High-Performance Anion Exchange Membrane Water Electrolyzers Enabled by Highly Gas Permeable and Dimensionally Stable Anion Exchange Ionomers.

Designing suitable anion exchange ionomers is critical to improving the performance and in situ durability of anion exchange membrane water electrolyzers (AEMWEs) as one of the promising devices for producing green hydrogen. Herein, highly gas-permeable and dimensionally stable anion exchange ionomers (QC6xBA and QC6xPA) are developed, in which bulky cyclohexyl (C6) groups are introduced into the polymer backbones. QC650BA-2.1 containing 50 mol% C6 composition shows 16.6 times higher H2 permeability and 22.3 times higher O2 permeability than that of QC60BA-2.1 without C6 groups. Through-plane swelling of QC650BA-2.1 decreases to 12.5% from 31.1% (QC60BA-2.1) while OH- conductivity slightly decreases (64.9 and 56.2 mS cm-1 for QC60BA-2.1 and QC650BA-2.1, respectively, at 30 °C). The water electrolysis cell using the highly gas permeable QC650BA-2.1 ionomer and Ni0.8Co0.2O in the anode catalyst layer achieves two times higher performance (2.0 A cm-2 at 1.69 V, IR-included) than those of the previous cell using in-house ionomer (QPAF-4-2.0) (1.0 A cm-2 at 1.69 V, IR-included). During 1000 h operation at 1.0 A cm-2, the QC650BA-2.1 cell exhibits nearly constant cell voltage with a decay rate of 1.1 µV h-1 after the initial increase of the cell voltage, proving the effectiveness of the highly gas permeable and dimensionally stable ionomer in AEMWEs.

Radiation-Grafted Anion-Exchange Membrane for Fuel Cell and Electrolyzer Applications: A Mini Review.

This review discusses the roles of anion exchange membrane (AEM) as a solid-state electrolyte in fuel cell and electrolyzer applications. It highlights the advancement of existing fabrication methods and emphasizes the importance of radiation grafting methods in improving the properties of AEM. The development of AEM has been focused on the improvement of its physicochemical properties, including ionic conductivity, ion exchange capacity, water uptake, swelling ratio, etc., and its thermo-mechano-chemical stability in high-pH and high-temperature conditions. Generally, the AEM radiation grafting processes are considered green synthesis because they are usually performed at room temperature and practically eliminated the use of catalysts and toxic solvents, yet the final products are homogeneous and high quality. The radiation grafting technique is capable of modifying the hydrophilic and hydrophobic domains to control the ionic properties of membrane as well as its water uptake and swelling ratio without scarifying its mechanical properties. Researchers also showed that the chemical stability of AEMs can be improved by grafting spacers onto base polymers. The effects of irradiation dose and dose rate on the performance of AEM were discussed. The long-term stability of membrane in alkaline solutions remains the main challenge to commercial use.