Experimental nano calcium aluminate/tri calcium silicate root repair: Synthesis, physical and mechanical properties compared to mineral trioxide aggregate and Biodentine / Reparo radicular experimental de nano aluminato de cálcio/silicato de tri cálcio: Síntese, propriedades físicas e mecânicas em comparação com agregado de trióxido mineral e Biodentine

Objective: Endodontic perforation is a challenging mishap that should be repaired with a biocompatible material, Mineral trioxide aggregate (MTA) and Biodentine are the most commonly used repair materials. However, these materials are expensive, (MTA) has prolonged setting time and difficult manipulation. The purpose of this study is to prepare the experimental nano calcium-aluminate/tri-calcium-silicate (CA/C3S) material and comparing its physical properties with biodentine and MTA, to evaluate the experimental material eligibility to compete the commercial repair materials. And to perform part two (animal study) that will evaluate the cytotoxicity, the biocompatibility and the efficacy of (CA/C3S) in furcal perforation repair compared to diode laser. Material and Methods: A mixture of calcium carbonate and aluminum oxide was used to formulate calcium aluminate phase (CA), tri-calcium-Silicate phase (C3S) was formulated by firing of calcium carbonate and quartz. The produced powders were investigated by X-ray diffraction, then (CA) and (C3S) mixed with water.(CA/ C3S) compared with MTA and biodentine for setting-time, micro-hardness, dimensional-stability and solubility. Results: Mean setting time of (CA/C3S) was (32.70±0.75min) which is significantly higher than MTA and Biodentine. The Mean microhardness of (CA/C3S) was (56.50±7.41VHN) which has no statical difference with MTA and Biodentine. Solubility results showed weight increase for (CA/C3S) as following (6.29±3.05)and loss of weight for MTA and Biodentine. The percentage of change in dimensions for(CA/C3S) increased as following (0.64±0.78) while decreased for MTA and Biodentine. Conclusion: The experimental (CA/C3S) material showed good microhardness, dimensional stability and acceptable setting time that could be improved in further work (AU)

Objetivo: A perfuração endodôntica é um percalço desafiador que deve ser reparado com um material biocompatível, Agregado de trióxido mineral (MTA) e Biodentina são os materiais de reparo mais comumente usados. No entanto, esses materiais são caros, (MTA) tem tempo de presa prolongado e difícil manipulação. O objetivo deste estudo é preparar o material experimental de nano aluminato de cálcio/silicato tricálcico (CA/C3S) e comparar suas propriedades físicas com biodentina e MTA, para avaliar a elegibilidade do material experimental para competir com os materiais de reparo comerciais. E realizar a segunda parte (estudo animal) que avaliará a citotoxicidade, a biocompatibilidade e a eficácia do (CA/C3S) no reparo de perfuração de furca em comparação ao laser de diodo.Material e Métodos: Uma mistura de carbonato de cálcio e óxido de alumínio foi usada para formular a fase de aluminato de cálcio (CA), a fase tri-cálcio-silicato (C3S) foi formulada por queima de carbonato de cálcio e quartzo. Os pós produzidos foram investigados por difração de raios X, em seguida (CA) e (C3S) misturados com água. (CA/ C3S) comparados com MTA e biodentina para tempo de presa, microdureza, estabilidade dimensional e solubilidade. Resultados: O tempo médio de presa de (CA/C3S) foi (32,70±0,75min) que é significativamente maior que MTA e Biodentine. A microdureza média de (CA/C3S) foi (56,50±7,41VHN) que não tem diferença estática com MTA e Biodentine. Os resultados de solubilidade mostraram aumento de peso para (CA/C3S) conforme a seguir (6,29±3,05) e perda de peso para MTA e Biodentine. A porcentagem de mudança nas dimensões para (CA/C3S) aumentou como segue (0,64±0,78), enquanto diminuiu para MTA e Biodentine. Conclusão: O material experimental (CA/C3S) apresentou boa microdureza, estabilidade dimensional e aceitável tempo de presa, que pode ser melhorado em trabalhos futuros (AU)

An evaluation of the effect of different veneer materials on fracture resistance of zirconia core / Avaliação dos diferentes efeitos de materiais de revestimento na resistência à fratura do núcleo de zircônia

Objectives: this in vitro study was done to evaluate the effect of packable P60 composite and Tetric N-Ceram composite veneer material on fracture strength of zirconia cores. Material and Methods:Twenty four zirconium cores (Vita, Germany) with 0.7 mm thickness were fabricated by CAD/CAM technology and then subjected to air abrasion with 50 µm of Al2O3. Cores were randomly divided into three groups according to veneering material (group A: control group sandblasted with 50 µm Al2O3 veneered by IPS E-max Ceram porcelain, group C: sandblasted with 50 µm Al2O3, etching with hydrofluoric acid and veneered with P60 composite, group E: sandblasted with 50 µm Al2O3, etching with hydrofluoric acid and veneered with Tetric N-Ceram composite). All crowns were subjected to fracture strength test in the testing machine, with load application by steel ball indenter and 0.5 mm/min. cross head speed. Results: statistical analysis was carried out utilizing one-way ANOVA, LSD. The results of fracture strength value test showed the highest mean value was registered for group (A), and the lowest mean for group (E). One-way ANOVA test represented that, there was a statistically high significant different among all groups. LSD results showed a high significant difference increase in fracture resistance for Group A at p value (*p < 0.001 High significant). Conclusions: Within the limitation of this study, sandblasting zirconia core with 50 µm Al2O3 and veneering with conventional ceramic produced restoration with acceptable fracture resistance value (AU)

Objetivo: o objetivo desse estudo in vitro foi avaliar o efeito dos compósitos P60 compactáveis e material laminado de compósitos Tetric-N Ceram na resistência à fratura de núcleos de zircônia. Material e métodos:Vinte e quatro núcleos de zircônia (Vita, Germany) com 0.7 mm de espessura fabricados por tecnologia de CAD/CAM e sinterizados em alta temperatura (1450ºC por 60 min) de acordo com as instruções do fabricante. Núcleos totalmente de zircônias foram submetidos a abração com 50 µm de Al2O3. Os núcleos de zircônia foram divididos de forma randomiza em três grupos de acordo com o material de revestimento (grupo A: grupo controle jateado com 50 µm Al2O3 folheado com porcelana IPS E-max Ceram, grupo C: jateado com 50 µm Al2O3 , coberto com concentração 9,5% de ácido fluorídrico e folheado com resina composta compatível, grupo E: jateado com 50 µm Al2O3 coberto com concentração 9,5% de ácido fluorídrico e folheado com porcelana IPS E-max Ceram. Todos os espécimes (coroas) foram submetidos a teste de resistência a fratura com máquina de teste universal, essa máquina utilizou para aplicação de carga bola de aço com 6mm de diâmetro 0,5 mm/min de velocidade da cruzeta. Resultados: análise estatística foi realizada utilizando One-way ANOVA, LSD. O resultado da resistência a fratura mostra que o maior valor médio foi registrado no grupo A e a menor média para o grupo E. O resultado do teste One-Way ANOVA representaram que houve uma diferença estatisticamente alta e significante entre todos os grupos. LSD foi executada para mostrar a fonte de significância. Os resultados do LSD mostraram um aumento da diferença significativa alta na resistência à fratura para o grupo A no valor de p (p < 0.001 signicancia alta). Conclusão: Dentro das limitações desse estudo o uso convencional de jateamento com 50 µm Al2O3 e estratificação com cerâmica convencional produziu restauração com valor aceitável de resistência a fratura (AU)

Influence of alumina air-abrasion for highly translucent partially stabilized zirconia on flexural strength, surface properties, and bond strength of resin cement

Abstract Objective This study aims to evaluate the influence of different air-abrasion pressures and subsequent heat treatment on the flexural strength, surface roughness, and crystallographic phases of highly translucent partially stabilized zirconia (Y-PSZ), and on the tensile bond strength of resin cement to Y-PSZ. Methodology Fully sintered zirconia specimens were ground with SiC paper (control) and/or air-abraded with 50 µm particles of alumina at 0.1, 0.15, 0.2, or 0.3 MPa or left as-sintered. After air-abrasion at 0.2 MPa (0.2AB), additional specimens were then heated to 1500°C, and held for one hour at this temperature (0.2AB+HT1h). Flexural strength and surface roughness were evaluated. Crystalline phase identification was also carried out using X-ray diffraction. Bonded zirconia specimens with self-adhesive resin cement were stored in distilled water at 37°C for 24 h, either with or without aging (thermal cycling 4-60°C/20000). Results were analyzed statistically by ANOVA and Tukey-Kramer tests. Results The flexural strength decreased with the increase in air-abrasion pressure, while in contrast, the surface roughness increased. The lowest flexural strength and the highest roughness value were found for the 0.2AB and 0.3AB groups, respectively. All groups contained cubic-, tetragonal ( t )-, and rhombohedral ( r )-ZrO2 phases with the exception of the as-sintered group. Upon increasing the air-abrasion pressure, the relative amount of the r -ZrO2 phase increased, with a significant amount of r -ZrO2 phase being detected for the 0.2AB and 0.3AB groups. The 0.2AB+HT1h group exhibited a similar flexural strength and t -ZrO2 phase content as the as-sintered group. However, the 0.2AB group showed a significantly higher tensile bond strength (p<0.05) than the 0.2AB+HT1h group before and after aging. Conclusion Micromechanical retention by alumina air-abrasion at 0.2 MPa, in combination with chemical bonding of a resin to highly translucent Y-PSZ using a MDP-containing resin cement may enable durable bonding.

Osseointegração de implantes com superfícies modificadas por LASER com e sem recobrimento de hidroxiapatita: caracterização topográfica, análises biomecânica e histológica / Osseointegration of LASER modified surface implants with and without hydroxyapatite coating: topographic characterization, biomechanical and histologic analyses

Objetivo: Avaliar o processo de reparo ao redor de implantes com as superfícies usinada (SU), superfície disponível comercialmente modificada por jateamento de óxido de alumínio seguido do condicionamento ácido (SJA), modificada por feixe de LASER (SL) e modificada por feixe de LASER com posterior recobrimento de hidroxiapatita através do método biomimético sem tratamento térmico (SLH). Material e Métodos: As superfícies foram analisadas através de microscopia eletrônica de varredura acoplado a espectroscopia por energia dispersiva de raios X (MEV-EDX) previamente a cirurgia. Vinte coelhos receberam randomicamente 40 implantes em suas tíbias direita e esquerda, sendo um implante de cada superfície em cada tíbia. No procedimento cirúrgicos e nos períodos de 2 e 4 semanas foi mensurado o coeficiente de estabilidade do implante através da análise de frequência por ressonância (FR), seguida da remoção por contra-torque dos implantes nos períodos de análise. Os dados obtidos foram submetidos à análise de variância e ao teste t de Tukey (FR) e Kruskal-Wallis (análise biomecânica). Resultados: MEV e EDX mostraram diferenças na topografia das superfícies. Não houve diferença estatisticamente significante entre os grupos na análise de frequência por ressonância. Foi observada diferença estatisticamente significante no torque de remoção entre o grupo SL e SLH quando comparados ao grupo SU no período de 2 semanas. Já no período de 4 semanas, foi observada diferença estatística entre as 2 superfícies experimentais SL e SLH quando comparadas as superfícies SU e SJA. Na análise histológica os grupos SL e SLH apresentaram remodelação óssea no período de 2 semanas e osso maduro no período de 4 semanas, diferente de SU e SJA que apresentaram um atraso no reparo perante as superfícies experimentais. Conclusão: Os implantes com superfície SL e SLH apresentaram propriedades topográficas, e biomecânicas superiores às das superfícies SU e SJA(AU)

Purpose: To evaluate the repair process around implants with the machined surfaces (SU), commercially available surface modified by aluminum oxide blasting followed by acid etching (SJA), modified by LASER beam (SL) and modified by LASER beam with subsequent coating of hydroxyapatite using the biomimetic method without thermal treatment (SLH). Material and Methods: The surfaces were analyzed using scanning electron microscopy coupled with dispersive energy X-ray spectroscopy (SEM-EDX) prior to surgery. Twenty rabbits randomly received 40 implants in their right and left tibiae, with one implant on each surface in each tibia. In the surgical procedure and in the periods of 2 and 4 weeks, the implant stability coefficient was measured through the resonance frequency (ISQ), followed by the removal by counter-torque of the implants in the analysis periods. The data obtained were subjected to analysis of variance and Tukey's t test (ISQ) and Kruskal-Wallis (biomechanical analysis). Results: SEM and EDX showed differences in surface topography. There was no statistically significant difference between the groups in the resonance frequency. There was a statistically significant difference in the removal torque between the SL and SLH group when compared to the SU group in the period of 2 weeks. In the 4-week period, a statistical difference was observed between the 2 experimental surfaces SL and SLH when comparing the SU and SJA surfaces. In the histological analysis, the SL and SLH groups presented bone remodeling in the period of 2 weeks and mature bone in the period of 4 weeks, unlike SU and SJA which presented a delay in repair before the experimental surfaces. Conclusion: Implants with SL and SLH surfaces showed topographic and biomechanical properties superior to those of SU and SJA surfaces(AU)

CO2 laser for dental alumina ceramic framework welding / O laser de CO2 para a soldagem de infraestruturas cerâmicas de alumina

Objective: Despite the increase of all-ceramic prosthesis in dental practice there is no evidence of the possibility of welding these structures if necessary. The objective of this study was to use CO2 laser (λ = 10.6 µm) as a welding agent to fuse dental polycrystalline alumina ceramic. Methods: Ceramic blocks of pre-sintered alumina were sectioned into 20 bars (10.0 x 1.5 x 1.5 mm) and sintered to the final cross section dimension of 1.2 x 1.2mm. The bars were adapted to an LHPG (Laser Heated Pedestal Growth) system device where the bars could be fixed in pairs and have their ends irradiated with CO2 laser to fusion. The ring-shaped laser beam (300 µm thickness) was directed with the aid of mirrors to reach samples' ends. The laser was continuously applied (40 W nominal power, 5 seconds). After welding, the samples were analyzed in stereomicroscope and SEM. A diffraction analysis was carried out with one sample. Results: CO2 laser was able to fuse the ceramic bars, but some of them showed some shape distortion in the fusion zone. The aspect of the fused alumina differed in color and translucency from the original sintered material. SEM evidenced the presence of porosity and voids in the center of the fusion zone. X-ray diffraction pointed to a reduction in crystallite size by two to four times in the welded region of samples. Conclusions: This study points to CO2 laser as a possible welding agent to polycrystalline alumina dental ceramic. Porosity observed in the molten zone gives cause for concern regarding weld resistance. (AU)

Objetivo: Apesar do aumento no número de próteses totalmente cerâmicas na prática clínica, não há evidência da possibilidade de se soldar essas estruturas se necessário. Este estudo testou o laser de CO2 (λ=10.6 µm) como um agente de solda para estruturas cerâmicas de alumina policristalina. Métodos: Blocos cerâmicos de alumina pré-sinterizada foram seccionados na forma de barras (10,0 x 1,5 x 1,5 mm) e sinterizados na dimensão final de 1,2 x 1,2 mm. As barras foram adaptadas a um sistema de crescimento de fibras cerâmicas (LHPG ­ Laser Heated Pedestal Growth) onde as barras foram fixadas em pares e tiveram suas extremidades irradiadas com laser de CO2 até a sua fusão. O feixe de laser foi direcionado com a ajuda de espelhos para atingir as extremidades das barras. O laser foi aplicado de forma contínua (40 W de potência nominal, 5 segundos). Depois da solda, os espécimes foram analisados em estereomicroscopia e MEV. Teste de difração foi conduzido com um espécime. Resutados: O laser de CO2 foi capaz de fundir as barras cerâmicas, mas algumas delas mostraram uma distorção da forma na zona de fusão. O aspecto da alumina soldada diferiu em cor e translucidez do material original. O MEV evidenciou a presença de porosidade no centro da zona de fusão. A difração por raio-x apontou para uma redução no tamanho dos cristalitos de duas a quatro vezes na região da solda. Conclusões: Esse estudo mostrou ser possível usar o laser de CO2 como um agente de solda para uma cerâmica policristalina de alumina. A porosidade observada na zona de fusão traz preocupação quanto à resistência da solda. (AU)

Estudo comparativo in vivo da osseointegração em duas diferentes superfícies de implantes em liga TiAlV: caracterização topográfica, análise de frequência por ressonância e histométrica / Comparative study in vivo of osseointegration on two different surfaces of TiAlV alloy implants: topographic characterization, resonance frequency and histometric analyzes

Objetivo: Avaliar o comportamento biológico do tecido ósseo ao redor de implantes manufaturados em liga Ti-6Al-4V diante das superfícies modificadas por jateamento de óxido de alumínio seguido condicionamento ácido (SBAS) e a superfície usinada (MS). Material e Métodos: Dez coelhos receberam aleatoriamente 20 implantes de hexágono externo com dimensões de 4,0 mm de diâmetro e 10 mm de comprimento em suas tíbias direita e esquerda, sendo um implante de cada superfície em cada tíbia. Os implantes de ambos os grupos foram analisados através de microscopia eletrônica de varredura (MEV-EDX) e microscopia de força atômica (AFM). Discos com as mesmas superfícies foram submetidos à análise de rugosidade média (Ra) e secção transversal. Nos períodos de 3 e 6 semanas foi mensurado o coeficiente de estabilidade primária por meio da análise de frequência por ressonância (ISQ), seguido da eutanásia dos animais. As peças obtidas foram submetidas ao processamento de inclusão em resina fotopolimerizável e levadas ao micrótomo para corte calcificado. Foi mensurada em porcentagem a extensão linear de contato entre tecido ósseo mineralizado e implante (ELCOMI) e área óssea neoformada (AON). Os dados foram submetidos à análise de variância e ao teste t de Tukey. Resultados: MEV e AFM mostraram diferenças na topografia das superfícies. Os valores médios obtidos pelas análises de frequência por ressonância, Ra e secção transversal para SBAS foram estatisticamente superiores (p<0,05) quando comparados a MS. Os valores médios em porcentagem de ELCOMI para SBAS foram de 69,65 e 71,56 respectivamente para 3 e 6 semanas, enquanto para MS os valores médios foram de 54,06 e 55,99 respectivamente para os mesmos períodos. Os valores médios de AO no grupo SBAS foram de 69,85 e 79,60 para os períodos de 3 e 6 semanas, enquanto para MS os valores médios foram de 59,59 e 74,32 respectivamente nos mesmos grupos. Houve diferenças estatisticamente superiores (p<0,05) nos implantes SBAS para a ELCOMI nos períodos de 3 e 6 semanas e AON no período de 3 semanas. Conclusão: A modificação na superfície nos implantes SBAS proporcionou alterações na topografia dos implantes, promovendo um maior contato entre tecido ósseo e a liga de titânio, permitindo melhores níveis de osseointegração. Relevância clínica: Implantes manufaturados em liga de Ti-6Al-4V modificados por jateamento de óxido de alumínio seguido condicionamento ácido (SBAS) apresentam bons níveis de osseointegração e podem ser usados com segurança para reabilitação protética de pacientes(AU)

Objective: Evaluate the biological behavior of bone tissue around implants manufactured in Ti-6Al-4V alloy before surfaces modified by aluminum oxide blasting followed by acid etching (SBAS) and machined surface (MS). Material and Methods: Ten rabbits randomly received 20 external hexagon implants with dimensions of 4.0 mm in diameter and 10 mm in length on their right and left tibiae, one implant of each surface on each tibia. The implants of both groups were analyzed by scanning electron microscopy (SEM-EDX) and atomic force microscopy (AFM). Disks with the same surfaces were submitted to analysis of average roughness (Ra) and cross section. In the periods of 3 and 6 weeks, the primary stability coefficient was measured by means of resonance frequency analysis (ISQ), followed by euthanasia of the animals. The obtained pieces were submitted to the inclusion processing in photopolymerizable resin and taken to the microtome for cutting without decalcification. The bone interface contact (BIC) and neoformed bone area (NBA) was measured in percentage. Data were submitted to analysis of variance and Tukey t test. Results: SEM and AFM showed differences in surface topography. The mean values obtained by the resonance, Ra and cross section analyzes for SBAS were statistically higher (p <0.05) when compared to MS. The mean values in percentage of BIC for SBAS were 69.65 and 71.56 respectively for 3 and 6 weeks, while for MS the mean values were 54.06 and 55.99 respectively for the same periods. The mean values of NBA in the SBAS group were 69.86 and 79.59 for the 3 and 6 week periods, while for MS the mean values were 59.59 and 74.32, respectively, in the same groups. There were statistically superior differences (p <0.05) in SBAS implants for BIC in the 3 and 6 week periods and AON in the 3 week period. Conclusion: The surface modification of the SBAS implants provided changes in the topography of the implants, promoting a better contact between bone tissue and titanium alloy, allowing better levels of osseointegration. Clinical Relevance: Implants manufactured in Ti-6Al-4V alloy modified by aluminum oxide etching followed by acid etching (SBAS) present good levels of osseointegration and can be safely used for prosthetic rehabilitation of patients(AU)

Eficácia do uso de plasma em pressão atmosférica na adesão de cerâmicas zircônia / Efficacy of the use of plasma at atmospheric pressure in zirconia adhesion

Um dos maiores desafios atuais da ciência dos materiais dentários é a obtenção de união efetiva e durável às cerâmicas de alto conteúdo cristalino. O objetivo do presente estudo foi avaliar a resistência de união, energia de superfície e tipos de fratura de dois sistemas cerâmicos após diferentes formas de tratamento de superfície associada à aplicação do plasma em pressão atmosférica. Para o estudo foram obtidas quarenta placas de zircônia (12 mm x 5 mm x 1,5 mm) de dois tipos de cerâmicas zircônia (E.max ZirCad e Calypso), polidas e limpas por ultrassom durante 5 minutos. Divididas aleatoriamente em 2 grupos de acordo com o sistema cerâmico e 4 subgrupos (n=5) de acordo com o tratamento de superfície, (I) controle (primer), (II) jateamento com partículas micrométricas de alumina (Al2O3) + primer, (III) jateamento com partículas micrométricas de alumina (Al2O3) + plasma + primer, (IV) plasma + primer. Foram confeccionados cento e vinte cilindros de resina composta (Z100), utilizando matrizes cilíndricas (1,0 mm x 3,0 mm) cimentadas com cimento resinoso, Multilink N, sobre as placas de zircônia. Os espécimes foram armazenados em água destilada durante 24 horas a 37° C, depois testados para microcisalhamento em máquina de teste Shimadzu EZ a 1,0 mm/min. Os dados obtidos foram submetidos à análise estatística para comparação entre os grupos E.max e Calypso em relação à resistência à união (força/área ­ MPa), ângulo de contato e os tipos de fratura. Os dados foram analisados pelos testes ANOVA One-Way e Kruskal-Wallis para resistência de união (p=0,003) e (p=0,005) e ângulo de contato (p<0,001) e (p<0,001). Não houve diferença significativa para os dados de fratura (p=0,145), pelo teste quiquadrado, com predomínio de fraturas mistas. Os valores de resistência de união das cerâmicas Y-TZP apresentaram maiores valores quando o plasma foi associado ao jateamento com óxido de alumínio e/ou primer e a aplicação somente do plasma não superou os valores alcançados pelas outras formas de tratamento da superfície. Essa associação resultou em menores valores dos ângulos de contato. Houve maior frequência de fraturas mistas quando realizado somente o tratamento com óxido de alumínio e quando em associação com o plasma.(AU)

One of the major challenges today in the science of dental materials is the achievement of effective and durable bonding to ceramics with high crystalline content. The objective of the present study was to evaluate the efficacy of plasma at atmospheric pressure in the adhesion of ceramic zirconia through the bond strength, surface energy and type of fracture of two ceramic systems after different forms of surface treatment associated with the application of plasma at atmospheric pressure. For the study forty zirconia plates (12 mm x 5 mm x 1.5 mm) were obtained from two zirconia ceramics (E.max ZirCad and Calypso), polished and cleaned by ultrasound for 5 minutes. Randomly divided into 2 groups according to the ceramic system and 4 subgroups (n = 5) according to the surface treatment, control (primer), primer + blasting with micrometric alumina (Al2O3) particles, primer + blasting with micrometric particles of alumina (Al2O3) + plasma, primer + plasma. One hundred and twenty cylinders of composite resin (Z-100) were made using cylindrical matrices (1.0 mm x 3.0 mm) cemented on the zirconia plates. The specimens were stored in distilled water for 24 hours at 37°C, then tested for microshear on a Shimadzu EZ test machine at 0.5 mm / min. The obtained data were submitted to statistical analysis for comparison between the E.max and Calypso groups in relation to the bond strength (strength / area - Mpa), contact angle and fracture types. The data were analyzed by ANOVA One-Way and Kruskal-Wallis tests for bond strength (p=0.003) and (p=0.005) and contact angle (p<0.001) and (p<0.001). There was no significant difference for the fracture data (p = 0.145), by the chi-square test, with a predominance of mixed fractures. The bond strength values of the Y-TZP ceramics showed higher values when the plasma was associated with blasting with aluminum oxide and / or primer and the application of only the plasma did not exceed the values reached by the other forms of surface treatment. This association resulted in lower values of contact angles. It is a higher frequency of mixed fractures when only aluminum oxide treatment is performed and when it is associated with plasma.(AU)

Effects of air abrasion with alumina or glass beads on surface characteristics of CAD/CAM composite materials and the bond strength of resin cements

ABSTRACT Objective The study aimed to evaluate effects of air abrasion with alumina or glass beads on bond strengths of resin cements to CAD/CAM composite materials. Material and Methods CAD/CAM composite block materials [Cerasmart (CS) and Block HC (BHC)] were pretreated as follows: (a) no treatment (None), (b) application of a ceramic primer (CP), (c) alumina-blasting at 0.2 MPa (AB), (d) AB followed by CP (AB+CP), and (e) glass-beads blasting at 0.4 MPa (GBB) followed by CP (GBB+CP). The composite specimens were bonded to resin composite disks using resin cements [G-CEM Cerasmart (GCCS) and ResiCem (RC)]. The bond strengths after 24 h (TC 0) and after thermal cycling (TC 10,000 at 4–60°C) were measured by shear tests. Three-way ANOVA and the Tukey compromise post hoc tests were used to analyze statistically significant differences between groups (α=0.05). Results For both CAD/CAM composite materials, the None group exhibited a significant decrease in bond strength after TC 10,000 (p<0.05). AB showed significantly higher bond strength after TC 10,000 than the None group, while CP did not (p<0.05). GBB exhibited smaller surface defects than did AB; however, their surface roughnesses were not significantly different (p>0.05). The AB+CP group showed a significantly higher bond strength after TC 10,000 than did the AB group for RC (p<0.05), but not for GCCS. The GBB+CP group showed the highest bond strength for both thermal cyclings (p<0.05). Conclusions Air abrasion with glass beads was more effective in increasing bond durability between the resin cements and CAD/CAM composite materials than was using an alumina powder and a CP.

Adaptação marginal em copings de dois sistemas cerâmicos livres de metal / Marginal fit in copings of two metal free ceramic systems

Este trabalhou avaliou a adaptação marginal de infraestruturas cerâmicas (copings em alumina) de dois sistemas cerâmicos livres de metal. Foram pesquisados os sistemas In-Ceram e Procera. Os valores de discrepância vertical presentes entre as margens de nove copings de cada sistema cerâmico e a margem de um modelo mestre metálico foram medidos com microscópio eletrônico de varredura em 5 pontos de cada infraestrutura. Esses valores foram medidos em micrômetros (pm). Os resultados foram analisados estatisticamente com o software SPSS (Statistical Package for the Social Sciences 11.0), através do teste t de Student, considerando-se significativos os valores de p<0(05. Os valores médios de discrepância marginal dos dois sistemas, medidos em microscópio eletrônico de varredura, mostraram diferença estatística entre si (p=0,001), sendo observadas desadaptações de 39±11pm (sistemas Procera) e 11 5±56pm (sistema In-Ceram). Conclui-se que os dois sistemas cerâmicos livres de metal avaliados apresentaram adaptação marginal dentro de limites aceitáveis clinicamente.

This work has evaluated the marginal fit of alumina copings of two metal free ceramic systems, namely Procera and In-Ceram systems. The marginal fit values of the margins in nine copings of each ceramic system and in a metal master model were assessed using electron- scanning microcopy in five points of the margin of each coping. Such values were measured in micrometers (pm). The results were analyzed statistically by the SPSS software (p<0.05). The marginal fit mean values for both systems have presented statistical difference (p=0.001), being of 39±11 pm and 115±56pm for the Procera and Inc-Ceram systems, respectively. Both systems have presented marginal fit according to the clinical acceptance.

Reparo em resina composta - efeito do condicionamento ácido e dos sistemas adesivos / Composite resin repair - effect of acid etching and adhesive systems

O objetivo deste trabalho foi avaliar o efeito do condicionamento ácido e do tipo de adesivo sobre a resistência de união de reparos em compósitos tratados com jato de óxido de alumínio. Foram confeccionados 60 discos com compósito, cor A2 (Filtek Z350 - 3M ESPE®), envelhecidos por seis meses em água. Após o polimento, as superfícies foram submetidas ao jato de óxido de alumínio (45 -jm) e distribuídas em seis grupos com dez espécimes cada um: G1: Adper Scotchbond Multi-Purpose (3M ESPE®), sem condicionamento ácido e sem "primer"; G2: Adper Scotchbond Multi-Purpose (3M ESPE®), após condicionamento com ácido fosfórico 37% e sem "primer"; G3: Adper Single Bond 2 (3M ESPE®), sem condicionamento ácido; G4: Adper Single Bond 2 (3M ESPE®), após condicionamento com ácido fosfórico 37%; G5: Adper Easy One (3M ESPE), sem condicionamento ácido e G6: Adper Easy One (3M ESPE®), após condicionamento com ácido fosfórico 37%. Os reparos foram confeccionados com o compósito Opallis (FGM®), cor A2. Após 24 horas os corpos de prova foram submetidos aos ensaios de cisalhamento (Instron - 0,5 mm/min). Os valores médios (MPa) após ANOVA2 e teste de Tukey e T de student (5%) foram: G1: 18,34 (6,73); G2: 16,49 (3,65); G3: 13,11 (3,64); G4: 19,86 (5,85); G5: 20,88 (4,82) e G6: 23,48 (4,36). O condicionamento com ácido fosfórico a 37% aumentou significativamente a resistência de união dos reparos confecciona¬dos com o sistema Adper Single Bond 2 (3M ESPE®) e não proporcionou aumento significativo na resistência de união dos reparos com os sistemas Adper Scotchbond Multi-Purpose (3M ESPE®) e Adper Easy One (3M ESPE®).

The aim of this study was to evaluate the effect of acid etching and type of adhesive on the bond strength of composite repairs treated with aluminum oxide. Sixty discs were fabricated with composite shade A2 (Filtek Z350 - 3M ESPE®), and aged for 6 months in water. After polishing, the surfaces were subjected to aluminum oxide treatment (45 pm) and divided into 6 groups with 10 specimens each: G1: Adper Sotchbond Multipurpose (ASM) (3M ESPE®) without etching and without primer, G2: Adper Sotchbond Multipurpose (ASM) (3M ESPE®) after etching with phosphoric acid 37% and without primer, G3: Adper Single Bond 2 (ASB) (3M ESPE®) without etching, G4: Adper Single Bond 2 (ASB) (3M ESPE®) after etching with phosphoric acid 37%, G5: Adper Easy One (AEO) (3M ESPE®) without etching, and G6: Adper Easy One (AEO) (3M ESPE®) after etching with phosphoric acid 37%. Repairs were made with the composite Opallis (FGM®), shade A2. After 24 hours the specimens were submitted to shear tests (Instron - 0.5 mm/min). Mean values (MPa) after ANOVA2, Tukey test and T stu¬dent (5%) were: G1: 18.34(6.73), G2: 16.49 (3.65), G3: 13.11 (3.64), G4: 19.86 (5.85), G5: 20.88 (4.82), and G6: 23.48 (4.36). The phosphoric acid at 37% significantly increased the bond strength of repair with the system ASB and did not increase the bond strength of repair with the systems ASM and AEO.

Efeito de protocolos de jateamento na resistência à flexão e transformação de fase cristalina em cerâmicas de Y-TZP / Effect of sandblasting protocols on flexural strength and crystalline phase change in Y-TZP ceramic

O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de jateamento na resistência à flexão biaxial e transformação de fase cristalina de cerâmica policristalina de Y-TZP. Foram confeccionados 740 discos de zircônia estabilizada parcialmente por ítrio - Cercon®Zirconia (DENTSPLY Ceramco, EUA) e In Ceram 2000 YZ cubes (Vita Zahnfabrik, Alemanha) segundo a norma ISO 6872 (15 mm diâmetro x 2 mm espessura). As amostras foram jateadas com partículas de óxido de alumínio (30 μm) revestido por sílica (RocatecSoft - 3M ESPE) e divididas em 74 grupos (n = 10), incluindo-se os grupos controle (ausência de jateamento)(n = 10) para cada cerâmica, de acordo com os fatores: pressão de jateamento (2, 3 e 4 bar); ângulo formado entre a ponta do jateador e a superfície da cerâmica (45º, 60º, 90º); distância do microjateador à cerâmica (5 e 10 mm) e tempo de jateamento (15 s e 20 s). Foi realizado teste de resistência à flexão biaxial em máquina de ensaio universal (1 mm/min, 1000 kg). Os dados (MPa) foram submetidos a análise de variância e ao teste de Duncan. Parte das amostras (n=3) foram submetidas à difração por raios-X (DRX) para quantificação das fases cristalinas e à microcopia eletrônica de varredura (MEV) para análise da topografia superficial. Pressão (p = 0,00) afetou significativamente os resultados, porém tempo (p = 0,49), distância (p = 0,46) e angulação (p = 0,13) não afetaram a Cercon. Já para Vita YZ, a pressão (p = 0,00) foi estatisticamente significante, porém tempo (p=0,66), distância (p = 0,70) e angulação (p=0,14) não foram. Fase monoclínica foi encontrada nos grupos da Cercon (0 a 11%), enquanto para Vita YZ, nenhuma fase foi encontrada. Para Vita YZ, a pressão 3 bar teve maior resistência à flexão biaxial e 4 bar apresentou menor valor. Angulação de 45° associado a 2 bar foi a melhor combinação (1012,21 ± 108,36 MPa) comparado a 4 bar (556,65 ± 117,41 MPa). MEV revelou grãos superficiais regulares e uniformes. A contagem dos grãos ...

The aim of this study was to evaluate the effect of different sandblasting protocols on biaxial flexural strength and crystalline phase transformation in Y - TZP ceramic. 740 discs of Yttria-Partially-Stabilized Zirconia were made - Cercon ® Zirconia (DENTSPLY Ceramco, USA) and In Ceram 2000 YZ cubes (Vita Zahnfabrik, Germany) according to the standards of ISO 6872 (15 mm diameter x 2 mm thick) . The samples were sandblasted with aluminum oxide - coated silica 30 μm (Rocatec Soft - 3M ESPE ) and divided into 74 groups (n = 10 ) , according: pressure (2, 3 and 4 bar) ; nozzle angle (45°, 60°, 90°); nozzle distance (5 and 10 mm) and time (15 s and 20 s) . The biaxial flexural strength on universal testing machine (1mm/min, 1,000 kg) was performed. Data (MPa) were submitted to ANOVA and to Duncan´s test (α = 0.05). Samples (n = 2) were subjected to X- ray diffraction to quantify crystalline phases. Pressure (p = 0.00) significantly affected the results, but deposition time (p = 0.49), nozzle distance (p = 0.46) and nozzle angles (p=0.13) did not affect to Cercon ceramic. Pressure (p = 0.00) affected significantly the results to Vita YZ, but deposition time (p = 0.66), nozzle distance (p = 0.70) and nozzle angles (p = 0.14) did not affect. Some monoclinical phase was achieved in Cercon groups (0 a 11%) and none for Vita YZ. For Vita YZ ceramic, 3 bar pressure had the biggest flexural strength value and 4 bar was the worst one and angle 45° associated to 2 bar were the best combination (1012.21 ± 108.36 MPa) compared to 4 bar (556.65 ± 117.41 MPa) (p < 0.001). EDS analysis demonstrated regular superficial grains. SEM images indicated grain size of 0.712 μm (Vita YZ), and 0.705 μm (Cercon). The Cercon density was 98% compared to the theoretical density of zirconia, while VITA YZ was 99%

Efeito de protocolos de jateamento na resistência à flexão e transformação de fase cristalina em cerâmicas de Y-TZP / Effect of sandblasting protocols on flexural strength and crystalline phase change in Y-TZP ceramic

O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de jateamento na resistência à flexão biaxial e transformação de fase cristalina de cerâmica policristalina de Y-TZP. Foram confeccionados 740 discos de zircônia estabilizada parcialmente por ítrio - Cercon®Zirconia (DENTSPLY Ceramco, EUA) e In Ceram 2000 YZ cubes (Vita Zahnfabrik, Alemanha) segundo a norma ISO 6872 (15 mm diâmetro x 2 mm espessura). As amostras foram jateadas com partículas de óxido de alumínio (30 μm) revestido por sílica (RocatecSoft - 3M ESPE) e divididas em 74 grupos (n = 10), incluindo-se os grupos controle (ausência de jateamento)(n = 10) para cada cerâmica, de acordo com os fatores: pressão de jateamento (2, 3 e 4 bar); ângulo formado entre a ponta do jateador e a superfície da cerâmica (45º, 60º, 90º); distância do microjateador à cerâmica (5 e 10 mm) e tempo de jateamento (15 s e 20 s). Foi realizado teste de resistência à flexão biaxial em máquina de ensaio universal (1 mm/min, 1000 kg). Os dados (MPa) foram submetidos a análise de variância e ao teste de Duncan. Parte das amostras (n=3) foram submetidas à difração por raios-X (DRX) para quantificação das fases cristalinas e à microcopia eletrônica de varredura (MEV) para análise da topografia superficial. Pressão (p = 0,00) afetou significativamente os resultados, porém tempo (p = 0,49), distância (p = 0,46) e angulação (p = 0,13) não afetaram a Cercon. Já para Vita YZ, a pressão (p = 0,00) foi estatisticamente significante, porém tempo (p=0,66), distância (p = 0,70) e angulação (p=0,14) não foram. Fase monoclínica foi encontrada nos grupos da Cercon (0 a 11%), enquanto para Vita YZ, nenhuma fase foi encontrada. Para Vita YZ, a pressão 3 bar teve maior resistência à flexão biaxial e 4 bar apresentou menor valor. Angulação de 45° associado a 2 bar foi a melhor combinação (1012,21 ± 108,36 MPa) comparado a 4 bar (556,65 ± 117,41 MPa). MEV revelou grãos superficiais regulares e uniformes. A contagem dos grãos...

The aim of this study was to evaluate the effect of different sandblasting protocols on biaxial flexural strength and crystalline phase transformation in Y - TZP ceramic. 740 discs of Yttria-Partially-Stabilized Zirconia were made - Cercon ® Zirconia (DENTSPLY Ceramco, USA) and In Ceram 2000 YZ cubes (Vita Zahnfabrik, Germany) according to the standards of ISO 6872 (15 mm diameter x 2 mm thick) . The samples were sandblasted with aluminum oxide - coated silica 30 μm (Rocatec Soft - 3M ESPE ) and divided into 74 groups (n = 10 ) , according: pressure (2, 3 and 4 bar) ; nozzle angle (45°, 60°, 90°); nozzle distance (5 and 10 mm) and time (15 s and 20 s) . The biaxial flexural strength on universal testing machine (1mm/min, 1,000 kg) was performed. Data (MPa) were submitted to ANOVA and to Duncan´s test (α = 0.05). Samples (n = 2) were subjected to X- ray diffraction to quantify crystalline phases. Pressure (p = 0.00) significantly affected the results, but deposition time (p = 0.49), nozzle distance (p = 0.46) and nozzle angles (p=0.13) did not affect to Cercon ceramic. Pressure (p = 0.00) affected significantly the results to Vita YZ, but deposition time (p = 0.66), nozzle distance (p = 0.70) and nozzle angles (p = 0.14) did not affect. Some monoclinical phase was achieved in Cercon groups (0 a 11%) and none for Vita YZ. For Vita YZ ceramic, 3 bar pressure had the biggest flexural strength value and 4 bar was the worst one and angle 45° associated to 2 bar were the best combination (1012.21 ± 108.36 MPa) compared to 4 bar (556.65 ± 117.41 MPa) (p < 0.001). EDS analysis demonstrated regular superficial grains. SEM images indicated grain size of 0.712 μm (Vita YZ), and 0.705 μm (Cercon). The Cercon density was 98% compared to the theoretical density of zirconia, while VITA YZ was 99%.

Influência do óxido de alumínio na colagem dos bráquetes linguais / The influence of the aluminun oxide on lingual brackets bonding

A descolagem acidental do bráquete é uma severa complicação no decorrer do tratamento ortodôntico, especialmente quando o tratamento é feito com bráquetes linguais. A força de adesão entre o bráquete e o dente é um importante requisito para o sucesso da Ortodontia Lingual na prática diária do consultório. O presente estudo analisou a influência do jateamento do óxido de alumínio na superfície lingual dos dentes antes do condicionamento do esmalte na colagem indireta do aparelho lingual. A força de cisalhamento foi medida 24 horas após a colagem dos bráquetes. Os dentes foram divididos em quatro grupos: G1 - 10 pré-molares com bráquetes da marca American Orthodontics com condicionamento de ácido ortofosfórico a 37%; G2 - 10 pré-molares com bráquetes da marca American Orthodontics com aplicação do jato de óxido de alumínio e ácido ortofosfórico a 37% no esmalte; G3 - 10 pré-molares com bráquetes da marca Ormco com condicionamento de ácido ortofosfórico a 37% e G4 - 10 pré-molares com bráquetes da marca Ormco com aplicação do jato de óxido de alumínio e ácido ortofosfórico a 37% no esmalte. Avaliou-se a resistência ao cisalhamento e observou-se que não ocorreu diferença estatisticamente significante entre os grupos quanto aos diferentes modos de preparo de esmalte. Com relação às marcas comerciais, os bráquetes da American Orthodontics apresentaram resistência à descolagem maior do que os bráquetes da marca Ormco. Concluindo, a resistência à descolagem dos bráquetes não foi aumentada com a aplicação prévia do jato de óxido de alumínio no esmalte hígido, nas duas marcas comerciais de bráquetes.

Accidental bracket debonding is a severe complication throughout orthodontic treatment, especially when using lingual brackets. The bond strength between the bracket and the tooth is an important requirement for the success of Lingual Orthodontics. This study has analyzed the influence of aluminum oxide blasting on the lingual surface of the teeth, before conditioning of the enamel, over indirect bonding of the lingual brace. Shear strength was measured 24 hours after brackets bonding. Teeth were divided into four groups: G1 - 10 premolar teeth with American Orthodontics brackets and 37% orthophosphoric acid conditioning; G2 - 10 premolar teeth with American Orthodontics brackets and application of aluminum oxide and 37% orthophosphoric acid blasting on the enamel; G3 - 10 premolar teeth with Ormco brackets and 37% orthophosphoric acid conditioning; G4 - 10 premolar teeth with Ormco brackets, application of aluminum oxide and 37% orthophosphoric acid blasting on the enamel. When evaluating the shear resistance through mechanical assay, it was not observed statistically significant difference between the groups regarding different enamel preparation modes. Concerning the different commercial brands, the American Orthodontics brackets showed higher debonding resistance than the Ormco brackets. It was concluded that, for both brands of brackets, the resistance to bracket debonding did not increase with the previous application of aluminum oxide blasting on the ename.

Influence of sandblasting distance on enamel and ceramic structure bond strength / Influência do jateamento na estrutura cerâmica e esmalte, alterando a distância na resistência de união

Objetive: The purpose of this study was to evaluate the influence of sandblasting distance on ceramic and enamelbond strength. Material & Methods: Sixtythird molars were selected, enamel surfaces were ground flat with wet 600 - 2000 grit aluminum oxide abrasive papers and polished with three, one, and one-fourth micrometer-grit diamond pastes. On hundred and twentylithium disilicate-based core ceramic discs (2 mm diameter; 1 mm thickness) were also obtained and further divided into 7 groups [Group C, no sandblasting, Group SB-E(5-10) enamel sandblasting - 5 and 10 mm of distance, Group SBC(5-10) ceramic sandblasting 5 mm and 10 mm of distance, Group SB-EC(5-10) enamel and ceramic sandblasting 5 mm and 10 mm of distance]. After treatments,shear and Atomic Force Microscopy (AFM) tests were performed.Data were analyzed by Statistic Tests of normality, one-way ANOVA and Tukey post-test (α: 0.05). Results: Group C presented the highestbond strength values(59.2 ±12.5), while group SB-E 5 mm showed the lowest values (21.7 ± 08.8) (p < 0.005). Conclusion: The use of sandblasting treatment of enamel surface at 5mm distance decreases the bonding strength to shear.

Objetivo: o objetivo do estudo foi avaliar influência do jateamento na estrutura cerâmica e esmalte sob resistência de união, mudando a distância. Materiais e Métodos: 60 terceiros molares, foram selecionados, superfícies de esmalte foram planificadas com lixa com grão 600 - 2000 lixas e polido com pastas de diamante de um grão -micrômetro. Obtidos 120 discos cerâmica em dissilicato de lítio de (2 mm de diâmetro e 1 mm de espessura), dividido em sete grupos [Grupo C, não jateamento, Grupo SB-E (5-10) esmalte jateamento 5 e 10 mm, Grupo SB -C (5-10) de jacto de areia cerâmica 5 mm e 10 mm, Grupo SB-CE (5-10) e esmalte cerâmico areação 5 milímetros e 10 mm], depois foi realizado o microcisalhamento e a microscopia de forca atômica (AFM), estatística como Teste de Normalidade , após análise de variância one-way e teste de Tukey (α: 0,05). Resultados: A força do grupo C apresentou maiores valores de resistência de união (59,2 ± 12,5), o grupo SB-E 5 mm (21,7 ± 08,8) (p < 0,005), o grupo SB-E10 (53,6 ± 14,3). Conclusão: o uso de jateamento tratamento da superfície do esmalte de 5 mm, de 20 s diminui a força de ligação de microcisalhamento.

Condicionamento do esmalte com óxido de alumínio associado ao ácido fosfórico na colagem indireta de braquetes / Enamel conditioning with aluminum oxide associated to phosphoric acid in indirect bonding of brackets

O objetivo deste estudo foi comparar a resistência de união e a interface de falha da colagem de braquetes colados pela técnica indireta após o condicionamento do esmalte com jato de óxido de alumínio de 27, 50 e 90 m seguido da aplicação de ácido fosfórico a 37%; e avaliar quantitativa e qualitativamente as alterações da superfície do esmalte após os diferentes tipos de condicionamento. A amostra foi constituída por 104 pré-molares superiores. Na primeira parte da pesquisa 80 dentes foram divididos aleatoriamente em 4 grupos (n=20) que receberam diferentes condicionamentos das faces linguais: G1 (controle)- ácido fosfórico a 37%; G2, G3 e G4- jato de óxido de alumínio de 27, 50 e 90 m, respectivamente, antes da aplicação de ácido fosfórico. Braquetes linguais foram colados indiretamente com o mesmo material e metodologia nos 4 grupos. A força máxima de cisalhamento requerida para descolar os braquetes foi determinada por meio de uma máquina de ensaios mecânicos universal, e a interface de falha na colagem, por meio do Índice de Resina Remanescente (ARI). Para a avaliação quantitativa dos efeitos provocados no esmalte pelos diferentes condicionamentos, 20 dentes foram divididos aleatoriamente em 4 grupos, e suas faces linguais foram condicionadas de acordo com o protocolo proposto anteriormente. A rugosidade do esmalte (Ra) antes e após o seu condicionamento foi determinada por meio de um microscópio a laser confocal. Na avaliação qualitativa foram utilizados 4 dentes, que foram condicionados segundo protocolo descrito anteriormente. O teste ANOVA de um critério foi utilizado para comparar a resistência adesiva e o incremento de rugosidade entre os grupos. As diferenças entre as pontuações do ARI foram avaliadas com o teste de Kruskal-Wallis.

Foi adotado nível de significância de 5% em todas as avaliações estatísticas. Não foram observadas diferenças estatisticamente significantes entre os quatro tipos de condicionamento de esmalte quando avaliou-se as médias de resistência de união e o incremento de rugosidade. Também não foram verificadas diferenças estatisticamente significativas entre as pontuações do ARI. O resultado da avaliação qualitativa evidenciou padrões diferentes de condicionamento entre o esmalte condicionado com ácido fosfórico e o esmalte condicionado com óxido de alumínio associado ao ácido. No esmalte condicionado com ácido, observaram-se leves irregularidades correspondentes com o padrão tipo III de Silverstone; enquanto no esmalte condicionado com jato de óxido de alumínio de 27, 50 e 90 m mais ácido fosfórico verificaram-se padrões similares de condicionamento, com superfícies de textura áspera bastante uniforme, presença de múltiplas elevações com diferentes alturas e bordas arredondadas, semelhantes ao padrão tipo II de Silverstone. Assim, concluiu-se que o condicionamento do esmalte com óxido de alumínio associado ao ácido não incrementou a resistência de união de braquetes colados indiretamente, não modificou a quantidade de resina remanescente, nem aumentou a rugosidade do esmalte. No entanto, produz um padrão de condicionamento diferente ao obtido com o ácido.

The purpose of this study was to compare the bond strength and the bond failure location of indirectly bonded brackets after enamel conditioning with 27, 50 and 90 m aluminum oxide followed by application of 37% phosphoric acid; and to analyze quantitatively and qualitatively the alterations on the enamel surface after the different conditionings. The sample consisted of 104 superior premolars. In the first stage of this research, 80 teeth were randomly divided into 4 groups (n=20) that received different conditionings at the lingual faces: G1 (control)- 37% phosphoric acid, G2, G3 and G4- 27, 50 and 90 m aluminum oxide, respectively, before applying phosphoric acid. The lingual brackets were indirectly bonded using the same material and methodology in the 4 groups. The maximum shear bond strength required to debond the brackets was determined using a mechanical testing machine, and the bond failure location through the Adhesive Remnant Index (ARI). For the quantitative analysis of the effects caused in the enamel due to the different conditionings, 20 teeth were randomly divided into 4 groups, and their lingual faces were conditioned according to the previously described protocol. The enamel roughness (Ra) before and after conditioning was measured using a confocal laser scanning microscope. In the qualitative analysis 4 teeth that were conditioned according to the previously described protocol were used. One-way ANOVA analysis was used to compare the bond strength and the roughness increment between the groups.

The differences among the ARI scores were analyzed with the Kruskal-Wallis test. A 5% significance level was adopted for all statistical analysis. No statistical differences were observed among the 4 types of enamel conditionings when the mean shear bond strength and roughness increase were compared. There were not also statistically significant differences between the ARI scores. The results of the qualitative analysis showed different conditioning patterns between the enamel prepared with phosphoric acid and the enamel treated with aluminum oxide associated to phosphoric acid. In the acid-etching enamel, slight irregularities corresponding to Silverstones type III pattern were found; while in the enamel conditioned with aluminum oxide of 27, 50 and 90 m followed by phosphoric acid, similar conditioning patterns were found, with rough surfaces highly uniform, presence of multiple elevations of different heights and rounded edges, similar to Silverstones type II pattern.

Caracterização de sistemas cerâmicos aluminizados infiltrados por vidro / Characterization of glass-infused alumina-based ceramic systems

A realização deste trabalho se deu justamente pela pouca informação sobre sistemas cerâmicos amplamente utilizados no mercado odontológico, sendo o objetivo deste estudo caracterizar e analisar a microestrutura, a composição e as propriedades mecânicas destes materiais, testando a compatibilidade entre os sistemas, além da hipótese de que todos eles apresentam ótimas propriedades. Este estudo caracterizou e comparou os sistemas cerâmicos In-Ceram (Vita Zahnfabrik, Bad Säckingen, Alemanha), Vitro-Ceram (Angelus, Londrina, Brasil) e Alglass (EDG, São Carlos, Brasil) utilizando as seguintes metodologias: 1 ­ Análise da fase vítrea por fluorescência de raios-X; 2 ­ Análise da granulometria da fase cristalina e da fase vítrea; 3 ­ Avaliação da resistência ao ensaio equibiaxial; 4 ­ Análise da microestrutura através de microscopia eletrônica de varredura (MEV). A análise por fluorescência de rx da fase vítrea dos três sistemas mostrou que as suas composições em relação aos elementos principais, como o lantânio (La2O3), alumínio (Al2O3) e silício (SiO2), são semelhantes, diferindo nos aditivos que servem para dar cor e outros ajustes. De acordo com os resultados da granulometria, pode-se observar que o In-Ceram e o Vitro-Ceram apresentam tamanhos de partículas semelhantes, e a alumina do sistema Alglass mostrou uma composição mais heterogênea com grãos maiores que 10 µm e uma grande quantidade de grãos inferiores a 0,6 µm. Isso permite uma maior aglomeração dos grãos, favorecendo a formação de uma estrutura cerâmica mais compacta após a pré-sinterização, o que gera poros de pequeno diâmetro e sem interconexão. Este fato prejudica a infiltração vítrea no compósito cerâmico final, o que pode resultar em um material com mais defeitos e uma redução nas propriedades mecânicas. Além disso, caracterizou-se também o vidro, que não apresentou semelhança entre os três sistemas, porém a sua granulometria elevada facilita seu manuseio e a justaposição sobre as estruturas de alumina pré-sinterizadas, não interferindo na sua infiltração. No ensaio de flexão, os grupos compostos pela alumina do sistema In-Ceram apresentaram as maiores médias, se diferenciando estatisticamente dos demais grupos. Os grupos com a alumina do sistema Vitro-Ceram, por mais que tenham apresentado valores maiores de resistência, não se diferenciaram estatisticamente com relação aos grupos da alumina do sistema Alglass. A infiltração de vidros diferentes em uma mesma alumina não influenciou estatisticamente a resistência mecânica dos materiais. Porém, os grupos que utilizaram a fase vítrea do Alglass apresentaram os maiores valores de resistência. Na análise de validação fractográfica nenhuma das amostras teve de ser descartada por falha na fratura, nos quais 70% dos corpos de prova dos três sistemas cerâmicos estudados tiveram fraturas de baixa força, 30% sofreram fraturas de média força e nenhuma amostra sofreu uma fratura de alta força. Os valores mais baixos encontrados para o sistema cerâmico Vitro-Ceram podem ser justificados pela presença muito maior de bolhas e poros na parte interna do material, consequentemente, esta característica se traduz em perda de resistência mecânica da cerâmica. Por mais que todos os sistemas cerâmicos estejam aptos para utilização clínica, o material In-Ceram de destaca pelas suas características e confiabilidade.

This work took place because of the very few information available about ceramic systems widely used at the dental market. The aim of this study was to characterize and analyze the microstructure, composition and mechanical properties of these materials, testing the compatibility of the systems and the assumption that they all have excellent properties. This study characterized and compared the In-Ceram ceramic systems (Vita Zahnfabrik, Bad Säckingen, Germany), Vitro-Ceram (Angelus, Londrina, Brazil) and Alglass (EDG, São Carlos, Brazil) using the following methods: 1 - Analysis of the vitreous phase by X-ray fluorescence; 2 - Analysis of the particle size of the crystalline phase and the vitreous phase; 3 - Evaluation of resistance at the equibiaxial test; 4 - Analysis of the microstructure by scanning electron microscopy (SEM). The RX fluorescence analysis of the glass phase of the three systems showed that their compositions in relation to their main elements, such as lanthanum (La2O3), aluminum (Al2O3) and silicon (SiO2), are similar, differing in the additives which serves to give color and other settings. According to the results, it can be seen that Vitro-Ceram and In-Ceram have similar particle size, and the alumina from the Alglass system showed a more heterogeneous composition with grains larger than 10 µm and a large amount of grains below 0,6 µm. This allows a larger agglomeration of the grains, forming a more compact ceramic structure after pre-sintering, which creates pores of small diameter and without interconnection. This fact undermines vitreous infiltration in the final ceramic composite, which can result in a material with more defects and a reduction of the mechanical properties. Also, the glass was also characterized, which showed no similarity between the three systems, but its high grain facilitates its handling and the overlap over the structure of pre-sintered alumina, not interfering in their infiltration. In the bending test, the groups composed by the alumina present at the In-Ceram system had the highest average, being statistically different from the other groups. Despite showing higher values of resistance, the groups with the alumina present at the Vitro-Ceram system did not statistically differ from the groups of Alglass system's alumina. The infiltration of different glasses in the same alumina did not statistically influenced the mechanical strength of the materials. However, groups using the glassy phase of Alglass showed higher resistance. In the fractographic validation analysis none of the samples had to be discarded because of its fracture failure, in which 70% of the specimens of the three studied ceramic systems had low-power fractures, 30% suffered fractures of average strength and no sample suffered a high-strength fracture. Lower values found for the Vitro-Ceram ceramic system can be justified by the presence of much larger blisters and pores inside the material, thus, this feature translates into loss of mechanical strength of the ceramic. As much as all ceramic systems are suitable for clinical use, the In-Ceram material stands out for its features and reliability.

Influência do tratamento de superfície nas características e propriedades de zircônia e na resistência de união com a porcelana de cobertura / Influence of surface treatment on the characteristics and properties of the zirconia and its bond strength with the veneering ceramic

O objetivo deste trabalho, dividido em três estudos, foi avaliar: (1) a influência do tratamento de superfície na resistência de união da zircônia com a porcelana de cobertura; (2) a resistência à flexão e as características morfológicas e estruturais das infraestruturas em zircônia após diferentes tratamentos de superfície e (3) o efeito do laser nas características da zircônia e na sua resistência de união com a porcelana de cobertura. No primeiro e segundo estudos, para os testes de resistência de união ao cisalhamento e resistência à flexão um total de 70 e 210 corpos-de-prova, respectivamente, de infraestrutura de zircônia foram obtidos e divididos aleatoriamente em 7 grupos experimentais C (Controle), JAS (Jateamento Antes Sinterização), JAAS (Jateamento Antes e Após Sinterização), JPS (Jateamento Pós Sinterização), RAS (Rocatec Antes Sinterização), RAAS (Rocatec Antes e Após Sinterização), e RPS (Rocatec Pós Sinterização). Os dados obtidos para a resistência de união ao cisalhamento mostrou uma diferença estatística significativa entre os grupos com tratamentos de superfície feitos antes e antes e após a sinterização com os grupos em que foram feitos apenas após a sinterização (p<0,001). Uma diferença significativa também foi observada entre o grupo controle e os grupos JAS, JAAS, RAS e RAAS (p<0,001), e não foi observada diferença estatística entre o grupo C e os grupos JPS e RPS (p=0,615). Os dados de resistência à flexão mostrou uma diferença estatística significativa entre os grupos com tratamentos de superfície feitos antes e antes e após a sinterização com os grupos em que foram feitos apenas após a sinterização, com exceção do grupo RAAS (p<0,001). Uma diferença significativa foi também observada entre o grupo controle e os grupos JAS, JAAS e RAS (p<0,001), e não foi observada diferença estatística entre o grupo C e os grupos JPS, RPS e RAAS. No terceiro estudo, para o teste de resistência de união ao cisalhamento um total de 60 corpos-de-prova de infraestrutura de zircônia foram obtidos e divididos aleatoriamente em 6 grupos experimentais C, LAS (Laser Antes Sinterização), LAAS (Laser Antes e Após Sinterização), LPS (Laser Pós Sinterização), JPS e RPS. ANOVA não mostrou diferença estatística significativa entre os grupos com tratamentos de superfície feitos com laser antes e antes e após a sinterização com os grupos em que foram feitos apenas após a sinterização (p>0,001). Uma diferença significativa foi observada entre o grupo LAAS e os grupos controle, JPS e RPS (p<0,001), e não foi observada diferença estatística entre o grupo C e os grupos JPS e RPS. Desta maneira, baseados nos resultados apresentados nos três estudos, pode-se concluir que tratamentos de superfícies como o jateamento com partículas de óxido de alumínio e a deposição triboquímica de sílica (Rocatec) realizados antes ou antes e após a sinterização devem ser evitados por promoverem a diminuição dos valores de resistência à flexão e união, além de formarem um superfície irregular e com defeitos na zircônia. E o uso do laser de Er: YAG pode representar um método eficaz para o tratamento de superfície da zircônia, aumentando a retenção micromecânica e melhorando a resistência de união da porcelana de cobertura a zircônia

The aim of this work, divided into three studies, was evaluate: (1) the influence surface treatment on the bond strength of zirconia with the veneering ceramic, (2) the flexural strength and structural and morphological characteristics of the infrastructure on zirconia after different surface treatments, and (3) the laser effect on the characteristics of zirconia and its bond strength with veneering ceramic. In the first and the second studies, for testing shear bond strength and flexural strength a total of 70 and 210 specimens, respectively, infrastructure zirconia were obtained and randomly divided into 7 experimental groups: C (Control), JBS (Sandblasting Before Sintering), JBAS (Sandblasting Before and After Sintering), JAS (Sandblasting After Sintering), RBS (Rocatec Before Sintering), RBAS (Rocatec Before and After Sintering) e RAS (Rocatec After Sintering). The data obtained for shear bond strength showed a statistically significant difference between groups with surface treatments performed before and after sintering and prior to the groups which were made only after sintering (p<0.001). A significant difference was also observed between the control group and groups JBS, JBAS, RBS and RBAS (p <0.001), and no statistical difference were observed between group C and groups JAS and RAS (p=0.615). The flexural strength data showed a statistically significant difference between groups with surface treatments done before and before and after sintering with the groups they were made only after sintering, with the exception of the RBAS group (p<0.001). A significant difference was also observed between the control group and groups JBS, JBAS and RBS (p <0.001), and no statistical difference were observed between group C and groups JAS, RAS and RBAS. In the third study, for testing shear bond strength a total of 60 specimens infrastructure zirconia were obtained and randomly divided into 6 experimental groups: C (Control), LBS (Laser Before Sintering), LBAS (Laser Before and After Sintering), LAS (Laser After Sintering), JAS and RAS. ANOVA showed no statistically significant difference between groups with surface treatments made with laser before and before and after sintering with the groups they were made only after sintering (p>0.001). A significant difference was observed between the LBAS group and control groups, JAS and RAS (p<0.001), and no statistical difference was observed between group C and groups JAS and RAS. Thus, based on the results presented in the three studies, concluded that surface treatments such as sandblasting with particles of aluminum oxide and silica deposition (Rocatec) performed before or before and after sintering should be avoided for promoting the decrease of the flexural and bon strength as well as form a surface with irregular and defects on zirconia. The use of Er: YAG can represent an efficient method for the surface treatment of zirconia, micromechanical increasing retention and improving the bond strength of the zirconia and vennering ceramic

Influência do tratamento de superfície na resistência de união por cisalhamento de um cerômero indireto / Surface treatment effect on shear bond strength of an indirect ceromer

Objetivo: o presente estudo realizou uma análise comparativa da resistência ao cisalhamento em dentina após diferentes tratamentos de superfície do cerômero BelleGlass HP (Kerr). Materiais e métodos: para isso, trinta molares humanos tiveram suas faces livres desgastadas até expor a superfície dentinária, nas quais foram cimentados os corpos de prova (belleGlass HP) com cimento resinoso (RelyX ARC, 3M ESPE), com três tratamentos de superfície: grupo 1 (controle): sem tratamento de superfície; grupo 2: condicionamento com ácido fluorídrico 10%; e grupo 3: jateamento com óxido de alumínio com granulação de 50um. Os espécimes foram avaliados em relação à resistência de união por cisalhamento, com velocidade de 1,0mm/min. Os dados foram analisados estatisticamente através dos testes ANOVA e Tukey, com nível de significância de 5%. Resultados: como resultado, obteve-se diferenças estatisticamente significativas (P=0,002) entre o grupo controle e o grupo 3. Conclusão: concluiu-se que o tipo de tratamento de superfície do cerômero Belleglass influenciou a resistência de união dos espécimes cimentados, sendo o jateamento com óxido de alumínio o que apresentou melhor desempenho

Aim: The present study showed a comparative analysis of shear bond strength of a ceromer after different surface treatments. Material and methods: For that, thirty human molars had their free surfaces drilled until exposing the dentin tissue, where the ceromer specimen were cemented (belleGlass HP), with three surface treatments before cementation: control group, without surface treatment (group 1); group 2: etched with fluoridric acid (10%) and group 3: etched with aluminum oxide jet (50um). All groups were tested in a universal testing machine, with 1mm/min crosshead speed, in a shear bond strength test. Data were analysed by ANOVA and Tukey tests. Results: It was shown statistically significant differences (p=0.002) between control group and group 3. Conclusions: Ceromer surface treatment Intervenes on shear bond strength to dentin, being the aluminium oxide jet the best way to improve bond strength.

Colagem indireta lingual: aplicação do óxido de alumínio na base individualizada do braquete / Lingual indirect bonding: application of aluminum oxide on individual base bracket

O estudo foi realizado com o objetivo de analisar doistratamentos de superfície feitos nas bases individualizadas de resinados braquetes linguais (pad), anteriormente a colagem ao esmaltedental humano. Os dentes foram divididos em dois grupos - grupo I:dez braquetes STB, pad confeccionado com resina Filtek Z-250 corAl (3M Espe), sem aplicação do óxido de alumínio na superfície deresina do pad previamente a colagem indireta; grupo 11:dez braquetes8TB, pad confeccionado com resina Filtek Z-250 cor Al (3M Espe),com aplicação do óxido de alumínio na superfície de resina do padpreviamente a colagem indireta. Avaliou-se à força de resistência sobcisalhamento 24 horas após a colagem em uma máquina de ensaiosmecânicos Mini-Instron modelo 4.442. Com base nos resultados desteestudo, concluiu-se que a resistência a descolagem dos braqueteslinguais por cisalhamento não foi aumentada com a aplicação préviado jato de óxido de alumínio na superfície do pad.

The aim of this study was to analyze two surface treatmentsmade on the basis of the lingual brackets pad prior to bondingto human enamel. The teeth were divided into two groups: Group I: i OSTB brackets, pad made of Filtek Z-250 A1 (3M Espe) resin, withoutapplication of aluminum oxide on the surface of the pad prior to resinbonding. Group li: i O STB brackets, pad made of Filtek Z-250 Ai(3M Espe) resin, with application of aluminum oxide on the surface ofthe pad prior to resin. The shear resistance force was evaluated 24hours after the pad confection in a mechanical testing machine Instronmodel 4442 Mini. Based on the results of this study it was concludedthat the resistance of lingual bracket debonding was not increasedwith the prior application of the air abrasion of aluminum oxide on thesurface of the pad.

Influência de diferentes métodos de condicionamento superficial em pinos pré-fabricados resinosos fibro-reforçados em vidro e quartzo na resistência adesiva a compósito de polimerização dual: teste de push-out / Influence of different pretreatments in glass and quartz fiber posts on the bond strength of a dual-cure resin core material: push-out test

O objetivo deste estudo foi realizar uma avaliação tridimensional da rugosidade superficial em 3 tipos de pinos de fibra - DT LightPost®, FRC Postec Plus® e Transluma Post™ - submetidos a diferentes tratamentos de superfície e avaliar os efeitos dos pré-tratamentos na resistência adesiva a um compósito de presa dual Biscore™. Os tratamentos de superfície foram: imersão em ácido hidrofluorídrico, jateamento com óxido de alumínio a 50µm, imersão em peróxido de hidrogênio, jateamento com óxido de alumínio a 50µm seguido de imersão em ácido hidrofluorídrico e jateamento com óxido de alumínio a 50µm seguido de imersão em peróxido de hidrogênio. No experimento 1, 75 pinos foram divididos em 3 grupos (n = 25), de acordo com seu fabricante e subdivididos em cinco subgrupos. A rugosidade superficial foi medida usando um rugosímetro tridimensional e analisada com o software de análise 3D. Os valores de rugosidade foram obtidos antes e após diferentes tratamentos de superfície na área dos mesmos corpos-de-prova. Para o experimento 2, foram utilizados os mesmos corpos-de-prova, os mesmos grupos e subgrupos do experimento 1, tendo sido adicionado o subgrupo de controle (n=90) e a resistência adesiva a um compósito presa dual Biscore™ foi mensurada através de um teste push-out. A resistência adesiva foi medida em uma máquina universal de ensaios, com uma célula de carga tipo SLBL-5kN em uma velocidade de 0,5 mm / min. Os resultados do experimento 1 foram analisados através de um teste estatístico t-Student. Jateamento e jateamento seguido de imersão em ácido hidrofluorídrico produziram um aumento estatisticamente significante na rugosidade, contudo somente o tratamento por jateamento proporcionou um aumento significativo nos valores de rugosidade. Os resultados do experimento 2 foram obtidos através de um um teste t-unilateral de hipótese com variância desconhecida. Concluiu-se que o jateamento com óxido de alumínio a 50μm em uma distância de 30 mm a 2,5 bar ...

The aim of this study was to perform a tridimensional surface roughness test evaluation of different surface treatments to 3 types of fiber posts - DT LightPost®, FRC Postec Plus® e Transluma Post™ - and evaluate the effects of the different pretreatments on the bond strength of a dual-cure resin core material Biscore™. The different surface treatments were: immersion in hydrofluoric acid, sandblasting abrasion with 50 µ alumina particles, immersion in hydrogen peroxide, sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrofluoric acid and sandblasting abrasion with 50 µ alumina particles followed by immersion in hydrogen peroxide. In the first experiment seventy five fiber posts were divided into 3 groups (n = 25), according to their manufacturer and subdivided into 5 subgroups. Surface roughness was measured using a tridimensional surface roughness test and analyzed with 3D analysis software. Surface roughness was obtained before and after the different surface treatments at the same post area. In the second experiment the same samples divided in groups and subgroups were used, but a control group (no treatment) was added (n = 90) and the bond strength to a composite resin core material Biscore™ was measured using a push-out design. The interfacial push-out bond strength was measured in a universal testing machine, with a load cell type SLBL-5kN at a crosshead speed of 0.5 mm/min. Results in experiment 1 were statistically analyzed using Student´s t-Test. Sandblasting and sandblasting followed by immersion in hydrofluoric acid produced a significant increase in roughness, but the sandblasting treatment was able to provide a significant roughness increase. Results in experiment 2 were statistically analysed using one-sided t-Test of Hypothesis with unknown variance. It was concluded that sandblasting airborne-particle abrasion with alumina 50µ at a distance of 30 mm at 2.5 bars pressure for 5 seconds was ...