Extreme Enhancement of Carbon Hydrogasification via Mechanochemistry.

Carbon hydrogasification is the slowest reaction among all carbon-involved small-molecule transformations. Here, we demonstrate a mechanochemical method that results in both a faster reaction rate and a new synthesis route. The reaction rate was dramatically enhanced by up to 4 orders of magnitude compared to the traditional thermal method. Simultaneously, the reaction exhibited very high selectivity (99.8 % CH4 , versus 80 % under thermal conditions) with a cobalt catalyst. Our study demonstrated that this extreme increase in reaction rate originates from the continuous activation of reactive carbon species via mechanochemistry. The high selectivity is intimately related to the activation at low temperature, at which higher hydrocarbons are difficult to form. This work is expected to advance studies of carbon hydrogasification, and other solid-gas reactions.

Merging Platinum Single Atoms to Achieve Ultrahigh Mass Activity and Low Hydrogen Production Cost.

Single atom catalysts (SACs) with isolated active sites exhibit the highest reported mass activity for hydrogen evolution catalysis, which is crucial for practical applications. Here, we demonstrate that ultrahigh mass activity can also be achieved by rationally merging the isolated platinum (Pt) active sites in SAC. The catalyst was obtained by the thermodynamically driven diffusing and merging phosphorus-doped carbon (PC) supported Pt single atoms (Pt1@PC) into Pt nanoclusters (PtM@PC). X-ray absorption spectroscopy analysis revealed that the merged nanoclusters exhibit much stronger interactions with the support than the traditional method, enabling more efficient electron transfer. The optimized PtM@PC exhibited an order of magnitude higher mass activity (12.7 A mgPt-1) than Pt1@PC (0.9 A mgPt-1) at an overpotential of 10 mV in acidic media, which is the highest record to date, far exceeding reports for other outstanding SACs. Theoretical study revealed that the collective active sites in PtM@PC exhibit both favorable hydrogen binding energy and fast reaction kinetics, leading to the significantly enhanced mass activity. Despite its low Pt content (2.2 wt %), a low hydrogen production cost of ∼3 USD kg-1 was finally achieved in the full-water splitting at a laboratory scale.

Achieving volatile potassium promoted ammonia synthesis via mechanochemistry.

Potassium oxide (K2O) is used as a promotor in industrial ammonia synthesis, although metallic potassium (K) is better in theory. The reason K2O is used is because metallic K, which volatilizes around 400 °C, separates from the catalyst in the harsh ammonia synthesis conditions of the Haber-Bosch process. To maximize the efficiency of ammonia synthesis, using metallic K with low temperature reaction below 400 °C is prerequisite. Here, we synthesize ammonia using metallic K and Fe as a catalyst via mechanochemical process near ambient conditions (45 °C, 1 bar). The final ammonia concentration reaches as high as 94.5 vol%, which was extraordinarily higher than that of the Haber-Bosch process (25.0 vol%, 450 °C, 200 bar) and our previous work (82.5 vol%, 45 °C, 1 bar).

Ruthenium anchored on carbon nanotube electrocatalyst for hydrogen production with enhanced Faradaic efficiency.

Developing efficient and stable electrocatalysts is crucial for the electrochemical production of pure and clean hydrogen. For practical applications, an economical and facile method of producing catalysts for the hydrogen evolution reaction (HER) is essential. Here, we report ruthenium (Ru) nanoparticles uniformly deposited on multi-walled carbon nanotubes (MWCNTs) as an efficient HER catalyst. The catalyst exhibits the small overpotentials of 13 and 17 mV at a current density of 10 mA cm-2 in 0.5 M aq. H2SO4 and 1.0 M aq. KOH, respectively, surpassing the commercial Pt/C (16 mV and 33 mV). Moreover, the catalyst has excellent stability in both media, showing almost "zeroloss" during cycling. In a real device, the catalyst produces 15.4% more hydrogen per power consumed, and shows a higher Faradaic efficiency (92.28%) than the benchmark Pt/C (85.97%). Density functional theory calculations suggest that Ru-C bonding is the most plausible active site for the HER.

Edge-Functionalized Graphene Nanoplatelets as Metal-Free Electrocatalysts for Dye-Sensitized Solar Cells.

A scalable and low-cost production of graphene nanoplatelets (GnPs) is one of the most important challenges for their commercialization. A simple mechanochemical reaction has been developed and applied to prepare various edge-functionalized GnPs (EFGnPs). EFGnPs can be produced in a simple and ecofriendly manner by ball milling of graphite with target substances (X = nonmetals, halogens, semimetals, or metalloids). The unique feature of this method is its use of kinetic energy, which can generate active carbon species by unzipping of graphitic CC bonds in dry conditions (no solvent). The active carbon species efficiently pick up X substance(s), leading to the formation of graphitic CX bonds along the broken edges and the delamination of graphitic layers into EFGnPs. Unlike graphene oxide (GO) and reduced GO (rGO), the preparation of EFGnPs does not involve toxic chemicals, such as corrosive acids and toxic reducing agents. Furthermore, the prepared EFGnPs preserve high crystallinity in the basal area due to their edge-selective functionalization. Considering the available edge X groups that can be selectively employed, the potential applications of EFGnPs are unlimited. In this context, the synthesis, characterizations, and applications of EFGnPs, specifically, as metal-free carbon-based electrocatalysts for dye-sensitized solar cells (DSSCs) in both cobalt and iodine electrolytes are reviewed.