In situ siloxane passivation of colloidal lead halide perovskite via hot injection for light-emitting diodes.
Opt Lett
; 47(3): 593-596, 2022 Feb 01.
Article
em En
| MEDLINE
| ID: mdl-35103684
ABSTRACT
All-inorganic cesium lead halide perovskite (CsPbX3; X = Cl, Br) nanocrystals (NCs) are synthesized via a modified hot injection method using 3-mercaptopropyltrimethoxysilane (MPTMS), together with oleic acid and oleylamine, for in situ passivation of the surface defects. The surface chemistry, revealed by Fourier transform infrared spectroscopy (FTIR) and x-ray photoelectron spectroscopy (XPS) techniques, shows an absence of Si-O-Si network and C-O groups on these in situ passivated CsPbX3 NCs, denoted as InMP-CsPbX3, which is in strong contrast to the counterpart NCs obtained via a postsynthesis exchange strategy. The x-ray diffraction (XRD) pattern indicates a lattice structure significantly strained from the cubic structure. The synthesis of these InMP-CsPbX3 NCs is highly reproducible, and the colloids are stable in nonpolar solvents. The emission wavelength of CsPb(Cl/Br)3 mixed halide perovskite NCs is tuned from 405â
nm to 508â
nm by reducing the nominal Cl/Br ratio, while the photoluminescence quantum yield (PLQY) is greatly enhanced over the whole spectral range. More importantly, the InMP-treatment is among the few strategies that are promising for electroluminescence in light-emitting diodes.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Opt Lett
Ano de publicação:
2022
Tipo de documento:
Article