RESUMO
Germanium selenide (GeSe) bulk crystals, thin films and solar cells are investigated with a focus on acceptor-doping with silver (Ag) and the use of an Sb2Se3 interfacial layer. The Ag-doping of GeSe occurred by a stoichiometric melt growth technique that created Ag-doped GeSe bulk crystals. A combination of capacitance voltage measurements, synchrotron radiation photoemission spectroscopy and surface space-charge calculations indicates that Ag-doping increases the hole density from 5.2 × 1015 cm-3 to 1.9 × 1016 cm-3. The melt-grown material is used as the source for thermally evaporated GeSe films within solar cells. The cell structure with the highest efficiency of 0.260% is FTO/CdS/Sb2Se3/undoped-GeSe/Au, compared with solar cells without the Sb2Se3 interfacial layer or with the Ag-doped GeSe.
RESUMO
The structures and band gaps of copper-zinc-tin selenosulfides (CZTSSe) are investigated for a range of anion compositions through experimental analysis and complementary first-principles simulations. The band gap was found to be extremely sensitive to the Sn-anion bond length, with an almost linear correlation with the average Sn-anion bond length in the mixed anion phase Cu2ZnSn(SxSe1-x)4. Therefore, an accurate prediction of band gaps using first-principles methods requires the accurate reproduction of the experimental bond lengths. This is challenging for many widely used approaches that are suitable for large supercells. The HSE06 functional was found to predict the structure and band gap in good agreement with the experiment but is computationally expensive for large supercells. It was shown that a geometry optimization with the MS2 meta-GGA functional followed by a single point calculation of electronic properties using HSE06 is a reasonable compromise for modeling larger supercells that are often unavoidable in the study of point and extended defects.
RESUMO
The improvement of antimony selenide solar cells by short-term air exposure is explained using complementary cell and material studies. We demonstrate that exposure to air yields a relative efficiency improvement of n-type Sb2Se3 solar cells of ca. 10% by oxidation of the back surface and a reduction in the back contact barrier height (measured by J-V-T) from 320 to 280 meV. X-ray photoelectron spectroscopy (XPS) measurements of the back surface reveal that during 5 days in air, Sb2O3 content at the sample surface increased by 27%, leaving a more Se-rich Sb2Se3 film along with a 4% increase in elemental Se. Conversely, exposure to 5 days of vacuum resulted in a loss of Se from the Sb2Se3 film, which increased the back contact barrier height to 370 meV. Inclusion of a thermally evaporated thin film of Sb2O3 and Se at the back of the Sb2Se3 absorber achieved a peak solar cell efficiency of 5.87%. These results demonstrate the importance of a Se-rich back surface for high-efficiency devices and the positive effects of an ultrathin antimony oxide layer. This study reveals a possible role of back contact etching in exposing a beneficial back surface and provides a route to increasing device efficiency.
RESUMO
Alternatives to lead- and tin-based perovskites for photovoltaics and optoelectronics are sought that do not suffer from the disadvantages of toxicity and low device efficiency of present-day materials. Here we report a study of the double perovskite Cs2TeI6, which we have synthesized in the thin film form for the first time. Exhaustive trials concluded that spin coating CsI and TeI4 using an antisolvent method produced uniform films, confirmed as Cs2TeI6 by XRD with Rietveld analysis. They were stable up to 250 °C and had an optical band gap of â¼1.5 eV, absorption coefficients of â¼6 × 104 cm-1, carrier lifetimes of â¼2.6 ns (unpassivated 200 nm film), a work function of 4.95 eV, and a p-type surface conductivity. Vibrational modes probed by Raman and FTIR spectroscopy showed resonances qualitatively consistent with DFT Phonopy-calculated spectra, offering another route for phase confirmation. It was concluded that the material is a candidate for further study as a potential optoelectronic or photovoltaic material.