We demonstrate an effective method for fabricating large area periodic two-dimensional semiconductor nanostructures by means of single-pulse laser interference. Utilizing a pulsed nanosecond laser with a wavelength of 355 nm, precisely ordered square arrays of nanoholes with a periodicity of 300 nm were successfully obtained on UV photoresist and also directly via a resist-free process onto semiconductor wafers. We show improved uniformity using a beam-shaping system consisting of cylindrical lenses with which we can demonstrate highly regular arrays over hundreds of square micrometers. We propose that our novel observation of direct pattern transfer to GaAs is due to local congruent evaporation and subsequent droplet etching of the surface. The results show that single-pulse interference can provide a rapid and highly efficient route for the realization of wide-area periodic nanostructures on semiconductors and potentially on other engineering materials.
RESUMEN
Precisely ordered arrays of InAs quantum dots are formed on a nanoisland-structured GaAs (100) surface using in situ laser interference during self-assembled molecular beam epitaxial growth. Nanoislands induced by single-pulse four-beam laser interference act as preferential nucleation sites for InAs quantum dots and result in site occupation dependent on the size of nanoislands, the InAs coverage, and the laser parameters. By optimizing the growth and interference conditions, regular dense ordering of single dots was obtained for the first time using this in situ noninvasive approach. The photoluminescence spectra of the resulting quantum dot arrays with a period of 300 nm show good optical quality and uniformity. This technique paves the way for the rapid large-scale fabrication of arrays of single dots to enable quantum information technology device platforms.