Does cancellous screw insertion torque depend on bone mineral density and/or microarchitecture?

During insertion of a cancellous bone screw, the torque level reaches a plateau, at the engagement of all the screw threads prior to the screw head contact. This plateau torque (T(Plateau)) was found to be a good predictor of the insertion failure torque (stripping) and also exhibited strong positive correlations with areal bone mineral density (aBMD) in ovine bone. However, correlations between T(Plateau) and aBMD, as well as correlations between T(Plateau) and bone microarchitecture, have never been explored in human bone. The aim of this study was to determine whether T(Plateau), a predictor of insertion failure torque, depends on aBMD and/or bone microarchitecture in human femoral heads. Fifty-two excised human femoral heads were obtained. The aBMD and microarchitecture of each specimen were evaluated using dual X-ray Absorptiometry and micro-computed tomography. A cancellous screw was inserted into specimens using an automated micro-mechanical test device, and T(Plateau) was calculated from the insertion profile. T(Plateau) exhibited the strongest correlation with the structure model index (SMI, R=-0.82, p<0.001), followed by bone volume fraction (BV/TV, R=0.80, p<0.01) and aBMD (R=0.76, p<0.01). Stepwise forward regression analysis showed an increase for the prediction of T(Plateau) when aBMD was combined with microarchitectural parameters, i.e., aBMD combined with SMI (R(2) increased from 0.58 to 0.72) and aBMD combined with BV/TV and BS/TV (R(2) increased from 0.58 to 0.74). In conclusion, T(Plateau), a strong predictor for insertion failure torque, is significantly dependent on bone microarchitecture (particularly SMI and BV/TV) and aBMD.

Pullout strength of cancellous screws in human femoral heads depends on applied insertion torque, trabecular bone microarchitecture and areal bone mineral density.

For cancellous bone screws, the respective roles of the applied insertion torque (TInsert) and of the quality of the host bone (microarchitecture, areal bone mineral density (aBMD)), in contributing to the mechanical holding strength of the bone-screw construct (FPullout), are still unclear. During orthopaedic surgery screws are tightened, typically manually, until adequate compression is attained, depending on surgeons' manual feel. This corresponds to a subjective insertion torque control, and can lead to variable levels of tightening, including screw stripping. The aim of this study, performed on cancellous screws inserted in human femoral heads, was to investigate which, among the measurements of aBMD, bone microarchitecture, and the applied TInsert, has the strongest correlation with FPullout. Forty six femoral heads were obtained, over which microarchitecture and aBMD were evaluated using micro-computed tomography and dual X-ray absorptiometry. Using an automated micro-mechanical test device, a cancellous screw was inserted in the femoral heads at TInsert set to 55% to 99% of the predicted stripping torque beyond screw head contact, after which FPullout was measured. FPullout exhibited strongest correlations with TInsert (R=0.88, p<0.001), followed by structure model index (SMI, R=-0.81, p<0.001), bone volume fraction (BV/TV, R=0.73, p<0.001) and aBMD (R=0.66, p<0.01). Combinations of TInsert with microarchitectural parameters and/or aBMD did not improve the prediction of FPullout. These results indicate that, for cancellous screws, FPullout depends most strongly on the applied TInsert, followed by microarchitecture and aBMD of the host bone. In trabecular bone, screw tightening increases the holding strength of the screw-bone construct.