Electrochemical Activation of Fe-LiF Conversion Cathodes in Thin-Film Solid-State Batteries.

Transition metal fluoride (TMF) conversion-type cathodes promise up to 4 times higher gravimetric energy densities compared to those of common intercalation-type cathodes. However, TMF cathodes demonstrate sluggish kinetics, poor efficiencies, and incompatibility with many liquid electrolytes. In this work, coevaporated heterostructured iron and lithium fluoride (Fe-LiF) cathodes are investigated in thin-film solid-state batteries with a LiPON electrolyte and a lithium metal anode. The cells were cycled 2000 times at a cycling rate of 6C. They show a gradual improvement in voltaic efficiency (37-53%) and specific capacity (146-216 mAh/g) during cycling. After 2000 cycles, the cathode capacity reaches 480 mAh/g at a cycling rate of C/3.6, close to its theoretical capacity of 498 mAh/g, at room temperature conditions. This capacity gain is correlated with an observed electrochemically activated nanorestructuring of the cathode, characterized by cycling-induced coarsening (from 2.8 to 4.2 nm) of the metallic iron phase and its accumulation near the current collector interface, as well as lithium fluoride phase accumulation near the LiPON interface.

Influence of Au, Pt, and C Seed Layers on Lithium Nucleation Dynamics for Anode-Free Solid-State Batteries.

In the concept of anode-free lithium-ion batteries, cells are manufactured with a bare anode current collector where the lithium metal anode is electrochemically formed from the lithium-containing cathode during the first charge cycle. While this concept has many attractive aspects from a manufacturing and energy density standpoint, stable plating and stripping remain challenging. We have investigated gold, platinum, and amorphous carbon as seed layers placed between the copper current collector and the lithium phosphorus oxynitride thin-film solid electrolyte. These layers guide lithium nucleation and improve the plating and stripping dynamics. All seed layers facilitate reversible lithium plating and stripping even at high current densities up to 8 mA cm-2. Of particular note is the amorphous carbon seed layer, which allowed a significant reduction in plating potential from 300 mV to as low as 50 mV. These results underscore the critical role of seed layers in improving the efficiency of anode-free solid-state batteries and open the door to simplified manufacturing of anode-free battery designs.

Hysteresis and Its Correlation to Ionic Defects in Perovskite Solar Cells.

Ion migration has been reported to be one of the main reasons for hysteresis in the current-voltage (J-V) characteristics of perovskite solar cells. We investigate the interplay between ionic conduction and hysteresis types by studying Cs0.05(FA0.83MA0.17)0.95Pb(I0.9Br0.1)3 triple-cation perovskite solar cells through a combination of impedance spectroscopy (IS) and sweep-rate-dependent J-V curves. By comparing polycrystalline devices to single-crystal MAPbI3 devices, we separate two defects, ß and γ, both originating from long-range ionic conduction in the bulk. Defect ß is associated with a dielectric relaxation, while the migration of γ is influenced by the perovskite/hole transport layer interface. These conduction types are the causes of different types of hysteresis in J-V curves. The accumulation of ionic defects at the transport layer is the dominant cause for observing tunnel-diode-like characteristics in the J-V curves. By comparing devices with interface modifications at the electron and hole transport layers, we discuss the species and polarity of involved defects.

Alleviating nanostructural phase impurities enhances the optoelectronic properties, device performance and stability of cesium-formamidinium metal-halide perovskites.

The technique of alloying FA+ with Cs+ is often used to promote structural stabilization of the desirable α-FAPbI3 phase in halide perovskite devices. However, the precise mechanisms by which these alloying approaches improve the optoelectronic quality and enhance the stability have remained elusive. In this study, we advance that understanding by investigating the effect of cationic alloying in CsxFA1-xPbI3 perovskite thin-films and solar-cell devices. Selected-area electron diffraction patterns combined with microwave conductivity measurements reveal that fine Cs+ tuning (Cs0.15FA0.85PbI3) leads to a minimization of stacking faults and an increase in the photoconductivity of the perovskite films. Ultra-sensitive external quantum efficiency, kelvin-probe force microscopy and photoluminescence quantum yield measurements demonstrate similar Urbach energy values, comparable surface potential fluctuations and marginal impact on radiative emission yields, respectively, irrespective of Cs content. Despite this, these nanoscopic defects appear to have a detrimental impact on inter-grains'/domains' carrier transport, as evidenced by conductive-atomic force microscopy and corroborated by drastically reduced solar cell performance. Importantly, encapsulated Cs0.15FA0.85PbI3 devices show robust operational stability retaining 85% of the initial steady-state power conversion efficiency for 1400 hours under continuous 1 sun illumination at 35 °C, in open-circuit conditions. Our findings provide nuance to the famous defect tolerance of halide perovskites while providing solid evidence about the detrimental impact of these subtle structural imperfections on the long-term operational stability.