Interface Structures on Mechanically Polished Surface of Spinel Ferrite and Its Effect on the Magnetic Domains.

Soft magnetic spinel ferrites are indispensable parts in devices such as transformers and inductors. Mechanical surface processing is a necessary step to realize certain shapes and surface roughness in producing the ferrite but also has a negative effect on the magnetic properties of the ferrite. In the past few years, a new surface layer was always believed to form during the mechanical surface processing, but the change of atomic structure on the surface and its effect on the magnetic structure remain unclear. Herein, an interface structure consisting of a rock-salt sublayer, distorted NiFe2O4 sublayer, and pristine NiFe2O4 was found to form on mechanically polished single-crystal NiFe2O4 ferrite. Such an interface structure is produced by phase transformation and lattice distortion induced by the mechanical processing. The magnetic domain observation and electrical property measurement also indicate that the magnetic and electrical anisotropy are both enhanced by the interface structure. This work provides deep insight into the surface structure evolution of spinel ferrite by mechanical processing.

Atomic-scale observation of calcium occupation in spinel cobalt ferrite towards the regulation of intrinsic magnetic properties.

Spinel ferrites have drawn intensive attention because of their adjustable magnetic properties by ion doping, among which calcium (Ca) is an essential dopant that is widely employed in massive production. However, its exact lattice occupation and relationship with intrinsic magnetic properties remain unclear. Here, we successfully prepared Ca-doped cobalt ferrite (CoFe2O4) nanoparticles by electrospinning. Ca2+ is observed to occupy both the tetrahedral Fe site and the octahedral Co site using spherical aberration correction transmission electron microscopy (TEM) and prefers to occupy the octahedral site at a high doping level. Such dual occupation behavior affects the tetrahedral and octahedral sublattices differently, resulting in nonmonotonic saturation magnetization variation, reduced magnetocrystalline anisotropy and negative magnetization in the zero field cooling (ZFC) process. By controlling the Ca doping amount, increased saturation magnetization and reduced coercivity can be obtained simultaneously. Our findings establish the relationship between the atomic-scale structural change and the macroscopic magnetic properties of spinel ferrites, promoting the development of new ferrite materials.