RESUMEN
The primary drawback of concrete lies in its low tensile strength, prompting the development of various solutions to enhance this aspect. A notable approach is the utilization of Prestressed Reinforced Concrete (PRC) with tendons, aimed at bolstering its tensile strength. As the use of diverse tendon types in the PRC continues to surge, a review becomes imperative to delve into this evolution. Therefore, this study delved into the engineering characteristics, performance, and evolution of different tendon varieties, encompassing both steel and composite options. Despite certain drawbacks associated with employing composite materials such as Fiber Reinforced Polymer (FRP) tendons - such as heightened costs, limited availability of composite materials, and intricate manufacturing processes - there are distinct advantages and merits to incorporating FRP composite tendons in the realm of construction. In this respect, Carbon FRP tendons exhibited superior strength, comparable to their steel counterparts. Glass FRP tendons, lacking metallic components, possessed non-magnetic properties, rendering them resistant to corrosion. Additionally, Aramid FRP tendons boasted low flammability and exceptional resistance to elevated temperatures. Lastly, Basalt FRP tendons offered sustainability, rust resistance, and non-corrosiveness. The findings derived from this review study serve as a valuable resource for researchers seeking to advance the applications of steel tendons and FRP composite materials within the construction industry.
RESUMEN
Around 8% of the global carbon dioxide emissions, are generated during cement manufacturing, which also involves significant use of raw materials, leading to adverse environmental effects. Consequently, extensive research is being conducted worldwide to explore the feasibility of utilizing different industrial waste by-products as alternatives to cement in concrete production. Fly ash (FA), Metakaolin (MK), Silica fume (SF), and ground granulated blast furnace slag (GGBS) are potential industrial materials that can serve as cement substitutes in pervious concrete. However, there exist conflicting findings in the literature regarding the impact of industrial supplementary cementitious materials (ISCMs) as partial cement replacements on the physical, mechanical, and durability properties of pervious concrete. The aim of this review is to investigate the feasibility and potential benefits of using ISCMs and compare them as partial cement replacements in the production of pervious concrete. The analysis primarily examines the effect of ISCMs as partial cement replacements on cementitious properties, including properties of ISMCs, mechanical properties, and durability of pervious concrete. The influence of ISCMs primarily stems from their pozzolanic reaction and filler characteristics. SF has the highest reactivity due to its high surface area and amorphous structure, resulting in a rapid pozzolanic reaction. GGBS and FA have moderate reactivity, while MK has relatively low reactivity due to its crystalline structure. Results from various studies indicate that the addition of FA, SF, and MK up to approximately 20% leads to a reduction in porosity and permeability while improving compressive strength and durability due to the filler effect of SF and MK. Incorporating GGBS increases permeability slightly while causing a slight decrease in compressive strength. The range of permeability and compressive strength for pervious concrete incorporating FA, SF, GGBS and MK were 0.17-1.46 cm/s and 4-35 MPa, 0.56-2.28 cm/s and 3.1-35 MPa, 0.19-0.64 cm/s and 8-42 MPa, 0.10-1.28 cm/s and 5.5-41 MPa, respectively, which are in the acceptable range for non-structural application of pervious concrete. In conclusion, it is possible to produce sustainable pervious concrete by substituting up to 20% of cement with FA, SF, GGBS, and MK, thereby reducing cement consumption, carbon footprint, energy usage, and air pollution associated with conventional cement production. However, further research is required to systematically assess the durability properties, long-term behavior, and, develop models for analyzing CO2 emissions and cost considerations of pervious concrete containing ISMCs.
RESUMEN
The dataset currently available comprises data on the removal rates of heavy metals (Ba, Se, Cr, Fe, Cd, As, and Co) through the incorporation of seashells and palm oil kernel shells into pervious concrete for stormwater treatment. Stormwater runoff was collected from commercial areas in Taman University, Skudai, Johor, Malaysia. The stormwater samples underwent filtration and were preserved in high-density polyethylene (HDPE) bottles at a temperature of 4 °C for use as incoming water. The outgoing water, referred to as effluent, was obtained from tests performed on pervious concrete samples after a curing period of 28 days. The pervious concrete mixes were created with a water-to-binder ratio (w/b ratio) of 32% and a sand ratio of 10%. Three different levels of palm oil kernel shell and seashell content were used as coarse aggregate replacements: 0%, 25%, and 50%. Two single-size group were considered for both palm oil kernel shell and seashell: (6.3-9.5 mm) and (4.75-6.3 mm). Heavy metal analyses were conducted on the influent and effluent using a PerkinElmer ELAN 6100 Series Inductively Coupled Plasma- Mass Spectrometer (ICP-MS). The available datasets consist of both raw and analyzed data.