RESUMEN
OBJECTIVE: Viscoelastic properties of articular cartilage have been characterised at physiological frequencies. However, studies investigating the interaction between cartilage and subchondral bone and the influence of underlying bone histomorphometry on the viscoelasticity of cartilage are lacking. METHOD: Dynamic Mechanical Analysis (DMA) has been used to quantify the dynamic viscoelasticity of bovine tibial plateau osteochondral cores, over a frequency sweep from 1 to 88 Hz. Specimens (approximately aged between 18 and 30 months) were neither osteoarthritic nor otherwise compromised. A maximum nominal stress of 1.7 MPa was induced. Viscoelastic properties of cores have been compared with that of its components (cartilage and bone) in terms of the elastic and viscous components of both structural stiffness and material modulus. Micro-computed tomography scans were used to quantify the histomorphological properties of the subchondral bone. RESULTS: Opposing frequency-dependent loss stiffness, and modulus, trends were witnessed for osteochondral tissues: for cartilage it increased logarithmically (P < 0.05); for bone it decreased logarithmically (P < 0.05). The storage stiffness of osteochondral cores was logarithmically frequency-dependent (P < 0.05), however, the loss stiffness was typically frequency-independent (P > 0.05). A linear relationship between the subchondral bone plate (SBP) thickness and cartilage thickness (P < 0.001) was identified. Cartilage loss modulus was linearly correlated to bone mineral density (BMD) (P < 0.05) and bone volume (P < 0.05). CONCLUSION: The relationship between the subchondral bone histomorphometry and cartilage viscoelasticity (namely loss modulus) and thickness, have implications for the initiation and progression of osteoarthritis (OA) through an altered ability of cartilage to dissipate energy.
Asunto(s)
Huesos/patología , Cartílago Articular/patología , Animales , Huesos/diagnóstico por imagen , Cartílago Articular/diagnóstico por imagen , Bovinos , Elasticidad , Tibia/diagnóstico por imagen , Tibia/patología , Viscosidad , Microtomografía por Rayos XRESUMEN
BACKGROUND: Mitral valve failure can require repair or replacement. Replacement bioprosthetic valves are treated with glutaraldehyde prior to implantation. The aim of this study was to determine the changes in mechanical properties following glutaraldehyde fixation of mitral valve chordae. METHODS: To investigate the impact of glutaraldehyde on mitral valve chordae, 24 basal chordae were dissected from four porcine hearts. Anterior and posterior basal (including strut) chordae were used. All 24 chordae were subjected to a sinusoidally varying load (mean level 2N, dynamic amplitude 2N) over a frequency range of 0.5-10 Hz before and after glutaraldehyde treatment. RESULTS: The storage and loss modulus of all chordal types decreased following glutaraldehyde fixation. The storage modulus ranged from: 108 to 119 MPa before fixation and 67.3-87.4 MPa following fixation for basal chordae; 52.3-58.4 MPa before fixation and 47.9-53.5 MPa following fixation for strut chordae. Similarly, the loss modulus ranged from: 5.47 to 6.25 MPa before fixation and 3.63-4.94 MPa following fixation for basal chordae; 2.60-2.97 MPa before fixation and 2.31-2.93 MPa following fixation for strut chordae. CONCLUSION: The viscoelastic properties of mitral valve chordae are affected by glutaraldehyde fixation; in particular, the reduction in storage moduli decreased with an increase in chordal diameter.
Asunto(s)
Cuerdas Tendinosas/efectos de los fármacos , Cuerdas Tendinosas/metabolismo , Elasticidad/efectos de los fármacos , Glutaral/farmacología , Válvula Mitral , Animales , Porcinos , Viscosidad/efectos de los fármacosRESUMEN
Cracks can occur in the articular cartilage surface due to the mechanical loading of the synovial joint, trauma or wear and tear. However, the propagation of such cracks under different frequencies of loading is unknown. The objective of this study was to determine the effect of frequency of loading on the growth of a pre-existing crack in cartilage specimens subjected to cyclic tensile strain. A 2.26mm crack was introduced into cartilage specimens and crack growth was achieved by applying a sinusoidally varying tensile strain at frequencies of 1, 10 and 100Hz (i.e. corresponding to normal, above normal and up to rapid heel-strike rise times, respectively). These frequencies were applied with a strain of between 10-20% and the crack length was measured at 0, 20, 50, 100, 500, 1000, 5000 and 10,000 cycles of strain. Crack growth increased with increasing number of cycles. The maximum crack growth was 0.6 ± 0.3 (mean ± standard deviation), 0.8 ± 0.2 and 1.1 ± 0.4mm at frequencies of 1, 10 and 100Hz, respectively following 10,000 cycles. Mean crack growth were 0.3 ± 0.2 and 0.4 ± 0.2 at frequencies of 1 and 10Hz, respectively. However, this value increased up to 0.6 ± 0.4mm at a frequency of 100Hz. This study demonstrates that crack growth was greater at higher frequencies. The findings of this study may have implications in the early onset of osteoarthritis. This is because rapid heel-strike rise times have been implicated in the early onset of osteoarthritis.
Asunto(s)
Cartílago Articular/patología , Cartílago/patología , Osteoartritis/fisiopatología , Membrana Sinovial/patología , Animales , Bovinos , Elasticidad , Marcha , Humanos , Estrés Mecánico , Resistencia a la Tracción , Viscosidad , Soporte de PesoRESUMEN
The urinary bladder is an organ which facilitates the storage and release of urine. The bladder can develop tumours and bladder cancer is a common malignancy throughout the world. There is a consensus that there are differences in the mechanical properties of normal and malignant tissues. However, the viscoelastic properties of human bladder tumours at the macro-scale have not been previously studied. This study investigated the viscoelastic properties of ten bladder tumours, which were tested using dynamic mechanical analysis at frequencies up to 30Hz. The storage modulus ranged between 0.052MPa and 0.085MPa while the loss modulus ranged between 0.019MPa and 0.043MPa. Both storage and loss moduli showed frequency dependent behaviour and the storage modulus was higher than the loss modulus for every frequency tested. Viscoelastic properties may be useful for the development of surgical trainers, surgical devices, computational models and diagnostic equipment.