RESUMEN
Energy storage and modern electronics industries are in essential need of high dielectric and highly flexible materials. In this study, polyacrylonitrile and reduced graphene oxide (PAN/GO) were prepared by electrospinning. The composite morphology produced a homogeneous, smooth, and flexible surface with high tensile strength and durability. The diameter of the fibers in the composite mats ranged from 232 to 592 nm. The X-ray diffraction pattern recording displayed a sharp peak characteristic centered between 20 and 30° angles with a maximum degree of crystallinity of 86.23%. The evaluation of the Fourier-transform infrared spectrum indicated the interaction between GO and PAN through hydrogen bonds. The differential scanning calorimetry measurements confirmed that GO acted as a nucleating agent that improves the thermal stability of the composite. The dielectric properties exhibited the relative permittivity of the composite of 86.4 with a dielectric loss (tan δ) of 4.97 at 102 Hz, and the maximum conductivity was achieved at 34.9 × 10-6 Sm-1 at high frequencies.
RESUMEN
Graphene oxide derived from palm kernel shells (rGOPKS) and polyacrylonitrile (PAN) were electrospun into composite fiber mats and evaluated as supercapacitor electrode materials. Their morphologies and crystalline properties were examined, and chemical interactions between rGOPKS and PAN were investigated. The diameters of individual fibers in the rGOPKS/PAN composite mats ranged from 1.351 to 1506 µm and increased with increasing rGOPKS content. A broad peak centered near 23° in the X-ray diffraction (XRD) pattern of rGOPKS corresponded to the (002) planes in graphitic carbon. Characteristic rGOPKS and PAN peaks were observed in the XRD patterns of all the composite fibers, and their Fourier-transform infrared (FTIR) spectra indicated hydrogen bond formation between rGOPKS and PAN. The composite fiber mats had smooth and homogeneous surfaces, and they exhibited excellent flexibility and durability. Their electrochemical performance as electrodes was assessed, and a maximum specific capacitance of 203 F g-1 was achieved. The cycling stability of this electrode was excellent, and it retained over 90% of its capacitance after 5000 cycles. The electrode had an energy density of 17 W h kg-1 at a power density of 3000 W kg-1. Dielectric results showed a nanofiber composite dielectric constant of 72.3 with minor leakage current (tan δ) i.e., 0.33 at 51 Hz. These results indicate that the rGOPKS/PAN composite fibers have great promise as supercapacitor electrode materials.