Effects of silica surface modification with silane and poly(ethylene glycol) on flexural strength, protein-repellent, and antibacterial properties of acrylic dental nanocomposites.

OBJECTIVE: The main aim of the current work was to develop dental acrylic-based composites with protein-repellent and antibacterial properties by using surface-modified silica nanoparticles. The effects of surface modification of silica nanoparticles in protein-repellent and antibacterial activity and mechanical properties of dental composites including flexural strength, flexural modulus, and hardness were discussed. METHODS: The surface of silica nanoparticles was first chemically treated with 3-methacryloxypropyltrimethoxysilane (MPS) as a coupling agent and then with poly(ethylene glycol) (PEG) bonded to MPS. Dental acrylic-based composites were prepared with mass fractions of 10, 15, 20, 30, and 40 % of PEG-modified MPS-silica nanoparticles (PMS). The chemical surface modification of silica nanoparticles with MPS and PEG was confirmed by Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). RESULTS: The dental composite containing 20 wt% PMS nanoparticles could reduce the protein adsorption by 28 % as compared with a composite containing 20 wt% MPS-modified silica. The antibacterial test indicated that the PMS nanoparticles can significantly reduce the adhesion of Streptococcus mutans and the biofilm formation on the surface of dental composites. It was found that the flexural strength increased by increasing the PMS nanoparticles from 0 to 20 wt% and then decreased by the incorporation of higher percentages of these nanoparticles. Also, with increasing the weight percentage of PMS nanoparticles, the elastic and the flexural modulus and the hardness of resin nanocomposites were increased. SIGNIFICANCE: In the current work, for the first time, dental resin composites containing PEG were prepared with excellent protein-repellent and antibacterial properties.

Towards the development of self-healing and antibacterial dental nanocomposites via incorporation of novel acrylic microcapsules.

OBJECTIVE: The main aim of the current work was to develop the novel self-healing dental composites contained poly(methyl methacrylate) (PMMA) microcapsules. The effects of PMMA microcapsule content in self-healing performance and mechanical properties of dental composites including flexural strength, flexural modulus, and fracture toughness were discussed. The antibacterial activity and non-toxicity properties of optimum self-healing dental composites were also investigated. METHODS: Novel acrylic microcapsules were prepared using triethylene glycol dimethacrylate (TEGDMA) as healing agent and PMMA as microcapsule shell via solvent evaporation method. The silica nanoparticles with the mean size of 15-20 nm were treated by 3-methacryloxypropyltrimethoxysilane (MPS) to enhance their adhesion and dispersion within the acrylic matrix of composite. Acrylic microcapsules with mass fractions of 0%, 5%, 10%, and 15% were added into a mixture of acrylic resins and MPS-grafted SiO2 nanoparticles. The strength and elastic modulus of dental composites were measured by the flexural test. The single edge V-notched beam (SEVNB) method was applied to investigate fracture toughness (KIC) and healing efficiency. The results were then statistically analyzed using one-way analysis of variance (ANOVA) at the confidence level of 0.95. RESULTS: Acrylic microcapsules were synthesized with the mean size around 30 µm and the core content of about 15 wt%. The grafting percentage of MPS surface modifier onto SiO2 nanoparticles was measured 3.2%. The incorporation of PMMA microcapsules into the dental composites had no significant effect on flexural properties. The self-healing dental composites also indicated the high efficient healing performance in the range of 78-121%. The self-healing dental composites also exhibited impressive antibacterial activity against Streptococcus mutans (S. mutans). The MTT assay also revealed that the incorporation of acrylic microcapsules in dental composites has no cytotoxicity effects. SIGNIfiCANCE: In the current study, for the first time, the self-healing dental nanocomposites contained acrylic microcapsules were prepared with excellent healing performance and antibacterial properties.

Recent advances in chemical surface modification of metal oxide nanoparticles with silane coupling agents: A review.

Nowadays, metal oxide nanoparticles (NPs) have been applied in various fields of nanotechnology including catalysis of chemical reactions, drug delivery, water treatment, textile industries, polymer composites, adhesives, and coatings. The greatest challenge in relation to metal oxide NPs is high tendency to aggregation. Chemical surface modification of metal oxide NPs has gained widely interest to control of dispersion and aggregation of NPs. Silane modifiers are one of the most important bifunctional modifiers that are frequently used for surface treatment of metal oxide NPs. In this review paper, we first focus on the synthesis, surface thermodynamic properties, surface modification techniques, and kinetic of silanization reaction of metal oxide NPs. Then, the recent development in using silane modifiers for treatment of metal oxide NPs in various applications were investigated. It was found that the unmodified NPs have high surface energy and are thermodynamically unstable. The thermodynamic properties of NPs including Gms, Hms, and Smsincrease with decreasing the particle size. Aggregation phenomena is the simple way to reduce the excess surface energy of NPs that leads to an increase in particle size. Therefore, the chemical surface modification of NPs using silane modifiers can be used as an effective method for the prevention of NPs agglomeration and improvement of NPs stability.