RESUMEN
Background: This research study aimed to evaluate and compare the capability of four various bite registration materials to reproduce precise interocclusal relationships in the vertical dimension. Materials and Methods: Ideal maxillary and mandibular casts were mounted on the semi-adjustable articulator in maximum intercuspation after mock tooth preparation on 46, 47, and 48. Models were scanned by the Medit T500 Dental Lab Scanner, and initial reading was noted at the predetermined points. Ten interocclusal bite registrations were made using four materials (CADbite, Jet Bite, Ramitec, and Aluwax). The mandibular model was demounted and again remounted using the interocclusal records, and the final reading was noted after scanning. Results: Ramitec showed superior results when compared to polyvinyl bite registration material and Aluwax, but the differences between Ramitec, CADbite, and Jet Bite were nonsignificant. Conclusions: Although all four materials are suitable for clinical use, elastomeric materials showed superior results. In that, polyether was found to be the best.
RESUMEN
PURPOSE: Acrylic denture base tends to fracture frequently during their service due to poor strength. The surface roughness of denture base is a critical property because denture base with rough surface will cause accumulation of food particles ,thereby leading plaque retention . Microbes such as candida albicans are seen inhabitating the surface. MATERIALS AND METHODS: Conventional heat cure denture base reins(DPI) and heat cure denture base resin with incorporation of 15wt% aluminium oxide was studied in two groups with 20 samples each. A mold of size 65 mm × 10 mm × 3 mm (ISO Standard) was obtained by investing brass rectangles. About forty specimens were prepared. Specimens were divided into two groups (n = 20) coded A and B. Group A was the control group (n = 20) without addition of aluminum oxide. Group B was the experimental group (n = 20) with addition of 15 wt % aluminum oxide. All the specimens were stored in distilled water for 14 days. The flexural strength was measured using a three-point bending test in a universal testing machine, and the surface roughness was measured using contact-type profilometer. RESULTS: Incorporation of 15wt% aluminum oxide leads to a significant increase in flexural strength and surface roughness of conventional heat-cure denture base resin.