RESUMEN
In this work, a vapor cooling condensation system was utilized to deposit various amounts of p-type gold-black nanoparticles (NPs) onto the surface of n-type gallium oxide (Ga2O3) nanorods forming p-n heterojunction-structured sensing membranes of nitrogen dioxide (NO2) gas sensors. The role and the sensing mechanism of the various gold-black NP-decorated Ga2O3 nanorods in NO2 gas sensors were investigated. The coverage and atomic percentage of the sensing membranes were observed using high-resolution transmission electron microscopy (HRTEM) measurements and energy-dispersive spectroscopy (EDS), respectively. For the NO2 gas sensor using the sensing membrane of 60 s-deposited gold-black NP-decorated Ga2O3 nanorods under a NO2 concentration of 10 ppm, the highest responsivity of 5221.1% was obtained. This result was attributed to the spillover effect and the formation of the p-n heterojunction, which increased more ionized-oxygen adsorption sites and promoted the reaction between NO2 gas and Ga2O3 nanorods. Furthermore, the NO2 gas sensor could detect the low NO2 concentration of 100 ppb and achieved a responsivity of 56.9%. The resulting NO2 gas sensor also exhibited excellent selectivity for detecting NO2 gas, with higher responsivity at a NO2 concentration of 10 ppm compared with that of the C2H5OH and NH3 concentrations of 100 ppm.
Asunto(s)
Nanotubos , Dióxido de Nitrógeno , Adsorción , Gases , OroRESUMEN
In this work, Ga2O3 nanorods were converted from GaOOH nanorods grown using the hydrothermal synthesis method as the sensing membranes of NO2 gas sensors. Since a sensing membrane with a high surface-to-volume ratio is a very important issue for gas sensors, the thickness of the seed layer and the concentrations of the hydrothermal precursor gallium nitrate nonahydrate (Ga(NO3)3·9H2O) and hexamethylenetetramine (HMT) were optimized to achieve a high surface-to-volume ratio in the GaOOH nanorods. The results showed that the largest surface-to-volume ratio of the GaOOH nanorods could be obtained using the 50-nm-thick SnO2 seed layer and the Ga(NO3)3·9H2O/HMT concentration of 12 mM/10 mM. In addition, the GaOOH nanorods were converted to Ga2O3 nanorods by thermal annealing in a pure N2 ambient atmosphere for 2 h at various temperatures of 300 °C, 400 °C, and 500 °C, respectively. Compared with the Ga2O3 nanorod sensing membranes annealed at 300 °C and 500 °C, the NO2 gas sensors using the 400 °C-annealed Ga2O3 nanorod sensing membrane exhibited optimal responsivity of 1184.6%, a response time of 63.6 s, and a recovery time of 135.7 s at a NO2 concentration of 10 ppm. The low NO2 concentration of 100 ppb could be detected by the Ga2O3 nanorod-structured NO2 gas sensors and the achieved responsivity was 34.2%.
RESUMEN
Photodetectors based on reduced graphene oxide (rGO) have attracted much attention owing to their simple and low-cost fabrication process. However, the aggregation and defects of rGO flakes still limit the performance of rGO photodetectors. Controlling the composition of rGO has become a vital factor for its prospective applications. For example, the interconnection between rGO and polymers for modified morphologies of rGO films leads to an enhanced performance of devices. In this work, a practical approach to engineer surface uniformity and enhance the performance of a photodetector by modifying the rGO film with hydrophilic polymers poly(vinyl alcohol) (PVA) is reported. Compared with the rGO photodetector, the on/off ratio for the PVA/rGO photodetector shows 3.5 times improvement, and the detectivity shows 53% enhancement even when the photodetector is operated at a low bias of 0.3 V. This study provides an effective route to realize PVA/rGO photodetectors with a low-power operation which shows promising opportunities for the future development of green systems.
RESUMEN
In this work, Ga2O3 films were deposited on sapphire substrates using a plasma-enhanced atomic layer deposition system with trimethylgallium precursor and oxygen (O2) plasma. To improve the quality of Ga2O3 films, they were annealed in an O2 ambient furnace system for 15 min at 700, 800, and 900 °C, respectively. The performance improvement was verified from the measurement results of X-ray diffraction, X-ray photoelectron spectroscopy, and photoluminescence spectroscopy. The optical bandgap energy of the Ga2O3 films decreased with an increase of annealing temperatures. Metal-semiconductor-metal ultraviolet C photodetectors (MSM UVC-PDs) with various Ga2O3 active layers were fabricated and studied in this work. The cut-off wavelength of the MSM UVC-PDs with the Ga2O3 active layers annealed at 800 °C was 250 nm. Compared with the performance of the MSM UVC-PDs with the as-grown Ga2O3 active layers, the MSM UVC-PDs with the 800 °C-annealed Ga2O3 active layers under a bias voltage of 5 V exhibited better performances including photoresponsivity of 22.19 A/W, UV/visible rejection ratio of 5.98 × 104, and detectivity of 8.74 × 1012 cmHz1/2W-1.
RESUMEN
In the study, the yttrium (Y)-doped vanadium oxide (VOx:Y) films used as the sensitive layers of microbolometers were deposited using a radio frequency magnetron co-sputtering system. The temperature coefficient of resistance (TCR) of the VOx:Y films was enhanced from -1.88%/°C to -2.85%/°C in comparison with that of the VOx films. To further improve the performance of microbolometers, the nanomesh antireflection layer was placed on the top surface of the microbolometers to reduce the infrared reflection. The responsivity, thermal time constant, thermal conductivity, absorptance, and detectivity of the VOx:Y microbolometers with nanomesh antireflection layer were 931.89 ± 48 kV/W, 4.48 ms, 6.19×10-8 W/K, 74.41% and 2.20×108 cmHz0.5W-1, respectively.