Titanium Silicide: A Promising Candidate of Recombination Layer for Perovskite/Tunnel Oxide Passivated Contact Silicon Two-Terminal Tandem Solar Cells.

This study proposes a titanium silicide (TiSi2) recombination layer for perovskite/tunnel oxide passivated contact (TOPCon) 2-T tandem solar cells as an alternative to conventional transparent conductive oxide (TCO)-based recombination layers. TiSi2 was formed while TiO2 was made by oxidizing a Ti film deposited on the p+-Si layer. The reaction formation mechanism was proposed based on the diffusion theory supported by experimental results. The optical and electrical properties of the TiSi2 layer were optimized by controlling the initial Ti thicknesses (5-100 nm). With the initial Ti of 50 nm, the lowest reflectance and highly ohmic contact between the TiO2 and p+-Si layers with a contact resistivity of 161.48 mΩ·cm2 were obtained. In contrast, the TCO interlayer shows Schottky behavior with much higher contact resistivities. As the recombination layer of TiSi2 and the electron transport layer of TiO2 are formed simultaneously, the process steps become simpler. Finally, the MAPbI3/TOPCon tandem device yielded an efficiency of 16.23%, marking the first reported efficiency for a device including a silicide-based interlayer.

Perovskites fabricated on textured silicon surfaces for tandem solar cells.

The silicon surface texture significantly affects the current density and efficiency of perovskite/silicon tandem solar cells. However, only a few studies have explored fabricating perovskite on textured silicon and the effect of texture on perovskite films because of the limitations of solution processes. Here we produce conformal perovskite on textured silicon with a dry two-step conversion process that incorporates lead oxide sputtering and direct contact with methyl ammonium iodide. To separately analyze the influence of each texture structure on perovskite films, patterned texture, high-resolution photoluminescence (µ-PL), and light beam-induced current (µ-LBIC), 3D mapping is used. This work elucidates conformal perovskite on textured surfaces and shows the effects of textured silicon on the perovskite layers with high-resolution 3D mapping. This approach can potentially be applied to any type of layer on any type of substrate.