RESUMEN
Abstract Background/purpose: Self-adhesive resins (SARs) do not require additional restorative adhesives and provide adequate adhesion to mineralized dental structures by shortening the bonding time in clinics where moisture control and isolation are difficult. The aim of this study was to evaluate the mechanical and biological properties of SARs containing mesoporous bioactive glass nanoparticles (MBNs) and 2-methacryloyloxyethyl phosphorylcholine (MPC) and to determine their antibacterial and remineralization effects. Materials and methods: MBNs and MPC were added to SARs to improve their physical properties and remineralization ability. The experimental resins assessed in this study were SARs mixed with 3%MPC, 5%MPC, 1%MBN+3%MPC, or 3%MBN+3%MPC. The shear bond strength, microhardness, adhesive remnant index, ion dissolution, degree of conversion, and antibacterial properties of the SARs were evaluated. To assess the remineralization properties, micro-computed tomography analysis was performed after pH cycling. Results: Increasing the MBN content in SAR resulted in higher microhardness compared to the control SAR. The shear bond strength decreased in the SAR+5%MPC group and increased in the SAR+1%MBN+3%MPC and SAR+3%MBN+5%MPC groups. Conclusion: Our findings suggest that SARs containing MBNs and MPC have antibacterial and remineralization effects on the enamel.
RESUMEN
Self-adhesive resins (SARs) contain adhesives, which simplify the procedures of resin application, and primers, which provide sufficient bonding ability. In this study, mesoporous bioactive glass nanoparticles (MBN) were added to a SAR to easily improve the physical properties and remineralization ability. The experimental resins comprised 1%, 3%, and 5% MBN mixed in Ortho Connect Flow (GC Corp, Tokyo, Japan). As the MBN content in the SAR increased, the microhardness increased, and a statistically significant difference was observed between the cases of 1% and 5% MBN addition. Shear bond strength increased for 1% and 3% MBN samples and decreased for 5% MBN. The addition of MBN indicated a statistically significant antibacterial effect on both gram-negative and gram-positive bacteria. The anti-demineralization experiment showed that the remineralization length increased with the MBN content of the sample. Through the above results, we found that SAR containing MBN has antibacterial and remineralization effects. Thus, by adding MBN to the SAR, we investigated the possibility of orthodontic resin development, wherein the strength is enhanced and the drawbacks of the conventional SAR addressed.
RESUMEN
This study aimed to investigate whether dentin remineralization and micro-tensile bond strength increase when using calcium phosphate ion clusters (CPICs) or metastable Ca-P. After being etched, each dentin specimen was designated into four groups and treated with the appropriate solution for 1 min: 100% ethanol, 2 and 1 mg/mL of CPICs, and metastable Ca-P. The specimens were then prepared for scanning electron microscopy (SEM), transmission electron microscropy (TEM) imaging, a matrix metalloproteinases inhibition assay, and the micro-tensile bond strength test. To compare among the groups, one-way analysis of variance was performed. In the SEM imaging, with a rising concentration of CPICs, the degree of remineralization of dentin increased significantly. The metastable Ca-P treated specimens showed a similar level of remineralization as the 1 mg/mL CPICs treated specimens. The TEM imaging also revealed that dentin remineralization occurs in a CPICs concentration-dependent manner between the demineralized dentin and the resin layer. Furthermore, the results of micro-tensile bond strength showed the same trend as the results confirmed by SEM and TEM. We demonstrated that a 1 min pretreatment of CPICs or metastable Ca-P in etched dentin collagen fibril can achieve biomimetic remineralization and increase micro-tensile bond strength.