A novel electrochemical method for preparing flower-like nanostructured silver particles using polyvinyl alcohol (PVA) modified carbon cloth as a cathode is reported. The method does not involve the use of any morphological control agents in aqueous solution. The morphology of the silver nanoparticles obtained was studied using scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The effects of the operating conditions on the deposited silver nanoparticles were investigated. It was found that PVA concentration for carbon cloth modification had a significant effect on the deposited silver morphology. With 1% PVA modification, current density of 10 µA cm-2 and silver nitrate concentration of 1 mM, a flower-like nanostructured silver with petal thickness of 100 nm can be prepared. With the reaction proceeding, silver nanocrystals nucleated on the cathode in a few seconds, then the nuclei grew and the rudimental flower-like silver started to form in 1 min. The perfect flower-like nanostructure of silver was formed in 20 min. However overlong reaction time led to micrometer sized blocks. The specific silver nanostructure growth might be attributed to the silver ion concentration gradient caused by reaction and diffusion rate and the effects of PVA.
RESUMEN
A novel bioelectrochemical system (BES) was designed to recover copper and nickel from wastewater sequentially. The BES has two chambers separated by a bipolar membrane and two cathodes. Firstly, the copper ions were reduced on a graphite cathode with electricity output, and then with an additional bias-potential applied, the nickel ions were recovered sequentially on a copper sheet with electricity input. In this design, nickel and copper can be recovered and separated sequentially on two cathodes. By adjusting the molar ratio of copper and nickel ions to 2.99:1 in wastewater, 1.40 mmol Cu²âº could be recovered with 143.78 J electricity outputs, while 50.68 J electricity was input for 0.32 mmol nickel reduction. The total energy output of copper recovery was far more than the electricity input of nickel reduction. The present technology provides a potential method for heavy metal ion separation and recovery.