RESUMEN
In the present work, the dielectric properties of recycled liquid crystals (LCs) (non-purified, purified, and doped with diamond nanoparticles at 0.05, 0.1, and 0.2 wt%) were investigated. The studied LC mixtures were obtained from industrial recycling of end-of-life LC displays presenting mainly nematic phases. Dielectric measurements were carried out at room temperature on a frequency range from 0.1 to 106 Hz using an impedance analyzer. The amplitude of the oscillating voltage was fixed at 1 V using cells with homogeneous and homeotropic alignments. Results show that the dielectric anisotropy of all purified samples presents positive values and decreases after the addition of diamond nanoparticles to the LC mixtures. DC conductivity values were obtained by applying the universal law of dielectric response proposed by Jonscher. In addition, conductivity of the doped LC mixtures is lower than that of the undoped and non-purified LC.
RESUMEN
The mechanism of charge motion in conductive and photosensitive mesogenic block copolymers containing polyethylene oxide (PEO) segments is investigated over a wide frequency and temperature range with the broadband dielectric spectroscopy technique. It is found that the ultraviolet (UV) irradiation, the UV intensity, and the anchoring conditions of mesogenic unit in the cells produce changes in conductivity properties and in the molecular arrangement. The anisotropic nature of the conductivity is established.
RESUMEN
Several liquid crystalline imprinted materials have been synthesized from polysiloxanes or polyacrylates bearing mesogenic side-chains and low contents of cross-linkers. They were imprinted by various achiral or chiral templates, then tested for molecular recognition or assessed as specific catalysts. All mesogenic imprinted networks exhibit a much higher affinity towards the template than non-imprinted networks. On the other hand, the molecular trapping capacity was shown to be much greater than that of most of the previously studied non-mesomorphous systems. Moreover, it was shown that mesomorphic order provides significant enhancement to the bonding between the template and the liquid crystalline network and reinforces the shape memory of the imprinted cavities. Some of these materials were used to catalyze the isomerization of benzisoxazole. They exhibited an acceleration effect close to 100 between imprinted sites and non-imprinted ones. Lastly, cholesteric networks, that were imprinted by a chiral template, showed good properties for the enantiomer separation leading to an enantiomeric excess of 35% and a capacity of around 1 mmol g(-1).
RESUMEN
The reflection properties of cholesteric films with thermally induced pitch gradients are theoretically and experimentally studied. It is shown that the optical behavior of such films corresponds to the averaged contribution of a number of stochastic pitch variation profiles, due to the transversal and longitudinal nonuniformities that develop in the helical structure of such samples. Depending on the annealing time, both narrow-band and broadband behavior can be selectively achieved. The influence of the pitch profile gradient on the broadband reflection performance of cholesteric samples is theoretically analyzed, and a multi-slab structure for achieving optimum efficiency is proposed.
RESUMEN
Liquid crystalline thin films elastomers that are able to bind pesticides have been developed. The synthesis involves grafting mesogen and crosslinkable groups on a polysiloxane chain in the presence of a template molecule. The molecular imprinted material is obtained after thin film deposition, UV crosslinking and washing. Experiments of readsorption of pesticide are presented. Development of a multisensor platform based on thermal and capacitive sensors is described and tests of deposition of the polymer film are presented.