Herein, NaP and LTA zeolites were successfully synthesised from woody biomass ash with alkali fusion-assisted hydrothermal method by altering the NaOH/ash ratio, crystallisation time and crystallisation temperature. In order to reduce the synthesis costs, NaP zeolite was synthesised with no additional source of aluminium and silicon. The synthesised zeolites were utilized for the monocomponent and simultaneous adsorption of Cu(II), Cd(II), Pb(II) and Zn(II) ions. The maximum adsorbed amount of metals had the trend Pb(II) > Cu(II) > Cd(II) > Zn(II) for both NaP and LTA zeolite. The kinetic data fit well to the pseudo-second order model indicating that chemisorption is the rate-limiting step. The isotherm data were well described with Sips and Redlich-Peterson models indicating a non-ideal heterogeneous adsorption process. Maximum adsorption capacity of NaP zeolite was 42.9 mg/g for Cu(II) and 117.3 mg/g for Cd(II), while LTA had 140.1 mg/g and 223.5 mg/g for Cu(II) and Cd(II) ions, respectively.
RESUMEN
In this study, a series of layered double hydroxide (ZxAy LDH) material was synthesized with different molar ratios and calcination temperatures to remove phosphate and sulfate ions from synthetic solution. ZxAy LDH was characterized by XRD, FTIR, BET and SEM analysis. The highest removal was obtained by Z3A200 LDH that is LDH with a Zn-Al molar ratio of 3 and calcined at 200⯰C. The leaching of Zn and Al was more under highly acidic pH compared to pH 5 and 8. Adsorption isotherms data had a good fit with Langmuir model and maximum adsorption under optimum conditions led to 2.6-2.72 and 1.02-1.31â¯mmol/g for phosphate and sulfate, respectively. Kinetic studies have been performed by applying reaction based models and diffusion-based models, which indicated the chemisorption interaction for Z3A200 by a controlling step of the macro-pore and micro-pore diffusion for phosphate and sulfate adsorption process onto Z3A200, respectively. Thermodynamic studies showed that adsorption process onto Z3A200 was endothermic and spontaneous. Thus, phosphate and sulfate adsorption by using optimized Zn-Al LDH appears to be a promising adsorbent for their removal.