Flexible Supercapacitor with Wide Electrochemical Stable Window Based on Hydrogel Electrolyte.

Hydrogel electrolyte can endow supercapacitors with excellent flexibility, which has developed rapidly in recent years. However, the water-rich structures of hydrogel electrolyte are easy to freeze at subfreezing and dry at high temperatures, which will affect its energy storage characteristics. The low energy density of micro supercapacitors also hinders their development. Herein, a strategy is proposed to reduce the free water activity in the hydrogel to improve the operating voltage and the energy density of the device, which is achieved through the synergistic effect of the hydrogel skeleton, N, N'-dimethylformamide (DMF), NaClO4 and water. High concentrations of DMF and NaClO4 are introduced into sodium alginate/polyacrylamide (SA/PAAM) hydrogel through solvent exchange to obtain SA/PAAM/DMF/NaClO4 hydrogel electrolyte, which exhibited a high ionic conductivity of 82.1 mS cm-1, a high breaking strength of 563.2 kPa, and a wide voltage stability window of 3.5 V. The supercapacitor devices are assembled by the process of direct adhesion of the hydrogel electrolyte and  laser induced graphene (LIG). The micro-supercapacitor exhibited an operating voltage of 2.0 V, with a specific capacitance of 2.41 mF cm-2 and a high energy density of 1.34 µWh cm-2, and it also exhibit a high cycle stability, good flexibility, and integration performance.

Superhydrophilic and oleophobic sponges prepared based on Mussel-Inspired chemistry for efficient oil-water separation.

Superhydrophilic/oleophobic materials are considered to be the best materials for achieving oil-water separation, but their preparation is difficult and the existing methods are not universal. In this paper, a two-step modification strategy was used to prepare superhydrophilic/oleophobic sponges by adjusting the polar and nonpolar components of the materials using mussel-inspired chemistry. While remaining superhydrophilic, the modified sponge surface has a maximum contact angle of 135° with different oils in air. The modified sponge exhibited superoleophobicity in water, and the contact angle of oil could reach more than 150°. In addition, the modified sponges were also reusable, chemically stable, and mechanically durable. Its oil-water separation flux was up to 24900 Lm-2 h-1 bar-1 , and the separation efficiency was above 97 %. We believe that this method will provide an environmentally friendly and efficient way to prepare the superhydrophilic/oleophobic materials.