Aim: To determine the effect of an herbal toothpaste containing Little Ironweed and Java Tea, on reducing dentine permeability in vitro. Materials and Methods: Dentine discs from human mandibular third molars were divided into three groups and brushed with herbal toothpaste, nonherbal toothpaste, or deionized water. Each group was immersed in artificial saliva (AS) or 6% citric acid. The permeability of each dentine disc was evaluated before and after saliva or acid challenge using a fluid filtration system. The morphology of dentine discs after treatment was observed using scanning electron microscopy (SEM). The mean permeabilities were statistically analyzed using analysis of variance and Tukey's test. Results: The nonherbal and herbal toothpaste groups demonstrated reduced dentine permeability. AS immersion decreased dentine permeability in both toothpaste groups with values lower than the control group. Dentine permeability values increased after acid immersion in the toothpaste groups and were similar to each other. SEM revealed small granular crystal-like and round particles on the dentine surface and opening of dentinal tubules of both toothpaste groups. More dentinal tubules were opened after brushing with deionized water. Conclusions: The reduction of dentine permeability caused by the herbal toothpaste was similar to that of the nonherbal toothpaste after brushing and the simulated oral conditions. Both herbal plants have the possibility to alleviate clinical hypersensitivity by reducing dentine permeability. Little Ironweed and Java Tea in the toothpaste composition is a potential choice for treating hypersensitive dentine.
RESUMEN
This study investigated the influence of different surface treatments on unfiring or firing zirconia-reinforced lithium silicate (ZLS) glass-ceramics. Celtra Duo and IPS e.max CAD blocks were cut and process following manufacturer protocols. The specimen surface was treated with seven different protocols. Two ceramic blocks with the same surface treatment were bonded with luting agent and prepared for mini-interfacial fracture toughness tests (mini-iFT). The specimens were tested after 1-week storage. The data was statistically analyzed using two-way ANOVA and Dunnett's T3 comparison (α=0.05). The highest mini-iFT of both Celtra Duo unfired and fired was shown in the HF+S group, which was not significantly different from HF+S+UA. For IPS e.max CAD, the mini-iFT was higher in the groups treated with hydrofluoric acid. Additional adhesive after silane application did not significantly improve bonding effectiveness. Therefore, surface treatment with hydrofluoric acid and silane is recommended for both unfiring and firing ZLS glass ceramics.