RESUMEN
Metal halide perovskites are an attractive class of semiconductors, but it has proven difficult to control their electronic doping by conventional strategies due to screening and compensation by mobile ions or ionic defects. Noble-metal interstitials represent an under-studied class of extrinsic defects that plausibly influence many perovskite-based devices. In this work, doping of metal halide perovskites is studied by electrochemically formed Au+ interstitial ions, combining experimental data on devices with a computational analysis of Au+ interstitial defects based on density functional theory (DFT). Analysis suggests that Au+ cations can be easily formed and migrate through the perovskite bulk via the same sites as iodine interstitials (Ii + ). However, whereas Ii + compensates n-type doping by electron capture, the noble-metal interstitials act as quasi-stable n-dopants. Experimentally, voltage-dependent, dynamic doping by current density-time (J-t), electrochemical impedance, and photoluminescence measurements are characterized. These results provide deeper insight into the potential beneficial and detrimental impacts of metal electrode reactions on long-term performance of perovskite photovoltaic and light-emitting diodes, as well as offer an alternative doping explanation for the valence switching mechanism of halide-perovskite-based neuromorphic and memristive devices.
RESUMEN
Understanding and controlling the energy level alignment at interfaces with metal halide perovskites (MHPs) is essential for realizing the full potential of these materials for use in optoelectronic devices. To date, however, the basic electronic properties of MHPs are still under debate. Particularly, reported Fermi level positions in the energy gap vary from indicating strong n- to strong p-type character for nominally identical materials, raising serious questions about intrinsic and extrinsic defects as dopants. âIn this work, photoemission experiments demonstrate that thin films of the prototypical methylammonium lead triiodide (MAPbI3 ) behave like an intrinsic semiconductor in the absence of oxygen. Oxygen is then shown to be able to reversibly diffuse into and out of the MAPbI3 bulk, requiring rather long saturation timescales of ≈1 h (in: ambient air) and over 10 h (out: ultrahigh vacuum), for few 100 nm thick films. Oxygen in the bulk leads to pronounced p-doping, positioning the Fermi level universally ≈0.55 eV above the valence band maximum. The key doping mechanism is suggested to be molecular oxygen substitution of iodine vacancies, supported by density functional theory calculations. This insight rationalizes previous and future electronic property studies of MHPs and calls for meticulous oxygen exposure protocols.
RESUMEN
We consider the Br vacancy in CsPbBr3 as a prototype for the impact of structural dynamics on defect energetics in halide perovskites (HaPs). Using first-principles molecular dynamics based on density functional theory, we find that the static picture of defect energetics breaks down; the energy level associated with a Br vacancy is found to be intrinsically dynamic, oscillating by as much as 1 eV on the picosecond time scale at room temperature. These significant energy fluctuations are correlated with the distance between the neighboring Pb atoms across the vacancy and with the electrostatic potential at these Pb atomic sites. We expect this unusually strong coupling of structural dynamics and defect energetics to bear important implications for both experimental and theoretical analyses of defect characteristics in HaPs. It may also hold significant ramifications for carrier transport and defect tolerance in this class of photovoltaic materials.