Effect of artificial aging on optical properties of ultra-translucent zirconia ceramics of different brands.

OBJECTIVES: This work aimed to evaluate the effect of artificial aging on the translucency and color difference (ΔE) of ultra-translucent zirconia and provide a reference for clinical application. METHODS: The discs of ultra-translucent zirconia from six brands (Wieland, 3M ESPE, Amann Girrbach, Kuraray Noritake, Upcera, and Besmile) were cut and sintered according to each manufacturer's product instructions; the experimental groups were named ZNT, LVP, AG, KAT, UPC, and BSM, respectively. IPS e.max Press was used as the control group (PLT). The specimens (n=6) were prepared with a diameter of 14 mm and a thickness of 1 mm. The specimens were subjected to artificial aging treatment according to the following conditions: in an autoclave at 134 ℃ at 0.2 MPa for 4, 8, and 12 h. According to the CIE1976Lab system, the CIE L*, a*, and b* values of the specimens before and after aging were measured by a co-lorimeter. The translucency parameter (TP) and ΔE were calculated. RESULTS: The mean TP values of each group before aging inorder were PLT>KAT>AG>ZNT>BSM>UPC>LVP. We found no significant difference in translucency in all experimental groups after aging for 4 and 8 h compared with those before aging. After 12 h of aging, the TP values of the KAT and ZNT groups were not significantly different from those before aging, but the TP values of the AG, BSM, LVP, and UPC groups were significantly lower than those before aging (P<0.05). The TP value of the control group was significantly higher than that of the other experimental groups at different stages (P<0.05). ΔE=3.3 was considered the visible color difference, and ΔE was less than 3.3 in all groups after 4 h of aging. After aging for 8 h, ΔE of the UPC group was slightly higher than 3.3. ΔE of the BSM and UPC groups was greater than 3.3 after 12 h of aging. CONCLUSIONS: The TP and ΔE of different brands of ultra-translucent zirconia may change after various aging times. The translucency of some zirconia showed a decreasing trend and the color difference showed an increasing trend with the aging time.

Research Status of High-Purity Metals Prepared by Zone Refining.

The zone refining method is a physical method for effectively purifying metals. Increasing yield and reducing impurity content have always been the focus of its research. This article systematically summarizes the relevant research on the production of high-purity metals by zone refining, including mechanisms, parameter optimization, zone refining types, analysis methods, limitations, and future development directions, and it provides relevant theoretical foundations for the production of high-purity metals as well.