Pesqui. bras. odontopediatria clín. integr ; 23: e220022, 2023. tab, graf
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-1529120

RESUMO

ABSTRACT Objective: To evaluate the 24-month clinical performance of composite resin restorations with and without polyethylene fiber in the first permanent molars of pediatric patients with extensive caries. Material and Methods: In total, 75 Class II restorations were placed in the permanent molar teeth of 75 children (mean age 11.3 years) with (FC; n=38) or without (C; n=37) fiber. One operator placed all the restorations. The restorations were evaluated using the modified USPHS criteria in terms of retention, color match, marginal discoloration, anatomic form, marginal adaptation, secondary caries, and postoperative sensitivity. Statistical data were analyzed using chi-square and Cochran tests (p<0.05). Results: At the end of two years, 65 restorations (FC:31; C:34) were followed up. No changes were observed during the first six months. After 24 months of follow-up, there were minor changes in marginal adaptation and marginal color in both groups; however, no statistically significant difference was observed between the clinical performances for all criteria (p>0.05). Conclusion: Extensive composite restorations with or without fibers displayed good clinical performance in high load-bearing areas after 24 months.


Assuntos
Humanos , Masculino , Feminino , Criança , Adolescente , Dentição Permanente , Polietileno , Técnicas In Vitro/métodos , Radiografia Dentária , Distribuição de Qui-Quadrado , Estatísticas não Paramétricas
2.
Araçatuba; s.n; 2020. 109 p. ilus, tab.
Tese em Inglês | BBO - Odontologia, LILACS | ID: biblio-1390946

RESUMO

O objetivo deste estudo foi avaliar a influência das suplementações de ômega-3 e melatonina sobre a resposta tecidual de cimentos endodônticos. Foram utilizados 72 ratos Wistar alocados em 3 grupos principais: ratos controle tratados com água (TA), ratos tratados com ômega-3 (TO) e ratos tratados com melatonina (TM). Em cada rato foram implantados 4 tubos de polietileno, sendo 1 tubo vazio para controle, e os demais contendo um dos cimentos endodônticos: Sealapex®, AH Plus® e Endofil®. Os períodos de avaliação foram de 5, 15 e 30 dias (n=8/tempo). Após eutanásia, os tubos foram removidos e processados para análise microscópica. A inflamação foi avaliada em coloração de H.E. e técnica imunohistoquímica para IL-6 e TNF-α, o colágeno pela coloração de Picrosírios red e a deposição de cálcio, pela técnica de von Kossa e luz polarizada. A estatística foi realizada de acordo com cada tipo de análise, com nível de significância de 5% (p <0,05) e considerando cada tipo de suplementação comparado ao controle. Podese observar infiltrado inflamatório reduzido com o tempo e de menor intensidade nos grupos TO ou TM comparado a TA, assim como a imunomarcação para IL-6 e TNF-α. O cimento Sealapex induziu menor inflamação aos 30 dias, tanto em TO quanto em TM. Em relação ao colágeno, foi observado maior expressão de fibras imaturas no grupo TO aos 15 e 30 dias, entretanto, no grupo TM, foi observado maior quantidade de fibras maduras aos 5 dias, ambos comparados a TA. O cimento Sealapex foi único a apresentar marcação positiva para cálcio e cristais de calcita birrefringentes à luz polarizada, independente das suplementações. Pode-se concluir que a suplementação com ômega-3 ou melatonina modularam a inflamação, diminuindo o infiltrado inflamatório e a imunomarcação de IL-6 e TNF- α, estimularam o reparo tecidual e não influenciaram no processo de deposição de cálcio(AU)


The aim of this study was to evaluate the influence of omega-3 and melatonin supplements on the tissue response of endodontic sealers. 72 Wistar rats were allocated in 3 main groups: control rats treated with water (TW), rats treated with omega-3 (TO) and rats treated with melatonin (TM). In each rat, 4 polyethylene tubes were implanted, 1 empty tube for control, and the others containing one of the endodontic sealers: Sealapex®, AH Plus® and Endofil®. The evaluation periods were of 5, 15 and 30 days (n = 8 / time). After euthanasia, the tubes were removed and processed for microscopic analysis. Inflammation was evaluated in H.E. staining and immunohistochemical technique for IL-6 and TNF-α, collagen by Picrosírios red staining and calcium deposition by von Kossa and polarized light technique. Statistics were performed according to each type of analysis, with a significance level of 5% (p <0.05) and considering each type of supplementation compared to the control. It is possible to observe a reduced inflammatory infiltrate over time and less intensity in the TO or TM groups compared to TW, as well as the immunolabeling for IL-6 and TNF-α. Sealapex sealer induced less inflammation at 30 days, both in TO and TM. Regarding collagen, a greater expression of immature fibers was observed in the TO group at 15 and 30 days, however, in the TM group, a greater amount of mature fibers was observed at 5 days, both compared to TW. Sealapex sealer was the only one to present positive marking for calcium and birefringent calcite crystals under polarized light, regardless of supplementation. It can be concluded that supplementation with omega-3 or melatonin modulated the inflammation, reducing the inflammatory infiltrate and the immunolabeling of IL-6 and TNF-α, they stimulated tissue repair and did not influence the calcium deposition process(AU)


Assuntos
Animais , Ratos , Ácidos Graxos Ômega-3 , Cimentos Dentários , Melatonina , Cálcio , Colágeno , Ratos Wistar , Polietileno , Biomineralização , Inflamação
3.
Araçatuba; s.n; 2017. 70 p. tab, ilus.
Tese em Português | BBO - Odontologia | ID: biblio-915541

RESUMO

Entre os materiais aloplásticos, o Medpor® apresentou um aumento consideravel no uso de 17% a 30%, portanto o objetivo desse trabalho foi avaliar a utilização do Medpor® na reconstrução do assoalho orbitário. Foram utilizados 18 ratos que sofreram trauma cirúrgico no assoalho orbitário, simulando uma fratura tipo "blow-out". O lado direito do animal recebeu implante de Medpor® e o lado esquerdo não recebeu qualquer tipo de material. Nos períodos de 15, 40 e 90 dias foram realizadas as eutanásias e obtenção das peças para processamento histológico e imunohistoquímico. Os cortes obtidos foram corados com hematoxilina e eosina, tricrômico de Masson e marcação imunohistoquímica nos períodos de 15, 40 e 90 dias com a osteocalcina e RUNX2. O processo de reparo no lado controle finalizou com neoformação óssea aos 40 dias e perda do contorno ósseo inicial, criando um defeito no assoalho de órbita. O grupo tratado mostrou prevalência de tecido conjuntivo em contato com o implante de Medpor®, tanto em sua periferia quanto no seu interior. Não houve processo inflamatório intenso e ou agudo junto ao material. A imunomarcação mostrou escores intensos de OC após 15 dias de pósoperatórios e manteve expressão moderada após 40 e 90 dias pós-operatório, a RUNX2 foi moderadamente expressa em todos os períodos avaliados. Concluimos que o polietileno poroso (Medpor®) é um biomaterial bionert seguro e eficaz, a sua presença levou ao reparo ósseo local e compensou a ausência de tecido ósseo na sustentação do globo ocular(AU)


The aim of this research was to assessed histological and immunohistochemi cal properties in the use of porous polyethylene (Medpor®) for orbital floor reconstruction. Under general anesthesia 18 male rats (Rattus, norvegicus, albinus, Wistar) underwent bilateral surgical defect, simulating blowout fracture and infraorbital rim. Groups were divided as follow: GI control group and GII surgical defects were reconstructed with Medpor®. After 15, 40, and 90 days animals were euthanized with anesthetic overdose. Orbital specimens were laboratorial process, coronal slices were stained in Hematoxylin and Eosin and Masson trichrome. Immunohistochemical assess of osteocalcin (OC) and Corebinding factor alpha1 (Cbfa1) were performed. Bone repair at the control group was achieved after 40 days with loss of the orbital rim and lack of ocular support. Immunolabeling showed intense scores of OC after 15 days post-operative and maintain moderate expression after 40 and 90 days postoperative, Cbfa1 was moderately express within all the periods evaluated. Medpor® group showed fibrous tissue in contact with the implant in the inner and outer surface, without newbone formation and without intense inflammatory infiltrate nearby the biomaterial, the Medpor® gave enough support for the ocularglobe(AU)


Assuntos
Animais , Ratos , Fraturas Orbitárias , Polietileno , Materiais Biocompatíveis , Órbita/cirurgia , Ratos Wistar
4.
J. appl. oral sci ; 23(6): 614-622, Nov.-Dec. 2015. tab, graf
Artigo em Inglês | LILACS, BBO - Odontologia | ID: lil-769822

RESUMO

ABSTRACT Plasma technology has the potential to improve the adherence of fibers to polymeric matrices, and there are prospects for its application in dentistry to reinforce the dental particulate composite. Objectives This study aimed to investigate the effect of oxygen or argon plasma treatment on polyethylene fibers. Material and Methods Connect, Construct, InFibra, and InFibra treated with oxygen or argon plasma were topographically evaluated by scanning electron microscopy (SEM), and chemically by X-ray photoelectron spectroscopy (XPS). For bending analysis, one indirect composite (Signum) was reinforced with polyethylene fiber (Connect, Construct, or InFibra). The InFibra fiber was subjected to three different treatments: (1) single application of silane, (2) oxygen or argon plasma for 1 or 3 min, (3) oxygen or argon plasma and subsequent application of silane. The samples (25x2x2 mm), 6 unreinforced and 60 reinforced with fibers, were subjected to three-point loading tests to obtain their flexural strength and deflection. The results were statistically analyzed with ANOVA and the Bonferroni correction for multiple comparison tests. Results SEM analysis showed that oxygen and argon plasma treatments promote roughness on the polyethylene fiber surface. X-ray photoelectron spectroscopy (XPS) analysis shows that both plasmas were effective in incorporating oxygenated functional groups. Argon or oxygen plasma treatment affected the flexural strength and deflection of a fiber reinforced composite. The application of silane does not promote an increase in the flexural strength of the reinforced composites. Conclusions Oxygen and argon plasma treatments were effective in incorporating oxygenated functional groups and surface roughness. The highest strength values were obtained in the group reinforced with polyethylene fibers treated with oxygen plasma for 3 min.


Assuntos
Argônio/química , Oxigênio/química , Plasma/química , Polietileno/química , Análise de Variância , Resinas Compostas/química , Colagem Dentária/métodos , Teste de Materiais , Microscopia Eletrônica de Varredura , Espectroscopia Fotoeletrônica , Maleabilidade , Valores de Referência , Silanos/química , Propriedades de Superfície , Fatores de Tempo
5.
J. appl. oral sci ; 23(1): 42-48, Jan-Feb/2015. tab, graf
Artigo em Inglês | LILACS, BBO - Odontologia | ID: lil-741586

RESUMO

Objective: To evaluate the response of rat subcutaneous tissue in implanted polyethylene tubes that were filled with GMTA Angelus and Portland cements containing different arsenic concentrations. Material and Methods: Atomic absorption spectrophotometry was utilized to obtain the values of the arsenic concentration in the materials. Thirty-six rats were divided into 3 groups of 12 animals for each experimental period. Each animal received two implants of polyethylene tubes filled with different test cements and the lateral of the tubes was used as a control group. After 15, 30 and 60 days of implantation, the animals were killed and the specimens were prepared for descriptive and morphometric analysis considering: inflammatory cells, collagen fibers, fibroblasts, blood vessels and other components. The results were analyzed utilizing the Kuskal-Wallis test and the Dunn's Multiple test for comparison (p<0.05). Results: The materials showed, according to atomic absorption spectrophotometry, the following doses of arsenic: GMTA Angelus: 5.01 mg/kg, WPC Irajazinho: 0.69 mg/kg, GPC Minetti: 18.46 mg/kg and GPC Votoran: 10.76 mg/kg. In a 60-day periods, all specimens displayed a neoformation of connective tissue with a structure of fibrocellular aspect (capsule). Control groups and MTA Angelus produced the lower amount of inflammatory reaction and GPC Minetti, the highest reaction. Conclusions: There was no direct relationship between the concentration of arsenic present in the composition of the materials and the intensity of the inflammatory reactions. Higher values, as 18.46 mg/kg of arsenic in the cement, produce characteristics of severe inflammation reaction at the 60-day period. The best results were found in MTA angelus. .


Assuntos
Animais , Masculino , Arsênio/toxicidade , Bismuto/toxicidade , Compostos de Cálcio/toxicidade , Cimentos Dentários/toxicidade , Óxidos/toxicidade , Silicatos/toxicidade , Tela Subcutânea/efeitos dos fármacos , Arsênio/administração & dosagem , Bismuto/química , Vasos Sanguíneos/efeitos dos fármacos , Colágeno/efeitos dos fármacos , Cimentos Dentários/química , Fibroblastos/efeitos dos fármacos , Teste de Materiais , Óxidos/química , Polietileno/química , Ratos Wistar , Valores de Referência , Espectrofotometria Atômica , Fatores de Tempo
6.
Arch. oral res. (Impr.) ; 8(2): 97-101, maio-ago. 2012. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: lil-706357

RESUMO

Objectives: Different fiber types are available for reinforcing composite restorations. Little information exists regarding flexural strength of various fiber used to reinforce direct composites. This in vitro study examined the flexural strength of polyethylene and glass fibers when used to reinforce composite and influence of moisture exposure on the same materials. Materials and methods: The two types of fiber were used to reinforce blocks of composite (RX Flow, Dental Life Sciences) prepared to test flexural properties and compared with the unreinforced controls. Mean flexural strengths values were determined in a 3-point bend test at a crosshead speed of 8 mm/min by use of a universal testing machine. Results: Significant increases in mean flexural strength were found for all fiber-reinforced groups in comparison to the unreinforced controls at both before and after moisture exposure. The polyethylene fiber gave the greatest reinforcing effect. After 1 month of storage in an artificial saliva substitute, a significant decline occurred in the mean flexural strength of all the groups tested. Conclusion: Within the limitations of this study, the choice of fiber type was shown to have a significant increase on the flexural properties of the fiber-reinforced composite. Polyethylene fibers increased the flexural strength of the composite the most.


Objetivo: Diferentes tipos de fibras estão disponíveis para reforçar restaurações em resinas compostas. Há pouca informação sobre a resistência flexural de fibras usadas para reforçar compósitos diretos. Este estudo in vitro avaliou a resistência à flexão de fibras de polietileno e de vidro, quando usadas para reforçar resina composta e a influência da exposição à umidade sobre os mesmos materiais. Materiais e métodos: Os dois tipos de fibras foram usados para reforçar blocos de resina composta (RX Flow, Dental Life Sciences), preparados para testar as propriedades mecânicas e comparados com os controles não reforçados. Os valores médiosde flexão foram determinados em um ensaio de flexão de três pontos a uma velocidade de 8 mm/min em uma máquina de ensaio universal. Resultados: Um aumento significativo na resistência à flexão média foi encontrado para todos os grupos reforçados com fibras, em comparação com os controles não reforçadas, tanto antes quanto depois da exposição à umidade. A fibra de polietileno forneceu o maior efeito de reforço. Após 1 mês de armazenamento em saliva artificial, houve uma diminuição significativa na força média de flexão de todos os grupos testados. Conclusão: Dentro das limitações do presente estudo, o tipo de fibra demonstrou exercer um aumento significativo sobre as propriedades de flexão do compósito reforçado com fibras. Fibras de polietileno aumentaram mais a resistência à flexão do compósito.


Assuntos
Polietileno/química , Resinas Compostas/química , Vidro/química , Análise de Variância , Teste de Materiais , Resistência à Tração , Fatores de Tempo
7.
Londrina; s.n; 2012. 52 p. ilus, tab.
Tese em Português | LILACS, BBO - Odontologia | ID: lil-681493

RESUMO

Esta dissertação foi dividida em dois capítulos. O Capítulo 1 avaliou a morfologia superficial (in vitro) e a densidade radiográfica (in vivo) de dois tipos de implantes de polietileno poroso de alta densidade (PPAD): o primeiro tipo, composto apenas por grânulos de polietileno foi denominado padrão (PPADp); e o segundo tipo foi uma versão do primeiro modificado por meio da adição de um marcador radiográfico radiopaco, o óxido de bismuto a 7% (PPADmr). A partir de lâminas padronizadas de PPADp e PPADmr com medidas de 40x50x2mm fornecidas pelo fabricante, foram confeccionados 90 corpos de provas cilíndricos (45 PPADp e 45 PPADmr), medindo 4,5mm de diâmetro por 2mm de altura, sendo estes submetidos à esterilização por meio de óxido de etileno. Para avaliação da morfologia topográfica in vitro foram selecionados aleatoriamente 5 corpos de prova de cada tipo de PPAD os quais foram submetidos a microscopia eletrônica de varredura (MEV) para análise superficial descritiva e mensuração dos espaços inter-grânulos (poros). Os dois tipos de PPAD apresentaram estruturas semelhantes entre si com relação ao tamanho e distribuição dos poros aleatoriamente; ainda foi demonstrada a presença dos cristais de óxido de bismuto no PPADmr, onde estes se apresentavam distribuídos uniformemente sobre a superfície dos corpos de prova. Os valores de distância mínima entre poros do PPADp e PPADmr foram de 136,4µm e 144,2µm respectivamente. Para mensuração da densidade radiográfica dos PPAD, foram empregados 20 coelhos, adultos, machos, da raça Nova Zelândia que foram submetidos à implantação de 4 corpos de prova em cada animal, sendo 2 implantes em defeitos ósseos criados na calota craniana (1 PPADp e 1 PPADmr) e 2 implantes em o tendão do músculo flexor digital superficial das patas posteriores (1 PPADp e 1 PPADmr). Os animais foram divididos em 4 grupos de 5 animais cada, diferindo entre sí o período ao qual os animais foram mortos (7, 14, 45 e 90 dias pós-operatórios), uma vez que...


Assuntos
Animais , Masculino , Coelhos , Osso e Ossos , Tecido Conjuntivo , Teste de Materiais , Microscopia Eletrônica de Varredura , Fotomicrografia , Polietileno , Tomografia
8.
Bauru; s.n; 2011. 109 p. ilus, tab, graf.
Tese em Português | BBO - Odontologia | ID: biblio-866057

RESUMO

Os nervos periféricos são extensões do sistema nervoso central e responsáveis pela interação das atividades das extremidades, em suas funções sensitiva e motora. São vulneráveis aos mesmos tipos de traumas que afetam outros tecidos: contusão, compressão, esmagamento, estiramento, avulsão e laceração. Desta forma, a interrupção de continuidade da estrutura do nervo, por algum tipo de trauma, resulta na interrupção de transmissão dos impulsos nervosos e na desorganização de suas atividades funcionais. Para tanto, em vista da evolução tecnológica e o desenvolvimento de equipamentos mais sofisticados, a microcirurgia vem ganhando cada vez mais espaço no campo da investigação experimental referente a recuperação de nervos periféricos lesionados. Em uma secção simples, sem perda tecidual, a neurorrafia denominada término-terminal apresenta bons resultados, contudo, quando ocorre perda de tecido nervoso ou, não se têm mais os cotos distais do nervo, outras técnicas devem ser empregadas, até porque, não se pode de modo algum tencionar o nervo numa tentativa de coaptá-lo novamente. Várias técnicas de tubulização utilizando-se materiais biológicos e não biológicos, para criar um meio por onde ocorrerá a regeneração nervosa já foram ou ainda estão sendo testados com resultados insatisfatórios sob o aspecto funcional.É sabido que em um trauma sem perda tecidual, numa neuropraxia, por exemplo, o nervo recupera espontaneamente de forma satisfatória. É sabido também que em um feixe vásculo-nervoso, o nervo periférico encontra-se em íntimo contato com a adventícia de artérias e veias. A adventícia dos vasos é constituída por tecido conjuntivo frouxo, rico em adipócitos. Assim, em um trauma, os neuritos oriundos do coto proximal do nervo lesado, ficam diretamente em contato com esses adipócitos. Seguindo este raciocínio, e com base em trabalhos anteriores onde foi usada veia preenchida com músculo esquelético a fresco como enxerto...


Peripheral nerves are extensions of the central nervous system and are responsible for the interaction of the activities of the extremities in their sensory and motor function. They are vulnerable to these types of injuries that affect other tissues: contusion, compression, crush, stretch, tear and avulsion. Thus, the interruption of continuity of the nerve structure, due to some sort of trauma, results in the interruption of transmission of nerve impulses and disruption of their functional activities. Therefore, in view of technological evolution and development of more sophisticated equipment, microsurgery is gaining more space in the field of experimental research concerning the recovery of injured peripheral nerves. In a single section, without loss of tissue, called the end-terminal neurorrhaphy was also good, however, when there is loss of nervous tissue or, if not longer have the distal nerve stumps, other techniques must be employed, because, in any circumstance the nerve should be tensioned as an attempt to coaptation again. Several techniques of tubing, using biological materials and non-biological means to create a place where nerve regeneration have been or are still being tested with unsatisfactory results in the functional aspect. It is known that in a trauma without loss of tissue, a neuropraxia, for example, the nerve recovers spontaneously and satisfactorily. It is also known that in a neurovascular bundle, the peripheral nerve is in close contact with the adventitia of arteries and veins. The adventitia of the vessels is composed of loose connective tissue rich in adipocytes. Thus, in trauma, the neurites from the proximal stump of injured nerve, are directly in contact with these adipocytes. Following this reasoning, and based on previous work where it was used vein filled with fresh skeletal muscle as a graft, decided to test the possibility of axonal growth by grafting polyethylene tube filled with autologous adipose tissue...


Assuntos
Animais , Masculino , Ratos , Nervos Periféricos/transplante , Polietileno/uso terapêutico , Tecido Adiposo/transplante , Axônios/fisiologia , Ratos Wistar , Reprodutibilidade dos Testes , Transplante Autólogo/métodos
9.
Bauru; s.n; 2011. 138 p.
Tese em Português | BBO - Odontologia | ID: biblio-866193

RESUMO

Problemas relacionados a lesões de nervos periféricos com consequentes perdas sensitivas e motoras tornaram-se frequentes no dia a dia da prática clínica e hospitalar, em consequência do aumento da violência urbana, dos acidentes de trânsito, acidentes profissionais e domésticos. Por esta razão, a busca por estratégias e técnicas que possam reparar a lesão nervosa e restabelecer a função do tecido lesado é importante e de grande valia no âmbito da saúde. Para reparar lesões nervosas com perda de tecido nervoso, várias técnicas cirúrgicas têm sido utilizadas, uma das técnicas mais comum é o uso do enxerto autógeno, mas técnicas alternativas têm sido propostas a fim de evitar as complicações ao local doador e acelerar o processo de regeneração nervosa como, por exemplo, a da tubulização. O uso desta técnica tem sido mais utilizado para o preenchimento dos tubos com substâncias que acelerem ou induzam o crescimento axonal. Baseado no exposto anteriormente pensou-se na realização desta pesquisa com o objetivo de verificar se uso de tubo de polietileno poroso preenchido ou não com tecido adiposo na técnica de tubulização alteraria a recuperação dos músculos sóleo (de contração lenta) e Extensor longo dos dedos (de contração rápida). Para isso foram utilizados 45 ratos (Rattus norvegicus),Wistar, machos, que foram divididos em cinco grupos, sendo, três controles, e dois experimentais. Nos grupos experimentais foram realizados a tubulização de polietilieno poroso preenchido ou não com tecido adiposo (GECP e GESP, respectivamente). Os tubos foram testados para avaliar a eficácia em reduzir a lacuna crítica de 10 mm do nervo isquiático. Os animais dos grupos experimentais foram sacrificados 150 dias após a cirurgia. Dos três grupos controles, dois não sofreram intervenção cirúrgica, e receberam o nome de inicial (GCI) e final (GCF) e foram sacrificados com 80 e 230 dias de vida respectivamente. E no outro grupo controle, denominado desnervado (GCD)...


Problems related to injuries of peripheral nerves with consequent sensory and motor losses are seen more frequently in daily clinical and hospital practice due to an increase in urban violence, traffic accidents, domestic and labour accidents. For this reason, the search for strategies and techniques that can repair nerve damage and restore function of damaged tissue is important and of great value in health care. To repair nerve damage with loss of nerve tissue, several surgical techniques have been used, one of the common techniques is the use of the autograft, but alternative techniques have been proposed to avoid complications to the donor site and accelerate the process of nerve regeneration, such as tubulization. The use of this technique has been further utilized by filling the tubes with substances that speed up or induce axonal growth. Based on the previous work, in this research we wanted to see whether tubilization with the help of porous polyethylene tube filled with and without adipose tissue alter the recovery of the soleus (slow twitch) and extensor digitorum longus (fast twitch) muscles. For this we used 45 male Wistar rats (Rattus norvegicus), who were divided into five groups, three control and two experimental. In the experimental groups, tubulization was performed using porous polyethylene filled with (GECP) and without adipose tissue (GESP). The conduits were tested for efficacy in bridging the critical gap length of 10 mm in sciatic nerves.The animals of experimental groups were sacrificed 150 days after surgery. Of the three control groups, two did not undergo surgery, and were named as (GCI) for Initial and (GCF) for final group in which the animals were sacrificed at 80 and 230 days old respectively. And another control group, called denervated (GCD), the animals were subjected to sciatic nerve section. Prior to sacrifice the animals were subjected to functional analysis of gait. During the sacrifice, samples were taken...


Assuntos
Animais , Masculino , Ratos , Músculos/inervação , Polietileno/uso terapêutico , Tecido Adiposo/transplante , Músculos/anatomia & histologia , Ratos Wistar , Tecido Nervoso/transplante
10.
Bauru; s.n; 2011. 132 p. ilus, tab, graf.
Tese em Português | BBO - Odontologia | ID: biblio-865831

RESUMO

O MTA (Agregado Trióxido Mineral) tem sido utilizado na endodontia com diferentes finalidades terapêuticas. Essencialmente ele é constituído pelo cimento Portland acrescido de um radiopacificador. Entre seus componentes, é destacada a presença do arsênico, o qual sofre variação de concentração em função da origem do calcário. A dúvida é que se diferentes concentrações de arsênico representam alguma influência na sua biocompatibilidade. O objetivo deste estudo foi avaliar, microscopicamente, a reação tecidual em subcutâneo de ratos frente a cimentos Portland contendo diferentes concentrações de arsênico. Foram utilizados 36 ratos Wistar albinos, distribuídos em 4 grupos experimentais segundo o material empregado perfazendo um total de 6 implantes por período (15, 30 e 60 dias). A lateral dos tubos serviram como grupo controle. Após 15, 30 e 60 dias, os animais foram mortos e os espécimes foram preparados histotecnicamente para análise microscópica. Os dados da avaliação morfométrica foram submetidos à análise de variância a dois critérios (ANOVA) e teste de Tukey para a comparação (p<0,05). Os resultados mostraram uma maior densidade de volume de células inflamatórias aos 15 dias, com redução dessa densidade com o passar do tempo para todos os materiais. Os resultados da análise descritiva mostraram inflamação crônica induzida pelos materiais, com intensidade de leve a moderada, e organização de uma cápsula fibrosa ao redor de todos os espécimes e em todos os períodos. Os cimentos analisados produziram respostas inflamatórias semelhantes, mesmo apresentando quantidades diferentes de arsênico na composição, apenas com diferença estatisticamente significante entre o cimento Portland cinza Votoran e os demais cimentos nos três períodos estudados.Título em inglêsMicroscopic evaluation of the tissue reaction in subcutaneous of rats to Portland cements containing different.


The MTA (Mineral Trioxide Aggregate) has been used in Endodontics for different therapeutic purposes. Essentially, it is composed of Portland cement with addition of a radiopacifier. Its components include arsenic, whose concentration is variable according to the origin of the calcareous. There is doubt whether different arsenic concentrations might influence its biocompatibility. This microscopic study evaluated the reaction of subcutaneous tissue of rats to Portland cements containing different arsenic concentrations. The study was conducted on 36 albinus Wistar rats, divided in 12 animals for each study group. Each animal received two implants of polyethylene tubes, completely filled with the test cements, and the lateral aspect of the tubes was taken as control group. The animals were killed after 15, 30 and 60 days and the specimens were submitted to histotechnical preparation for microscopic analysis. Data of the morphometric analysis were submitted to two-way analysis of variance (ANOVA) and the Tukey test for comparison (p<0.05). The results evidenced greater density of volume of inflammatory cells at 15 days, which was reduced with time for all materials. The results of this descriptive analysis demonstrated chronic inflammation induced by the materials, of mild to moderate intensity, and organization of a fibrous capsule around all specimens and in all periods. The cements induced similar tissue responses, despite the different arsenic concentrations in their composition.


Assuntos
Animais , Ratos , Cimentos Dentários/farmacologia , Tela Subcutânea , Materiais Biocompatíveis , Compostos de Alumínio/farmacologia , Compostos de Cálcio/química , Teste de Materiais , Óxidos/farmacologia , Polietileno/farmacologia , Silicatos/química , Fatores de Tempo
11.
Rev. cir. traumatol. buco-maxilo-fac ; 7(3): 49-58, jul.-set. 2007. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: biblio-873485

RESUMO

O objetivo deste estudo foi comparar histologicamente o comportamento de implantes nacionais de polietilenoporoso (Polipore®) e de enxerto ósseo autógeno em defeitos ósseos em osso parietal de coelho. Foram utilizados 20 coelhos, os quais receberam osteotomias parietais bilaterais com o auxílio de uma trefina de 6mm dediâmetro. No Grupo I (GI), a cavidade foi preenchida com enxerto ósseo retirado do lado oposto, e, no GrupoII (GII), a cavidade foi preenchida com Polipore®. Não foram utilizados meios de fixação para os enxertos e implantes. Após 5, 15, 30, 60 e 120 dias, ocorreu a eutanásia dos animais, e as calotas cranianas foram processadas, segundo rotina histológica para coloração em H.E. Observou-se reação inflamatória discreta no(GI) aos 5 dias e moderada no GII, persistindo até aos 30 dias no GII. Os enxertos ósseos apresentaram-se incorporados ao leito receptor aos 120 dias. E somente aos 120 dias, no GII, observou-se presença de tecido conjuntivo no interior dos poros do implante. Concluímos que os enxertos foram eficientes na reparação do defeito ósseo, devido à incorporação ao leito receptor; O Polipore® foi biocompatível, mas não possui quantidadee tamanho de poros adequados para permitir o crescimento fibrovascular no interior do material


The aim of this study was to histologically compare national porous polyethylene implants and autogenous bone graft in cranial vault defects in rabbits. Cranial vaults defects were surgically created with a trephineburr of 6mm diameter in the parietal bones of 20 rabbits. In group I (GI) the bone defects were filled with autogenous bone graft from the contralateral parietal side, and in group II (GII), the bone defects were filledwith Polipore®. The grafts and implants were not fixed on the site. After 5, 15, 30, 60 and 120 days the animals were sacrificed and the cranial vaults were processed according to histological routine for stainingwith H&E. On the 5th day a discreet inflammatory reaction was observed in GI , while in GII, a moderate, inflammatory reaction persisted up to the 30th day. The bone grafts were incorporated to the host bedwithin 120 days. Only then, connective fibrous tissue was observed into the pores of the implant in GII. Bone grafts can efficiently repair bone defects, due to their incorporation into the bone host bed; the Polipore®implant is biocompatible, but does not have the adequate quantity and size of pores to permit fibrovascular tissue ingrowth into the material


Assuntos
Coelhos , Implantes Experimentais , Osso Parietal , Polietileno , Transplante Autólogo
12.
JBC j. bras. clin. odontol. integr ; 10(54): 219-223, jul.-set. 2006. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-500803

RESUMO

É apresentado um caso clínico que tem como objetivo mostrar um método alternativo na confecção de uma prótese fixa temporária, visando a espera durante um período de osseointegração. Utilizou-se uma fibra de polietileno Connect (Kerr), como infra-estrutura para suportar um pôntico em resina composta Solidex (Shofu). Este método elimina a necessidade da tradicional estrutura metálica para reforçar a prótese fixa. As fibras reforçadas por compósitos têm a vantagem de um custo menor, menor tempo clínico e um mínimo de potencial de toxicidade na técnica, e ainda uma estética mais favorável no resultado final pela ausência de metal. Como resultado deste trabalho clínico, temos: alto resultado estético e uma adaptação psicológica favorável durante o período de espera para a osseointegração.


Assuntos
Humanos , Feminino , Pessoa de Meia-Idade , Compômeros , Prótese Adesiva , Polietileno , Prótese Parcial Temporária , Estética Dentária/psicologia , Osseointegração
13.
J. appl. oral sci ; 14(2): 100-104, Apr. 2006. tab, graf
Artigo em Inglês | LILACS, BBO - Odontologia | ID: biblio-873197

RESUMO

O objetivo deste estudo foi avaliar a performance clínica (percentagem de retenção) de próteses parciais fixas reforçadas por fibras. Fibras de polietileno (Ribbond«) foram usadas em combinação com resina composta durante a confecção das próteses. Os tratamentos foram realizadas em 13 pacientes, em uma clínica privada., sendo que 19 próteses foram reavaliadas. O espaço protético era preenchido com um pôntico usando o próprio dente extraído (2 casos), dentes de acrílico (11 casos) ou confeccionados com resina composta (6 casos), em todas as situações eram empregadas fibras de polietileno. Os critérios clínicos usados foram baseados na percentagem de retenção das próteses parciais fixas. As próteses que estavam em função no momento da avaliação, sem nunca necessitar de qualquer reparo prévio, foram classificadas como sobrevivência completa (SC). A classificação de sobrevivência com nova colagem (SR) foi utilizada para os casos de falha adesiva, com posterior cimentação da peça, a qual permanecia em função. O tratamento era classificado como falha (F) quando a restauração era perdida. O tempo médio de avaliação foi de 41,15 meses (±15,13). Nenhum caso de falha foi detectado, em apenas um caso houve falha adesiva com posterior colagem da peça (SR=5,25 por cento) e em 94.75 por cento dos casos as próteses permaneciam em função.. De acordo com o método de sobrevida de Kaplan-Meyer o tempo médio de sobrevida foi de 42,3 meses. As próteses parciais fixas reforçadas por fibras mostraram uma percentagem de retenção favorável neste estudo preliminar


Assuntos
Humanos , Masculino , Feminino , Resinas Compostas , Prótese Parcial Fixa , Polietileno , Prótese Dentária , Falha de Restauração Dentária
14.
J. appl. oral sci ; 14(2): 100-104, Apr. 2006. tab
Artigo em Inglês | LILACS, BBO - Odontologia | ID: lil-448145

RESUMO

The aim of this study was to evaluate the clinical performance (retention rate) of fiber-reinforced composite fixed partial dentures (FPDs). Polyethylene fiber (Ribbond®) was used combined with restorative composite during FPDs fabrication. FPDs were placed in thirteen patients in a private clinic. Nineteen FPDs were evaluated. The prosthetic space was filled with only one pontic using extracted teeth (2 cases), acrylic resin teeth (11 cases), or with composite resin (6 cases), combined with Polyethylene fiber. The clinical criterion used was based on retention rate of FPDs. If FPDs were in function in the mouth at the time of examination without previous repair they were classified as Complete Survival (CS) restorations. A classification of Survival with Rebonding (SR) was assigned in the event of an adhesive failure, but after rebonding the FPD still remained under evaluation. Treatment was classified as a Failure (F) if the FPD restoration was lost. The time of evaluation was 41.15 months (±15.13). The FPDs evaluated were retained (CS=94.75 percent), and no failure was found except for in one situation which required rebonding (SR=5.25 percent). According to the survival estimation method of Kaplan-Meyer the mean survival time was 42.3 months. At the time of evaluation investigated, polyethylene-reinforced FPDs showed a favorable retention rate in preliminary data.


O objetivo deste estudo foi avaliar a performance clínica (percentagem de retenção) de próteses parciais fixas reforçadas por fibras. Fibras de polietileno (Ribbond®) foram usadas em combinação com resina composta durante a confecção das próteses. Os tratamentos foram realizadas em 13 pacientes, em uma clínica privada., sendo que 19 próteses foram reavaliadas. O espaço protético era preenchido com um pôntico usando o próprio dente extraído (2 casos), dentes de acrílico (11 casos) ou confeccionados com resina composta (6 casos), em todas as situações eram empregadas fibras de polietileno. Os critérios clínicos usados foram baseados na percentagem de retenção das próteses parciais fixas. As próteses que estavam em função no momento da avaliação, sem nunca necessitar de qualquer reparo prévio, foram classificadas como sobrevivência completa (SC). A classificação de sobrevivência com nova colagem (SR) foi utilizada para os casos de falha adesiva, com posterior cimentação da peça, a qual permanecia em função. O tratamento era classificado como falha (F) quando a restauração era perdida. O tempo médio de avaliação foi de 41,15 meses (±15,13). Nenhum caso de falha foi detectado, em apenas um caso houve falha adesiva com posterior colagem da peça (SR=5,25 por cento) e em 94.75 por cento dos casos as próteses permaneciam em função.. De acordo com o método de sobrevida de Kaplan-Meyer o tempo médio de sobrevida foi de 42,3 meses. As próteses parciais fixas reforçadas por fibras mostraram uma percentagem de retenção favorável neste estudo preliminar.


Assuntos
Humanos , Masculino , Feminino , Resinas Compostas , Prótese Parcial Fixa , Polietileno , Prótese Dentária , Falha de Restauração Dentária
15.
RPG rev. pos-grad ; 12(3): 323-329, jul.-set. 2005. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-556088

RESUMO

Este trabalho teve como objetivo verificar as reações teciduais, após a implantação de fragmentos quadrangulares de polietileno poroso (Polietileno poroso), na região subcutânea do dorso de ratos. Foram utilizados 27 ratos, machos e fêmeas, com peso corporal entre 250 e 300 g. Após a implantação do material, os animais foram divididos em nove grupos de 3 ratos cada um e sacrificados após decorridos 7, 14, 30, 60, 90, 120, 150, 180, 210 dias da cirurgia. As áreas contendo as inclusões foram removidas e fixadas em formol a 10%, incluídas em parafina e submetidas a análise histológica sob microscopia de luz. Os resultados obtidos possibilitaram concluir que o Polietileno poroso permitiu a penetração de tecido conjuntivo neoformado para o interior de seus poros, promovendo a boa aderência no local da sua implantação. Esse tecido neoformado apresentava-se bem vascularizado. Durante as análises dos períodos de observação, nenhum sinal de infecção foi constatado e o material não foi reabsorvido até o período final de 210 dias, sendo bem tolerado pelos tecidos hospedeiros, apesar de ocorrer um discreto infiltrado inflamatório crônico no último período de observação.


Assuntos
Animais , Ratos , Histocompatibilidade , Polietileno , Adesivos Teciduais , Materiais Biocompatíveis , Tecido Conjuntivo/crescimento & desenvolvimento
17.
JBC j. bras. clin. odontol. integr ; 7(40): 307-312, jul.-ago. 2003. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-436365

RESUMO

Com a evolução da Odontologia baseada em procedimentos adesivos, as indicações dos materiais estéticos aumentaram, oferecendo novas possibilidades clínicas. Neste contexto surgiram as fibras de reforço para uso em Odontologia. Situações que exigem um reforço estrutural são favoráveis ao uso de fibras, principalmente de vidro e polietileno, como uma forma de aumento da resistência à flexão dos materiais em situações de carga mecânica induzida. O objetivo deste trabalho é revisar as fibras utilizadas em Odontologia para reforço de estruturas, abordando as propriedades mecânicas destes materiais, bem como as aplicações em diferentes situações clínicas


Assuntos
Materiais Dentários , Resinas Compostas , Vidro , Teste de Materiais , Polietileno
20.
JBC j. bras. clin. estet. odontol ; 5(25): 65-68, jan.-fev. 2001. ilus
Artigo em Português | LILACS, BBO - Odontologia | ID: lil-312734

RESUMO

A desvantagem das próteses fixas adesivas indiretas convencionais é a estética, que nem sempre é alcançada em regiöes de pré-molares e molares inferiores, pelo aparecimento das aletas axiais e apoios oclusais metálicos. Dessa maneira, o paciente precisa optar entre a preservaçäo da estrutura dentária ou o aparecimento do metal. As resinas laboratoriais atuais tiveram um aumento na carga mineral de sua composiçäo, melhorando suas propriedades mecânicas, podendo ser utilizadas para tratamentos protéticos onde uma maior carga oclusal é requisitada. O reforço dessas resinas laboratoriais com fibras tem sido relatado na literatura desde o início da década de 90, para a confecçäo de coroas unitárias posteriores e próteses parciais fixas pequenas. Com base no exposto, será apresentada a reabilitaçäo de um pequeno espaço edêntulo posterior, abordando os processos clínicos envolvidos na confecçäo de uma prótese fixa adesiva sem metal, utilizando a resina Solidex (Shofu Dental Corporation - USA) impregnada com fibras de polietileno Ribbond (Ribbond Inc - USA), como alternativa às próteses fixas adesivas convencionais


Assuntos
Humanos , Feminino , Adulto , Materiais Dentários , Prótese Parcial Fixa , Polietileno , Resinas