RESUMEN
A successful attempt was made to fabricate a thin foil of natural Mo target on a thick Au backing with Indium in between to improve adhesion between the foils. Rolling at elevated temperature was considered to fabricate Mo foil while gold foil was fabricated employing conventional rolling technique. The heating of Mo foil under natural environment lead to the oxidation or carbonization on foil surface which was confirmed through Energy Dispersive X-ray Spectroscopy (EDS) measurements. Indium of thickness â¼86µg/cm2 was evaporated on Mo foil to improve adhesion between Mo and Au foils. The characterization of fabricated thin Mo foil was done using the Energy Dispersive X-ray Spectroscopy (EDS) and the Scanning Electron microscope (SEM) techniques. Thickness measurement of the target (Mo-Au) was done using Energy Dispersive X-ray Fluorescence (EDXRF) technique, in the measurements the thickness of the Mo foil and of gold backing are found out to be 1.3 mg/cm2 and 9 mg/cm2 respectively.