Análise da adaptação marginal e interna em próteses sobre implantes cimentadas com diferentes tipos de cimentos / Analysis of marginal and internal fi t of cement retained implant-supported single crowns luted with different cements
Oliveira, Mario Cezar; Vieira, Alex Correia; Andrade, Adriana Castro V.
Afiliação
  • Oliveira, Mario Cezar; Universidade Estadual de Feira de Santana. Feira de Santana. BR
  • Vieira, Alex Correia; Universidade Estadual de Feira de Santana. Feira de Santana. BR
  • Andrade, Adriana Castro V; Universidade Estadual de Feira de Santana. Feira de Santana. BR
ImplantNewsPerio ; 1(8): 1514-1521, nov.-dez. 2016. ilus, tab
Artigo em Português | LILACS, BBO - Odontologia | ID: biblio-848535
Biblioteca responsável: BR510.1
RESUMO

Objetivo:

avaliar a desadaptação marginal vertical e interna entre o cilindro cimentável e o coping metálico de próteses sobre implantes com o uso de três diferentes tipos de cimentos um provisório, o cimento de hidróxido de cálcio (Dycal, Dentsply); e dois definitivos, o cimento de fosfato de zinco (SSWhite) e o cimento resinoso (Relyx Unicem, 3M Espe). Material e

métodos:

foram confeccionados 30 corpos-de-prova constituídos pelo cilindro cimentável e coping metálico, divididos em três grupos (n=10) que receberam os diferentes agentes de cimentação. As amostras foram submetidas à termociclagem, em seguida hemisseccionadas e então avaliadas em microscópio eletrônico de varredura (MEV) com aumento de 420 vezes.

Resultados:

não foram observadas diferenças signifi cativas entre os valores de desajuste marginal vertical para os três cimentos, porém, para a desadaptação interna, a maior discrepância foi obtida pelo cimento de hidróxido de cálcio.

Conclusão:

o cimento provisório apresentou comportamento similar aos cimentos definitivos em relação à adaptação marginal, porém, foi menos eficiente no desajuste interno dos copings.
ABSTRACT

Objective:

to evaluate the vertical and internal marginal leakage between the cement cylinder and the metallic coping using three different types of cements, one temporary cement, calcium hydroxide cement (Dycal, Dentsply) and two definitive cements, zinc phosphate cement (SSWhite) and resin cement (Relyx Unicem, 3M Espe). Material and

methods:

30 specimens were prepared, constituted by the cement cylinder and the metallic coping, divided into 3 groups (n=10) which received different luting agents. The samples were submitted to thermocycling and then hemisected. These were then evaluated in a scanning electron microscope (SEM) with 420 x magnification.

Results:

there were no statistically signifi cant differences between the vertical misfit values for the three cements, however, for the internal fit, the largest discrepancy was obtained by the calcium hydroxide cement.

Conclusion:

the temporary cement showed similar behavior to definitive cements on the marginal adaptation, but its internal misfit was higher.
Assuntos

Buscar no Google
Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Hidróxido de Cálcio / Implantes Dentários / Adaptação Marginal Dentária / Prótese Dentária Fixada por Implante / Cimentos de Resina / Cimentos Dentários Tipo de estudo: Estudo de avaliação Limite: Humanos Idioma: Português Revista: ImplantNewsPerio Assunto da revista: Odontologia Ano de publicação: 2016 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Universidade Estadual de Feira de Santana/BR
Buscar no Google
Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Hidróxido de Cálcio / Implantes Dentários / Adaptação Marginal Dentária / Prótese Dentária Fixada por Implante / Cimentos de Resina / Cimentos Dentários Tipo de estudo: Estudo de avaliação Limite: Humanos Idioma: Português Revista: ImplantNewsPerio Assunto da revista: Odontologia Ano de publicação: 2016 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Universidade Estadual de Feira de Santana/BR
...