Effect of Water and Chlorhexidine with Different Pressures of Oral Irrigation Device on the Surface Roughness and Topography of Giomer

Abstract Objective: To evaluate the effect of different pressures of an oral irrigation device (OID) and the irrigation solution type on the surface roughness of the giomer restorative material. Material and Methods: In this in vitro study, disk-shaped giomer samples were fabricated and assigned to 5 groups (n=23): Group 1, storage in distilled water (control); Group 2, OID #7 pressure/ water; Group 3, OID #10 pressure/ water; Group 4, OID #7 pressure/ 0.05% CHX; Group 5, OID #10 pressure/ 0.05% CHX. The samples' treatment simulated a one-year application of OID. Surface roughness (Ra) and topography of the giomer were evaluated using profilometry and scanning electron microscopy. The data were analyzed with Paired t-test, Tukey, and ANOVA tests (α=0.05). Results: The Ra of the samples increased significantly after treatment with OID (p<0.001). The roughness increase in groups with a pressure of 10 was higher than those with a pressure of 7 (p<0.001). The effect of pressure on surface changes was significant (p<0.001). However, the solution type and the cumulative effect of these two factors were insignificant (p=0.08 and p=0.43, respectively). Conclusion: Oral irrigation device with both solutions significantly increased the surface roughness and topographic changes of the giomer. The severity of these changes was related to the device's pressure.

A microscopia eletrônica de varredura pode ser usada para medir quantitativamente a rugosidade da dentina? / Can Scanning Electron Microscopy be used to quantitatively measure dentine roughness?

Objective: The aim of this study was to determine if SEM used with imaging software could be used to quantitatively determine the extent of dentine roughness due to tooth-brushing. Material and methods: Flat, polished dentine surfaces were subjected to 25,000 cycles of simulated tooth-brushing at 2 strokes per second with a load of 200 g. At the end of the brushing cycle, dentine surfaces were first assessed using profilometry and then subjected to SEM analysis. Ra (average roughness) readings were obtained for profilometric assessment. Using imaging software, the horizontal distance between adjacent characteristic grooves noted on micrographs was measured, ensuring that the middle of each crest of the associated groove was used as the reference point, the Crest-to-Crest distance (C-C distance). These two parameters were examined statistically for correlation. Results: When Spearman Rank tests were utilized the correlation between average Ra and crest to crest measurements was 0.709 (p <0.01). The Bland Altman plot, however, showed poor agreement between the two test parameters. Conclusion: Further work is needed to validate the use of this methodology in the quantitative assessment of tooth surface loss due to abrasion (AU)

Objetivo: O objetivo deste estudo foi determinar se o MEV usado com software de imagem poderia ser usado para determinar quantitativamente a extensão da rugosidade da dentina devido à escovação dentária. Material e Métodos: Superfícies dentinárias planas e polidas foram submetidas a 25.000 ciclos de escovação dentária simulada a 2 movimentos por segundo com uma carga de 200g. No final do ciclo de escovação, as superfícies dentinárias foram primeiro avaliadas por perfilometria e depois submetidas à análise MEV. Leituras de Ra (rugosidade média) foram obtidas para avaliação perfilométrica. Utilizando um software de imagem, foi medida a distância horizontal entre sulcos característicos adjacentes observados nas micrografias, garantindo que o meio de cada crista do sulco associado fosse usado como ponto de referência, a distância crista a crista (distância CC). Esses dois parâmetros foram examinados estatisticamente para correlação. Resultados: Quando foram utilizados os testes de Spearman Rank, a correlação entre a média de Ra e as medidas de crista a crista foi de 0,709 (p<0,01). O gráfico de Bland Altman, no entanto, mostrou fraca concordância entre os dois parâmetros de teste. Conclusão: Mais trabalhos são necessários para validar o uso desta metodologia na avaliação quantitativa da perda da superfície dentária devido à abrasão(AU)

Efeito dos diferentes tipos de polimento sobre a rugosidade de superfície de uma resina acrílica comercial quimicamente ativada: estudo in vitro / Effect of different types of polishing on the surface roughness of a chemically activated commercial acrylic resin: an in vitro study

Objetivo: avaliar in vitro o polimento sobre resina acrílica quimicamente ativada (RAQA), por meio da rugosidade de superfície (Ra). Materiais e Método: Foram confeccionadas 40 amostras de RAQA, com dimensões de 10 a 10 x 2 mm, e foram divididas em quatro grupos (n=10): ausência do acabamento (AA); Ausência de polimento (AP); Polimento químico (PQ); Polimento com borrachas siliconadas + Escovas (PM). Os espécimes foram avaliados no quanto a rugosidade média (Ra) antes e após o envelhecimento em água destilada em uma estufa por 60 dias. Três medições de Ra (µm), na horizontal foram realizadas e calculada uma média para cada espécime. Os dados foram analisados de forma descritiva e inferencial, ANOVA de medidas repetidas e teste de Tukey com nível de significância de 5%. Resultados: Inicialmente, o grupo AA teve os menores valores de Ra e o grupo AP os maiores valores de rugosidade, com média e desvio padrão respectivamente 0,17 (±0,11) e 0,52 (±0,10). Após o envelhecimento, o grupo AA teve as menores médias e o grupo PQ os maiores valores de Ra, sendo 0,38 (±0,20) e 1,33 (±0,32), respectivamente. Os resultados evidenciaram diferença estatística significante quando as amostras foram submetidas ao acabamento com brocas. Conclusão: A RAQA necessita de polimento após acabamento com brocas, uma vez que a ausência de polimento comprometerá a lisura de superfície do material.(AU)

Objective: to evaluate in vitro polishing on chemically activated acrylic resin (RAQA), using surface roughness (Ra). Materials and Method: 40 RAQA samples were made, measuring 10 to 10 x 2 mm, and divided into four groups (n=10): absence of finishing (AA); Lack of polishing (AP); Chemical polishing (PQ); Polishing with silicone rubbers + Brushes (PM). The specimens were evaluated for their average roughness (Ra) before and after aging in distilled water in an oven for 60 days. Three horizontal Ra (µm) measurements were taken and an average was calculated for each specimen. Data were analyzed descriptively and inferentially, using repeated measures ANOVA and Tukey test with a significance level of 5%. Results: Initially, the AA group had the lowest Ra values and the AP group the highest roughness values, with mean and standard deviation respectively 0.17 (±0.11) and 0.52 (±0.10). After aging, the AA group had the lowest averages and the PQ group the highest Ra values, being 0.38 (±0.20) and 1.33 (±0.32), respectively. The results showed a statistically significant difference when the samples were finished with drills. Conclusion: RAQA requires polishing after finishing with drills, as the lack of polishing will compromise the surface smoothness of the material.(AU)

Root filling quality and bond strength of endodontic sealers to human and bovine dentin / Qualidade da obturação e resistência de união de cimentos endodônticos à dentina humana e bovina

Objetivo: Este estudo teve como objetivo comparar a qualidade da obturação e a resistência de união de dois cimentos endodônticos, AH Plus e Bio-C Sealer, em dentes humanos e bovinos. Métodos: Os canais radiculares de 60 dentes unirradiculares [30 humanos (H) e 30 bovinos (B)] foram preparados e obturados por condensação lateral da guta-percha e AH Plus (grupos AP-H e AP-B) ou Bio-C Sealer (grupos BC-H e BC-B). Seis fatias de 1,5 mm de espessura foram obtidas de cada raiz. Os espécimes foram observados em estereomicroscópio para avaliar a qualidade da obturação, considerando possíveis espaços vazios no material obturador. Posteriormente, as fatias radiculares foram avaliadas em termos de resistência de união por push-out e modo de falha. Os dados foram analisados pelos testes de Mann-Whitney e coeficientes de correlação de Spearman (α=5%). Resultados: A qualidade de obturação fornecida por AP e BC foi semelhante em ambos os substratos de dentina. No entanto, ao comparar dentes humanos e bovinos, os escores de espaços vazios foram maiores nas amostras bovinas, para ambos os cimentos. AP teve maior resistência de união à dentina humana e bovina do que BC. No entanto, não houve diferença significativa na resistência de união entre os substratos dentinários, para ambos os cimentos testados. Além disso, houve uma correlação positiva e moderada entre os valores de resistência de união de dentes humanos e bovinos. O modo de falha misto foi o mais prevalente. Conclusão: AP e BC fornecem qualidade de obturação semelhante, mas o primeiro apresenta maiores valores de resistência de união à dentina humana e bovina. A utilização de dentes bovinos como substitutos de amostras humanas parece ser adequada em estudos relacionados à resistência de união, mas não naqueles que testam a qualidade da obturação endodôntica.(AU)

Objective: This study aimed to compare the filling quality and bond strength of two endodontic sealers, AH Plus and Bio-C Sealer, in human and bovine teeth. Methods: The root canals of 60 [30 human (H) and 30 bovine (B)] single-rooted teeth were prepared and filled by lateral condensation of gutta-percha and AH Plus (groups AP-H and AP-B) or Bio-C Sealer (groups BC-H and BC-B). Six 1.5-mm-thick slices were obtained from each root. The specimens were observed under a stereomicroscope to assess filling quality, considering possible voids within the filling material. Subsequently, root slices were evaluated in terms of push-out bond strength and failure mode. Data were analyzed by Mann-Whitney tests and Spearman correlation coefficients (α=5%). Results: The filling quality provided by AP and BC was similar in both dentin substrates. However, when comparing human and bovine teeth, void scores were greater in the bovine samples, for both sealers. AP had higher bond strength to human and bovine dentin than BC. However, there was no significant difference in bond strength between dentin substrates, for both sealers tested. Also, there was a positive and moderate correlation between the bond strength values of human and bovine teeth. The mixed failure mode was the most prevalent. Conclusion: AP and BC provide similar filling quality, but the first presents higher bond strength values to human and bovine dentin. The use of bovine teeth as substitutes for human samples seems adequate in studies related to bond strength, but not in those testing root canal filling quality.(AU)

Advances in surface treatment of dental implants: a literature review

Amplamente utilizados para substituir dentes perdidos, os implantes dentários nos últimos anos vêm apresentando tecnologias como superfícies com micro e nanotopografia e ajustes nas composições químicas, dentre outros, para melhorar a osseointegração e reduzir o prazo de tratamento, permitindo, assim, carga funcional imediata ou precoce em pacientes com densidade óssea reduzida. Vários métodos são aplicados com intuito de modificar a superfície do implante, como jateamento com areia, corrosão ácida, oxidação anódica, tratamento com flúor, usinagem, pulverização de plasma de titânio e revestimento de fosfato de cálcio; esses métodos podem aumentar notavelmente a área de superfície quando operada a técnica adequadada de modificação, quer por procedimento de adição ou subtração. Tais modificações promovem superfícies rugosas, as quais aumentam a porcentagem de contato osso-implante (BIC) durante o processo de cicatrização óssea inicial. Os principais benefícios da modificação da superfície são melhorar a molhabilidade (hidrofilicidade), adesão e fixação de células a implantes e proliferação celular. Dentre os tratamentos de superfície de implantes dentários destaca-se o jateamento de areia com granulação grossa e ataque-ácido com HCL/H2SO4 (SLA) em altas temperaturas, o revestimento de superfície do implante com hidroxiapatita, oxidação anódica e o duplo ataque ácido. O objetivo deste trabalho é realizar uma revisão de literatura discutindo a importância e eficácia desses métodos para a osseointegração e, por conseguinte, para a redução do período de tratamento.

Widely used to replace lost teeth, dental implants have been presenting technologies such as surfaces with micro and nano topography and adjustments in chemical compositions, among others, to improve osseointegration and reduce treatment time, thus allowing immediate or early functional load in patients with reduced bone density. Several methods are applied to modify the implant surface, such as sandblasting, acid corrosion, anodic oxidation, fluoride treatment, machining, titanium plasma spraying, and calcium phosphate coating; these methods can notably increase the surface area when the appropriate modification technique is operated, either by the addition or subtraction procedure. Such modifications promote rough surfaces, which increase the percentage of bone-implant contact (BIC) during the initial bone healing process. The main benefits of surface modification are to improve wettability (hydrophilicity), adhesion and attachment of cells to implants, and cell proliferation. Among the surface treatments for dental implants, sandblasting with large grit and acid-etching with HCL/H2SO4 (SLA) stands out at high temperatures. The surface coating of the implant with hydroxyapatite, anodic oxidation, and double acid-etching. This work aims to conduct a literature review discussing the importance and effectiveness of these methods for osseointegration and, therefore, for reducing the treatment period.

Effect of laboratory and chairside polishing methods on the surface topography of occlusal splint materials manufactured using conventional, subtractive and additive digital technologies / Efeito de métodos de polimento em laboratório e em consultório na topografia de superfície de materiais de splint oclusal fabricados usando tecnologias digitais convencionais, subtrativas e aditivas

Objetivo: Este estudo avaliou as propriedades de polimento dos materiais de splint oclusal obtidos usando métodos de fabricação subtrativos e aditivos com os procedimentos de polimento laboratorial (LP) e polimento em consultório (CP). Material e Métodos: As amostras (N=180, n=60 para cada grupo) foram fabricadas usando um dos seguintes métodos: método de fabricação subtrativo (SMM) (M-PM Disc, Merz Dental GmbH), método de fabricação aditivo (AMM) (Freeprint Splint 2.0, DETAX GmbH & Co. KG) e o método de fabricação convencional (CMM) (Promolux HC, Merz Dental GmbH). Seguindo os procedimentos de LP e CP, a rugosidade da superfície dos espécimes foi medida usando um perfilômetro de superfície digital. Um espécime representativo foi selecionado de cada grupo, e uma imagem de microscópio eletrônico de varredura (SEM) foi obtida. Resultados: Tanto o método de fabricação quanto os procedimentos de polimento afetaram significativamente os resultados (P<0,01). Os termos de interação também foram significativos (P<0,001). Conclusão: Com ambos os métodos de polimento, a rugosidade superficial do grupo AMM foi a maior e a do grupo CMM a menor. Embora o procedimento CP tenha sido mais eficaz do que LP com ambos os métodos, a rugosidade da superfície ficou abaixo do limite de 0,2 µm após ambos os procedimentos de polimento testados (AU)

Objective: This study evaluated the polishing properties of the occlusal splint materials obtained using subtractive and additive manufacturing methods with the laboratory-type polishing (LP) and chairside-type polishing (CP) procedures. Material and Methods: Specimens (N=180, n=60 each group) were manufactured using one of the following methods: subtractive manufacturing method (SMM) (M-PM Disc, Merz Dental GmbH), additive manufacturing method (AMM) (Freeprint Splint 2.0, DETAX GmbH & Co. KG), and the conventional manufacturing method (CMM) (Promolux HC, Merz Dental GmbH). Following LP and CP procedures, surface roughness of the specimens was measured using a digital surface profilometer. One representative specimen was selected from each group, and a scanning electron microscope (SEM) image was made. Results: Both the manufacturing method and the polishing procedures significantly affected the results (P<0.01). Interaction terms were also significant (P<0.001). Conclusion: With both polishing methods, surface roughness of the AMM group was the highest and the CMM group the least. Although the CP procedure was more effective than LP with both methods, surface roughness was below the 0.2 µm threshold after both polishing procedures tested. (AU)

Rugosidade dos implantes dentários: análise comparativa da reutilização de ácidos no tratamento de superfície / Roughness of dental implants: comparative analysis of reuse of acids in surface treatment

Introdução: A importância da rugosidade para a osseointegração se dá pela correlação das interações das proteínas com a superfície do implante, a adsorção. Diferentes métodos são utilizados nos tratamentos de superfície, em que ocorre a remoção de partes da camada superficial, como o ataque ácido. Objetivo: Analisar as alterações de rugosidade na superfície dos implantes osseointegrados tratadas por duplo ataque ácido com uso único e até quatro reutilizações dos ácidos. Material e método As amostras de implantes dentários de liga de titânio (SINGULAR Implants ®) (n = 10) foram subdividas em cinco grupos: controle, tratamento 1, 2, 3 e 4, conforme as reutilizações dos ácidos. As capturas dos implantes no aumento de 500x, 1000x, 2000x e 4000x foram realizadas no microscópio eletrônico de varredura, para posterior análise de rugosidade pelo software ImageJ. Os valores de Ra e Rq foram analisados estatisticamente pelo teste ANOVA e o pós-teste de Tukey. Resultado: Os dados obtidos pelas imagens capturadas e pelos números de Ra e Rq adquiridos pelo ImageJ demonstraram que o tratamento com o duplo ataque ácido com cinco utilizações dos mesmos ácidos foi positivo para o tratamento de superfície do implante de liga de titânio. Conclusão: Pode-se concluir que até quatro reutilizações dos ácidos não interferiu estatisticamente nos valores de rugosidade em diferentes aumentos. São necessários mais estudos referentes à reutilização dos ácidos, contribuindo para a diminuição dos custos aos fabricantes, aumentando a sustentabilidade e mantendo-se a qualidade do produto.

Introduction: The importance of roughness for osseointegration is due to the configuration of proteins with the surface of the implant, and adsorption. Different methods are used in surface treatments, in which parts of the surface layer are removed, such as acid attack. Objective: To analyze changes in roughness on the surface of osseointegrated implants treated by double acid etching with single-use and up to 4 reuses of serums at a magnification of 500x, 1000x, 2000x, and 4000x in the scanning microscope (SEM). Method Samples of adherent implants (SINGULAR Implants ®) of lever alloy (n=10) were subdivided into 5 groups: control, treatment 1, 2, 3, and 4, according to the reuses. For the surface topography of the samples, SEM was used, followed by analysis by ImageJ software. Using the ANOVA test and Turkeys post-test, Ra and Rq values were statistically analyzed. Result: The data obtained both by the images captured in the SEM and by the Ra and Rq numbers acquired by the ImageJ illustrate that the treatment with the double acid attack with 5 uses of the same ones served, was positive for the surface treatment of the alloy implant of independent. Conclusion: It can be concluded that up to four reuses of food do not statistically interfere with roughness values. More studies are needed regarding the reuse of acids, certainly to reduce costs to manufacturers, increasing sustainability while maintaining product quality.

Influence of pH-cycling and abrasion wear on the mechanical properties of conventional and bulk fill resin composites

The objective of this study was to evaluate the effect of abrasion wear on surface roughness and microhardness of different commercially available resin composites simulating pH-challenges of the oral cavity. Methods: Three resin composites (RC) were used in this study: one conventional: Z250; and two bulk fill resin composites (BRC): Tetric N-Ceram (TNC) and Sonic Fill (SF). The RC was inserted in a prefabricated mold (15mm wide x 4mm thickness) in two layers, or in a single layer for BRC. Thirty samples were prepared and surface roughness (Ra) and Knoop microhardness (KHN) test were performed at three different time-points of evaluation: baseline (24h after sample preparation); partial (after pH cycling); and final (after simulated toothbrushing procedure). Two samples of each group were selected after different treatments and analyzed descriptively on a scanning electron microscopy (SEM). Data from Ra and KHN were analyzed by two-way repeated-measures ANOVA and Bonferroni's post-hoc test with a significance level set at 5%. Results: Ra increased for all groups (p<0.001), at the final time-point, Z250 and TNC groups present the highest values. Oppositely, KHN decreased for all groups (p<0.001), Z250 group showed the highest KHN values for all time-points (p<0.001). The SEM imagens showed a regular surface for samples cycled and irregular with inorganic particles exposed for samples toothbrushed. Conclusion: pH-cycling and simulated toothbrushing affected the superficial properties (roughness and Knoop microhardness), as observed at SEM imagens, with irregular surface with inorganic particles exposure

Cigarette Smoking Effect on Microhardness and Flexural Properties of Denture Base Resins

ABSTRACT Objective: To identify the tobacco effect on flexural properties and the microhardness of three acrylic resins. Material and Methods: Three resins were tested: two thermo-polymerizable acrylic resins (RMB 20 and BMS 014) and one autopolymerized acrylic resin. The 3-point bending and microhardness tests were carried out with a universal tensile-compression machine and a micro-Vickers hardness tester. The acrylic resin specimens have been exposed for 21 days to cigarette smoke in a smoking room. Their mechanical strength was compared to unexposed samples. Statistical analysis was performed using the data processing software SPSS Statistics 21.0. Results: The flexural properties of the resins were affected by cigarette smoke only in the case of Major Base 20® (drop in strength with p= 0.02; 0.6; 0.7 and in elastic modulus with p= 0.86; 0.74 and 0.85 for Major Base 20®, BMS 014® and Major Repair®). The cigarette smoke affected significantly microhardness for all groups (p<0.001). Conclusion: Cigarette smoking does not affect the flexural properties of the acrylic resin (BMS 014® and Major Repair® unlike Major Base 20®), but it does reduce the microhardness.

Avaliação das características de superfície e variação de massa de diferentes tipos de resina após escovação simulada / Evaluation of surface characteristics and mass variation of different types of resin after simulated toothbrushing

Introdução: O aumento da exigência estética pelos pacientes e o contínuo desenvolvimento de materiais - tais como resinas bulk fill de alta e baixa viscosidade e flow, demanda uma crescente necessidade de estudos nesta área para avaliar as propriedades dos materiais quando submetidos ao desgaste ocasionado pela escovação dentária ao longo do tempo. Objetivo: Avaliar as características superficiais de restaurações antes e após o processo de escovação simulada e comparar os resultados entre os mesmos. Materiais e métodos: Foram confeccionados ao total 80 corpos de prova (7x4mm), sendo 20 para cada tipo de resina utilizada, na cor A1: Bulk Fill One (3M/ESPE, St. Paul, MN, USA), Bulk Fill Flow (3M/ESPE, St. Paul, MN, USA), Z350XT (3M/ESPE St. Paul, MN, USA) e Z350XT Flow (3M/ESPE, St. Paul, MN, USA). Após a confecção, os corpos de prova permaneceram por 24 horas imersos em água destilada em estufa a 37°C, momento no qual foi realizado o acabamento e polimento com a sequência de discos de lixa Praxis (TDV, Brasil). Metade dos corpos de prova foi submetida a 60,000 ciclos de escovação simulada, enquanto a outra metade foi o grupo controle (n=10). A superfície das restaurações foi avaliada por meio do Microscópio Eletrônico de Varredura (MEV), rugosidade superficial (Ra) e variação de massa (através de pesagem) das restaurações antes e após o processo de escovação simulada. Para análise estatística, foi utilizada a análise de variância ANOVA dois fatores e pós teste de Tukey. Resultados: Na análise feita pelo MEV, em amplificação de 500x, foi observada a protuberância de partículas médias e pequenas em todas as resinas após a escovação simulada, com exceção da resina de tipo Z350 flow. Todos os materiais apresentaram aumento da Ra após a escovação simulada. Com relação a variação de massa, não houve diferença estatisticamente significativa. Conclusão: O processo abrasivo ocasionado pela escovação leva a mudanças na disposição das partículas, o que ocasiona mudanças na superfície do material e aumento na rugosidade. Por outro lado, não foi demonstrada diferença com relação a variação de massa (AU).

Introduction: The increasing of the aesthetic exigency by the patients and the continual development of materials ­ such as bulk fill and flow composites, demands a crescent need of studies on this area to evaluate the properties of the materials when submitted to the wear occasioned by toothbrushing abrasion over time. Objective: To evaluate the surface characteristics of restorations performed before and after the process of simulated toothbrushing and to compare the results between the composites. Materials and methods: In total, 80 samples were made (7x4mm), being 20 to each type of resin utilized, color A1: Bulk Fill One (3M/ESPE, St. Paul, MN, USA), Bulk Fill Flow (3M/ESPE, St. Paul, MN, USA), Z350XT (3M/ESPE St. Paul, MN, USA) and Z350XT Flow (3M/ESPE, St. Paul, MN, USA). After the confection of the specimens, the samples were immersed in distilled water for 24 hours and stored at 37°C in stove, moment that was performed the finishing and polishing with the sequence of sandpaper discs (TDV, Brasil). Half of the specimens was submitted to 60,000 cycles of simulated toothbrushing, meanwhile the other half was the control group (n=10). The surface of the restorations was evaluated through Scanning Electronic Microscopy (SEM), surface roughness (Ra), and weight loss (through measurements), in two moments: before and after the process of simulated toothbrushing. To the statistical analysis, it was used the variance analysis ANOVA two factors and Tukey's post test. Results: In the analysis performed by SEM, in amplification of 500x, it was observed the presence of medium and small protruding particles in all resins tested after simulated toothbrushing, with exception of the resin Z350 flow. All materials presented increasing on Ra after simulated toothbrushing. Regarding to mass variation, there was not any significant statistical difference. Conclusion: The abrasive process occasioned by toothbrushing leads to changes on the particles disposition, which causes changes on the surface and increase on the roughness. On the other hand, there was not any difference regarding to mass variation (AU).

Avaliação da resposta óssea de uma superfície de implante revestida com odanacatib em ratas ovariectomizadas: estudo experimental in vivo / Evaluation of the bone response of an odanacatib coated implant surface in ovariectomized rats: in vivo experimental study

Atualmente novos princípios ativos de função reabsortiva têm ganhado campo de estudo para avaliar seus mecanismos e comportamento biológico. Com isso, um novo antirreabsortivo, inibidor da catepsina K tem apresentado efeito positivo na osseointegração. Este estudo tem como objetivo avaliar a resposta óssea da superfície de implantes revestida por duplo ataque ácido e Odanacatib (MK-0822) em ratas ovariectomizadas. Neste estudo foram utilizadas ratas (Albinus, Wistar) ovariectomizadas ou sham (placebo). Cinquenta e dois (52) tiveram as superfícies revestidas por duplo ataque ácido e MK-0822 a 0,06 mg/ml através do método biomimético, e 48 implantes foram instalados em tíbias de ratas ovariectomizadas ou sham. Microscopia eletrônica de varredura (MEV) e energia dispersiva de raios-x (EDS) foram realizadas em 4 implantes após tratamento de superfície, para análise da topografia e composição química, além da realização da análise do ângulo de contato em 16 discos de titânio comercialmente puro tratados com as mesmas superfícies. Aos 15 e 40 dias após instalação de implantes (n=6), foi realizada microtomografia computadorizada. Dados quantitativos foram avaliados adotando-se o nível de significância p< 0,05. Além dos resultados topográficos favoráveis para os grupos tratados com MK-0822, os resultados microtomográficos apresentaram diferença estatisticamente significante entre os grupos SHAM e OVX na maioria dos parâmetros (p< 0,05). Ainda assim, os grupos tratados com MK-0822 apresentaram resultado semelhante ou maior, porém sem diferença estatística, em relação ao grupo controle em todos os parâmetros (TV, BV, BV ̸TV, Tb.Sp e Tb.N)(AU)

Currently new active principles of resorptive function have gained field of study to evaluate their mechanisms and biological behavior. Thereby a new anti-absorbent, cathepsin K inhibitor has had a positive effect on osseointegration. This study aims to evaluate the bone response of the surface of implants coated by double acid-etched and Odanacatib (MK-0822) in ovariectomized rats. In this study, either ovariectomized rats (Albinus, Wistar) or sham (placebo) have been used. Fifty-two (52) implants had the surfaces coated with double acid-etched and MK-0822 at 0,06 mg/ml by the biomimetic method and 48 implants were installed on sham or ovariectomized rat tibias. Scanning electron microscopy (SEM) and X-ray dispersive energy (EDS) were performed in 4 implants after surface treatment for analysis of topography and chemical composition, in addition to performing contact angle analysis on 16 commercially pure titanium discs treated with the same surfaces. At 15 and 40 days after implant installation, microcomputer tomography was performed. Quantitative data was evaluated by adopting the significance level of p< 0.05. Besides the favorable topographic results to MK-0822 coated implants group, the microtomographic results presents statistically significant differences between the SHAM and OVX groups at most of the parameters (p< 0,05). Nevertheless, the MK-0822 coated group presents similar or higher values, although without statistic differences related to the control group in all parameters (TV, BV, BV ̸TV, Tb.Sp and Tb.N)(AU)

Color and translucency stability of CAD/CAM restorative materials

Aim: This study assessed the color and translucency stability of a polymer infiltrated ceramic network (PICN) and compared it with a resin composite (RC) and a feldspathic ceramic (FEL). Methods: Disc-shaped samples of a PICN (Vita Enamic), a feldspathic ceramic (Vitablocks Mark II), and a resin composite (Brava block) were prepared from CAD/CAM blocks. PICN and RC surfaces were finished with a sequence of polishing discs and diamond paste. FEL samples received a glaze layer. The samples were subjected to 30-min immersions in red wine twice a day for 30 days. CIEL*a*b* coordinates were assessed with a spectrophotometer at baseline and after 15 and 30 days of immersion. Color alteration (ΔE00) and translucency parameter (TP00) were calculated with CIEDE2000. Average roughness was measured before the staining procedures. Color difference and translucency data were analyzed with repeated-measures ANOVA and Tukey's tests. Roughness was analyzed with the Kruskal-Wallis test. Results: Roughness was similar among the experimental groups. All materials had their color alteration significantly increased from 15 to 30 days of staining. PICN reached an intermediate ΔE00 between FEL and RC at 15 days. PICN revealed a color alteration as high as the composite after 30 days. No statistical difference was observed regarding translucency. Conclusion: PICN was not as color stable as the feldspathic ceramic at the end of the study. Its color alteration was comparable to the resin composite when exposed to red wine. However, the translucency of the tested materials was stable throughout the 30-day staining

Ação dos desafios erosivo e erosivo-abrasivo sobre a superfície de dentina e de diferentes sistemas restauradores / Effects of erosive and erosive-abrasive challenges on dentin and different restorative systems surface

O desgaste dentário é um processo de perda de estrutura dental, de etiologia multifatorial, com incidência crescente na população e ocasionado, principalmente, pela frequência do contato da superfície dentária com substâncias químicas e mecânicas, resultantes da alimentação e de hábitos orais. Os efeitos da ação dos desafios químicos e/ou mecânicos no dente, hígido ou restaurado, podem variar conforme as propriedades e características do substrato dentina, material restaurador. O estudo objetivou analisar os efeitos dos desafios erosivo (DE) e erosivo-abrasivo (DEA) na superfície de diferentes materiais restauradores (MR), sistemas adesivos (SA) e da dentina adjacente às restaurações (DAR). Molares humanos hígidos (n=75) foram limpos e preparados até obtenção de dentina oclusal uniforme. Os espécimes foram aleatoriamente divididos em 5 grupos (n=15). Na superfície dentinária, uma cavidade 4 x 2 mm foi confeccionada por meio de uma ponta diamantada, e restaurada por diferentes tipos de SR: Amaris® (AMA), Beautifil® II (BEA), ClearfilTM SE Bond 2 (CFB), FL-Bond II (FLB) e RIVA Self Cure (RIVA). Após restauração, a superfície do espécime foi delimitada em três partes duas, nas extremidades, que foram protegidas por fita adesiva anticorrosiva, e uma, intermediária (2 mm), que foi deixada livre para exposição da área aos desafios. No DE, o espécime foi imerso em solução de ácido cítrico 1% (pH 2.3) por dois min, seguido de imersão em saliva artificial por 60 min. Esse ciclo foi realizado durante 5 dias (6x/dia). No DEA, os espécimes foram submetidos ao mesmo DE descrito, porém foram escovados em máquina de escovação (escova macia, 45 ciclos/150g/15s), 2x/dia (após 30 min do primeiro e do último ciclo erosivo do dia). Os efeitos dos desafios foram avaliados pela análise das propriedades de perda de superfície (PS, m) e rugosidade superficial (RS, m) (Perfilometria óptica); e dureza superficial (HB, nanoindentação, Kg/mm2). Os dados foram analisados estatisticamente (p=0.05) pelos testes ANOVA, de Tukey e pela Correlação Linear de Pearson. Após desafios, as DAR de todos os grupos apresentaram elevada perda e diminuição na dureza. O DE ocasionou maior PS na dentina (PS>20 m). Não houve diferença entre a rugosidade dos materiais restauradores após desafios. O material RIVA apresentou elevada perda (PS>2 m), elevada rugosidade (RS=0.93048±0.2) e diminuição na dureza (HB<35 Kg/mm2) após desafios, principalmente após escovação. A rugosidade dentinária de AMA+CFB (RS=0.61921±0.1) foi menor após abrasão. Os desafios agiram igualmente sobre a dureza da interface adesiva. A dureza da interface de BEA+FLB (HB=16.97627±2.32) foi menor após escovação. Após erosão, a dureza dos materiais bioativos BEA, FLB e RIVA reduziram. Os efeitos observados dependeram do tipo de desafio e substrato envolvido no processo. A ação isolada do ácido cítrico foi mais agressiva no substrato dentinário. Os desafios tiveram efeitos sobre as propriedades dos materiais restauradores, principalmente nas dos bioativos. Nenhum material foi eficaz contra a desmineralização severa da dentina.

Cyclic Fatigue Resistance and Surface Roughness of Rotary NiTi Instruments after Simulated Clinical Use in Curved Root Canals - An Atomic Force Microscopy Study

Abstract Objective: To examine the cyclic fatigue resistance and surface topography of TruNatomy and ProTaper Gold nickel-titanium rotary files and evaluate the presence of alterations to surface topography following instrumentation in simulated curved canals. Material and Methods: Twenty-four nickel-titanium instruments, twelve each of TN and PTG file systems, were evaluated for cyclic fatigue resistance. The rotary files were rotated in a simulated root canal with standardized diameter, angle of curvature, and radius of curvature in a custom-made cyclic fatigue testing device until the instrument fracture occurred. The time to fracture for each instrument was recorded with a stopwatch; in seconds in each group. Fractured instruments were subjected to atomic force microscopy analysis measuring the average roughness and the root mean square values to investigate surface features of endodontic files. Mean values and standard deviation were calculated. Data were analyzed using the Mann-Whitney U test. Results: Time to fracture was marginally higher in PTG instruments than in the TN file systems. PTG files exhibited higher surface roughness when compared with TN files (p<0.05). Conclusion: TN file system had a higher cyclic fatigue resistance than PTG. Cyclic fatigue causing file breakage did affect the surface topography of the files. PTG files showed a higher surface porosity value than the TN files (AU).

The Effect of Coloring Beverages on Color Stability of Hybrid Ceramics with Different Surface Treatments

ABSTRACT Objective To assess the effects of coloring beverages on the color stability of two types of hybrid ceramics with different surface treatments. Material and Methods 180 specimens of two hybrid ceramics (Vita Enamic and Mazic Duro) and a feldspathic ceramic (Vita Mark II) were prepared (n=60 in each group). Half of the discs in each group were glazed while the other was polished. The specimens were then divided into three subgroups and immersed in distilled water, carrot juice, and coffee. The overall color difference (∆E) was calculated based on CIE L*a*b* color space. Data were analyzed using three-way and one-way ANOVA; Tukey's honest significant difference was also done for pairwise comparisons (α=0.05). Results Vita Mark II specimens revealed less overall color changes compared to other groups. The ∆E of the glazed Vita Enamic specimens was greater than polished specimens following immersion in distilled water (p=0.03) and coffee (p=0.001), but it was not significant for carrot juice. The same results were obtained for polished Mazic Duro specimens. Relatively similar amounts of ∆E were recorded in polished and glazed subgroups of Vita Mark II. Conclusion The ∆E of hybrid ceramics was higher than Vita Mark II. Polishing could be recommended for surface treatment of hybrid ceramics instead of glazing, saving time and facilitating the process.

Effect of Spondias mombin L. extract on the wettability, roughness, color and morphology of bovine enamel

Although Spondias mombin L. extract has an excellent antimicrobial effect against oral microorganisms, it should be clarified how it affects enamel surface properties. Aim: To evaluate the color change, wettability/contact angle, surface roughness and morphology of bovine enamel submitted to the Spondias mombin L. extract. Methods: Thirty bovine teeth were distributed into the following groups: 0.12% chlorhexidine digluconate, 1:32 Spondias mombin L. extract and distilled water. Color change (CC) was evaluated after immerging specimens into the solutions for 14 days. Surface roughness (Ra) was measured using a roughness meter; wettability/contact angles (CA) were determined by the sessile drop method, and scanning electron microscopy images were obtained to characterize the morphology (SMA). The pH of the solutions was evaluated using a pHmeter. The Ra, CA, and CC data were parametric (Kolmogorov-Smirnov; p>0.05). Two-way ANOVA (for Ra and CA) and one-way ANOVA (for CC) with Tukey's posthoc tests at a significance level of 5% were used. SMA was analyzed descriptively. Results: The Spondias mombin L. extract revealed an acidic pH, and when in contact with the bovine teeth, it increased the wettability, but it did not cause statistically significant differences in the Ra. Spondias mombin L. extract caused the highest color change. The SEM images showed differences in the specimens' surface submitted to the extract compared to the other groups. Conclusion: Spondias mombin L. extract provided negative effects on bovine enamel's surface, including a high color change and a more wettable substrate

Surface treatment and adhesion approaches on polymer-infiltrated ceramic network: influence on the bond strength to resin cement

Aim: To evaluate the effect of different surface treatments and adhesive approaches on the microshear bond strength of resin cement to a polymer-infiltrated ceramic network (PICN). Methods: PICN blocks were randomly assigned into 9 groups (n=10): CTRL: no treatment; HF: 5% hydrofluoric acid etching; HF-S: HF + silane; HF-S-A: HF-S + adhesive (Adper Single Bond 2); HF-UA: HF + universal adhesive (Single Bond Universal); SB: sandblasting with 50 µm Al2O3 particles; SB-S: SB + silane; SB-S-A: SB-S + adhesive; SB-UA: SB + universal adhesive. Resin cement microcylinders (Ø = 0.96 mm; height = 1 mm) (RelyX Ultimate) were built upon the PICN surface after roughness and contact angle measurements. Next, microshear bonding tests (µSBS) were performed (0.5 mm/min) after water storage (37ºC, 90 days) and thermocycling (12,000 cycles; 5ºC-55ºC). Failure modes were observed under stereomicroscope. Bond strength data were analyzed by two-way ANOVA/Tukey's test and t-tests. Kruskal-Wallis/Dunn's tests were conducted for roughness and contact angle data (α = 0.05). Results: A rougher surface and lower contact angles were observed for Sandblasting. HF-S (18.54 ± 2.03 MPa), SB-S (19.00 ± 1.66 MPa) and SB-UA (18.07 ± 2.36 MPa) provided the highest bond strength values, followed by the other treated groups. The CTRL group resulted in lower bond strength (7.18 ± 2.34 MPa). Conclusion: Hydrofluoric acid etching followed by silane application and sandblasting followed by silane or universal adhesive are useful clinical steps to enhance bonding to PICN. Adhesive applications after HF etching have no advantages in bonding to PICN

Post-cure heat treatments influence on mechanical and optical properties of resin composites

Abstract This study evaluated the effect of post-cure heat treatment (PCHT) on the Knoop microhardness (KHN), degree of conversion (DC), color changes, and contrast ratio (CR) of four resin composites (RCs): Z100 (3M ESPE), Z350 XT (3M ESPE), Estelite Omega (Tokuyama) and Empress Direct (Ivoclar Vivadent). Specimens (12 × 1 mm) were prepared for each material (n = 10 / group). After curing, samples were subjected to PCHT for 10 min at 100°C or 170°C. Control group was maintained at room temperature (24°C) for the same time. The DC was analyzed by FT-NIR immediately and 24 h after the PCHT (n = 3 / group). KHN was analyzed 24 h after PCHT (n = 10 / group). According to CIEDE2000 (∆E00), color measurements were obtained immediately after curing, five minutes after PCHT, and after seven days of storage in water, coffee, and red wine. Data were analyzed by One and Two-Way ANOVA (p < 0.05). Z100, Z350, and Estelite Omega showed increases in KHN with increased temperature (p < 0.05). PCHT at 100°C and 170°C led to a higher DC of all RCs (p < 0.05). Initially, the PCHT lead to increased ∆E00 values (p < 0.05), which was decreased after immersion in coffee and wine (p < 0.05). Considering the effect of PCHT and staining solutions, lower color changes were observed in the thermally treated specimens (p < 0.05). Taken collectively, the results suggest the PCHT as an economical and practical alternative to enhance direct RC's properties in direct-indirect and indirect restorations.

Resumo Este estudo avaliou o efeito do tratamento térmico pós-cura (PCHT) na microdureza Knoop (KHN), grau de conversão (DC), mudanças de cor e razão de contraste (CR) de quatro compósitos resinosos (RCs): Z100 (3M ESPE ), Z350 XT (3M ESPE), Estelite Omega (Tokuyama) e Empress Direct (Ivoclar Vivadent). Corpos de prova (12 × 1 mm) foram preparadas para cada material (n = 10 / grupo). Após a cura, as amostras foram submetidas ao PCHT por 10 min a 100 ou 170° C. O grupo controle foi mantido à temperatura ambiente (24° C) pelo mesmo tempo. O DC foi analisada por FT-NIR imediatamente e 24 h após a PCHT (n = 3 / grupo). KHN foi analisado 24 h após PCHT (n = 10 / grupo). De acordo com o CIEDE2000 (∆E00), as medidas de cor foram obtidas imediatamente após a cura, cinco minutos após a PCHT e após sete dias de armazenamento em água, café e vinho tinto. Os dados foram analisados por ANOVA de um e dois fatores (P < 0,05). Z100, Z350 XT e Estelite Omega mostraram aumentos no KHN com o aumento da temperatura (P < 0,05). PCHT a 100 ° C e 170 ° C levou a uma maior DC de todos os RCs (P < 0,05). Inicialmente, o PCHT levou ao aumento dos valores de ∆E00 (P < 0,05), que diminuiu após a imersão em café e vinho (P < 0,05). Considerando o efeito de PCHT e soluções de coloração, menores mudanças de cor foram observadas nas amostras tratadas termicamente (P < 0,05). Os resultados sugerem o PCHT como uma alternativa econômica e prática para aumentar as propriedades diretas de compósitos resinosos em restaurações diretas-indiretas e indiretas.

Análise da eficácia de dentifrícios clareadores e seus efeitos na superfície dental: um estudo in vitro / Analysis of the effectiveness of whitening dentifrices and their effects on the dental surface: an in vitro study

O clareamento dos dentes pode ser realizado de várias maneiras, em consultório, no âmbito caseiro ou com a utilização de produtos OTC (Over-the-Counter). Dentre esses produtos, existem os dentifrícios clareadores que prometem clarear e prevenir o manchamento dentário. Objetivos: (1) Investigar o potencial clareador e abrasivo de diferentes dentifrícios no esmalte; e (2) avaliar o efeito do dentifrício Oral-B 3D White Perfection® (Oral-B) na prevenção do escurecimento. Materiais e Métodos: Amostras de esmalte bovino foram pigmentadas e escovadas por 14 dias com água (controle negativo) ou com diferentes produtos: Colgate Total 12® (controle), Oral-B, Sensodyne Branqueador Extra Fresh® (Sensodyne) ou Colgate Luminous White Advanced® (Colgate). Oral-B foi testado antes e após pigmentação. As amostras foram avaliadas quanto à cor (espectrofotômetro) e rugosidade superficial (rugosímetro). Para cálculo de alteração de cor (ΔDE00) se utilizou o sistema CIEDE2000. Os dados foram analisados com os testes Kruskal-Wallis, SNK e Mann-Whitney (α=5%). Resultados: O controle negativo apresentou a menor ΔE00 (p<0,05) e o grupo tratado com Sensodyne resultou nos maiores valores (p<0,05). Quanto à rugosidade superficial, não houve diferença significativa entre os grupos avaliados. O dentifrício Oral-B demonstrou efeito protetivo ao manchamento, resultando em menor alteração de cor (p=0,002). Conclusão: Somente o dentifrício Sensodyne apresentou potencial clareador maior que o dentifrício convencional. A escovação prévia com Oral-B reduziu o manchamento dental, embora não tenha prevenido este totalmente de acontecer. Não foram observadas alterações significativas na rugosidade dos dentes após aplicação dos tratamentos, quando comparado ao controle.

Tooth whitening can be performed at the dental office, at-home or upon the use of OTC (Over-the-Counter) pro-ducts. Among the latter, there are whitening toothpastes that promise to bleach and to prevent tooth staining. Objectives: (1) To investigate the bleaching and abrasive potential of different whitening dentifrices to enamel; and (2) to evaluate the effect of Oral-B 3D White Perfection®(Oral-B) toothpaste in preventing staining. Materials and Methods: Bovine enamel samples were stained and brushed for 14 days with water (negative control) or with different products: Colgate Total 12® (control), Oral-B, Sensodyne Branqueador Extra Fresh® (Sensodyne), and Colgate Luminous White Advanced® (Colgate). Oral-B was also tested before and after staining. The samples were tested by their color (spectrophotometer) and surface roughness (profilometer). Color change (ΔDE00) was cal-culated using the CIEDE2000 color system. The data were analyzed using Kruskal-Wallis, SNK, and Mann-Whitney tests (α=5%). Results: The negative control showed the lowest ΔE00 (p<0.05), whereas the group treated with Sensodyne resulted in the greatest color change (p<0.05). For surface roughness, there was not any significant difference among the groups. The Oral-B toothpaste showed a protective effect against staining, resulting in the lowest color change (p=0,002). Conclusion: Only Sensodyne toothpaste showed higher whitening potential than the conventional toothpaste. By using Oral-B prior staining reduced significantly the intensity of staining, although without the complete prevention of this event. Significant differences were not observed after treatment concerning roughness in comparison to the control.

Microhardness homogeneity of RBCs light-cured with a multiple-peak LED and surface characterization after wear

Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.

Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.