RESUMEN
An experimental approach is described in which well-defined perturbations of the gas feed into an Ambient Pressure X-ray Photoelectron Spectroscopy (APXPS) cell are fully synchronized with the time-resolved x-ray photoelectron spectroscopy data acquisition. These experiments unlock new possibilities for investigating the properties of materials and chemical reactions mediated by their surfaces, such as those in heterogeneous catalysis, surface science, and coating/deposition applications. Implementation of this approach, which is termed perturbation-enhanced APXPS, at the SPECIES beamline of MAX IV Laboratory is discussed along with several experimental examples including individual pulses of N2 gas over a Au foil, a multi-pulse titration of oxygen vacancies in a pre-reduced TiO2 single crystal with O2 gas, and a sequence of alternating precursor pulses for atomic layer deposition of TiO2 on a silicon wafer substrate.
RESUMEN
Herein, we report an atomic layer deposition (ALD) process for Cu2O thin films using copper(II) acetate [Cu(OAc)2] and water vapor as precursors. This precursor combination enables the deposition of phase-pure, polycrystalline, and impurity-free Cu2O thin films at temperatures of 180-220 °C. The deposition of Cu(I) oxide films from a Cu(II) precursor without the use of a reducing agent is explained by the thermally induced reduction of Cu(OAc)2 to the volatile copper(I) acetate, CuOAc. In addition to the optimization of ALD process parameters and characterization of film properties, we studied the Cu2O films in the fabrication of photoconductor devices. Our proof-of-concept devices show that approximately 20 nm thick Cu2O films can be used for photodetection in the visible wavelength range and that the thin film photoconductors exhibit improved device characteristics in comparison to bulk Cu2O crystals.
RESUMEN
Two heteroleptic titanium precursors were investigated for the atomic layer deposition (ALD) of titanium dioxide using ozone as the oxygen source. The precursors, titanium (N,N'-diisopropylacetamidinate)tris(isopropoxide) (Ti(O(i)Pr)3(N(i)Pr-Me-amd)) and titanium bis(dimethylamide)bis(isopropoxide) (Ti(NMe2)2(O(i)Pr)2), exhibit self-limiting growth behavior up to a maximum temperature of 325 °C. Ti(NMe2)2(O(i)Pr)2 displays an excellent growth rate of 0.9 Å/cycle at 325 °C while the growth rate of Ti(O(i)Pr)3(N(i)Pr-Me-amd) is 0.3 Å/cycle at the same temperature. In the temperature range of 275-325 °C, both precursors deposit titanium dioxide in the anatase phase. In the case of Ti(NMe2)2(O(i)Pr)2, high-temperature X-ray diffraction (HTXRD) studies reveal a thickness-dependent phase change from anatase to rutile at 875-975 °C. X-ray photoelectron spectroscopy (XPS) indicates that the films have high purity and are close to the stoichiometric composition. Reaction mechanisms taking place during the ALD process were studied in situ with quadrupole mass spectrometry (QMS) and quartz crystal microbalance (QCM).
RESUMEN
The effect of fluorine substitution on the aromaticity of polycyclic hydrocarbons (PAH) is investigated. Magnetically induced current densities, current pathways, and current strengths, which can be used to assess molecular aromaticity, are calculated using the gauge-including magnetically induced current method (GIMIC). The degree of aromaticity of the individual rings is compared to those obtained using calculated nucleus-independent chemical shifts at the ring centers (NICS(0) and NICS(0)(zz)). Calculations of explicitly integrated current strengths for selected bonds show that the aromatic character of the investigated polycyclic hydrocarbons is weakened upon fluorination. In contrast, the NICS(0) values for the fluorinated benzenes increase noteworthy upon fluorination, predicting a strong strengthening of the aromatic character of the arene rings. The integrated current strengths also yield explicit current pathways for the studied molecules. The current pathways of the investigated linear polyacenes, pyrene, anthanthrene, coronene, ovalene, and phenanthro-ovalene are not significantly affected by fluorination. NISC(0) and NICS(0)(zz) calculations provide contradictory degrees of aromaticity of the fused individual ring. Obtained NICS values do not correlate with the current strengths circling around the individual rings.