Novel resin-based material containing ß-tricalcium phosphate nanoparticles for the reduction of dentin permeability.

OBJECTIVES: To synthesize and characterize a novel dentin adhesive containing Beta-Tricalcium Phosphate (ß-TCP) nanoparticles and test its ability to reduce dentin permeability (dP). METHODS: Experimental adhesives were prepared by mixing Bis-GMA, TEGDMA, HEMA (50/25/25 wt.%), photo-initiators, and inhibitors. The following groups were tested: Experimental adhesives without ß-TCP (Exp.); with 10 wt.% ß-TCP (Exp.10 wt.% ß-TCP); with 15 wt.% ß-TCP (Exp.15 wt.% ß-TCP), Scotchbond Multi-Purpose (SBMP) and Clearfil SE Protect Bond (CFPB). Degree of conversion (DC%, 10 and 20 s); Flexural Strength (FS), Knoop Hardness (KHN), and Cell Viability (OD%) tests were performed. dP was evaluated by hydraulic conductance, using human dentin disks (n=12), at three-time intervals: post-EDTA (T0); post-treatment (T1); and post-erosion/abrasion cycling (T2). Data were statistically analyzed (α=0.05). RESULTS: For all groups, exposure time for 20 s presented a higher DC% than for 10 s. For FS, filled adhesives did not differ from unfilled and from CFPB. Experimental adhesives did not differ among them and showed lower KHN than the commercial products. Cell viability did not differ among adhesives, except Exp. 15 wt.%, which showed lower OD% than Exp., Exp. 10% and, CFPB. For dP, only Exp.10 and 15 wt.% ß-TCP did not present difference between the times T1 and T2. After cycling, Exp.10 wt.% ß-TCP presented lower permeability than Exp. and CFPB. CONCLUSIONS: The incorporation of 10 wt.% ß-TCP nanoparticles into the resin-based dental material did not affect its mechanical properties and biocompatibility, and promoted the greatest reduction in dentin permeability, sustaining this effect under erosive/abrasive challenges. CLINICAL SIGNIFICANCE: A novel resin-based dental material containing ß-TCP nanoparticles was able to reduce dentin permeability, maintaining its efficacy after erosive/abrasive challenges. The synthesized material did not affect dental pulp cell viability and might be promising for other conditions that require dental remineralization, such as tooth wear and dental caries.

Varnish with S-PRG filler reduces dentin permeability after erosive/abrasive challenge.

PURPOSE: To evaluate the effect of different varnishes on dentin permeability to erosive/abrasive challenges. METHODS: 60 superficial dentin discs were randomly allocated to six groups (n=10): Duraphat, PRG Barrier Coat, Clinpro XT, Profluorid, Fluor Protector S and untreated (control). Permeability tests were carried out: after acid conditioning, after treatment, and after abrasive/erosive challenges. The abrasive-erosive challenges were performed for 5 days (citric acid and in remineralizing saliva), as well as abrasion with toothpaste slurry (Colgate Total 12). Scanning electron microscopy (SEM) images were obtained of the dentin surfaces (5,000x) after the treatments, and after the erosive/abrasive challenges. RESULTS: Kruskal-Wallis and Dunn tests showed that all the varnishes promoted a decrease in dentin permeability directly after application, with Clinpro XT showing the highest percentage (69.52%) of dentin sealing (P= 0.0188). After the erosive/abrasive challenge, only PRG Barrier Coat varnish showed dentin sealing ability with reduced dentin permeability (42.16%) (P= 0.0014). However, none of the applied varnishes promoted a statistically significant difference in the percentage of dentin sealing, compared with the control group (P> 0.05). Clinpro XT showed a higher percentage of dentin sealing, while only PRG Barrier Coat showed reduced dentin permeability after the erosive/abrasive challenge. CLINICAL SIGNIFICANCE: Varnish containing S-PRG filler has the efficacy needed to be used as a coating material to reduce dentin permeability in situations of erosive/abrasive challenges.

Effect of a modified adhesive system with encapsulated arginine and calcium carbonate on dentin permeability.

To modify an adhesive system with halloysite clay nanotubes (HNTs) containing arginine and calcium carbonate and to evaluate their cytocompatibility, viscosity and efficacy in reducing dentin permeability. HNTs containing arginine and calcium carbonate were incorporated into the primer and adhesive of a three-step adhesive system (SBMP), and their viscosity was measured. Discs (n = 4/group) were prepared: SBMP (control), HNT-PR (modified primer), HNT-ADH (modified adhesive) and HNT-PR + ADH (modified primer and adhesive) were evaluated regarding cell death and viability. Dentin discs were prepared and randomly assigned into the following treatments (n = 10): NC (no treatment), SBMP, HNT-PR, HNT-ADH, HNT-PR + ADH and COL (Colgate® Sensitive Pro-relief™ prophylaxis paste). After, they were submitted to an erosive-abrasive cycling. Dentin permeability (hydraulic conductance) was evaluated at baseline, 24 h after treatment and after cycling. Both the modified primer and adhesive showed significantly higher viscosity than their controls. Group HNT-PR resulted in significantly higher cytotoxicity when compared to SBMP and HNT-PR + ADH groups. Group HNT-ADH resulted in the highest cell viability compared to all other groups. All groups showed significantly lower dentin permeability when compared to the NC group. Post-cycling, SBMP and HNT-ADH groups showed significantly lower permeability when compared to COL group. The addition of encapsulated arginine and calcium carbonate did not affect the cytocompatibility of the materials nor their ability to reduce dentin permeability.

In vitro dentin permeability and tubule occlusion of experimental in-office desensitizing materials.

OBJECTIVES: This study investigates the dentin permeability (by hydraulic conductance) and tubule occlusion (by confocal and scanning electron microscopies) of in-office desensitizing materials. MATERIALS AND METHODS: Bovine dentin blocks were immersed in EDTA to open dentinal tubules. Placebo varnish (PLA), fluoride varnish (FLU), NaF 5% + 5% nanoparticulate sodium trimetaphosphate varnish (TMP), universal adhesive system (SBU), S-PRG filler varnish (SPRG), Biosilicate (BIOS), and amelotin (AMTN) solution were the materials tested. After application, the specimens underwent an erosive-abrasive challenge. Dentin permeability was evaluated at T0 (initial), T1 (after treatment), and T2 (after challenge). Confocal and scanning electron microscopy (SEM) were used to evaluate, respectively, length and number of dentinal tubule occlusions and opened dentinal tubules, after challenge. Permeability and SEM data were analyzed by two-way repeated measures ANOVA and Tukey's tests. Confocal data were analyzed by one-way ANOVA, Tukey's test, and Kruskal-Wallis and Dunn's tests. Spearman and Pearson's correlation tests were also used. Significance level was set at 5%. RESULTS: At T1, the AMTN group showed the lowest permeability value, following the increasing order at T2: AMTN = SBU < BIOS = SPRG < TMP < FLU < PLA. The SBU group had the highest value of occluded dentinal tubule length. The AMTN group presented more occluded dentinal tubules compared to PLA and FLU. AMTN and SBU had the lowest values of opened dentin tubules. Results showed a negative correlation between the analyses. CONCLUSION: The SBU and AMTN solution were more effective in reducing dentin permeability by occluding dentin tubules. CLINICAL RELEVANCE: All materials reduced permeability after challenge, except fluoride varnish.

Iontophoresis effects of two-step self-etch and total-etch systems on dentin permeability and sealing of composite restoration under simulated pulpal pressure.

BACKGROUND: Studies demonstrated the bond strength enhancement and the decrease in degradation of the adhesive interface after applying either self-etch adhesives or two-step, etch-and-rinse adhesives under an electric field. However, the presence of dentinal fluid driven by the pulpal pressure in vivo is a profounding factor affecting both the sealing ability and bond strength of adhesives. This study aimed to evaluate the effect of three-step etch-and-rinse and two-step self-etch adhesives when applied with iontophoresis under simulated pulpal pressure on the permeability of dentin, resin infiltration, and the sealing ability of resin composite. METHODS: The experiments were done on 32 recently extracted premolars, randomly assigned into four groups (n = 8) according to two adhesive systems (SBMP and SE), applied following the manufacturer's instructions (control) for two groups or with iontophoresis for the others (SBMPi and SEi). For the iontophoresis, the anodal current was applied at 75 µA for 20 s through the cavity electrode during the bond. The fluid flow rate of dentin was recorded after cavity preparation (smear-layer-covered dentin; T1), bonding (T2), and composite restoration (T3) during the maintained pulpal pressure of 20 mm Hg. The flow rates were expressed as a percentage relative to the initial smear-layer-covered value for each specimen. Results were analyzed using repeated measures ANOVA. Scanning electron microscopy (SEM) was performed to observe the resin/dentin interface. RESULTS: There were no significant increases in the mean flow rates from T1 to T3 in the SBMP (P = 0.355), while these changes in the SE were significant between T1 (100%) and T2 (166.77%) and T1 and T3 (221.16%) (P = 0.002; one-way RM ANOVA; Holm-Sidak test). For the iontophoresis groups, the mean flow rates decreased significantly from T1 to T2 and T1 to T3 of both SBMPi (T2 = 86.43, and T3 = 79.53; P < 0.001) and SEi groups (T2 = 87.96, and T3 = 81.48; P = 0.004). The iontophoresis of both adhesives produced the optimal resin infiltration with improved quality of the hybrid layer and resin tags. CONCLUSIONS: SBMP bonded with or without iontophoresis performed better sealing ability than SE under the same condition. Both adhesives applied with anodal iontophoresis significantly decreased the dentin permeability, contributing to the improved resin infiltration.

Effectiveness and cytotoxicity of two desensitizing agents: a dentin permeability measurement and dentin barrier testing in vitro study.

BACKGROUND: When evaluating the efficacy and safety of various desensitizing products in vitro, their mechanism of action and clinical utility should be considered during test model selection. This study aimed to evaluate the effects of two desensitizers, an in-office use material and an at-home use material, on dentin specimen permeability, and their dentin barrier cytotoxicity with appropriate test models. METHODS: Two materials, GLUMA desensitizer (GLU) containing glutaraldehyde and remineralizing and desensitizing gel (RD) containing sodium fluoride and fumed silica, were selected. Human dentin specimens were divided into three groups (n = 6): in groups 1 and 2, GLU was applied, and in group 3, RD was applied and immersed in artificial saliva (AS) for 24 h. Dentin specimen permeability before and after each treatment/post-treatment was measured using a hydraulic device under a pressure of 20 cm H2O. The perfusion fluid was deionized water, except in group 2 where 2% bovine serum albumin (BSA) was used. The representative specimens before and after treatment from each group were investigated using scanning electron microscopy. To measure cytotoxicity, test materials were applied to the occlusal surfaces of human dentin disks under which three-dimensional cell scaffolds were placed. After 24-h contact within the test device, cell viability was measured via 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assays. RESULTS: GLU significantly reduced the dentin permeability and occluded the dentinal tubules when 2% BSA was used as perfusion fluid. RD significantly reduced dentin permeability and occluded the tubules, but permeability rebounded after AS immersion. GLU significantly decreased cell viability, but RD was non-cytotoxic. CONCLUSIONS: In vitro GLU application induced effective dentinal tubule occlusion only following the introduction of simulated dentinal fluid. RD provided effective tubule occlusion, but its full remineralization potential was not realized after a short period of immersion in AS. GLU may harm the pulp, whereas RD is sufficiently biocompatible.

Resin-based materials to control human dentin permeability under erosive conditions in vitro: A hydraulic conductance, confocal microscopy and FTIR study.

OBJECTIVES: To characterize the behavior of three different polymeric agents before and after an erosive challenge on dentin permeability, to analyze their degradation in both conditions, and to analyze their degree of conversion (DC). METHODS: The permeability of human dentin disks (1.0 ± 0.2 mm) was measured with smear layer, after its removal, after treatment (LpTreat) with Gluma Desensitizer, PRG Barrier Coat (PBC) or Icon infiltrant (n = 11/group) and after exposure to citric acid (LpEro) (6%, pH 2.1, 1 min). The specimens were analyzed under a Laser Scanning Confocal Microscope (n = 2/group) and the products' DC were calculated. Data were subjected to 2-way repeated measures ANOVA and post-hoc Bonferroni (permeability analysis), to paired t-test (for specimens treated with Icon) and to t-test (DC analysis) (α < 0.05). RESULTS: Icon showed the lowest LpTreat and LpEro values, while PBC and Gluma did not differ from each other under these conditions. Icon and PBC showed LpEro similar to a dentin with smear layer. Under the Laser Scanning Confocal Microscope, more deposits were noticeable on dentin after treating with PBC. Gluma presented the deepest penetration in dentin. The DC of PBC was the highest. SIGNIFICANCE: Icon caused the highest reduction on permeability values, followed by PBC and Gluma. PBC generated more deposits covering dentin and seemed to be more efficient after an erosive challenge. The association of a polymeric resin with inorganic ion-releasing fillers seem to be a great strategy to manage dentin hypersensitivity under erosive conditions.

The effect of iontophoresis delivery of fluoride in stannous fluoride desensitizing toothpaste on dentin permeability in human extracted teeth.

This study aimed to determine the effect of iontophoresis delivery of fluoride in stannous fluoride (SnF2) toothpaste on dentin permeability in human extracted third molars. For dentin permeability test, 26 dentin specimens were randomly divided into 4 groups; SnF2 without-iontophoresis (n = 10), SnF2 with-iontophoresis (n = 10), no SnF2 without-iontophoresis (n = 3), and no SnF2 with-iontophoresis (n = 3). The hydraulic conductance of dentin (HD) was measured after smear layer removal, immediate treatment, 7 days, and acid challenge. The other 26 specimens were also prepared under these different conditions to assess degree of dentinal tubule occlusions using scanning electron microscopy (SEM). Percentage decrease of HD in SnF2 without-iontophoresis after immediate treatment, 7 days and acid challenge were 38.38 ± 13.61, 56.92 ± 17.22 and 33.07 ± 23.57%. The corresponding values in SnF2 with-iontophoresis were 42.16 ± 14.49, 62.35 ± 15.67 and 50.01 ± 12.60%, respectively. There was a significant difference between without- and with-iontophoresis groups after acid challenge (p < 0.05). For SEM, after 7 days, SnF2 with-iontophoresis showed deeper dentinal tubule occlusion (p < 0.05) and more resistance to acid challenge than SnF2 without-iontophoresis. No significant change was observed in groups of no SnF2 treatment. Cathode iontophoresis could enhance the effect of SnF2 toothpaste in decreasing dentin permeability and increasing resistance to acid challenge.

S-PRG-based toothpastes compared to NaF toothpaste and NaF varnish on dentin permeability in vitro.

OBJECTIVES: To analyze the effect of 5 toothpastes containing different percentages of S-PRG fillers compared to NaF toothpaste and NaF varnish on the dentin hydraulic conductance (Lp). METHODOLOGY: Dentin disks (1.0±0.2 mm thickness) were cut from third molars, and their Lp values were evaluated using Flodec. The specimens were allocated into 7 groups (n=8). The minimum (smear layer) and the maximum (after acid etching) Lp values were recorded. Lp was also assessed after treatment with either a 0wt.%, 1wt.%, 5wt.%, 20wt.%, or 30wt.% S-PRG toothpaste, a NaF toothpaste, or a NaF varnish. Toothpastes were applied by brushing for 15 s, allowing it to settle for 1 min, and rinsing with deionized water. The NaF varnish was applied for 4 min and was removed with a probe. Specimens were exposed to citric acid (6%, pH 2.1, 1 min) and their final Lp was recorded. The pH of all products was recorded (n=3) and specimens from each group were analyzed by Laser Scanning Confocal Microscopy (LSCM). Data were subjected to 2-way repeated measures ANOVA and post-hoc Bonferroni (a=0.05). RESULTS: The highest Lp reduction was noticed for the 5wt.% S-PRG toothpaste, NaF toothpaste, and NaF varnish. However, the toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG were similar to all toothpastes but differed from the NaF varnish. After erosion, all groups retrieved their maximum Lp values, except for the NaF varnish. The LSCM evidenced deposits on the surface of specimens treated with 5%, 20%, and 30% S-PRG-based toothpastes and NaF toothpaste. Even more deposits were observed for the NaF varnish. After the erosive challenge, the deposits were diminished in all groups. CONCLUSION: Toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG fillers behaved similarly to a conventional NaF toothpaste, even after an erosive challenge. The NaF varnish promoted better reduction of the Lp, but its effect was also diminished after erosion.

Experimental pastes containing niobophosphate and 45S5 bioactive glasses for treatment of dentin hypersensitivity: dentin permeability and tubule obliteration.

OBJECTIVES: This study tested the ability of bioactive pastes containing niobophosphate and 45S5 glasses to reduce dentin permeability and to obliterate dentinal tubules, as a mean of reducing human dentin hypersensitivity. MATERIALS AND METHODS: Experimental pastes with concentrations of 10, 20, and 30 wt% of two bioactive glasses (45S5 or niobophosphate [NbG]) were formulated. A paste without bioactive glass (placebo) and a commercial paste (Nano P, FGM) were used as controls. Forty dentin disc specimens were obtained from caries-free extracted third human molars and divided in 8 groups (n = 5). Percentage of permeability (%Lp) was assessed in a dental permeability machine considering hydraulic conductance, immediately after pastes application and at day 7, day 14, and day 21. The precipitates formed on the surface of the dentin discs (and dentinal tubules) were analyzed by SEM/EDS and micro-Raman spectra. Data of dentin permeability (%) 2-way repeated-measures (ANOVA) and Holm-Sidak post-tests (α = 0.05). Dentinal tubule obliteration was visually (and elemental) evaluated and descriptively reported. RESULTS: The experimental bioactive glass pastes containing NbG and 45S5, regardless of the concentration, reduced dentin permeability in comparison with pastes without bioactive glasses (P < 0.05). The formulated placebo and commercial paste did not reduce permeability over time (P < 0.05). SEM/EDS and micro-Raman analyses showed that both type of bioactive pastes (NbG or 45S5-based) presented mineral precipitates obliterating the dentinal tubules at day 21. NbG seems to offer a better initial effect than 45S5, while at 21 days there is no difference between both glasses. CONCLUSION: Experimental bioactive pastes containing NbG and 45S5 (at concentrations of 10%, 20%, or 30%) have potential to reduce dentin permeability (over time) in comparison with pastes without bioactive glasses; and this occurs on behalf of obliteration of dentinal tubules by microparticle and precipitate formation. CLINICAL RELEVANCE: Bioactive pastes containing NbG and 45S5 may benefit patients presenting dentin hypersensitivity, because these pastes can start acting fast after application and maintain their action up to 21 days.

Bonding strategy of a universal adhesive system containing chitosan: influence on dentin permeability, and effect on adhesive layer micromorphology.

AIM: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. MATERIALS AND METHOD: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. RESULTS: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. CONCLUSIONS: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.

OBJETIVO: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. RESULTADOS: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levou a uma menor permeabilidade dentinária e a mais irregularidades na superfície da camada adesiva.

Effect of different toothpastes on permeability and roughness of eroded dentin.

Dentin hypersensitivity (DH) is characterized by rapid, acute pain arising from exposed dental tubules. AIM: the aim of this study was to evaluate the roughness, tubule occlusion, and permeability of eroded dentin brushed with different toothpastes. MATERIALS AND METHOD: ninety bovine teeth were cut into blocks. Thirty hemifaces were protected with varnish and the other sixty were submitted to permeability tests. Specimens were divided into groups according to the dentifrices: without fluoride (WF), sodium fluoride (NaF), and stannous fluoride (SnF2). The blocks were subjected to a 5-day erosive-abrasive protocol. Surface roughness and dentinal tubule occlusion (n=10) were assessed for both control and test hemifaces of the same sample along with permeability analysis (n=20). Two-way RM ANOVA and Tukey's post-hoc test were performed (p≤0.05). RESULTS: NaF and SnF2 presented higher roughness than WF. The number of open tubules was higher in WF. Permeability was higher in SnF2, but there was no significant difference between WF and NaF. CONCLUSIONS: both fluoride toothpastes occluded dentinal tubules and increased roughness. NaF toothpaste promoted greater decrease in dentin permeability.

A hipersensibilidade dentinária (HD) é caracterizada por dor rápida e aguda decorrente de túbulos dentais expostos. Objetivo: este estudo teve como objetivo avaliar a rugosidade, oclusão tubular e permeabilidade da dentina erodida escovada com diferentes dentifrícios. Materiais e Método: noventa dentes bovinos foram seccionados em blocos. Trinta hemifaces foram protegidas com verniz e outras sessenta foram submetidas à permeabilidade. Os espécimes foram divididos em grupos de acordo com os dentifrícios: sem flúor (SF), fluoreto de sódio (NaF) e fluoreto estanoso (SnF2). Em seguida, os blocos foram submetidos a um protocolo erosivo-abrasivo de 5 dias. A rugosidade da superfície e a oclusão do túbulo dentinário (n = 10) foram avaliadas para ambas as hemifaces de controle e teste da mesma amostra, também realizou-se a análise de permeabilidade (n = 20). Two-way RM ANOVA e pós-teste de Tukey foram realizados (p≤0,05). Resultados: NaF e SnF2 apresentaram rugosidade superior ao SF. O número de túbulos abertos foi maior em SF. Não encontramos diferenças significativas entre SF e NaF em relação à permeabilidade; entretanto, SnF2 apresentou maior permeabilidade. Conclusão: ambos os dentifrícios fluoretados foram capazes de ocluir os túbulos dentinários e aumentar a rugosidade. No entanto, o dentifrício NaF promoveu uma maior diminuição da permeabilidade dentinária.

Effect of bioactive glasses containing strontium and potassium on dentin permeability.

Dentin hypersensitivity (DH) is characterized by pain caused by an external stimulus on exposed dentin. Different therapeutic approaches have been proposed to mitigate this problem; however, none of them provide permanent pain relief. In this study, we synthesized and characterized experimental bioactive glasses containing 3.07 mol% SrO or 3.36 mol% K2 O (both equivalent to 5 wt% in the glass), and evaluated their effect on dentin permeability to verify their potential to treat DH. The experimental materials were characterized by field-emission scanning electron microscopy, Fourier transform infrared spectroscopy, micro-Raman spectroscopy, and X-ray diffraction to confirm the respective structures and chemical compositions. The reduction in the hydraulic conductance of dentin was evaluated at the three stages: minimum permeability; maximum permeability (24% ethylenediaminetetraacetic acid [EDTA] treatment); and final dentin permeability after treatment with the bioactive glasses. They all promoted a reduction in dentin permeability, with a significant difference for each sample and posttreatment group. Also, a significant reduction in dentin permeability was observed even after a simulated toothbrushing test, demonstrating effective action of these materials against DH. Besides, incorporating 3.07 mol% SrO was a positive factor. Therefore, strontium's desensitizing and re-mineralizing properties can be further exploited in bioactive glasses to promote a synergistic effect to treat DH.

Dentin Permeability and Nanoleakage of Universal Adhesives in Etch-and-rinse vs Self-etch Modes.

PURPOSE: This study evaluates the reduction in dentin permeability (P) and the expression of nanoleakage in resin-dentin interfaces made with universal adhesives, comparing the self-etch mode of application with the etch-and-rinse mode of application. METHODS AND MATERIALS: To measure dentin P at the baseline and after adhesive polymerization, 80 extracted noncarious human third molars (N=80) were sectioned to obtain 0.7-mm-thick midcoronal dentin disks. The specimens were randomly assigned to 8 groups according to the different adhesive systems and application modes used: Scotchbond Universal (SBU; etch-and-rinse [ER] mode vs self-etch [SE] mode), OptiBond XTR (OPT; etch-and-rinse mode vs self-etch mode), Clearfil Universal Bond Quick (CL; etch-and-rinse mode vs self-etch mode), and Adhese Universal (ADH; etch-and-rinse mode vs self-etch mode). A two-way analysis of variance with interaction was used to evaluate the P reduction differences among the groups (α=0.05). Sixteen additional 0.7-mm-thick dentin disks were similarly prepared and treated, immersed in 50 wt% ammoniacal silver nitrate, and then processed according to conventional methods for analysis under transmission electron microscopy. RESULTS: The differences in P reduction among the adhesives were significant (p=0.029). For OPT and ADH (p=0.0304 and p=0.0120, respectively), the P reduction was higher in the ER mode than in the SE mode. For CL and SBU, no differences in P reduction was observed between the two application modes (p>0.05). All the groups showed some pattern of nanoleakage. CONCLUSIONS: No adhesive system completely reduced dentin P. Dentin sealing was higher for OPT and ADH in the ER mode, while for SBU and CL, there was no difference between the two modes. All the adhesive systems showed nanoleakage.

Obliterating potential of active products for dentin hypersensitivity treatment under an erosive challenge.

OBJECTIVES: To compare the effect of 5 desensitizing agents on the hydraulic conductance (Lp) of dentin and to analyze its surface under a Laser Scanning Confocal Microscope (LSCM) before and after an erosive challenge. METHODS: Lp was analyzed in the following sequence: in the presence of smear layer (pMin), after a 15-second acid etching (pMax), after treatment with a desensitizing agent (pTreat) and after a 1-minute erosive challenge (6% citric acid - pEro). Fifty 1.0 ± 0.2 mm-thick dentin disks were prepared from sound human third molars and were randomly distributed into 5 groups (n = 10): FG-Fluoride gel (control), SA-Sensiactive, PR-Sensitive Pro-Relief, NP-Desensibilize Nano-P and EV-Enamel Pro Varnish. Data were analyzed by two-way ANOVA and Tukey tests (α<0.05). Additional specimens were analyzed under a Laser Scanning Confocal Microscope (LSCM) and by Energy Dispersive X-ray Spectroscopy (EDS). RESULTS: All materials reduced the Lp in some extent, except for FG and EV. After the erosive challenge, SA was the only material effectively able to keep the same Lp of the post-treatment phase, while the other products showed lower resistance upon an erosive challenge. Under the LSCM, the SA and NP materials were more effective to obliterate the opened dentin tubules and demonstrated higher resistance upon an erosive challenge. The EDS analysis evidenced levels of Ca, O, P, Si, Na and S. CONCLUSIONS: Product containing potassium oxalate was the most effective in reducing Lp of dentin samples before and after an erosive challenge. Under a LSCM, products containing potassium oxalate or hydroxyapatite crystals seemed to be occluding the dentin tubules after an erosive challenge.

Avian Eggshell Slurry as a Dentin Desensitizing Agent:An In Vitro Assessment Using Two Techniques.

AIM: This study aims to evaluate the efficacy of avian eggshell slurry as a desensitizing agent compared to casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) containing Tooth Mousse. MATERIALS AND METHODS: Eggshell powder was prepared and characterized using a scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), and energy-dispersive X-ray spectroscopy (EDX). Forty dentin disks were immersed in 6% citric acid for 2 min to simulate hypersensitive dentin (baseline). Disks were then divided into two groups (n = 20) according to treatment received: eggshell slurry and commercially available Tooth Mousse desensitizing agent. Each group was further divided into two subgroups (n = 10). In subgroup 1, dentin discs were immersed in artificial saliva for four weeks whereas, in subgroup 2, discs underwent acid challenge. Environmental scanning electron microscope (ESEM) analysis and hydraulic conductance test were utilized to calculate dentinal tubules occlusion and reduction of dentin permeability percentages, respectively. Statistical analysis was performed using SPSS 22.0 at a significance level p ≤ 0.05. RESULTS: After application of desensitizing agents, the eggshell slurry group showed a significantly higher percentage of dentinal tubules occlusion compared to the Tooth Mousse group, whereas no significant difference existed in the percentage reduction of dentin permeability between both groups. After both immersion protocols, the eggshell slurry significantly occluded more dentinal tubules compared to Tooth Mousse. On the contrary, results of percentage reduction of dentin permeability revealed no significant difference between both subgroups after acid challenge. After artificial saliva immersion, Tooth Mousse showed a significantly higher percentage reduction of dentin permeability compared to the eggshell slurry. CONCLUSION: Avian eggshell slurry can effectively occlude open dentinal tubules compared to commercially available Tooth Mousse desensitizing agent. CLINICAL SIGNIFICANCE: Avian eggshell slurry can be considered a promising material for the treatment of dentin hypersensitivity. How to cite this article: El Tahlawy AA, Saba DA, Bakir NG. Avian Eggshell Slurry as a Dentin Desensitizing Agent: An In Vitro Assessment Using Two Techniques. J Contemp Dent Pract 2021;22(5):532-537.

Analysis of permeability and biological properties of dentin treated with experimental bioactive glasses.

OBJECTIVES: To evaluate obliterating capability and biological performance of desensitizing agents. METHODS: 50 dentin blocks were distributed according to the desensitizing agent used (n = 10): Control (Artificial saliva); Ultra EZ (Ultradent); Desensibilize Nano P (FGM); T5-OH Bioactive Glass (Experimental solution); F18 Bioactive Glass (Experimental solution). Desensitizing treatments were performed for 15 days. In addition, specimens were subjected to acid challenge to simulate oral environment demineralizing conditions. Samples were subjected to permeability analysis before and after desensitizing procedures and acid challenge. Cytotoxicity analysis was performed by using Alamar Blue assay and complemented by total protein quantification by Pierce Bicinchoninic Acid assay at 15 min, 24-h and 48-h time points. Scanning electron microscopy and energy dispersion X-ray spectroscopy were performed for qualitative analysis. Data of dentin permeability was analyzed by two-way repeated measures ANOVA and Tukey's test. For cytotoxicity, Kruskal-Wallis and Newman-Keuls tests. RESULTS: for dentin permeability there was no significant difference among desensitizing agents after treatment, but control group presented highest values (0.131 ± 0.076 Lp). After acid challenge, control group maintained highest values (0.044 ± 0.014 Lp) with significant difference to other groups, except for Desensibilize Nano P (0.037 ± 0.019 Lp). For cytotoxicity, there were no significant differences among groups. CONCLUSION: Bioglass-based desensitizers caused similar effects to commercially available products, regarding permeability and dentin biological properties. CLINICAL SIGNIFICANCE: There is no gold standard protocol for dentin sensitivity. The study of novel desensitizing agents that can obliterate dentinal tubules in a faster-acting and long-lasting way may help meet this clinical need.

Association of Nd:YAG laser and calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion.

OBJECTIVE: To evaluate the efficacy of Nd:YAG laser associated with calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion after erosive/abrasive challenges. METHODOLOGY: Dentin specimens were exposed to 17% ethylene diamine tetra-acetic acid (EDTA) solution for 5 min and randomly allocated into five groups: G1, control (no treatment); G2, Nd:YAG laser (1 W, 10 Hz, 100 mJ, 85 J/cm2); G3, Laser + TeethmateTM Desensitizer; G4, Laser + Desensibilize Nano P; and G5, Laser+Nupro®. Specimens underwent a 5-day erosion-abrasion cycling. Hydraulic conductance was measured post-EDTA, post-treatment, and post-cycling. Post-treatment and post-cycling permeability (%Lp) was calculated based on post-EDTA measurements, considered 100%. Open dentin tubules (ODT) were calculated at the abovementioned experimental moments using scanning electron microscopy and ImageJ software (n=10). Data were analyzed using two-way repeated measures ANOVA and Tukey's test (α=0.05). RESULTS: G1 presented the highest %Lp post-treatment of all groups (p<0.05), without significantly differences among them. At post-cycling, %Lp significantly decreased in G1, showed no significant differences from post-treatment in G3 and G4, and increased in G2 and G5, without significant differences from G1 (p>0.05). We found no significant differences in ODT among groups (p>0.05) post-EDTA. At post-treatment, treated groups did not differ from each other, but presented lower ODT than G1 (p<0.001). As for post-cycling, we verified no differences among groups (p>0.05), although ODT was significantly lower for all groups when compared to post-EDTA values (p<0.001). CONCLUSION: All treatments effectively reduced dentin permeability and promoted tubule occlusion after application. COMBINING ND: YAG laser with calcium-phosphate pastes did not improve the laser effect. After erosive-abrasive challenges, treatments presented no differences when compared to the control.

Duration of dentin tubule occlusion by the calcium phosphate precipitation method: An in vivo study in beagle dogs.

The aim of the present study was to assess the duration of dentin tubule occlusion by the calcium phosphate precipitation (CPP) method in the vital teeth of beagle dogs. Vital teeth were treated using the CPP method, potassium oxalate, or a bonding agent (Liner bond II) after cavity preparation and acid etching. The dentin tubules of all groups, except for the bonding agent, opened more widely with time in the absence of plaque control. Dentin tubules treated with the CPP method were open and no precipitate remained in the absence of plaque control. Differences were observed in dentin tubule occlusion when plaque control was achieved by daily tooth brushing. The majority of dentin tubules were occluded with an apatitic precipitate seven days after the CPP method with plaque control. The present results demonstrated that the CPP method is useful with proper plaque control.

Physicochemical characterization, water sorption and solubility of adhesive systems incorporated with titanium tetrafluoride, and its influence on dentin permeability.

Titanium tetrafluoride (TiF4) in an aqueous solution can decrease dentin permeability, but some effects of its incorporation into adhesive systems are not yet known. Therefore, the aim of this study was to characterize the physicochemical, water sorption (WS) and solubility (SL) properties of two adhesive systems (Clearfil SE Bond/C and Scotchbond Universal/S) incorporated with 0.0% (T0), 2.5% (T2) and 4.0% (T4) titanium tetrafluoride (TiF4), and determine dentin permeability (L) after application of these adhesive systems both immediately afterwards (baseline) and after 6 months of storage. The physicochemical analyses of the incorporated solutions were performed based on evaluating particle size (PS), polydispersity index (PDI) by dynamic light scattering, and zeta potential (ZP) by electrophoresis. WS and SL tests followed ISO 4049 standards, and used a 7-day water storage period. The L test was performed by analyzing human dentin discs before and after adhesive system application, and after storage. PS and PDI were higher for CT0 and ST4 (p < 0.0001; ANOVA, Tukey). ZP was lower for CT4, ST2 and ST4 (p < 0.0001; ANOVA, Tukey). A 4.0% TiF4 incorporation showed higher WS (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). Higher SL was observed for CT0 and ST4 (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). The L value at baseline was lower for ST4, but was not different from the CT4 groups after storage (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). It can be concluded that TiF4 affected the colloidal stability of Scotchbond, but did not alter the other properties. The 2.5% TiF4 did not affect the PDI, WS or L of the Clearfil, and can be considered an alternative for reducing hybrid layer degradation.