Green Approach for Synthesis of Silver Nanoparticles with Antimicrobial and Antioxidant Properties from Grapevine Waste Extracts.

The present work aims to study the possibilities of developing silver nanoparticles using natural extracts of grape pomace wastes originating from the native variety of Feteasca Neagra 6 Șt. This study focused on investigating the influence of grape pomace extract obtained by two different extraction methods (classical temperature extraction and microwave-assisted extraction) in the phytosynthesis process of metal nanoparticles. The total phenolic content of the extracts was assessed using the spectrophotometric method with the Folin-Ciocâlteu reagent, while the identification and quantification of specific components were conducted through high-performance liquid chromatography with a diode array detector (HPLC-DAD). The obtained nanoparticles were characterized by UV-Vis absorption spectroscopy, X-ray diffraction (XRD), and transmission electron microscopy (TEM), along with assessing their antioxidant and antimicrobial properties against Gram-positive bacteria. The data collected from the experiments indicated that the nanoparticles were formed in a relatively short period of time (96 h) and, for the experimental variant involving the use of a 1:1 ratio (v/v, grape pomace extract: silver nitrate) for the nanoparticle phytosynthesis, the smallest crystallite sizes (from X-ray diffraction-4.58 nm and 5.14 nm) as well as spherical or semispherical nanoparticles with the lowest average diameters were obtained (19.99-23 nm, from TEM analysis). The phytosynthesis process was shown to enhance the antioxidant properties (determined using the DPPH assay) and the antimicrobial potential (tested against Gram-positive strains) of the nanoparticles, as evidenced by comparing their properties with those of the parent extracts; at the same time, the nanoparticles exhibited a selectivity in action, being active against the Staphylococcus aureus strain while presenting no antimicrobial potential against the Enterococcus faecalis strain.

Enhancing the Mechanical Properties of Corn Starch Films for Sustainable Food Packaging by Optimizing Enzymatic Hydrolysis.

The objective of this study was to investigate the effects of enzymatic hydrolysis using α-amylase from Bacillus amyloliquefaciens on the mechanical properties of starch-based films. The process parameters of enzymatic hydrolysis and the degree of hydrolysis (DH) were optimized using a Box-Behnken design (BBD) and response surface methodology (RSM). The mechanical properties of the resulting hydrolyzed corn starch films (tensile strain at break, tensile stress at break, and Young's modulus) were evaluated. The results showed that the optimum DH for hydrolyzed corn starch films to achieve improved mechanical properties of the film-forming solutions was achieved at a corn starch to water ratio of 1:2.8, an enzyme to substrate ratio of 357 U/g, and an incubation temperature of 48 °C. Under the optimized conditions, the hydrolyzed corn starch film had a higher water absorption index of 2.32 ± 0.112% compared to the native corn starch film (control) of 0.81 ± 0.352%. The hydrolyzed corn starch films were more transparent than the control sample, with a light transmission of 78.5 ± 0.121% per mm. Fourier-transformed infrared spectroscopy (FTIR) analysis showed that the enzymatically hydrolyzed corn starch films had a more compact and solid structure in terms of molecular bonds, and the contact angle was also higher, at 79.21 ± 0.171° for this sample. The control sample had a higher melting point than the hydrolyzed corn starch film, as indicated by the significant difference in the temperature of the first endothermic event between the two films. The atomic force microscopy (AFM) characterization of the hydrolyzed corn starch film showed intermediate surface roughness. A comparison of the data from the two samples showed that the hydrolyzed corn starch film had better mechanical properties than the control sample, with a greater change in the storage modulus over a wider temperature range and higher values for the loss modulus and tan delta, indicating that the hydrolyzed corn starch film had better energy dissipation properties, as shown by thermal analysis. The improved mechanical properties of the resulting film of hydrolyzed corn starch were attributed to the enzymatic hydrolysis process, which breaks the starch molecules into smaller units, resulting in increased chain flexibility, improved film-forming ability, and stronger intermolecular bonds.

Coating Materials to Increase the Stability of Liposomes.

Liposomes carry various compounds with applications in pharmaceutical, food, and cosmetic fields, and the administration route is especially parenteral, oral, or transdermal. Liposomes are used to preserve and release the internal components, thus maintaining the properties of the compounds, the stability and shelf life of the encapsulated products, and their functional benefits. The main problem in obtaining liposomes at the industrial level is their low stability due to fragile phospholipid membranes. To increase the stability of liposomes, phospholipid bilayers have been modified or different coating materials have been developed and studied, both for liposomes with applications in the pharmaceutical field and liposomes in the food field. In the cosmetic field, liposomes need no additional coating because the liposomal formulation is intended to have a fast penetration into the skin. The aim of this review is to provide current knowledge regarding physical and chemical factors that influence stability, coating materials for liposomes with applications in the pharmaceutical and food fields to increase the stability of liposomes containing various sensitive compounds, and absorption of the liposomes and commercial liposomal products obtained through various technologies available on the market.

Accelerated Shelf-Life and Stability Testing of Hydrolyzed Corn Starch Films.

Nonbiodegradable food packaging films are made from plastics such as polyethylene and polypropylene, which can take hundreds of years to decompose and create environmental hazards. On the other hand, biodegradable food packaging films are made from renewable materials such as corn starch or cellulose, that degrade within a few weeks or months and prove to be more sustainable and environmentally friendly. In this work, we used corn starch hydrolyzed (CSH) with α-amylase to prepare a film with biodegradable properties. The film was tested for 60 days at different accelerated temperatures and relative humidity (RH), 13 ± 2 °C and 65 ± 5% RH, 23 ± 2 °C and 45 ± 5% RH, and 33 ± 2 °C and 30 ± 5% RH, to test its durability and stability. Soil biodegradation of the CSH film was evaluated by visual appearance, microscopic observation, weight loss, scanning electron microscopy (SEM), and Fourier-transformed infrared spectroscopy (FTIR) every 6 days. The film was found to have strong hygroscopic properties and was able to last up to 10 months if it is maintained at 20 ± 5 °C and 45 ± 5% RH. After the biodegradability test for at least 30 days, the film showed a significantly higher weight loss rate and microbial activity on the surface of the film, which indicates that the film is biodegradable. The present work recommends biodegradable CSH films as an excellent environmentally friendly choice for dried foods packaging, due to their good shelf life at room temperature, which is beneficial when shipping and storing products, but these films are not suitable for foods with high moisture content.