Nanoscale X-ray Imaging of Composition and Ferroelastic Domains in Heterostructured Perovskite Nanowires: Implications for Optoelectronic Devices.

Metal halide perovskites (MHPs) have garnered significant interest as promising candidates for nanoscale optoelectronic applications due to their excellent optical properties. Axially heterostructured CsPbBr3-CsPb(Br(1-x)Clx)3 nanowires can be produced by localized anion exchange of pregrown CsPbBr3 nanowires. However, characterizing such heterostructures with sufficient strain and real space resolution is challenging. Here, we use nanofocused scanning X-ray diffraction (XRD) and X-ray fluorescence (XRF) with a 60 nm beam to investigate a heterostructured MHP nanowire as well as a reference CsPbBr3 nanowire. The nano-XRD approach gives spatially resolved maps of composition, lattice spacing, and lattice tilt. Both the reference and exchanged nanowire show signs of diverse types of ferroelastic domains, as revealed by the tilt maps. The chlorinated segment shows an average Cl composition of x = 66 and x = 70% as measured by XRD and XRF, respectively. The XRD measurements give a much more consistent result than the XRF ones. These findings are consistent with photoluminescence measurements, showing x = 73%. The nominally unexchanged segment also has a small concentration of Cl, as observed with all three methods, which we attribute to diffusion after processing. These results highlight the need to prevent such unwanted processes in order to fabricate optoelectronic devices based on MHP heterostructures.

Perovskite-Compatible Electron-Beam-Lithography Process Based on Nonpolar Solvents for Single-Nanowire Devices.

Metal halide perovskites (MHPs) have been studied intensely as the active material for optoelectronic devices. Lithography methods for perovskites remain limited because of the solubility of perovskites in polar solvents. Here, we demonstrate an electron-beam-lithography process with a poly(methyl methacrylate) resist based on the nonpolar solvents o-xylene, hexane, and toluene. Features down to 50 nm size are created, and photoluminescence of CsPbBr3 nanowires exhibits no degradation. We fabricate metal contacts to single CsPbBr3 nanowires, which show a strong photoresponsivity of 0.29 A W-1. The presented method is an excellent tool for nanoscale MHP science and technology, allowing for the fabrication of complex nanostructures.

Free-Standing Metal Halide Perovskite Nanowire Arrays with Blue-Green Heterostructures.

Vertically aligned metal halide perovskite (MHP) nanowires are promising for various optoelectronic applications, which can be further enhanced by heterostructures. However, present methods to obtain free-standing vertically aligned MHP nanowire arrays and heterostructures lack the scalability needed for applications. We use a low-temperature solution process to prepare free-standing vertically aligned green-emitting CsPbBr3 nanowires from anodized aluminum oxide templates. The length is controlled from 1 to 20 µm by the precursor amount. The nanowires are single-crystalline and exhibit excellent photoluminescence, clear light guiding and high photoconductivity with a responsivity of 1.9 A/W. We demonstrate blue-green heterostructured nanowire arrays by converting the free-standing part of the nanowires to CsPbCl1.1Br1.9 in an anion exchange process. Our results demonstrate a scalable, self-aligned, and lithography-free approach to achieve high quality free-standing MHP nanowires arrays and heterostructures, offering new possibilities for optoelectronic applications.

Single-Crystalline Perovskite Nanowire Arrays for Stable X-ray Scintillators with Micrometer Spatial Resolution.

X-ray scintillation detectors based on metal halide perovskites have shown excellent light yield, but they mostly target applications with spatial resolution at the tens of micrometers level. Here, we use a one-step solution method to grow arrays of 15-µm-long single-crystalline CsPbBr3 nanowires (NWs) in an AAO (anodized aluminum oxide) membrane template, with nanowire diameters ranging from 30 to 360 nm. The CsPbBr3 nanowires in AAO (CsPbBr3 NW/AAO) show increasing X-ray scintillation efficiency with decreasing nanowire diameter, with a maximum photon yield of ∼5 300 ph/MeV at 30 nm diameter. The CsPbBr3 NW/AAO composites also display high radiation resistance, with a scintillation-intensity decrease of only ∼20-30% after 24 h of X-ray exposure (integrated dose 162 Gyair) and almost no change after ambient storage for 2 months. X-ray images can distinguish line pairs with a spacing of 2 µm for all nanowire diameters, while slanted edge measurements show a spatial resolution of ∼160 lp/mm at modulation transfer function (MTF) = 0.1. The combination of high spatial resolution, radiation stability, and easy fabrication makes these CsPbBr3 NW/AAO scintillators a promising candidate for high-resolution X-ray imaging applications.