RESUMEN
Herein, we report the Suzuki-Miyaura catalyst-transfer polycondensation (SCTP) of triolborate-type carbazole monomers, i.e., potassium 3-(6-bromo-9-(2-octyldodecyl)-9H-carbazole-2-yl)triolborate (M1) and potassium 2-(7-bromo-9-(2-octyldodecyl)-9H-carbazole-2-yl) triolborate (M2), as an efficient and versatile approach for precisely synthesizing poly[9-(2-octyldodecyl)-3,6-carbazole] (3,6-PCz) and poly[9-(2-octyldodecyl)-2,7-carbazole] (2,7-PCz), respectively. The SCTP of triolborate-type carbazole monomers was performed in a mixture of THF/H2O using an initiating system consisted of 4-iodobenzyl alcohol, Pd2(dba)3â¢CHCl3, and t-Bu3P. In the SCTP of M1, cyclic by-product formation was confirmed, as reported for the corresponding pinacolboronate-type monomer. By optimizing the reaction temperature and reaction time, we successfully synthesized linear end-functionalized 3,6-PCz for the first time. The SCTP of M2 proceeded with almost no side reaction, yielding 2,7-PCz with a functional initiator residue at the α-chain end. Kinetic and block copolymerization experiments demonstrated that the SCTP of M2 proceeded in a chain-growth and controlled/living polymerization manner. This is a novel study on the synthesis of 2,7-PCz via SCTP. By taking advantage of the well-controlled nature of this polymerization system, we demonstrated the synthesis of high-molecular-weight 2,7-PCzs (Mn = 5-38 kg mol-1) with a relatively narrow ÐM (1.35-1.48). Furthermore, we successfully synthesized fluorene/carbazole copolymers as well as 2,7-PCz-containing diblock copolymers, demonstrating the versatility of the present polymerization system as a novel synthetic strategy for well-defined polycarbazole-based materials.
RESUMEN
The mechanical properties and structural design flexibility of charge-trapping polymer electrets have led to their widespread use in organic field-effect transistor (OFET) memories. For example, in the electrets of polyfluorene-based conjugated/insulating block copolymers (BCPs), the confined fiberlike polyfluorene nanostructures in the insulating polymer matrix act as effective hole-trapping sites, leading to controllable memory performance through the design of BCPs. However, few studies have reported intrinsically stretchable charge-trapping materials and their memory device applications, and a practical method to correlate the thin-film morphology of BCP electrets with their charge-trapping ability has not yet been developed. In this study, a series of new conjugated/insulating BCPs, poly(9,9-di-n-hexyl-2,7-fluorene)-block-poly(δ-decanolactone)s (PF-b-PDLx, x = 1-3), as stretchable hole-trapping materials are reported. The linear and branched PDL blocks with comparable molecular weights were used to investigate the effect of polymer architecture on morphology and device performance. Moreover, the coverage area of the polyfluorene nanofibers on the BCP films was extracted from atomic force microscopy images, which can be correlated with the trapping density of the polymer electrets. The branched PDL segments not only improve stretchability but also tailor crystallinity and phase separation of the BCPs, thus increasing their charge-trapping ability. The OFET memory device with PF-b-PDL3 as the electret layer exhibited the largest memory window (102 V) and could retain its performance at up to 100% strain. This research highlights the importance of the BCP design for developing stretchable charge-trapping materials.
RESUMEN
We demonstrated a novel strategy for the preparation of light down-converter by combining rod-coil block copolymers with perovskite quantum dots (QDs) through electrospinning. Reports have shown that polymer deformability can be enhanced by incorporating a soft segment and controlled by varying the rod/coil ratio. Therefore, we first synthesized the rod-coil block copolymer through the click reaction of polyfluorene (PF) and poly(n-butyl acrylate) (PBA). Next, the CsPbBr3@PF8k-b-PBA12k composite fibers were fabricated by blending perovskite through electrospinning. Optical spectral evidence demonstrated the success of the strategy, as light down-converters were prepared through the controlled variance of QD/polymer ratios to achieve tunable color and stretchability. This result reveals the potential of using rod-coil block copolymers to fabricate color-tunable perovskite light down-converters.