Effect of preheating on cytotoxicity and physicochemical properties of light-cured calcium-based cements.

The aim of this study was to evaluate the degree of conversion, cytotoxicity, solubility and pH of photopolymerizable calciumbased cements submitted to preheating. The degree of conversion was analyzed by Fourier transform infrared, cytotoxicity by the MTT test and solubility through loss of mass. The data were subjected to statistical tests (ANOVA / Tukey's, p<0.05). The photopolymerizable materials showed a low degree of conversion, regardless of preheating. All materials caused a reduction in cell viability at 24 hours and 7 days, with the Dycal (control) being more cytotoxic. Heat had a positive effect on Biocal at 7 days. Dycal is the most soluble material. Heat had no effect on the solubility or pH of the polymerizable materials. It is concluded that photopolymerizable calcium-based cements have a low degree of conversion and are soluble, which results in mild to moderate cytotoxicity.

O objetivo do presente estudo foi avaliar o grau de conversão, citotoxicidade, solubilidade e pH de cimentos à base de cálcio fotopolimerizáveis submetidos a pré-aquecimento. O grau de conversão foi analisado por espectroscopia no infravermelho com transformada de Fourier, a citotoxicidade pelo teste de MTT e a solubilidade através da perda de massa. Os dados foram submetidos a testes estatísticos (ANOVA/Tukey, p<0,05). Os materiais fotopolimerizáveis apresentaram baixo grau de conversão, independente do pré-aquecimento. Todos os materiais causaram redução da viabilidade celular nas análises de 24 horas e 7 dias, sendo que o Dycal (controle) apresentouse mais citotóxico e o calor apresentou efeito positivo sobre o Biocal na análise de 7 dias. O Dycal é o material mais solúvel e o calor não causou efeito na solubilidade e pH dos materiais polimerizáveis. Assim, conclui-se que os cimentos à base de cálcio fotopolimerizáveis apresentam baixo grau de conversão e são solúveis, que resulta em citotoxicidade suave e moderada.

Effect of preheating on cytotoxicity and physicochemical properties of light-cured calcium-based cements / Efeito do pré-aquecimento na citotoxicidade e propriedades físico-químicas de cimentos à base de cálcio fotopolimerizáveis

ABSTRACT The aim of this study was to evaluate the degree of conversion, cytotoxicity, solubility and pH of photopolymerizable calciumbased cements submitted to preheating. The degree of conversion was analyzed by Fourier transform infrared, cytotoxicity by the MTT test and solubility through loss of mass. The data were subjected to statistical tests (ANOVA / Tukey's, p<0.05). The photopolymerizable materials showed a low degree of conversion, regardless of preheating. All materials caused a reduction in cell viability at 24 hours and 7 days, with the Dycal (control) being more cytotoxic. Heat had a positive effect on Biocal at 7 days. Dycal is the most soluble material. Heat had no effect on the solubility or pH of the polymerizable materials. It is concluded that photopolymerizable calcium-based cements have a low degree of conversion and are soluble, which results in mild to moderate cytotoxicity.

RESUMO O objetivo do presente estudo foi avaliar o grau de conversão, citotoxicidade, solubilidade e pH de cimentos à base de cálcio fotopolimerizáveis submetidos a pré-aquecimento. O grau de conversão foi analisado por espectroscopia no infravermelho com transformada de Fourier, a citotoxicidade pelo teste de MTT e a solubilidade através da perda de massa. Os dados foram submetidos a testes estatísticos (ANOVA/Tukey, p<0,05). Os materiais fotopolimerizáveis apresentaram baixo grau de conversão, independente do pré-aquecimento. Todos os materiais causaram redução da viabilidade celular nas análises de 24 horas e 7 dias, sendo que o Dycal (controle) apresentouse mais citotóxico e o calor apresentou efeito positivo sobre o Biocal na análise de 7 dias. O Dycal é o material mais solúvel e o calor não causou efeito na solubilidade e pH dos materiais polimerizáveis. Assim, conclui-se que os cimentos à base de cálcio fotopolimerizáveis apresentam baixo grau de conversão e são solúveis, que resulta em citotoxicidade suave e moderada.

Effect of At-home and In-office Bleaching on Marginal Microleakage in Composite Resin Restorations using Two Adhesive Systems.

AIM: The aim of this study is to assess marginal microleakage of cervical cavities restored with composite resins and two different adhesive techniques subjected to at-home and in-office bleaching. MATERIALS AND METHODS: In this randomized, blind laboratory experiment, 60 bovine teeth recently extracted were collected and divided into six groups (n = 10 each group). The teeth received cervical cavity preparations (2 mm × 3 mm × 1 mm) with enamel margins. Two different adhesive systems were used (Single Bond 2 and Clearfil SE Bond), in addition to composite resin (Z250). Restored teeth received two different bleaching gels (Opalescence PF and Opalescence Boost). Teeth were thermo-cycled and analyzed under confocal laser scanning microscopy. RESULTS: No significant differences were observed (p > 0.05) in microleakage scores between the two groups not subjected to bleaching nor between the four groups that received bleaching treatment (p > 0.05), regardless of the gel and adhesive system employed. However, when comparing nonbleached with bleached teeth, those not subjected to bleaching showed statistically lower marginal microleakage scores (p < 0.05). Data were statistically analyzed using the Kruskal-Wallis test followed by Student-Newman-Keuls post hoc test, with significance set at 5%. CONCLUSION: Marginal microleakage in composite resin restorations is influenced by the action of bleaching agents used both at-home and in-office, regardless of the adhesive system employed (total-etch or self-etch). CLINICAL SIGNIFICANCE: Both at-home and in-office bleaching agents have an influence on the adhesive interface of resin restorations, producing changes and inducing marginal leakage.