RESUMEN
Thermoplastic starch/polyvinyl alcohol (TPS/PVA) films have limitations for being used in long-term applications due to starch retrogradation. This leads to plasticizer migration, especially when low molecular weight plasticizers such as glycerol, are used. In this work, we employed mixtures of oligomers based on glycerol citrates with higher molecular weight than glycerol as plasticizers for potato-based TPS/PVA blends obtained by melt-mixing. This constitutes an alternative to reduce plasticizer migration while keeping high swelling degree, and to provide high mechanical performance. The novelty lies in the usage of these oligomers by melt-mixing technique, aspect not deeply explored previously and that represents the first step towards industrial scalability. Prior to the blending process, oligomers mixtures were prepared with different molar ratios of citric acid (0-40 mol%) and added them. This minimizes the undesirable hydrolysis effect of free carboxylic groups on starch chains. The results demonstrated that the migration of plasticizers in TPS/PVA blends decreased by up to 70 % when the citric acid content increased. This reduction was attributed to the higher molecular weight (the majority in the range 764-2060 Da) and the 3D structure of the oligomers compared to using raw glycerol. Furthermore, the films exhibited a 150 % increase in Young's modulus and tensile strength without a reduction in elongation at break, while maintaining a high gel content, due to a moderate crosslinking.
Asunto(s)
Plastificantes , Alcohol Polivinílico , Alcohol Polivinílico/química , Plastificantes/química , Glicerol/química , Poliésteres , Ácido Cítrico/química , Almidón/químicaRESUMEN
The first step towards the production and marketing of bioplastics based on renewable and sustainable materials is to know their behavior at a semi-industrial scale. For this reason, in this work, the properties of thermoplastic starch (TPS)/polyvinyl alcohol (PVA) films plasticized by a green solvent, as the 1-ethyl-3-methylimidazolium acetate ([Emim+][Ac-]) ionic liquid, produced by melt-mixing were studied. These blends were prepared with a different content of [Emim+][Ac-] (27.5-42.5 %wt.) as a unique plasticizer. According to the results, this ionic liquid is an excellent plasticizer due to the transformation of the crystalline structure of the starch to an amorphous state, the increase in flexibility, and the drop in Tg, as the [Emim+][Ac-] amount increases. These findings show that the properties of these biomaterials could be modified in the function of [Emim+][Ac-] content in the formulations of TPS, depending on their final use, thus becoming a functional alternative to conventional polymers.