RESUMEN
Laser cladding is one of the emerging additive manufacturing technologies and has been adopted in various industrial fields. In this study, the morphological characteristics of a single clad of Inconel 718 manufactured by coaxial laser cladding with high laser power from 4200 W to 5400 W, powder feeding rate from 25 g/min to 50 g/min, and cladding speed from 20 mm/s to 50 mm/s are studied. The cross-section of the melt pool is analyzed and classified by type into three types: shallow dilution, flat dilution, and fluctuating dilution. Nine parameters are designed to describe the morphological characteristics of the clad, and the corresponding linear regression models are developed to establish a quantitative relationship between the combined process parameters and morphological characteristics. The results indicate that the total area of the cross-section A, the clad area above the substrate Ac, the area of the molten substrate Am, the total height of the cross-section H, the height of the clad above the substrate hc, the penetration depth hm, the clad width W, the dilution ratio D, and the wetting angle θ are determined by complex coupling of energy input and mass accumulation, and they are proportional to PF0.4/V, P0.5F/V, P/F0.2/V0.4, P2F0.6/V, PF0.7/V, P2/F/V0.3, P/V0.8, P/FV0.2, and PF7/V0.8, respectively. The large linear regression coefficients and the analysis residuals indicate the high reliability of the statistical linear regression models. This work aims to provide a comprehensive understanding of the influence of the main processing parameters on the morphological characteristics of the clad, which is of great value in providing a reference and laying a basis for the practical application of laser cladding technology at a high deposition rate.
RESUMEN
The profile of the laser beam plays a significant role in determining the heat input on the deposition surface, further affecting the molten pool dynamics during laser-based directed energy deposition. The evolution of molten pool under two types of laser beam, super-Gaussian beam (SGB) and Gaussian beam (GB), was simulated using a three-dimensional numerical model. Two basic physical processes, the laser-powder interaction and the molten pool dynamics, were considered in the model. The deposition surface of the molten pool was calculated using the Arbitrary Lagrangian Eulerian moving mesh approach. Several dimensionless numbers were used to explain the underlying physical phenomena under different laser beams. Moreover, the solidification parameters were calculated using the thermal history at the solidification front. It is found that the peak temperature and liquid velocity in the molten pool under the SGB case were lower compared with those for the GB case. Dimensionless numbers analysis indicated that the fluid flow played a more pronounced role in heat transfer compared to conduction, especially in the GB case. The cooling rate was higher for the SGB case, indicating that the grain size could be finer compared with that for the GB case. Finally, the reliability of the numerical simulation was verified by comparing the computed and experimental clad geometry. The work provides a theoretical basis for understanding the thermal behavior and solidification characteristics under different laser input profile during directed energy deposition.
RESUMEN
Understanding heat and mass transfer and fluid flow in the molten pool is very helpful in the selection and optimization of processing parameters, and the surface-active element has an important effect on the heat and mass transfer in laser welding of dissimilar metals. A three-dimensional (3D) numerical model coupled with a sub-model of surface tension, which considers the influence of local temperature and the concentration of surface-active element sulfur at the gas/liquid surface, is used to analyze the thermal behavior, driving forces, fluid flow, and solute dilution during laser linear welding of 304SS and Ni. The relationship between surface tension, driving forces, and the temperature coefficient of surface tension with the spatial distribution of temperature and the surface-active element sulfur is quantitatively analyzed. The simulation results show that the molten pool is fully developed at 45 ms, and the collision of inward and outward convection, with the maximum velocity reaching 1.7 m/s, occurs at the isotherm with a temperature between 2200 K and 2500 K. The temperature-gradient term and concentration-gradient term of surface shear stress play different roles in different positions of the free surface. The local sulfur concentration changes the temperature sensitivity of the surface tension at different sides of the free surface and further determines the transition of convection. Complex fluid flow promotes solute dilution, and the distribution of solute becomes uniform from the front to the rear of the molten pool. The Ni element is transferred to 304SS mainly at the rear side. The work provides theoretical support for the control of joint quality by changing the content of surface-active elements in dissimilar welding.