RESUMEN
The increasing demand for large-scale energy storage propels the development of lithium-ion batteries with high energy and high power density. Low tortuosity electrodes with aligned straight channels have proved to be effective in building such batteries. However, manufacturing such low tortuosity electrodes in large scale remains extremely challenging. In contrast, high-performance electrodes with customized gradients of materials and porosity are possible to be made by industrial roll-to-roll coating process. Yet, the desired design of gradients combining materials and porosity is unclear for high-performance gradient electrodes. Here, triple gradient LiFePO4 electrodes (TGE) are fabricated featuring distribution modulation of active material, conductive agent, and porosity by combining suction filtration with the phase inversion method. The effects and mechanism of active material, conductive agent, and porosity distribution on electrode performance are analyzed by experiments. It is found that the electrode with a gradual increase of active material content from current collector to separator coupled with the distribution of conductive agent and porosity in the opposite direction, demonstrates the best rate capability, the fastest electrochemical reaction kinetics, and the highest utilization of active material. This work provides valuable insights into the design of gradient electrodes with high performance and high potential in application.
RESUMEN
Lithium sulfur batteries (LSBs) are regarded as one of the most promising energy storage devices due to the high theoretical capacity and energy density. However, the shuttling lithium polysulfides (LiPSs) from the cathode and the growing lithium dendrites on the anode limit the practical application of LSBs. To overcome these challenges, a novel three-dimensional (3D) honeycombed architecture consisting of a local interconnected Co3O4 successfully assembled into a scalable modified layer through mutual support, which is coated on commercial separators for high-performance LSBs. On the basis of the 3D honeycombed architecture, the modified separators not only suppress effectively the "shuttle effects" but also allow for fast lithium-ions transportation. Moreover, the theoretical calculations results exhibit that the collaboration of the exposed (111) and (220) crystal planes of Co3O4 is able to effectively anchor LiPSs. As expected, LSBs with 3D honeycombed Co3O4 modified separators present a reversible specific capacity with 1007 mAh g-1 over 100 cycles at 0.1 C. More importantly, a high reversible capacity of 808 mAh g-1 over 300 cycles even at 1 C is also acquired with the modified separators. Therefore, this proposed strategy of 3D honeycombed architecture Co3O4 modified separators will give a new route to rationally devise durable and efficient LSBs.