The ROS-generating photosensitizer-free NaYF4:Yb,Tm@SiO2upconverting nanoparticles for photodynamic therapy application.

In this work we adapt rare-earth-ion-doped NaYF4nanoparticles coated with a silicon oxide shell (NaYF4:20%Yb,0.2%Tm@SiO2) for biological and medical applications (for example, imaging of cancer cells and therapy at the nano level). The wide upconversion emission range under 980 nm excitation allows one to use the nanoparticles for cancer cell (4T1) photodynamic therapy (PDT) without a photosensitizer. The reactive oxygen species (ROS) are generated by Tm/Yb ion upconversion emission (blue and UV light). Thein vitroPDT was tested on 4T1 cells incubated with NaYF4:20%Yb,0.2%Tm@SiO2nanoparticles and irradiated with NIR light. After 24 h, cell viability decreased to below 10%, demonstrating very good treatment efficiency. High modification susceptibility of the SiO2shell allows for attachment of biological molecules (specific antibodies). In this work we attached the anti-human IgG antibody to silane-PEG-NHS-modified NaYF4:20%Yb,0.2%Tm@SiO2nanoparticles and a specifically marked membrane model by bio-conjugation. Thus, it was possible to perform a selective search (a high-quality optical method with a very low-level organic background) and eventually damage the targeted cancer cells. The study focuses on therapeutic properties of NaYF4:20%Yb,0.2%Tm@SiO2nanoparticles and demonstrates, upon biological functionalization, their potential for targeted therapy.

Mammalian cell defence mechanisms against the cytotoxicity of NaYF4:(Er,Yb,Gd) nanoparticles.

Water-soluble upconversion nanoparticles (UCNPs), based on polyvinylpyrrolidone (PVP)-coated NaYF4:Er3+,Yb3+,Gd3+, with various concentrations of Gd3+ ions and relatively high upconversion efficiencies, were synthesized. The internalization and cytotoxicity of the thus obtained UCNPs were evaluated in three cell lines (HeLa, HEK293 and astrocytes). No cytotoxicity was observed even at concentrations of UCNPs up to 50 µg ml-1. The fate of the UCNPs within the cells was studied by examining their upconversion emission spectra with confocal microscopy and confirming these observations with transmission electron microscopy. It was found that the cellular uptake of the UCNPs occurred primarily by clathrin-mediated endocytosis, whereas they were secreted from the cells via lysosomal exocytosis. The results of this study, focused on the mechanisms of the cellular uptake, localization and secretion of UCNPs, demonstrate, for the first time, the co-localization of UCNPs within discrete cell organelles.

Novel ZnO/MgO/Fe2O3 composite optomagnetic nanoparticles.

A facile sol-gel synthesis of novel ZnO/MgO/Fe2O3 nanoparticles (NPs) is reported and their performance is compared to that of ZnO/MgO. Powder x-ray diffraction (XRD) patterns reveal the crystal structure of the prepared samples. The average particle size of the sample was found to be 4.8 nm. The optical properties were determined by UV-vis absorption and fluorescence measurements. The NPs are stable in biologically relevant solutions (phosphate buffered saline (PBS), 20 mM, pH = 7.0) contrary to ZnO/MgO NPs which degrade in the presence of inorganic phosphate. Superparamagnetic properties were determined with a superconducting quantum interference device (SQUID). Biocompatible and stable in PBS ZnO/MgO/Fe2O3 core/shell composite nanocrystals show luminescent and magnetic properties confined to a single NP at room temperature (19-24 ° C), which may render the material to be potentially useful for biomedical applications.

Spin filtering in a hybrid ferromagnetic-semiconductor microstructure.

We fabricated a hybrid structure in which cobalt and permalloy micromagnets produce a local in-plane spin-dependent potential barrier for high-mobility electrons at the GaAs/AlGaAs interface. Spin effects are observed in ballistic transport in the range of tens of mT of the external field and are attributed to switching between Zeeman and Stern-Gerlach modes--the former dominating at low electron densities.