Composite bone graft of CaO-MgO-SiO2 glass-ceramics and CaSO4 ceramics for boosting bone formation rate.

This study develops a composite bone graft of CaO-MgO-SiO2 glass-ceramic and CaSO4 [abbreviated as (CMS)3-x(CS)x] via the sponge replication technique with weight fractions of x = 0, 1, 1.5, 2, and 3. The (CMS)1.5(CS)1.5 composite displays a superior degradability and, a suitable compressive strength of ∼3 MPa, and excellent cell proliferation and differentiation. The in vivo rat femur test in the hybrid-pore (CMS)1.5(CS)1.5 composite granules achieves a higher rate of bone formation, which is ∼2.7 times better than that of the commercial HAP/ß-TCP at 12 weeks. Improved expressions of osteocyte and mature osteocyte marker genes, namely (Spp1, Dmp1, and Fgf23), were observed in the (CMS)1.5(CS)1.5 group, indicating a faster differentiation into mature bone tissue. The ions release of (CMS)1.5(CS)1.5 through the ERK1/2 signaling pathway promotes osteogenic differentiation. The high bone generation rate can be attributed to faster active ions release and modified surface topography. This work highlights an excellent bone graft candidate for clinical applications in orthopedic surgery.

High Sensitivity SERS Substrate of a Few Nanometers Single-Layer Silver Thickness Fabricated by DC Magnetron Sputtering Technology.

Surface-enhanced Raman spectroscopy (SERS) is commonly used for super-selective analysis through nanostructured silver layers in the environment, food quality, biomedicine, and materials science. To fabricate a high-sensitivity but a more accessible device of SERS, DC magnetron sputtering technology was used to realize high sensitivity, low cost, a stable deposition rate, and rapid mass production. This study investigated various thicknesses of a silver film ranging from 3.0 to 12.1 nm by field emission scanning electron microscope, X-ray diffraction, and X-ray photoelectron spectroscopy. In the rhodamine 6G (R6G) testing irradiated by a He-Ne laser beam, the analytical enhancement factor (AEF) of 9.35 × 108, the limit of detection (LOD) of 10-8 M, and the relative standard deviation (RSD) of 1.61% were better than the other SERS substrates fabricated by the same DC sputtering process because the results showed that the 6 nm thickness silver layer had the highest sensitivity, stability, and lifetime. The paraquat and acetylcholine analytes were further investigated and high sensitivity was also achievable. The proposed SERS samples were evaluated and stored in a low humidity environment for up to forty weeks, and no spectrum attenuation could be detected. Soon, the proposed technology to fabricate high sensitivity, repeatability, and robust SERS substrate will be an optimized process technology in multiple applications.