Biogenic corrosion inhibitor on mild steel protection in concentrated HCl medium.

Turbinaria ornata (TO) extract was tested as green corrosion inhibitor on mild steel (MS) coupons in conc. HCl medium with an efficiency of 100% at 25 g l-1 during 5 min exposure. Antibacterial efficacy performed against 16 S rDNA identified marine biofilming bacteria (MBB) and human pathogenic bacteria (HPB). Maximum inhibition growth was 16 mm on MBB observed in Bacillus megaterium (MBF14 - AB894827) and 20 mm on HPB in Escherichia coli (B5 - NCIM 2931). Similarly, minimum of 10 mm on MBB witnessed in Pseudomonas sp., (MBF9 - AB894829). Toxicity studies proved 50.0% LC50 at 500 µg ml-1 in 24 hrs, whereas Balanus amphitrite resulted in 100% mortality within 12 hrs. Results including weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy, FT-IR and GC-MS confirm 10-Octadecaonic acid as a major corrosion inhibitor from T. ornata and is discovered as a novel antifoulant. Anticorrosion formulation will become available soon.

Multi metal assessment on biofilm formation in offshore environment.

Eight metal and non-metal coupons were exposed to seawater in offshore platform laboratory on biofilm formation in seven days of every month interval time for one year period. Among metal coupons, the highest mean heterotrophic biofilm bacteria population (HBBP) ranges were observed in mild steel (MS) coupon (33.03 to 40.00 [×104] CFUscm-2) and lowest in copper (Cu) coupon (3.0 to 5.1 [×104] CFUscm-2). Non-metal coupons show, highest mean HBBP ranges in glass (GL) coupon (29.6 to 66.0 [×104] CFUscm-2) and lowest in polyvinyl chloride (PVC) coupon (34.4 to 52.5 [×104] CFUscm-2). Within the studied coupons, high HBBP level was witnessed in GL and simultaneously low in Cu due to its toxic leaching product of Cu2O. Gram-positive bacterial deposit show dominated trend in all coupons with increasing order of Cu>SS>MS>PVC>GL>Cu-Ni 70/30>Cu-Ni 90/10>Br and Gram-negative show different in the order of Br>Cu-Ni 90/10>Cu-Ni 70/30>GL>PVC>MS>SS>Cu, respectively. The 16S rDNA sequence confirmed, heterotrophic biofilm Bacillus sp. (Gram-positive) were dominated in all coupons for all months.

Antifouling assessments on biogenic nanoparticles: A field study from polluted offshore platform.

Turbinaria ornata mediated silver nanoparticles (TOAg-NPs) were evaluated for antibacterial activity against 15 biofilm forming bacterial isolates. A field study in natural seawater for 60 days showed antifouling activity of TOAg-NPs on stainless steel coupons (SS-304) coated with Apcomin zinc chrome (AZC) primer. Though TOAg-NPs showed broad spectrum of antibacterial activity, the maximum zone of inhibition was with Escherichiacoli (71.9%) and a minimum with Micrococcus sp. (40%) due to the EPS secretion from Gram-positive bacteria. Compared to control coupons (18.9 [ × 10(3)], 67.0 [× 10(3)], 13.5 [ × 10(4)] and 24.7 [ × 10(4)]CFU/cm(2)), experimental biocide coupons (71.0 [ × 10(2)], 32.0 [ × 10(3)], 82.0 [ × 10(3)] and 11.3 [ × 10(4)]CFU/cm(2)) displayed lesser bacterial population density. Toxicity studies revealed 100% mortality for Balanus amphitrite larvae at 250 µg ml(-1) concentration within 24h, while 56.6% recorded for Artemia marina at the same concentration indicating less toxicity to non target species. It proved that AZC+TOAg-NPs prevent biofouling by its Ag-NS affinity and antimicrobial effectivity.