Estudo comparativo in vitro das estruturas orgânicas e inorgânicas da dentina saudável e esclerosada humana e bovina: nanodureza, concentração de Ca e P e análise morfológica / In vitro comparative study of organic and inorganic components analysis of health and sclerotic human and bovine dentin: nanohardness, Ca and P concentration and morphological analysis
São Paulo; s.n; 2010. 101 p. ilus, tab, graf. (BR).
Tese em Português | LILACS, BBO - Odontologia | ID: lil-594699
Biblioteca responsável: BR97.1
Localização: BR97.1; T4.520
RESUMO
A dentina esclerosada é um substrato comumente encontrado em pacientes idosos. No entanto, existem poucos estudos comparativos entre dentina humana e bovina esclerosadas. O objetivo deste estudo foi comparar os componentes inorgânicos e orgânicos da dentina saudável e esclerosada humana e bovina, através de cinco parâmetros nanodureza, módulo de elasticidade, análise quantitativa da concentração de Cálcio (Ca) e Fósforo (P), densidade tubular e morfologia do colágeno. Trinta dentes humanos e 30 bovinos foram distribuídos em 4 grupos experimentais (n=15 por grupo) dentina humana saudável (DHS), esclerosada humana (DEH), bovina saudável (DBS), e bovina esclerosada (DBE). Os dentes saudáveis foram preparados na mesma altura e inclinação dos dentes esclerosados expondo níveis similares da dentina e obtendo fragmentos com 2mm de espessura. Foram realizadas 3 medições por espécime em 3 áreas pré determinadas de dentina intertubular com a utilização do Nanoindentador (carga de 500N por 5 s). Cinco espécimes de cada grupo foram preparados para Microscopia Eletrônica de Varredura (MEV). Com o auxílio da Energia Dispersiva por Raios-X EDX foram obtidos os valores (em percentagem) das concentrações de Ca e P e calculada a relação CaP. A contagem dos túbulos por área foi realizada em todas as eletromicrografias. Após descalcificação e preparo, o restante dos espécimes foi analisado em Microscopia Eletrônica de Transmissão (MET)...
ABSTRACT
The sclerotic dentin has been commonly found in elderly patients. However, there are scarce reports in the literature comparing on the use of human and bovine sclerotic dentins. The objective of this study was to compare inorganic and organic components of healthy and sclerotic dentins from human and bovine. Five parameters were analyzed nanohardness, elastic modulus, quantitative analysis of Calcium (Ca) and Phosphorous (P) concentrations, tubular density and ultrastructural morphology. Thirty human teeth plus 30 bovine teeth were distributed in 4 experimental groups (n=15 per group) human healthy dentin (HHD), human sclerotic dentin (HSD), bovine healthy dentin (BHD) and bovine sclerotic dentin (BSD). Healthy teeth were cut in the same level and inclination of the sclerotic superficial dentins. The nanohardness and elastic modulus (GPa) of three pre determined areas of each exposed dentin was measured using a nanoindenter (500N for 5s). Five samples of each group were prepared for scanning electron microscopy (SEM) examination. Energy Dispersive X-ray (EDX) was used for obtaining the Ca/P ratio. The tubular density was obtained by counting the tubules in scanning electron micrographs taken in the same magnification and work distance...
Assuntos

Texto completo: Disponível Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Compostos Orgânicos / Microscopia Eletrônica / Dentina / Compostos Inorgânicos Limite: Animais / Feminino / Humanos / Masculino Idioma: Português Ano de publicação: 2010 Tipo de documento: Tese
Texto completo: Disponível Coleções: Bases de dados internacionais Base de dados: BBO - Odontologia / LILACS Assunto principal: Compostos Orgânicos / Microscopia Eletrônica / Dentina / Compostos Inorgânicos Limite: Animais / Feminino / Humanos / Masculino Idioma: Português Ano de publicação: 2010 Tipo de documento: Tese
...