RESUMEN
The importance of the microstzructure of silicone hydrogels is widely appreciated but is poorly understood and minimally investigated. To ensure comfort and eye health, these materials must simultaneously exhibit both high oxygen and high water permeability. In contrast with most conventional hydrogels, the water content and water structuring within silicone hydrogels cannot be solely used to predict permeability. The materials achieve these opposing requirements based on a composite of nanoscale domains of oxygen-permeable (silicone) and water-permeable hydrophilic components. This study correlated characteristic ion permeation coefficients of a selection of commercially available silicone hydrogel contact lenses with their morphological structure and chemical composition. Differential scanning calorimetry measured the water structuring properties through subdivision of the freezing water component into polymer-associated water (loosely bound to the polymer matrix) and ice-like water (unimpeded with a melting point close to that of pure water). Small-angle x-ray scattering, and environmental scanning electron microscopy techniques were used to investigate the structural morphology of the materials over a range of length scales. Significant, and previously unrecognized, differences in morphology between individual materials at nanometer length scales were determined; this will aid the design and performance of the next generation of ocular biomaterials, capable of maintaining ocular homeostasis.
Asunto(s)
Materiales Biocompatibles/química , Hidrogeles/química , Siliconas/química , Lentes de Contacto Hidrofílicos , Diseño de Equipo , Humanos , Interacciones Hidrofóbicas e Hidrofílicas , Ensayo de Materiales , Oxígeno , Permeabilidad , AguaRESUMEN
In situ wide-angle X-ray scattering (WAXS) has been measured during the spin coating process used to make the precursor films required for the formation of thin films of perovskite. A customized hollow axis spin coater was developed to permit the scattered X-rays to be collected in transmission geometry during the deposition process. Spin coating is the technique most commonly used in laboratories to make thin perovskite films. The dynamics of spin-casting MAPbI3-x Cl x and FAPbI3-x Cl x films have been investigated and compared to investigate the differences between the dynamics of MAPbI3-x Cl x and FAPbI3-x Cl x film formation. In particular, we focus on the crystallization dynamics of the precursor film formation. When casting MAPbI3-x Cl x , we observed relatively fast 1D crystallization of the intermediate product MA2PbI3Cl. There was an absence of the desired perovskite phase formed directly; it only appeared after an annealing step that converted the MA2PbI3Cl to MAPbI3. In contrast, slower crystallization via a 3D precursor was observed for FAPbI3-x Cl x film formation compared to MAPbI3-x Cl x . Another important finding was that some FAPbI3-x Cl x perovskite was generated directly during spin-casting before annealing. These findings indicate that there are significant differences between the crystallization pathways for these two perovskite materials. These are likely to explain the differences in the lifetimes of the resulting perovskite solar cell devices produced using FA and MA cations.
RESUMEN
In bulk heterojunction donor-acceptor (D-A) blends, high photovoltaic yields require charge carrier separation to outcompete geminate recombination. Recently, evidence for long-range electron transfer mechanisms has been presented, avoiding strongly-bound interfacial charge transfer (CT) states. However, due to the lack of specific optical probes at the D-A interface, a detailed quantification of the long-range processes has not been feasible, until now. Here, we present a transient absorption study of long-range processes in a unique phase consisting of perylene diimide (PDI) crystals intercalated with polyfluorene (PFO), as a widely used non-fullerene electron acceptor and donor, respectively. The intercalated PDI : PFO phase possesses specific well-separated spectral features for the excited states at the D-A interface. By use of femtosecond spectroscopy we reveal the excitation dynamics in this blend. PDI excitons undergo a clear symmetry-breaking charge separation in the PDI bulk, which occurs within several hundred femtoseconds, thus outcompeting excimer formation, known to limit charge separation yields when PDI is used as an acceptor. In contrast, PFO excitons are dissociated with very high yields in a one-step long-range process, enabled by large delocalization of the PFO exciton wavefunction. Moreover, both scenarios circumvent the formation of strongly-bound interfacial CT states and enable a targeted interfacial design for bulk heterojunction blends with near unity charge separation yields.
RESUMEN
The field of active colloids is attracting significant interest to both enable applications and allow investigations of new collective colloidal phenomena. One convenient active colloidal system that has been much studied is spherical Janus particles, where a hemispherical coating of platinum decomposes hydrogen peroxide to produce rapid motion. However, at present producing these active colloids relies on a physical vapor deposition (PVD) process, which is difficult to scale and requires access to expensive equipment. In this work, it is demonstrated that Pickering emulsion masking combined with solution phase metallization can produce self-motile catalytic Janus particles. Comparison of the motion and catalytic activity with PVD colloids reveals a higher catalytic activity for a given thickness of platinum due to the particulate nature of the deposited coating. This Pickering emulsion based method will assist in producing active colloids for future applications and aid experimental research into a wide range of active colloid phenomena.
RESUMEN
1,8-Diiodooctane (DIO) is an additive used in the processing of organic photovoltaics and has previously been reported, on the basis of small-angle X-ray scattering (SAXS) measurements, to deflocculate nano-aggregates of [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) in chlorobenzene. We have critically re-examined this finding in a series of scattering measurements using both X-rays and neutrons. With SAXS, we find that the form of the background solvent scattering is influenced by the presence of DIO, that there is substantial attenuation of the X-rays by the background solvent and that there appears to be beam-induced aggregation. All three factors call into question the suitability of SAXS for measurements on these samples. By contrast, small-angle neutron scattering (SANS) measurements, performed at concentrations of 15 mg ml-1 up to and including 40 mg ml-1, show no difference in the aggregation state for PC71BM in chlorobenzene with and without 3% DIO; we find PC71BM to be molecularly dissolved in all solvent cases. In situ film thinning measurements of spin-coated PC71BM solution with the DIO additive dry much slower. Optical imaging shows that the fullerene films possess enhanced molecular mobility in the presence of DIO and it is this which, we conclude, improves the nanomorphology and consequently solar cell performance. We propose that any compatible high boiling solvent would be expected to show the same behaviour.
RESUMEN
Microwave annealing has emerged as an alternative to traditional thermal annealing approaches for optimising block copolymer self-assembly. A novel sample environment enabling small angle X-ray scattering to be performed in situ during microwave annealing is demonstrated, which has enabled, for the first time, the direct study of the effects of microwave annealing upon the self-assembly behavior of a model, commercial triblock copolymer system [polystyrene-block-poly(ethylene-co-butylene)-block-polystyrene]. Results show that the block copolymer is a poor microwave absorber, resulting in no change in the block copolymer morphology upon application of microwave energy. The block copolymer species may only indirectly interact with the microwave energy when a small molecule microwave-interactive species [diethylene glycol dibenzoate (DEGDB)] is incorporated directly into the polymer matrix. Then significant morphological development is observed at DEGDB loadings ≥6 wt%. Through spatial localisation of the microwave-interactive species, we demonstrate targeted annealing of specific regions of a multi-component system, opening routes for the development of "smart" manufacturing methodologies.
RESUMEN
A new approach is described herein, where neutron reflectivity measurements that probe changes in the density profile of thin films as they absorb material from the gas phase have been combined with a Love wave based gravimetric assay that measures the mass of absorbed material. This combination of techniques not only determines the spatial distribution of absorbed molecules, but also reveals the amount of void space within the thin film (a quantity that can be difficult to assess using neutron reflectivity measurements alone). The uptake of organic solvent vapours into spun cast films of polystyrene has been used as a model system with a view to this method having the potential for extension to the study of other systems. These could include, for example, humidity sensors, hydrogel swelling, biomolecule adsorption or transformations of electroactive and chemically reactive thin films. This is the first ever demonstration of combined neutron reflectivity and Love wave-based gravimetry and the experimental caveats, limitations and scope of the method are explored and discussed in detail.
RESUMEN
This note reports changes to the author list and additional funding sources for [Appl. Opt.55, 6102 (2016)].APOPAI0003-693510.1364/AO.55.006102.
RESUMEN
The production and utilization of microbubbles are rapidly becoming of major importance in a number of global applications, from biofuel production to medical imaging contrast agents. Many aspects of bubble formation have been studied, with diffuser characteristics (such as pore size, pore orientation) and gas flow rate all being shown to influence the bubble formation process. However, very little attention has been paid to the influence of surface wettability of the diffuser and the detailed role it plays at the triple interface of gas-liquid-diffuser. Here, we investigate how the wettability of the diffuser surface impacts upon the dynamics of the bubble formation process and examine the effect both at the orifice and upon the bubble cloud produced as a result of the engineered wetting variations. Experimental data shown here indicate the presence of a switching point at a contact angle of θ = 90°, where bubble size vastly changes. When a surface exhibits a contact angle below 90°, bubbles emitted from it are considerably smaller than those emitted from a surface with an angle in excess of 90°. This effect is observable over flow rates ranging from 2.5 to 60 mL min(-1) from a single pore, an array of controlled pores, and the industrially relevant and commercially available sintered metals and sintered ceramic diffusers. It is also observed for both thiol and silane modified surfaces, encompassing a range of contact angles from 10° to 110°. In addition, the importance of the diffuser plate's surface topography is discussed, with elevated roughness acting to reduce the effect of surface chemistry in some instances.
RESUMEN
Spin-coating offers a facile fabrication route for the production of high quality colloidal crystals, which have potential as photonic band-gap materials. This paper presents the results of direct observations of the self-assembly of latex colloids during spin-coating through the use of stroboscopic microscopy. We have been able to identify several mechanisms by which self-assembly occurs, depending upon the dispersion properties, such as particle weight fraction, solvent volatility and viscosity. Through the use of stroboscopic microscopy we have directly observed ordering occurring due to high concentrations of colloid particles (where volatility is relatively low), resulting in the formation of regular close packed ordered particle arrays. Conversely when the system in spun-cast from a much more volatile solvent, highly disordered non-equilibrium arrangements of particles form. When spin-coating a low concentration, low volatility dispersion, ordering is dominated by the occurrence of capillary drying fronts, which drag the particles into ordered arrangements. At a volatility intermediate to that of water and ethanol, ordering occurring predominantly via shear forces. Finally when the volatility is increased beyond the shear ordering regime, excessive shear leads to the occurrence of drying fronts within the system and so again, capillary forces induce a large degree of order within the final film.
RESUMEN
The curvilinear velocity (VCL) of boar spermatozoa between standard microscopy glassware decreases when the slides are coated with the hydrophobic polymer polystyrene (PS) compared with the less hydrophobic poly(methyl methacrylate) (PMMA) coating. Sperm from three boars were observed and analyzed using particle tracking software. The VCL did not differ significantly between coatings of different thickness, indicating no penetration of the sperm into the coating and that only the surface layer of the polymer film interacts with the sperm and buffer medium. The VCL of sperm between PS-coated surfaces was significantly reduced compared with PMMA surfaces (P < 0.0001), and this was attributed to a stronger hydrophobic effect between PS and water. The size of this effect varied between different boars, perhaps as a consequence of variations in hydrophobicity of sperm from different boars or different ejaculates. The modification of surface properties in this way may improve our understanding of sperm behavior and may provide improvements to assisted conception techniques as animal or human sperm used in assisted conception are frequently manipulated in laboratory plastics as part of diagnostic procedures (e.g., semen analysis) or before injection into an oocyte or during the co-incubation with the oocyte in IVF. Controlling the velocity of sperm using the interaction properties of inert polymer coatings could lead to new sperm selection procedures for clinical use or the development of model systems to better understand sperm-surface interactions.
Asunto(s)
Interacciones Hidrofóbicas e Hidrofílicas , Motilidad Espermática/fisiología , Espermatozoides/química , Propiedades de Superficie , Porcinos , Animales , Masculino , Plásticos , Polimetil Metacrilato/química , Poliestirenos/química , Análisis de Semen , Agua/químicaRESUMEN
Results of a pioneering study are presented in which for the first time, crystallization, phase separation and Marangoni instabilities occurring during the spin-coating of polymer blends are directly visualized, in real-space and real-time. The results provide exciting new insights into the process of self-assembly, taking place during spin-coating, paving the way for the rational design of processing conditions, to allow desired morphologies to be obtained.
RESUMEN
We report on a novel experimental study of a pH-responsive polyelectrolyte brush at the silicon/D2O interface. A poly[2-(diethylamino)ethyl methacrylate] brush was grown on a large silicon crystal which acted as both a substrate for a neutron reflectivity solid/liquid experiment but also as an FTIR-ATR spectroscopy crystal. This arrangement has allowed for both neutron reflectivities and FTIR spectroscopic information to be measured in parallel. The chosen polybase brush shows strong IR bands which can be assigned to the N-D(+) stretch, D2O, and a carbonyl group. From such FTIR data, we are able to closely monitor the degree of protonation along the polymer chain as well as revealing information concerning the D2O concentration at the interface. The neutron reflectivity data allows us to determine the physical brush profile normal to the solid/liquid interface along with the corresponding degree of hydration. This combined approach makes it possible to quantify the charge on a polymer brush alongside the morphology adopted by the polymer chains.
Asunto(s)
Metacrilatos/química , Nylons/química , Óxido de Deuterio/química , Electrólitos/química , Concentración de Iones de Hidrógeno , Estructura Molecular , Difracción de Neutrones , Silicio/química , Espectroscopía Infrarroja por Transformada de Fourier , Propiedades de SuperficieRESUMEN
The propulsion velocity of active colloids that asymmetrically catalyze a chemical reaction is probed experimentally as a function of their sizes. It is found that over the experimentally accessible range, the velocity decays as a function of size, with a rate that is compatible with an inverse size dependence. A diffusion-reaction model for the concentrations of the fuel and waste molecules that takes into account a two-step process for the asymmetric catalytic activity on the surface of the colloid is shown to predict a similar behavior for colloids at the large size limit, with a saturation for smaller sizes.
Asunto(s)
Coloides/química , Modelos Químicos , Catálisis , Simulación por Computador , Difusión , Movimiento (Física)RESUMEN
Nonconductive Janus particle swimmers made by coating fluorescent polymer beads with hemispheres of platinum have been fully characterized using video microscopy to reveal that they undergo propulsion in hydrogen peroxide fuel away from the catalytic platinum patch. The platinum coating shadows the fluorescence signal from half of each swimmer to allow the orientation to be observed directly and correlated quantitatively with the resulting swimming direction. The observed swimmer direction is consistent with both the bubble release and diffusiophoretic propulsion mechanisms.
RESUMEN
In this paper, we show that silicon surfaces patterned with poly(methacrylic acid) brushes are able to control the Brownian motion of 2-3 µm iron particles, which sediment onto the surface in aqueous solution and experience differences in repulsive force depending upon their position. Differences in repulsion lead to different gravitational potential energies across the surface, which gives bias to the Brownian motion taking place. Three regimes have been identified depending upon the brush height: (i) no control of Brownian motion when the brush height is small, (ii) Brownian motion that is influenced by the polymer brush when the brush 17 height is intermediate, (iii) Brownian motion that is confined by polymer brush barriers when the brush height is greatest. The height of brush found necessary to significantly influence iron particle motion was small at 39 nm or 2% of the particle diameter.
Asunto(s)
Hierro/química , Ácidos Polimetacrílicos/química , Silicio/química , Hidrólisis , Tamaño de la Partícula , Soluciones , Propiedades de Superficie , Agua/químicaRESUMEN
Spin coating polymer blend thin films provides a method to produce multiphase functional layers of high uniformity covering large surface areas. Applications for such layers include photovoltaics and light-emitting diodes where performance relies upon the nanoscale phase separation morphology of the spun film. Furthermore, at micrometer scales, phase separation provides a route to produce self-organized structures for templating applications. Understanding the factors that determine the final phase-separated morphology in these systems is consequently an important goal. However, it has to date proved problematic to fully test theoretical models for phase separation during spin coating, due to the high spin speeds, which has limited the spatial resolution of experimental data obtained during the coating process. Without this fundamental understanding, production of optimized micro- and nanoscale structures is hampered. Here, we have employed synchronized stroboscopic illumination together with the high light gathering sensitivity of an electron-multiplying charge-coupled device camera to optically observe structure evolution in such blends during spin coating. Furthermore the use of monochromatic illumination has allowed interference reconstruction of three-dimensional topographies of the spin-coated film as it dries and phase separates with nanometer precision. We have used this new method to directly observe the phase separation process during spinning for a polymer blend (PS-PI) for the first time, providing new insights into the spin-coating process and opening up a route to understand and control phase separation structures.
Asunto(s)
Nanotecnología/métodos , Polímeros/química , Análisis de Fourier , Luz , Ensayo de Materiales , Membranas Artificiales , Microscopía de Fuerza Atómica/métodos , Nanoestructuras/química , Solventes/química , Propiedades de SuperficieRESUMEN
A series of high molecular weight poly(styrene-b-isoprene) block copolymers with optical properties defined by composition in a non-selective solvent were studied using simultaneous ultra small angle X-ray scattering (USAXS) and optical spectrometry. A small magnitude shear produces ordered and oriented states in the copolymer solutions that persist for extended periods of time, and also have superior optical properties that are directly attributable to the mesoscopic block copolymer (BCP) morphology. We have demonstrated that the optical transmission of these materials can be tuned by the addition of low molecular weight poly(isoprene) and poly(styrene) to swell their respective domains within the diblock copolymer. The optical transmission peak for the diblocks could be tuned; from 380 nm-440 nm for the 670k diblock, 425 nm-540 nm for the 850k diblock and 541 nm-625 nm for the 1 million diblock by altering the solution concentration and composition. The full width at half maximum that can be achieved for the optical transmission peaks is as small as 15 nm at 473 nm with a Δλ/λ of 0.03, highlighting the high quality ordering in these systems. Also a small shift in the transmission peak wavelength was observed across a wide angle of view (15 nm at 30°) suggesting that these materials could be used for large area narrow band optical filters.
RESUMEN
A class of artificial microswimmers with combined translational and rotational self-propulsion is studied experimentally. The chemically fueled microswimmers are made of doublets of Janus colloidal beads with catalytic patches that are positioned at a fixed angle relative to one another. The mean-square displacement and the mean-square angular displacement of the active doublets are analyzed in the context of a simple Langevin description, using which the physical characteristics of the microswimmers such as the spontaneous translational and rotational velocities are extracted. Our work suggests strategies for designing microswimmers that could follow prescribed cycloidal trajectories.
Asunto(s)
Biomimética , Movimiento (Física) , Coloides , Cinética , Microesferas , Platino (Metal)/química , Rotación , Procesos EstocásticosRESUMEN
We report the effect of a range of monovalent sodium salts on the molecular equilibrium swelling of a simple synthetic microphase separated poly(methyl methacrylate)-block-poly(2-(diethylamino)ethyl methacrylate)-block-poly(methyl methacrylate) (PMMA(88)-b-PDEA(223)-b-PMMA(88)) pH-responsive hydrogel. Sodium acetate, sodium chloride, sodium bromide, sodium iodide, sodium nitrate and sodium thiocyanate were selected for study at controlled ionic strength and pH; all salts are taken from the Hofmeister series (HS). The influence of the anions on the expansion of the hydrogel was found to follow the reverse order of the classical HS. The expansion ratio of the gel measured in solutions containing the simple sodium halide salts (NaCl, NaBr, and NaI) was found to be strongly related to parameters which describe the interaction of the ion with water; surface charge density, viscosity coefficient, and entropy of hydration. A global study which also included nonspherical ions (NaAce, NaNO(3) and NaSCN) showed the strongest correlation with the viscosity coefficient. Our results are interpreted in terms of the Collins model, where larger ions have more mobile water in the first hydration cage immediately surrounding the gel, therefore making them more adhesive to the surface of the stationary phase of the gel and ultimately reducing the level of expansion.