN: Cention N. O preenchimento das cavidades foi realizado seguindo as indicações do fabricante. Foi utilizado o dispositivo de fluorescência DIAGNOdentTM Pen para avaliação da recorrência de cárie. No estudo in vitro foram confeccionados 100 espécimes a partir de dentes bovinos. Foram divididos em 5 grupos (n=20) metade em esmalte e metade em dentina: Cention N sem adesivo (CN), Cention N com adesivo (CA), EQUIA Forte (EF); Tetric N-Ceram (TC); e sem restauração (SR). Foram submetidos a envelhecimento térmico; leitura de microdureza Knoop (KHN) inicial, esterilizados e expostos a um desafio cariogênico com Streptococcus mutans por 28 dias. Lesões de cárie artificial foi quantificado por meio de KHN superficial e de subsuperfície, e análise com microscopia de luz polarizada. Os dados foram submetidos a ANOVA 1 fator e teste Tukey no esmalte e teste de Kruskal-Wallis na dentina. Em esmalte os grupos EF, CN, CA apresentaram menor porcentagem de perda da microdureza (%PMS) 57,85%, 63,88% e 66,65% respectivamente. Na dentina, EF, CN e CA apresentaram menores valores de %PMD sendo 31,7%, 34,1% e 40,8% respectivamente. Os valores mais altos de %PMS foram registrados para os grupos TC e SR tanto na dentina como no esmalte. Na revisão sistemática, com base na pergunta de pesquisa e estratégia PICO: P- Dentes permanentes, I- Restaurações (classe I, classe II, classe III, classe V) com materiais bioativos, C- Restauração com materiais não bioativos, O- Retenção; foi traçada a estratégia de busca. Após a obtenção dos estudos eles foram analisados por dois revisores independentes. No total foram 27 ensaios clínicos randomizados, com acompanhamento mínimo de 2 anos, foram os qualificados para realizar a revisão e meta-análise em rede. Os resultados de meta-análise em rede mostraram que em cavidades classe III cimento de ionômero de vidro modificado (CIV modificado), foi significativamente mais propenso a falhas do que a resina composta (RC), em restaurações classe I e II, o compômero foi significativamente mais propenso a falhas do que a RC e em restaurações classe V o cimento de ionômero convencional (CIV convencional) foi significativamente mais propenso a falhas do que o CIV modificado. No estudo in vitro foi evidente o maior potencial de inibição da desmineralização dos materiais bioativos. Na revisão sistemática ficou evidente que a maioria de materiais bioativos apresentam um bom comportamento, em relação as taxas de retenção e desempenho clínico. (AU)

The objective of the clinical trial was to evaluate the clinical performance of 2 bioactive materials (Cention N and EQUIA Forte) compared to composite resin. The in vitro study aimed to evaluate the development of caries lesions induced by bacterial cariogenic challenge at the margin of enamel and dentin restorations with Cention N with and without adhesive, EQUIA Forte and composite resin. The systematic review aimed to answer the following question: Does the clinical evaluation of restorations in permanent teeth with bioactive materials show greater success than restorations with nonbioactive materials? For the clinical study, 120 participants were randomly selected and divided into 3 groups (n=40), TC: Tetric N-Ceram, EF: EQUIA Forte, CN: Cention N. The filling of the cavities was performed following the manufacturer's instructions. The DIAGNOdentTM Pen fluorescence device was used to assess caries recurrence. In the in vitro study, 100 specimens were made from bovine teeth. They were divided into 5 groups (n=20) half in enamel and half in dentin: Cention N without adhesive (CN), Cention N with adhesive (CA), EQUIA Forte (EF); Tetric N-Ceram (TC); and without restoration (SR). They were subjected to thermal aging; initial Knoop microhardness (KHN) reading, sterilized and exposed to a cariogenic challenge with Streptococcus mutans for 28 days. Artificial caries lesions were quantified using surface and subsurface KHN and analysis with polarized light microscopy. Data were submitted to 1-way ANOVA and Tukey test on enamel and Kruskal-Wallis test on dentin. In enamel, groups EF, CN, CA had the lowest percentage of microhardness loss (%PMS) 57.85%, 63.88% and 66.65% respectively. In dentin, EF, CN and CA presented lower %PMD values, being 31.7%, 34.1% and 40.8% respectively. The highest %PMS values were recorded for the TC and SR groups in both dentin and enamel. In the systematic review, based on the research question and PICO strategy: P- Permanent teeth, I- Restorations (class I, class II, class III, class V) with bioactive materials, C- Restoration with non-bioactive materials, O- Retention; the search strategy was designed. After obtaining the studies, they were analyzed by two independent reviewers. In total, 27 randomized clinical trials, with a minimum followup of 2 years, were qualified to perform the review and network meta-analysis. The results of network meta-analysis showed that in class III cavities modified glass ionomer cement (modified GIC) was significantly more prone to failure than composite resin (RC), in class I and II restorations, the compomer was significantly more prone to failure than RC and in class V restorations the conventional ionomer cement (conventional GIC) was significantly more prone to failure than the modified GIC. In the in vitro study, the greatest potential for inhibiting the demineralization of bioactive materials was evident. In the systematic review it was evident that most bioactive materials have a good behavior in relation to retention rates and clinical performance (AU).

Braquetes cerâmicos impressos 3D: ensaio biomecânico da resistência ao cisalhamento / 3D printed ceramic brackets: biomechanical test: shear bond strength

Objetivo: Avaliar, por meio de um ensaio biomecânico, a resistência ao cisalhamento dos braquetes cerâmicos confeccionados em impressora 3D. Metodologia: Foram testados três tipos distintos de braquetes: Braquetes cerâmicos LightForce Clear® - 3D - LFO System®, (Cambridge, Massac ­ EUA) (n=10), neste trabalho denominado como grupo LFC, braquetes cerâmicos LightForceWhite® - 3D ­ LFO System® - (Cambridge, Massac ­ EUA) (n=10), neste trabalho denominado como grupo LFW, e braquetes cerâmicos Clarity® da 3M® ­ UNITEK (Monrovia, Califórnia ­ EUA) (n=10), neste trabalho denominado como grupo C. Os braquetes do grupo C foram utilizados como controle. Foram colados em esmalte bovino, fixados em suportes para realização de teste em máquina universal de cisalhamento com acessórios de garra para suporte. Foi aplicada uma carga inciso-apical sobre o braquete com célula de carga de 50kgf e velocidade de deslocamento de 1 mm/min até o surgimento de falha na interface dente-braquete. O valor de força de pico registrado foi considerado como a força de cisalhamento (N) necessária para romper a união dente-suporte. A resistência ao cisalhamento foi obtida, em MPa, dividindo a carga de ruptura, em Newtons, pela área da superfície em mm2 . A análise da fratura foi feita com aumento de 15x utilizando microscópio estereoscópio binocular Discovery V20 - Carl Zeiss® (Oberkochen, Alemanha). Análise estatística: Foi realizada análise de variância utilizando teste ANOVA. O teste Tukey foi aplicado para determinar quaisquer diferenças significativas para valores de desempenho entre os grupos. Resultados: Os valores médios e desvio padrão obtidos no ensaio de resistência ao cisalhamento (Mpa) nos três grupos de braquetes foram: 12,00 ± 5,26 para C, 16,45 ± 3,57 para LFC e 14,58 ± 5,04 para LFW. Não houve diferença estatística na resistência ao cisalhamento de nenhum dos grupos testados, os grupos LFC e LFW se mostraram semelhantes ao grupo C (controle). Conclusão: Os braquetes cerâmicos confeccionados em impressora 3D apresentaram resultados satisfatórios de SBS quando comparados ao grupo controle. Todos os grupos apresentaram fratura adesiva semelhante demonstrando boas retenções em suas bases (AU)

Objective: to evaluate the shear strength of ceramic brackets produced in a 3D printer by a biomechanical test. Methodology: Three different types of brackets were tested: LightForce Clear® ceramic brackets - 3D - LFO System®, (Cambridge, Massac - USA) (n=10), referred to as the LFC group in this paper, LightForceWhite® ceramic brackets - 3D - LFO System® - (Cambridge, Massac - USA) (n=10), referred to as the LFW group in this paper, and Clarity® ceramic brackets from 3M® - UNITEK (Monrovia, California - USA) (n=10), referred to as Group C in this paper. Group C brackets were used as controls. They were bonded to bovine enamel and attached to holders for testing in a universal machine with shear claw accessories. The bracket was loaded with a load cell of 50 kgf and a displacement speed of 1 mm/min until failure occurred at the tooth-bracket interface. The peak force recorded was considered to be the shear force (N) required to break the tooth-bracket junction. The shear strength in MPa was determined by dividing the fracture load in Newtons by the area in mm2. Fracture analysis was performed at 15x magnification using a Discovery V20 binocular stereoscopic microscope - Carl Zeiss® (Oberkochen, Germany). Statistical analysis: Analysis of variance was performed using ANOVA test. The Tukey test was applied to determine any significant differences for performance values between groups. Results: The mean values and standard deviation obtained in the shear strength test (Mpa) in the three groups of brackets were: 12.00 ± 5.26 for C, 16.45 ± 3.57 for LFC and 14.58 ± 5.04 for LFW. There was no statistical difference in the shear strength of any of the groups tested, the LFC and LFW groups were similar to group C (control). Conclusion: Ceramic brackets printed on a 3D printer showed satisfactory SBS results when compared to the control group. All groups presented adhesive fracture demonstrating good retention at their bases (AU)

Análise comparativa das características e qualidade do acabamento de superfície de preparo em dentina bovina com ultrassom piezoelétrico e pontas diamantadas de alta rotação / Comparative analysis of the characteristics and quality of the preparation surface finish in bovine dentin with piezoelectric ultrasound and high-speed diamond burs

O objetivo deste trabalho foi comparar, in vitro, as características e qualidade do acabamento de superfície em dentes bovinos, através da análise de rugosidade superficial e análise de imagens em Microscopia Eletrônica de Varredura (MEV). Apesar de amplamente utilizadas, as pontas diamantadas apresentam limitações como baixa durabilidade e suas repetidas esterilizações causam diminuição da capacidade de corte. Com o surgimento das pontas odontológicas de diamante CVD (Chemical Vapor Deposition), sua indicação tem sido ampliada como alternativa, pois associadas a aparelhos de ultrassom apresentam boa resistência ao desgaste. Oitenta dentes bovinos foram selecionados para este estudo e foram divididos em oito grupos de acordo com o tipo de ponta utilizada para confecção do desgaste do preparo protético: Grupo I ­ ponta diamantada KG nº2135 acoplada em alta rotação (AR) grupo controle; Grupo II - ponta diamantada KG nº2135 (AR), ponta diamantada CVDentus CR4 acoplada em ultrassom (US); Grupo III - ponta diamantada KG nº2135 (AR), ponta diamantada CVDentus CR4 seguida da ponta CR4U, acopladas em US; Grupo IV ­ ponta diamantada KG nº2135 (AR), ponta diamantada TR18-H CVDentus AR; Grupo V ­ ponta diamantada KG nº2135 acoplada em AR, seguido de broca carbide multilaminada 30 lâminas de acabamento de preparo, acopladas em baixa rotação; Grupo VI­ ponta diamantada KG nº2135 (AR), seguido de broca carbide multilaminada 30 lâminas e finalização com ponta de borracha, Grupo VII - ponta diamantada KG nº2135 (AR), broca CVDentus TR18-H (AR), ponta diamante CR4-U (CVDentus) (US); Grupo VIII - ponta diamantada KG nº2135 (AR), ponta diamante CR4 (CVDentus), ponta diamante T1-F (US). Após confecção dos preparos, 10 amostras de dentes de cada grupo foram analisados quanto a rugosidade em rugosímetro e duas amostras de cada grupo serão avaliadas por Microscópio eletrônico de varredura (MEV). Os dados referentes à avaliação quantitativa (rugosidade superficial) foram submetidos à análise estatística. (AU)

The objective of this work was to compare, in vitro, the characteristics and quality of the surface finish in bovine teeth, through the analysis of surface roughness and image analysis in Scanning Electron Microscopy (SEM). Despite being widely used, diamond burs have limitations such as low durability and their repeated sterilization causes a decrease in cutting capacity. With the emergence of CVD (Chemical Vapor Deposition) diamond dental tips, their indication has been expanded as an alternative, because associated with ultrasound devices they present good resistance to wear. Eighty bovine teeth were selected for this study and were divided into eight groups according to the type of tip used to make the prosthetic preparation wear: Group I ­ diamond tip KG nº2135 coupled in high rotation (HR) control group; Group II - diamond bur KG nº2135 (AR), diamond bur CVDentus CR4 coupled to ultrasound (US); Group III - diamond bur KG nº2135 (AR), diamond bur CVDentus CR4 followed by the CR4U bur, coupled in US; Group IV ­ diamond bur KG nº2135 (AR), diamond bur TR18-H CVDentus AR; Group V ­ diamond bur KG nº2135 coupled in AR, followed by a multilaminated carbide bur 30 preparation finishing blades, coupled in low rotation; Group VI ­ diamond bur KG nº2135 (AR), followed by a 30-blade multi-blade carbide bur and finishing with a rubber tip, Group VII ­ diamond bur KG nº2135 (AR), CVDentus bur TR18-H (AR), diamond bur CR4-U (CVDentus) (US); Group VIII - diamond bur KG nº2135 (AR), diamond bur CR4 (CVDentus), diamond bur T1-F (US). After preparation of the preparations, 10 samples of teeth from each group were analyzed for roughness in a rugosimeter and two samples from each group will be evaluated by Scanning Electron Microscope (SEM). Data referring to the quantitative evaluation (surface roughness) were subjected to statistical analysis. (AU)