Green synthesis of Eucalyptus globulus zinc nanoparticles and its use in antimicrobial insect repellent paint formulation in bulk industrial production.

Mitigating climate change can be achieved by opting for sustainable, plant-based materials instead of relying on hazardous chemicals that come with various side effects. Various natural plant extracts find widespread application in synthesizing insect-repellent coatings, particularly in industries such as paint manufacturing. The increasing demand for these coatings has led us to find out the effects of different plant extracts for the efficient preparation of paints with more advanced impacts and low cost. For this purpose, zinc nanoparticles of Eucalyptus globulus L. and its extracts were used in this study due to their remarkable biocidal and antimicrobial activities. The extract was prepared by the process of oven-drying and heating followed by their filtration. Then, they were subjected to different phytochemical tests that were performed in which plant material did not contain flavonoids and glycol. The comparison of the size of nanoparticles was visible during the weighing which was found to be 4.451 mg. Advanced characterization techniques like FTIR, UV visible spectroscopy, and particle size analysis were adopted for the analysis of nanoparticles of plant extract. The FTIR analysis of the plant material was reported to lie in the range of 1000-1800 cm-1. On the other hand, the results of UV visible spectroscopy of nanoparticles of plant extract showed absorption peaks around 300 nm. The produced material was integrated into paint formulations to impart insect-repellent and antibacterial characteristics. Painted panels exhibited notable antibacterial efficacy, presenting an inhibition zone of 0.7 cm for Escherichia coli and 0.3 cm for Staphylococcus aureus when utilizing biocide. Plant nanoparticles yielded inhibition zones of 1 and 1.2, while aqueous extract resulted in zones of 0.2 and 0.5, respectively. A thorough evaluation of the paint's color attributes, including ΔL, Δa, Δb, and ΔE, indicated noteworthy differences. The CMC ΔE values from the trials exceeded 1, indicating a substantial change in shade. The batches of paints containing E. globulus extracts and nanoparticles were found to be lighter in color specifically green and yellow colors. Their antimicrobial and insect repellant activity was tested using the mosquitos of Aedes aegypti with an age of 4-5 weeks, revealing that formulations with plant extracts exhibited a 61 % effective period, greater than the 7 % observed in non-biocidal formulations. The paint responded best towards these mosquitoes in terms of repellency and the ultimate target of this study was achieved.

Synthesis of Electrical Conductive Metal-Organic Frameworks for Electrochemical Applications.

Electrical conductivity is very important property of nanomaterials for using wide range of applications especially energy applications. Metal-organic frameworks (MOFs) are notorious for their low electrical conductivity and less considered for usage in pristine forms. However, the advantages of high surface area, porosity and confined catalytic active sites motivated researchers to improve the conductivity of MOFs. Therefore, 2D electrical conductive MOFs (ECMOF) have been widely synthesized by developing the effective synthetic strategies. In this article, we have summarized the recent trends in developing the 2D ECMOFs, following the summary of potential applications in the various fields with future perspectives.