RSC Adv ; 9(28): 15763-15771, 2019 May 20.
Artículo en Inglés | MEDLINE | ID: mdl-35521395

RESUMEN

To improve their electrochemical performance and structural stability, Na2Li2Ti6O14 (NLTO) nanoparticles were synthesized and then coated with a very thin MgF2 layer. Microscopy confirmed that the MgF2-NLTO particles are about 150-250 nm in size, and that the thickness of the MgF2 layer for the MgF2-NLTO-5 sample is ∼5 nm. Electrochemical measurements showed that the charge-discharge specific capacities of the five samples under a current density of 50 mA g-1 after 100 cycles are 110.4/110.7, 150.7/151.3, 181.1/182.1, 205.7/206.9 and 238.9/239.2 mA h g-1, showing that the performance of MgF2-NLTO-5 is the best among all the samples. Thanks to the thin coating layer, the polarization of the anode was reduced significantly, and its reversibility and lithium diffusion dynamics were also improved obviously. The performance improvement can be attributed to the suppression of surface corrosion and the enhancement of structural stability.

SELECCIÓN DE REFERENCIAS
DETALLE DE LA BÚSQUEDA