RESUMEN
Developing commercially viable electrocatalyst lies at the research hotspot of rechargeable Zn-air batteries, but it is still challenging to meet the requirements of energy efficiency and durability in realistic applications. Strategic material design is critical to addressing its drawbacks in terms of sluggish kinetics of oxygen reactions and limited battery lifespan. Herein, a "raisin-bread" architecture is designed for a hybrid catalyst constituting cobalt nitride as the core nanoparticle with thin oxidized coverings, which is further deposited within porous carbon aerogel. Based on synchrotron-based characterizations, this hybrid provides oxygen vacancies and Co-Nx -C sites as the active sites, resulting from a strong coupling between CoOx Ny nanoparticles and 3D conductive carbon scaffolds. Compared to the oxide reference, it performs enhanced stability in harsh electrocatalytic environments, highlighting the benefits of the oxynitride. Furthermore, the 3D conductive scaffolds improve charge/mass transportation and boost durability of these active sites. Density functional theory calculations reveal that the introduced N species into hybrid can synergistically tune the d-band center of cobalt and improve its bifunctional activity. As a result, the obtained air cathode exhibits bifunctional overpotential of 0.65 V and a battery lifetime exceeding 1350 h, which sets a new record for rechargeable Zn-air battery reported so far.
RESUMEN
Developing high-efficiency and low-cost oxygen-evolving electrodes in anion exchange membrane (AEM) water electrolysis technology is one of the major challenges. Herein, it is demonstrated that the surface corrosion of a conventional Ni foam electrode in the presence of Fe3+ and V3+ cations can transform it into an electrode with a high catalytic performance for oxygen evolution reaction (OER). The corroded electrode consists of a ternary NiFeV layered double hydroxide (LDH) nanosheet array supported on the Ni foam surface. This NiFeV LDH electrode achieves an OER current density of 100 mA cm-2 at an overpotential of 272 mV in 1 m KOH, outperforming the IrO2 catalyst by 180 mV. Density functional theory calculations reveal that the unique structure and the presence of vanadium in NiFeV LDH play a key role in achieving improved OER activity. When coupled with a commercial Pt/C cathode catalyst, the resulting AEM water electrolyzer achieves a cell current density as high as 2.1 A cm-2 at a voltage of only 1.8 Vcell in 1 m KOH, which is similar to the performance of the proton exchange membrane water electrolyzer obtained from the IrO2 and Pt/C catalysts pair.
RESUMEN
Developing high performance, highly stable, and low-cost electrodes for the oxygen evolution reaction (OER) is challenging in water electrolysis technology. However, Ir- and Ru-based OER catalysts with high OER efficiency are difficult to commercialize as precious metal-based catalysts. Therefore, the study of OER catalysts, which are replaced by non-precious metals and have high activity and stability, are necessary. In this study, a copper-cobalt oxide nanosheet (CCO) electrode was synthesized by the electrodeposition of copper-cobalt hydroxide (CCOH) on Ni foam followed by annealing. The CCOH was annealed at various temperatures, and the structure changed to that of CCO at temperatures above 250 °C. In addition, it was observed that the nanosheets agglomerated when annealed at 300 °C. The CCO electrode annealed at 250 °C had a high surface area and efficient electron conduction pathways as a result of the direct growth on the Ni foam. Thus, the prepared CCO electrode exhibited enhanced OER activity (1.6 V at 261 mA/cm2) compared to those of CCOH (1.6 V at 144 mA/cm2), Co3O4 (1.6 V at 39 mA/cm2), and commercial IrO2 (1.6 V at 14 mA/cm2) electrodes. The optimized catalyst also showed high activity and stability under high pH conditions, demonstrating its potential as a low cost, highly efficient OER electrode material.
RESUMEN
Under acidic conditions, IrO2 exhibits high catalytic activity with respect to the oxygen evolution reaction (OER). However, the practical application of Ir-based catalysts is significantly limited owing to their high cost in addition to the scarcity of the metal. Therefore, it is necessary to improve the efficiency of the utilization of such catalysts. In this study, IrO2-coated Ti felt (IrO2/Ti) electrodes were prepared as high-efficiency catalysts for the OER under acidic conditions. By controlling the surface roughness of the Ti substrate via wet etching, the optimum Ti substrate surface area for application in the IrO2/Ti electrode was determined. Additionally, the IrO2 film that was electrodeposited on the 30 min etched Ti felt had a large surface area and a uniform morphology. Furthermore, there were no micro-cracks and the electrode obtained (IrO2/Ti-30) exhibited superior catalytic performance with respect to the OER, with a mass activity of 362.3 A g Ir - 1 at a potential of 2.0 V (vs. RHE) despite the low Ir loading (0.2 mg cm-2). Therefore, this proposed strategy for the development of IrO2/Ti electrodes with substrate surface control via wet etching has potential for application in the improvement of the efficiency of catalyst utilization with respect to the OER.
RESUMEN
We prepare three-dimensional honeycomb-like Cu0.81Co2.19O4 nanosheet arrays supported by Ni foam via electrochemical codeposition of cobalt and copper hydroxides on Ni foam followed by thermal oxidation. The codeposition with Cu changes the morphology of the cobalt hydroxide deposit to form honeycomb-like nanostructures, significantly decreasing the onset potential for oxygen evolution. The Cu0.81Co2.19O4 anode displays an exceptionally low overpotential of 290 mV at a current density of 10 mA cm-2 in 1 M KOH, and an anion-exchange membrane water electrolysis cell employing the above anode achieves a current density of 100 mA cm-2 at 1.68 V in 0.1 M KOH.