Thin-film materials with large electromechanical responses are fundamental enablers of next-generation micro-/nano-electromechanical applications. Conventional electromechanical materials (for example, ferroelectrics and relaxors), however, exhibit severely degraded responses when scaled down to submicrometre-thick films due to substrate constraints (clamping). This limitation is overcome, and substantial electromechanical responses in antiferroelectric thin films are achieved through an unconventional coupling of the field-induced antiferroelectric-to-ferroelectric phase transition and the substrate constraints. A detilting of the oxygen octahedra and lattice-volume expansion in all dimensions are observed commensurate with the phase transition using operando electron microscopy, such that the in-plane clamping further enhances the out-of-plane expansion, as rationalized using first-principles calculations. In turn, a non-traditional thickness scaling is realized wherein an electromechanical strain (1.7%) is produced from a model antiferroelectric PbZrO3 film that is just 100 nm thick. The high performance and understanding of the mechanism provide a promising pathway to develop high-performance micro-/nano-electromechanical systems.
RESUMO
Ordering of ferroelectric polarization1 and its trajectory in response to an electric field2 are essential for the operation of non-volatile memories3, transducers4 and electro-optic devices5. However, for voltage control of capacitance and frequency agility in telecommunication devices, domain walls have long been thought to be a hindrance because they lead to high dielectric loss and hysteresis in the device response to an applied electric field6. To avoid these effects, tunable dielectrics are often operated under piezoelectric resonance conditions, relying on operation well above the ferroelectric Curie temperature7, where tunability is compromised. Therefore, there is an unavoidable trade-off between the requirements of high tunability and low loss in tunable dielectric devices, which leads to severe limitations on their figure of merit. Here we show that domain structure can in fact be exploited to obtain ultralow loss and exceptional frequency selectivity without piezoelectric resonance. We use intrinsically tunable materials with properties that are defined not only by their chemical composition, but also by the proximity and accessibility of thermodynamically predicted strain-induced, ferroelectric domain-wall variants8. The resulting gigahertz microwave tunability and dielectric loss are better than those of the best film devices by one to two orders of magnitude and comparable to those of bulk single crystals. The measured quality factors exceed the theoretically predicted zero-field intrinsic limit owing to domain-wall fluctuations, rather than field-induced piezoelectric oscillations, which are usually associated with resonance. Resonant frequency tuning across the entire L, S and C microwave bands (1-8 gigahertz) is achieved in an individual device-a range about 100 times larger than that of the best intrinsically tunable material. These results point to a rich phase space of possible nanometre-scale domain structures that can be used to surmount current limitations, and demonstrate a promising strategy for obtaining ultrahigh frequency agility and low-loss microwave devices.
RESUMO
Calculation of Raman scattering from molecular dynamics (MD) simulations requires accurate modeling of the evolution of the electronic polarizability of the system along its MD trajectory. For large systems, this necessitates the use of atomistic models to represent the dependence of electronic polarizability on atomic coordinates. The bond polarizability model (BPM) is the simplest such model and has been used for modeling the Raman spectra of molecular systems but has not been applied to solid-state systems. Here, we systematically investigate the accuracy and limitations of the BPM parameterized from the density functional theory results for a series of simple molecules, such as CO2, SO2, H2S, H2O, NH3, and CH4; the more complex CH2O, CH3OH, CH3CH2OH, and thiophene molecules; and the BaTiO3 and CsPbBr3 perovskite solids. We find that BPM can reliably reproduce the overall features of the Raman spectra, such as shifts of peak positions. However, with the exception of highly symmetric systems, the assumption of non-interacting bonds limits the quantitative accuracy of the BPM; this assumption also leads to qualitatively inaccurate polarizability evolution and Raman spectra for systems where large deviations from the ground state structure are present.
RESUMO
The prospect of creating ferroelectric or high permittivity nanomaterials provides motivation for investigating complex transition metal oxides of the form Ba(Ti, MV)O3, where M = Nb or Ta. Solid state processing typically produces mixtures of crystalline phases, rarely beyond minimally doped Nb/Ta. Using a modified sol-gel method, we prepared single phase nanocrystals of Ba(Ti, M)O3. Compositional and elemental analysis puts the empirical formulas close to BaTi0.5Nb0.5O3-δ and BaTi0.5Ta0.5O3-δ. For both materials, a reversible temperature dependent phase transition (non-centrosymmetric to symmetric) is observed in the Raman spectrum in the region 533-583 K (260-310 °C); for Ba(Ti, Nb)O3, the onset is at 543 K (270 °C); and for Ba(Ti, Ta)O3, the onset is at 533 K (260 °C), which are comparable with 390-393 K (117-120 °C) for bulk BaTiO3. The crystal structure was resolved by examination of the powder x-ray diffraction and atomic pair distribution function (PDF) analysis of synchrotron total scattering data. It was postulated whether the structure adopted at the nanoscale was single or double perovskite. Double perovskites (A2B'Bâ³O6) are characterized by the type and extent of cation ordering, which gives rise to higher symmetry crystal structures. PDF analysis was used to examine all likely candidate structures and to look for evidence of higher symmetry. The feasible phase space that evolves includes the ordered double perovskite structure Ba2(Ti, MV)O6 (M = Nb, Ta) Fm-3m, a disordered cubic structure, as a suitable high temperature analog, Ba(Ti, MV)O3Pm-3m, and an orthorhombic Ba(Ti, MV)O3Amm2, a room temperature structure that presents an unusually high level of lattice displacement, possibly due to octahedral tilting, and indication of a highly polarized crystal.
RESUMO
Ferroelectrics have recently attracted attention as a candidate class of materials for use in photovoltaic devices, and for the coupling of light absorption with other functional properties. In these materials, the strong inversion symmetry breaking that is due to spontaneous electric polarization promotes the desirable separation of photo-excited carriers and allows voltages higher than the bandgap, which may enable efficiencies beyond the maximum possible in a conventional p-n junction solar cell. Ferroelectric oxides are also stable in a wide range of mechanical, chemical and thermal conditions and can be fabricated using low-cost methods such as sol-gel thin-film deposition and sputtering. Recent work has shown how a decrease in ferroelectric layer thickness and judicious engineering of domain structures and ferroelectric-electrode interfaces can greatly increase the current harvested from ferroelectric absorber materials, increasing the power conversion efficiency from about 10(-4) to about 0.5 per cent. Further improvements in photovoltaic efficiency have been inhibited by the wide bandgaps (2.7-4 electronvolts) of ferroelectric oxides, which allow the use of only 8-20 per cent of the solar spectrum. Here we describe a family of single-phase solid oxide solutions made from low-cost and non-toxic elements using conventional solid-state methods: [KNbO3]1 - x[BaNi1/2Nb1/2O3 - δ]x (KBNNO). These oxides exhibit both ferroelectricity and a wide variation of direct bandgaps in the range 1.1-3.8 electronvolts. In particular, the x = 0.1 composition is polar at room temperature, has a direct bandgap of 1.39 electronvolts and has a photocurrent density approximately 50 times larger than that of the classic ferroelectric (Pb,La)(Zr,Ti)O3 material. The ability of KBNNO to absorb three to six times more solar energy than the current ferroelectric materials suggests a route to viable ferroelectric semiconductor-based cells for solar energy conversion and other applications.
RESUMO
We show how finite-size scaling of a bulk photovoltaic effect-generated electric field in epitaxial ferroelectric insulating BaTiO_{3}(001) films and a photo-Hall response involving the bulk photovoltaic current reveal a large room-temperature mean free path of photogenerated nonthermalized electrons. Experimental determination of mesoscopic ballistic optically generated carrier transport opens a new paradigm for hot electron-based solar energy conversion, and for facile control of ballistic transport distinct from existing low-dimensional semiconductor interfaces, surfaces, layers, or other structures.
RESUMO
We report on the growth of polycrystalline BiFeO3 thin films on SiO2 /Si(001) and Pt(111) substrates by atomic layer deposition using the precursors ferrocene, triphenyl-bismuth, and ozone. By growing alternating layers of Fe2 O3 and Bi2 O3 , we employ a superlattice approach and demonstrate an efficient control of the cation stoichiometry. The superlattice decay and the resulting formation of polycrystalline BiFeO3 films are studied by in situ X-ray diffraction, in situ X-ray photoelectron spectroscopy, and transmission electron microscopy. No intermediate ternary phases are formed and BiFeO3 crystallization is initiated in the Bi2 O3 layers at 450 °C following the diffusion-driven intermixing of the cations. Our study of the BiFeO3 formation provides an insight into the complex interplay between microstructural evolution, grain growth, and bismuth oxide evaporation, with implications for optimization of ferroelectric properties.
RESUMO
We report intense, narrow line-width, surface chemisorption-activated and reversible ultraviolet (UV) photoluminescence from radiative recombination of the two-dimensional electron gas (2DEG) with photoexcited holes at LaAlO3/SrTiO3. The switchable luminescence arises from an electron transfer-driven modification of the electronic structure via H-chemisorption onto the AlO2-terminated surface of LaAlO3, at least 2 nm away from the interface. The control of the onset of emission and its intensity are functionalities that go beyond the luminescence of compound semiconductor quantum wells. Connections between reversible chemisorption, fast electron transfer, and quantum-well luminescence suggest a new model for surface chemically reconfigurable solid-state UV optoelectronics and molecular sensing.
Assuntos
Óxido de Alumínio/química , Técnicas Biossensoriais , Elétrons , Gases/química , Luminescência , Óxidos/química , Estrôncio/química , Propriedades de Superfície , Titânio/química , Raios UltravioletaRESUMO
We demonstrate spatial probing of carrier transport within GaAs/AlGaAs core-shell nanowires with nanometer lateral resolution and subsurface sensitivity by energy-variable electron beam induced current imaging. Carrier drift that evolves with applied electric field is distinguished from a coupled drift-diffusion length. Along with simulation of injected electron trajectories, combining beam energy tuning with precise positioning for selective probing of core and shell reveals axial position- and bias-dependent differences in carrier type and transport along parallel conduction channels. These results indicate how analysis of transport within heterostructured nanomaterials is no longer limited to nonlocal or surface measurements.
Assuntos
Alumínio/química , Gálio/química , Nanofios/química , ElétronsRESUMO
We report how a low vacuum pressure process followed by a few-minute annealing enables epitaxial stabilization, producing high-quality, phase-pure, single-crystalline epitaxial, and misfit dislocation-free BiFeO3(001) thin films on SrTiO3(001) at â¼450 °C less than current routes. These results unambiguously challenge the widely held notion that atomic layer deposition (ALD) is not appropriate for attaining high-quality chemically complex oxide films on perovskite substrates in single-crystalline epitaxial form, demonstrating applicability as an inexpensive, facile, and highly scalable route.
RESUMO
Group III-V coaxial core-shell semiconducting nanowire heterostructures possess unique advantages over their planar counterparts in logic, photovoltaic, and light-emitting devices. Dimensional confinement of electronic carriers and interface complexity in nanowires are known to produce local electronic potential landscapes along the radial direction that deviate from those along the normal to planar heterojunction interfaces. However, understanding of selected electronic and optoelectronic carrier transport properties and device characteristics remains lacking without a direct measurement of band alignment in individual nanowires. Here, we report on, in the GaAs/AlxGa1-xAs and GaAs/AlAs core-shell nanowire systems, how photocurrent and photoluminescence spectroscopies can be used together to construct a band diagram of an individual heterostructure nanowire with high spectral resolution, enabling quantification of conduction band offsets.
Assuntos
Alumínio/química , Arsenicais/química , Gálio/química , Nanofios/química , Óptica e Fotônica , Semicondutores , Análise EspectralRESUMO
Antiferroelectrics, which undergo a field-induced phase transition to ferroelectric order that manifests as double-hysteresis polarization switching, exhibit great potential for dielectric, electromechanical, and electrothermal applications. Compared to their ferroelectric cousins, however, considerably fewer efforts have been made to understand and control antiferroelectrics. Here, it is demonstrated that the polarization switching behavior of an antiferroelectric can be strongly influenced and effectively regulated by point defects. In films of the canonical antiferroelectric PbZrO3 , decreasing oxygen pressure during deposition (and thus increasing adatom kinetic energy) causes unexpected "ferroelectric-like" polarization switching although the films remain in the expected antiferroelectric orthorhombic phase. This "ferroelectric-like" switching is correlated with the creation of bombardment-induced point-defect complexes which pin the antiferroelectric-ferroelectric phase boundaries, and thus effectively delay the phase transition under changing field. The effective pinning energy is extracted via temperature-dependent switching-kinetics studies. In turn, by controlling the concentration of defect complexes, the dielectric tunability of the PbZrO3 can be adjusted, including being able to convert between "positive" and "negative" tunability near zero field. This work reveals the important role and strong capability of defects to engineer antiferroelectrics for new performance and functionalities.
RESUMO
Domain walls separating regions of ferroelectric material with polarization oriented in different directions are crucial for applications of ferroelectrics. Rational design of ferroelectric materials requires the development of a theory describing how compositional and environmental changes affect domain walls. To model domain wall systems, a discrete microscopic Landau-Ginzburg-Devonshire (dmLGD) approach with A- and B-site cation displacements serving as order parameters is developed. Application of dmLGD to the classic BaTiO3 , KNbO3, and PbTiO3 ferroelectrics shows that A-B cation repulsion is the key interaction that couples the polarization in neighboring unit cells of the material. dmLGD decomposition of the total energy of the system into the contributions of the individual cations and their interactions enables the prediction of different properties for a wide range of ferroelectric perovskites based on the results obtained for BaTiO3 , KNbO3, and PbTiO3 only. It is found that the information necessary to estimate the structure and energy of domain-wall "defects" can be extracted from single-domain 5-atom first-principles calculations, and that "defect-like" domain walls offer a simple model system that sheds light on the relative stabilities of the ferroelectric, antiferroelectric, and paraelectric bulk phases. The dmLGD approach provides a general theoretical framework for understanding and designing ferroelectric perovskite oxides.
RESUMO
We report the hot photoexcited electron transfer across the coaxial interface of a cylindrical core-shell nanowire. Modulation of the transfer rates, manifested as a large tunability of the voltage onset of negative differential resistance and of voltage-current phase, is achieved using three different modes. The coupling of electrostatic gating, incident photon energy, and the incident photon intensity to transfer rates is facilitated by the combined influences of geometric confinement and heterojunction shape on hot-electron transfer, and by electron-electron scattering rates that can be altered by varying the incident photon flux, with evidence of weak electron-phonon scattering. Dynamic manipulation of this transfer rate permits the introduction and control of a continuously adjustable phase delay of up to â¼130° within a single nanometer-scale device element.
RESUMO
We demonstrate that ferroelectric (FE) polarizations oriented along the finite thickness direction in ultrathin films are enhanced by the introduction of extreme curvature, thereby suppressing the finite-size-driven evolution of the FE phase transition temperature T(C). The measured responses within individual nanoshells possess magnitudes nearly three times that for their planar counterparts while exhibiting finite curvature-dependent offsets in FE switching hystereses. In stark contrast to the expected scaling of a depression of T(C) with inverse thickness, results based on modified Landau-Ginzburg model calculations indicate geometric curvature-driven polarization gradients in ultrathin films result in significant increases in T(C).
RESUMO
The quantum phenomenon of shift photovoltaic current was predicted decades ago, but this effect was never observed directly because shift and ballistic currents coexist. The atomic-scale relaxation time of shift, along with the absence of a photo-Hall behavior, has made decisive measurement of shift elusive. Here, we report a facile, direct-current, steady-state method for unambiguous determination of shift by means of the simultaneous measurements of linear and circular bulk photovoltaic currents under magnetic field, in a sillenite piezoelectric crystal. Comparison with theoretical predictions permits estimation of the signature length scale for shift. Remarkably, shift and ballistic photovoltaic currents under monochromatic illumination simultaneously flow in opposite directions. Disentangling the shift and ballistic contributions opens the way for quantitative, fundamental insight into and practical understanding of these radically different photovoltaic current mechanisms and their relationship.
RESUMO
We report on the high temperature thin film growth of BaTiO3 on Ti3C2Tx MXene flakes using van der Waals epitaxy on a degradable template layer. MXene was deposited on amorphous and crystalline substrates by spray- and dip-coating techniques, while the growth of BaTiO3 at 700 °C was accomplished using pulsed laser deposition in an oxygen rich environment. We demonstrate that the MXene flakes act as a temporary seed layer, which promotes highly oriented BaTiO3 growth along the (111) direction independent of the underlying substrate. The lattice parameters of the BaTiO3 films are close to the bulk value suggesting that the BaTiO3 films remains unstrained, as expected for van der Waals epitaxy. The initial size of the MXene flakes has an impact on the orientation of the BaTiO3 films with larger flake sizes promoting a higher fraction of the polycrystalline film to grow along the (111) direction. The deposited BaTiO3 film adopts the same morphology as the original flakes and piezoresponse force microscopy shows a robust ferroelectric behavior for individual grains. Transmission electron microscopy results indicate that the Ti3C2Tx MXene fully decomposes during the BaTiO3 deposition and the surplus Ti atoms are readily incorporated into the BaTiO3 film. Electrical measurements show a similar dielectric constant as a BaTiO3 film grown without the MXene seed layer. The demonstrated process has the potential to overcome the longstanding issue of integrating highly oriented complex oxide thin films directly on any desired substrate.
RESUMO
Traditionally, the ferroelectric Curie temperature can be manipulated by chemical substitution, e.g., in Ba1-xSrxTiO3 as one of the archetypical representatives. Here, we show a novel approach to tune the ferroelectric phase transition applicable for nanostructured thin films. We demonstrate this effect in nano-grained BaTiO3 films. Based on an enhanced metastable cation solubility with Ba/Ti-ratios of 0.8 to 1.06, a significant shift of the phase transition temperature is discovered. The transition temperature increases linearly from 212 K to 350 K with increasing Ba/Ti ratio. For all Ba/Ti ratios, a completely diffused phase transition is present resulting in a negligible temperature sensitivity of the dielectric constant. Schottky defects are identified as the driving force behind the off-stoichiometry and the shift of the phase transition temperature as they locally induce lattice strain. Complementary temperature dependent Raman experiments reveal the presence of the hexagonal polymorph in addition to the perovskite phase in all cases. Interestingly, the hexagonal BaTiO3 influences the structural transformation on the Ba-rich side, while on the Ti-rich side no changes for the hexagonal polymorph at the ferroelectric transition temperature are observed. This concerted structural change of both polymorphs on the Ba-rich side causes a broad phase transition region spanning over a wide range up to 420 K including the transition temperature of 350 K obtained from dielectric measurements. These findings are promising for fine adjustment of the phase transition temperature and low temperature coefficient of permittivity.
RESUMO
Thin films of ≈50 nm thickness with Ba/Ti-ratios ranging from 0.8 to 1.06 were prepared by depositing alternating layers of Ba(OH)2 and TiO2. Annealing at 750 °C promoted the solid-solid transformation into polycrystalline BaTiO3 films containing a mixture of the perovskite and the hexagonal polymorphs with average crystallite sizes smaller than 14 nm and without impurity phases. This, together with an increase of the cubic lattice parameters for Ba-rich films, suggests an extended metastable solubility range for the perovskite-phase in these nanocrystalline thin films on both sides of the stoichiometric composition. Mapping of the cation distribution utilizing energy-filtered transmission electron microscopy corroborates defect accommodation within the BaTiO3 grains. While the cation off-stoichiometry in thermodynamic equilibrium is negligible for BaTiO3, the metastable extended solubility range in the thin films can be directly correlated to the low annealing temperature and nanocrystalline nature. The leakage current behavior can be explained by the formation of Schottky defects for nonstoichiometric films, and the cation ratio has a distinct impact on the dielectric properties: while excess-BaO has a marginal detrimental effect on the permittivity, the dielectric constant declines rapidly by more than 50% towards the Ti-rich side. The present findings highlight the importance of compositional control for the synthesis of nanocrystalline BaTiO3 thin films, in particular for low annealing and/or deposition temperatures. Our synthesis approach using alternating layers of Ba(OH)2 and TiO2 provides a route to precisely control the cation stoichiometry.