The interface layer has great significance on the potential barrier height of the CdTe/GaAs heterointerface. In this study, the electronic properties of the CdTe/GaAs heterostructure prepared by molecular beam epitaxy was investigated in situ by synchrotron radiation photoemission spectroscopy for CdTe thicknesses ranging from 3.5 to 74.6 Å. During CdTe deposition, an As-Te and Ga-Te interface reaction occurred, which caused the out diffusion of Ga. As a result a stable GaTe interface dipole layer (more than 30 Å) was formed, which reduced the potential barrier height by 0.38 eV. The potential barrier height was in proportion to the chemical bonding density and thickness of the Ga-Te interface layer. These results provide a more fundamental understanding of the influencing mechanism of the interface layer on the potential barrier height of the CdTe/GaAs heterointerface.
RESUMO
Correction for 'Effects of Ga-Te interface layer on the potential barrier height of CdTe/GaAs heterointerface' by Shouzhi Xi et al., Phys. Chem. Chem. Phys., 2016, 18, 2639-2645.
RESUMO
The influence of damage induced by 2MeV protons on CdZnTe radiation detectors is investigated using ion beam induced charge (IBIC) microscopy. Charge collection efficiency (CCE) in irradiated region is found to be degraded above a fluence of 3.3×10(11)p/cm(2) and the energy spectrum is severely deteriorated with increasing fluence. Moreover, CCE maps obtained under the applied biases from 50V to 400V suggests that local radiation damage results in significant degradation of CCE uniformity, especially under low bias, i. e., 50V and 100V. The CCE nonuniformity induced by local radiation damage, however, can be greatly improved by increasing the detector applied bias. This bias-dependent effect of 2MeV proton-induced radiation damage in CdZnTe detectors is attributed to the interaction of electron cloud and radiation-induced displacement defects.
RESUMO
To understand the effects of tellurium (Te) inclusions on the device performance of CdZnTe radiation detectors, the perturbation of the electrical field in and around Te inclusions was studied in CdZnTe single crystals via Kelvin probe force microscopy (KPFM). Te inclusions were proved to act as lower potential centers with respect to surrounding CdZnTe matrix. Based on the KPFM results, the energy band diagram at the Te/CdZnTe interface was established, and the bias-dependent effects of Te inclusion on carrier transportation is discussed.