Manipulation of the electrical and memory properties of MoS2 field-effect transistors by highly charged ion irradiation.

Field-effect transistors based on molybdenum disulfide (MoS2) exhibit a hysteresis in their transfer characteristics, which can be utilized to realize 2D memory devices. This hysteresis has been attributed to charge trapping due to adsorbates, or defects either in the MoS2 lattice or in the underlying substrate. We fabricated MoS2 field-effect transistors on SiO2/Si substrates, irradiated these devices with Xe30+ ions at a kinetic energy of 180 keV to deliberately introduce defects and studied the resulting changes of their electrical and hysteretic properties. We find clear influences of the irradiation: while the charge carrier mobility decreases linearly with increasing ion fluence (up to only 20% of its initial value) the conductivity actually increases again after an initial drop of around two orders of magnitude. We also find a significantly reduced n-doping (≈1012 cm-2) and a well-developed hysteresis after the irradiation. The hysteresis height increases with increasing ion fluence and enables us to characterize the irradiated MoS2 field-effect transistor as a memory device with remarkably longer relaxation times (≈ minutes) compared to previous works.

Revealing the Heterogeneity of Large-Area MoS2 Layers in the Electrocatalytic Hydrogen Evolution Reaction.

The electrocatalytic activity concerning the hydrogen evolution reaction (HER) of micrometer-sized MoS2 layers transferred on a glassy carbon surface was evaluated by scanning electrochemical cell microscopy (SECCM) in a high-throughput approach. Multiple areas on single or multiple MoS2 layers were assessed using a hopping mode nanocapillary positioning with a hopping distance of 500 nm and a nanopipette size of around 55 nm. The locally recorded linear sweep voltammograms revealed a high lateral heterogeneity over the MoS2 sheet regarding their HER activity, with currents between -40 and -60 pA recorded at -0.89 V vs. reversible hygrogen electrode over about 4400 different measured areas on the MoS2 sheet. Stacked MoS2 layers did not show different electrocatalytic activity than the single MoS2 sheet, suggesting that the interlayer resistance influences the electrocatalytic activity less than the resistances induced by possible polymer residues or water layers formed between the transferred MoS2 sheet and the glassy carbon electrode.