Micro- and Nanostructure Analysis of Vapor-Phase-Grown AlN on Face-to-Face Annealed Sputtered AlN/Nanopatterned Sapphire Substrate Templates.

Micro- and nanostructures in vapor-phase-grown AlN on face-to-face annealed sputtered AlN (FFA Sp-AlN) templates formed on nanopatterned sapphire substrates (NPSS) were comprehensively analyzed using transmission electron microscopy. The comparison between metal-organic vapor-phase epitaxy-grown AlN/FFA Sp-AlN/hole-type NPSS (Sample MOH) and hydride vapor-phase epitaxy-grown AlN/FFA Sp-AlN/cone-type NPSS (Sample HVC) showed apparent differences in the morphology of dislocation propagation, presence of voids, shape of polarity inversion boundaries, and crystal structure on the slope region of NPSS. Notably, cross-sectional and plan-view observations revealed that the quality of FFA Sp-AlN significantly affects the threading dislocation density in the vapor-phase-grown layer. At the slope region of the AlN/NPSS interface, γ-AlON was observed in the MOH sample, while highly misaligned AlN grains were observed in the HVC sample. These characteristic crystal structures affect the occurrence of dislocations via different mechanisms in each sample. This study provides practical information for strategically controlling the micro- and nanostructures formed in AlN/NPSS structures for high-performance AlGaN-based deep-ultraviolet emitters. Supplementary Information: The online version contains supplementary material available at 10.1007/s11664-023-10348-3.

Comprehensive analysis of current leakage at individual screw and mixed threading dislocations in freestanding GaN substrates.

The electrical characteristics of Schottky contacts on individual threading dislocations (TDs) with a screw-component in GaN substrates and the structures of these TDs were investigated to assess the effects of such defects on reverse leakage currents. Micrometer-scale platinum/GaN Schottky contacts were selectively fabricated on screw- and mixed-TD-related etch pits classified based on the pit size. Current-voltage (I-V) data acquired using conductive atomic force microscopy showed that very few of the screw TDs generated anomalously large reverse leakage currents. An analysis of the temperature dependence of the I-V characteristics established that the leakage current conduction mechanisms for the leaky screw TDs differed from those for the other screw and mixed TDs. Specifically, anomalous current leakage was generated by Poole-Frenkel emission and trap-assisted tunneling via distinctive trap states together with Fowler-Nordheim tunneling, with the mechanism changing according to variations in temperature and applied voltage. The leaky TDs were identified as Burgers vector b = 1c closed-core screw TDs having a helical morphology similar to that of other screw TDs generating small leakage currents. Based on the results, we proposed that the atomic-scale modification of the dislocation core structure related to interactions with point defects via dislocation climbing caused different leakage characteristics of the TDs.